CN103030301A - Glass frosting powder for processing anti-dazzle glass and preparation method thereof - Google Patents
Glass frosting powder for processing anti-dazzle glass and preparation method thereof Download PDFInfo
- Publication number
- CN103030301A CN103030301A CN2012105578305A CN201210557830A CN103030301A CN 103030301 A CN103030301 A CN 103030301A CN 2012105578305 A CN2012105578305 A CN 2012105578305A CN 201210557830 A CN201210557830 A CN 201210557830A CN 103030301 A CN103030301 A CN 103030301A
- Authority
- CN
- China
- Prior art keywords
- ammonium
- glass
- powder
- preparation
- starch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses glass frosting powder for processing anti-dazzle glass and a preparation method thereof. The glass frosting powder is prepared by mixing the following raw materials in percentage by weight: 44-48% of ammonium bifluoride, 10-14% of ammonium bifluoride, 6-10% of ammonium fluosilicate, 6-10% of potassium fluoborate, 3-7% of calcium fluoride, 3-7% of precipitated barium sulphate, 3-7% of barium carbonate, 1-5% of polyethylene glycol, 0.5-1.5% of Arabic gum, 1-3% of starch and 3-7% of organic acid. The preparation method comprises the steps of grinding the raw materials into powder respectively, then pouring the fine powder into a mixer, and uniformly mixing.
Description
Technical field
The present invention relates to a kind of frosting powder for the processing anti-glare glass, the invention still further relates to the preparation method of this frosting powder.
Background technology
Chinese patent CN101654330B discloses a kind of like this glass anti-dazzle liquid and has utilized the method for this anti-dazzle liquid processing anti-glare glass, and this anti-dazzle liquid is mixed according to following weight proportion by following raw materials according: gum arabic powder 10-22 part, hydrochloric acid 40-45 part, hydrofluoric acid 20-23 part, ammonium bifluoride 10-15 part, polyoxyethylene glycol 10-20 part; The method is carried out according to the following step: ⑴ cleans glass; ⑵ the rubbish glass after will clean in anti-dazzle liquid is processed 30-120 second; ⑶ cool; ⑷ spray clear Xian, freeze-day with constant temperature.With above-mentioned prescription make for paste, it makes simple, crosses the net scope large, do not produce burr, be not subjected to the impact of temperature and humidity, relatively be suitable for fast making Glass Craft, but because Sudan Gum-arabic has thickening property, again because added deal is larger, therefore, this anti-dazzle liquid flowability is relatively poor, and is more coarse with the anti-glare glass surface that above-mentioned patent is produced, should not clean, should not polish, increase production cost, be not suitable with scale operation.
Summary of the invention
The purpose of this invention is to provide a kind of good fluidity, can make anti-glare glass smooth surface exquisiteness, should clean, should polish, can reduce production costs again, adapt to frosting powder that is used for the processing anti-glare glass of scale operation and preparation method thereof.
For achieving the above object, the present invention is used for the frosting powder of processing anti-glare glass, is mixed according to following weight proportion by following raw materials according: ammonium bifluoride 44～48%, Neutral ammonium fluoride 10～14%, ammonium silicofluoride 6～10%, potassium fluoborate 6～10%, Calcium Fluoride (Fluorspan) 3～7%, process white 3～7%, barium carbonate 3～7%, polyoxyethylene glycol 1～5%, Sudan Gum-arabic 0.5～1.5%, starch 1～3%, organic acid 3～7%.
Mixed according to following weight proportion by following raw materials according: ammonium bifluoride 46%, Neutral ammonium fluoride 12%, ammonium silicofluoride 8%, potassium fluoborate 8%, Calcium Fluoride (Fluorspan) 5%, process white 5%, barium carbonate 5%, polyoxyethylene glycol 3%, Sudan Gum-arabic 1%, starch 2%, organic acid 5%.
The preparation method who is used for the frosting powder of processing anti-glare glass, first with ammonium bifluoride 44～48%, Neutral ammonium fluoride 10～14%, ammonium silicofluoride 6～10%, potassium fluoborate 6～10%, Calcium Fluoride (Fluorspan) 3～7%, process white 3～7%, barium carbonate 3～7%, polyoxyethylene glycol 1～5%, Sudan Gum-arabic 0.5～1.5%, starch 1～3%, organic acid 3～7% grinds to form respectively fine powder, and then pours above-mentioned fine powder into stirrer and mix to evenly.
After adopting this working method, because the Sudan Gum-arabic deal is less, its good fluidity, the smooth exquisiteness of glass surface after the processing of frosting powder, reflectivity is lower than 1%, and mist degree should clean, should polish thereby reach between 4%-20%, can reduce production costs again, adapt to the purpose of scale operation.
EmbodimentBelow in conjunction with embodiment, the present invention is done to describe further.
Embodiment 1:
The frosting powder that is used for the processing anti-glare glass, mixed according to following weight proportion by following raw materials according: ammonium bifluoride 44%, Neutral ammonium fluoride 10%, ammonium silicofluoride 10%, potassium fluoborate 10%, Calcium Fluoride (Fluorspan) 3%, process white 3%, barium carbonate 3.5%, polyoxyethylene glycol 5%, Sudan Gum-arabic 1.5%, starch 3%, organic acid 7%.
The preparation method who is used for the frosting powder of processing anti-glare glass, first with ammonium bifluoride 44%, Neutral ammonium fluoride 10%, ammonium silicofluoride 10%, potassium fluoborate 10%, Calcium Fluoride (Fluorspan) 3%, process white 3%, barium carbonate 3.5%, polyoxyethylene glycol 5%, Sudan Gum-arabic 1.5%, starch 3%, organic acid 7% grinds to form respectively fine powder, and then pours above-mentioned fine powder into stirrer and mix to evenly.
Embodiment 2:
Be used for the frosting powder of processing anti-glare glass, mixed according to following weight proportion by following raw materials according: ammonium bifluoride 46%, Neutral ammonium fluoride 12%, ammonium silicofluoride 8%, potassium fluoborate 8%, Calcium Fluoride (Fluorspan) 5%, process white 5%, barium carbonate 5%, polyoxyethylene glycol 3%, Sudan Gum-arabic 1%, starch 2%, organic acid 5%.
The preparation method who is used for the frosting powder of processing anti-glare glass, first with ammonium bifluoride 46%, Neutral ammonium fluoride 12%, ammonium silicofluoride 8%, potassium fluoborate 8%, Calcium Fluoride (Fluorspan) 5%, process white 5%, barium carbonate 5%, polyoxyethylene glycol 3%, Sudan Gum-arabic 1%, starch 2%, organic acid 5% grinds to form respectively fine powder, and then pours above-mentioned fine powder into stirrer and mix to evenly.
Embodiment 3:
The frosting powder that is used for the processing anti-glare glass, mixed according to following weight proportion by following raw materials according: ammonium bifluoride 48%, Neutral ammonium fluoride 14%, ammonium silicofluoride 6%, potassium fluoborate 6%, Calcium Fluoride (Fluorspan) 7%, process white 7%, barium carbonate 3%, polyoxyethylene glycol 1%, Sudan Gum-arabic 1.5%, starch 2.5%, organic acid 4%.
The preparation method who is used for the frosting powder of processing anti-glare glass, first with ammonium bifluoride 48%, Neutral ammonium fluoride 14%, ammonium silicofluoride 6%, potassium fluoborate 6%, Calcium Fluoride (Fluorspan) 7%, process white 7%, barium carbonate 3%, polyoxyethylene glycol 1%, Sudan Gum-arabic 1.5%, starch 2.5%, organic acid 4% grinds to form respectively fine powder, and then pours above-mentioned fine powder into stirrer and mix to evenly.
Embodiment 4:
The frosting powder that is used for the processing anti-glare glass, mixed according to following weight proportion by following raw materials according: ammonium bifluoride 47%, Neutral ammonium fluoride 13%, ammonium silicofluoride 7%, potassium fluoborate 7%, Calcium Fluoride (Fluorspan) 6%, process white 6%, barium carbonate 3%, polyoxyethylene glycol 2.5%, Sudan Gum-arabic 0.5%, starch 1%, organic acid 7%.
The preparation method who is used for the frosting powder of processing anti-glare glass, first with ammonium bifluoride 47%, Neutral ammonium fluoride 13%, ammonium silicofluoride 7%, potassium fluoborate 7%, Calcium Fluoride (Fluorspan) 6%, process white 6%, barium carbonate 3%, polyoxyethylene glycol 2.5%, Sudan Gum-arabic 0.5%, starch 1%, organic acid 7% grinds to form respectively fine powder, and then pours above-mentioned fine powder into stirrer and mix to evenly.
Embodiment 5:
Be used for the frosting powder of processing anti-glare glass, mixed according to following weight proportion by following raw materials according: ammonium bifluoride 45%, Neutral ammonium fluoride 11%, ammonium silicofluoride 9%, potassium fluoborate 9%, Calcium Fluoride (Fluorspan) 4%, process white 4%, barium carbonate 7%, polyoxyethylene glycol 5%, Sudan Gum-arabic 1%, starch 2%, organic acid 3%.
The preparation method who is used for the frosting powder of processing anti-glare glass, first with ammonium bifluoride 44～48%, Neutral ammonium fluoride 10～14%, ammonium silicofluoride 6～10%, potassium fluoborate 6～10%, Calcium Fluoride (Fluorspan) 3～7%, process white 3～7%, barium carbonate 3～7%, polyoxyethylene glycol 1～5%, Sudan Gum-arabic 0.5～1.5%, starch 1～3%, organic acid 3～7% grinds to form respectively fine powder, and then pours above-mentioned fine powder into stirrer and mix to evenly.
Claims (3)
1. frosting powder that is used for the processing anti-glare glass, it is characterized in that: mixed according to following weight proportion by following raw materials according: ammonium bifluoride 44～48%, Neutral ammonium fluoride 10～14%, ammonium silicofluoride 6～10%, potassium fluoborate 6～10%, Calcium Fluoride (Fluorspan) 3～7%, process white 3～7%, barium carbonate 3～7%, polyoxyethylene glycol 1～5%, Sudan Gum-arabic 0.5～1.5%, starch 1～3%, organic acid 3～7%.
According to claim 1 for processing anti-glare glass the frosting powder, it is characterized in that: mixed according to following weight proportion by following raw materials according: ammonium bifluoride 46%, Neutral ammonium fluoride 12%, ammonium silicofluoride 8%, potassium fluoborate 8%, Calcium Fluoride (Fluorspan) 5%, process white 5%, barium carbonate 5%, polyoxyethylene glycol 3%, Sudan Gum-arabic 1%, starch 2%, organic acid 5%.
3. preparation method who is used for the frosting powder of processing anti-glare glass is characterized in that: first with ammonium bifluoride 44～48%, and Neutral ammonium fluoride 10～14%, ammonium silicofluoride 6～10%, potassium fluoborate 6～10%, Calcium Fluoride (Fluorspan) 3～7%, process white 3～7%, barium carbonate 3～7%, polyoxyethylene glycol 1～5%, Sudan Gum-arabic 0.5～1.5%, starch 1～3%, organic acid 3～7% grinds to form respectively fine powder, and then pours above-mentioned fine powder into stirrer and mix to evenly.