CN103013352B - Airplane leather and paint surface polishing agent - Google Patents
Airplane leather and paint surface polishing agent Download PDFInfo
- Publication number
- CN103013352B CN103013352B CN201210554684.0A CN201210554684A CN103013352B CN 103013352 B CN103013352 B CN 103013352B CN 201210554684 A CN201210554684 A CN 201210554684A CN 103013352 B CN103013352 B CN 103013352B
- Authority
- CN
- China
- Prior art keywords
- leather
- test
- airplane
- group
- polishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses an airplane leather and paint surface polishing agent. The airplane leather and paint surface polishing agent comprises the following components in percentage by weight: the components comprises a group A and a group B, wherein the group A comprises 4%-12% of bee wax, 8%-16% of paraffin wax, 9%-21% of glycerin and 28%-41% of 32# white oil; the group B comprises 0.5%-4% of a surface active agent, 0.5%-4% of S-80, 22%-29% of water and 0.1-1% of essences, and the sum of the components is 100%; and the surface active agent is nonylphenol polyoxyethylene ether. The airplane leather and paint surface polishing agent meets standard requirements of aviation chemical products of three major airline companies, namely Boeing, McDonnell Douglas and Airbus.
Description
Technical field
The present invention relates to civil aviation chemical article, what be specifically related to is the rumbling compound of the polishing of aircraft seat leather and aircraft painted surface.
Background technology
According to statistics; China has more than 2,000 of airline carriers of passengers at present; and every year with 5% speed increase; China is all improving constantly service quality and the quality of hardware of Civil Aviation Industry every year; aircraft interior trim quality is improving constantly; but can be for seat leather cleaning and protection in aircraft cabin, again can be clean for painted surface and the aeronautical chemistry articles for use of polishing.All do not find at present like product at home and abroad, though abroad have aircraft paint surface cleaning rumbling compound, can not be simultaneously for the leather surface of aircraft seat.
Summary of the invention
Object of the present invention aims to provide a kind ofly can, for the polishing of aircraft seat leather surface, can paint for aircraft the aeronautical chemistry articles for use of the clean polishing of surface finish again;
The object of the invention is to realize by following manner: below all by weight,
The present invention is formed and minute is formed by A group and B, and wherein A composition divides and comprises: beeswax 4-12%, paraffin 8-16%, glycerine 9-21%, 32# white oil 28-41%; B composition minute comprises that tensio-active agent 0.5-4%, the amount of emulsifying agent S-80 are 0.5-4%, water 22-29%; Described tensio-active agent is polyoxyethylene nonylphenol ether.
In described B component, also can add essence 0.1-1%.
Wherein said A group and the heating respectively of B group, then mix under agitation condition.
Product of the present invention is mainly used in scouring and the polishing of the interior seat leather of aircraft cabin and the inside and outside painted surface of aircraft, to protect various leather substances and painted surface, makes leather and painted surface beautiful as new.
Product of the present invention meets the standard-required of empty company of Boeing, McDonnell Douglas and Air Passenger three key airline companies boatization product.And can be simultaneously as the rumbling compound to aircraft leather and painted surface.
The following good performance of tool of the present invention
Economical: this product is solvent-borne type product, although stoste is used, consumption is few, on average cleans an airplane, and consumption only has 2/3 of other cleanings, and price is suitable with other clean-out systems, saves and cleans cost 1/3.
Effective: during scouring, thoroughly to wipe the dirt on leather (or paint) surface, and not stay vestiges, make to be wiped surperficial beautiful as new.
Environmental protection: the tensio-active agent that this product is selected and other hydro carbons compositions be biochemical degradation completely all, environmentally safe.
Compatible good: this product is not containing acid, ammonia and free alkali, corrosion-free to leather and painted surface safety.Can possess the polishing of aircraft seat leather surface simultaneously, can paint for aircraft two effects of clean polishing of surface finish again.
Feature of the present invention is:
1, wide adaptability, leather surface and painted surface all adapt to.
1,, without unpleasant odor, use in the environment after this product polishing and leave delicate fragrance;
2, the flash-point of product is high, >=60 ℃, uses safety;
3, consumption is few, and price is low, uses economical;
Using method is simple, processing ease.
Using method of the present invention:
First with the surface that clean rag will be cleaned, wipe clean;
By sticky a little this product of clean cotton yarn, being embrocated back and forth by wiping surface, until can't see this product, there is packing phenomenon.
The surface drying of processing by 6.2 modes, after 3 minutes, is wiped 5-8 time in the same direction with flannelette.
Embodiment
Following examples are intended to illustrate the present invention, rather than limitation of the invention further.
Embodiment 1
A: (lower same) gets by weight percentage: beeswax 10%, paraffin 10%, glycerine 19%, 32# white oil 30%, puts into steeliness blender at normal temperatures and pressures by above-mentioned raw materials; Being heated to raw material all melts.
B: (described tensio-active agent is polyoxyethylene nonylphenol ether to get tensio-active agent 2%, be NP-10), S-80 (that is: sorbester p17, that is: be sorbitan monooleate) 2%, water 26.7%, lemon flavour 0.3%, puts into above-mentioned raw materials in another steeliness blender at normal temperatures and pressures, is heated to all raw materials and all melts;
C: start in A step after agitator stirs, the raw material obtaining of B step is added in A, continue stir but do not reheat; After cooling, start to pack into large mouthful of (tinplate system) pail pack.
Embodiment 2
A: get by weight percentage: beeswax 8%, paraffin 12%, glycerine 15%, 32# white oil 34.5%, puts into steeliness blender at normal temperatures and pressures by above-mentioned raw materials; Being heated to raw material all melts.
B: (described tensio-active agent is polyoxyethylene nonylphenol ether to get tensio-active agent 2%, be NP-10), S-80 (that is: sorbester p17, that is: be sorbitan monooleate) 1.5%, water 26.7%, lemon flavour 0.3%, puts into above-mentioned raw materials in another steeliness blender at normal temperatures and pressures, is heated to all raw materials and all melts;
C is with embodiment 1.
Embodiment 3
A: get by weight percentage: beeswax 6%, paraffin 14%, glycerine 11%, 32# white oil 39%, puts into steeliness blender at normal temperatures and pressures by above-mentioned raw materials; Being heated to raw material all melts.
B: (described tensio-active agent is polyoxyethylene nonylphenol ether to get tensio-active agent 2%, be NP-10), S-80 (that is: sorbester p17, that is: be sorbitan monooleate) 1%, water 26.7%, lemon flavour 0.3%, puts into above-mentioned raw materials in another steeliness blender at normal temperatures and pressures, is heated to all raw materials and all melts;
C is with embodiment 1.
Embodiment 4
By rumbling compound of the present invention according to MH6021-2000 CAAC industry standard (this standard is according to the standard formulation of the empty company of Boeing, McDonnell Douglas and Air Passenger three key airline companies), strict carrying out following test:
The performance test of 1 product:
All tests in this all use stoste (be heated to liquid state, lower with) under undiluted state to carry out.
1.1 flash-point
According to ASTM D56, the flash-point of product is tested, its result not the end in 60 ℃.
Test-results: 68 ℃ of flash-points.Conclusion (of pressure testing): qualified.
1.2 cold and hot stability
Requirement according to the 2.9th of HB5334-85 is carried out, should be even when the product after test returns to normal temperature under defined terms, and without layering, without precipitating, separating out without floss.
Test-results: product appearance is without considerable change.
1.3 prolonged storage stability
According to ASTM F1104, test, the test period is low temperature 15 days and high temperature 15 days, and result should meet the requirement of ASTM F1104, and the product after experiment should be even, without layering, without precipitation, without floss, separates out.
Test-results: product appearance is without considerable change.Conclusion (of pressure testing): qualified.
The compatibility test of 2 aircraft materials
Tests all in this are all undertaken by stoste.
2.1 immersion corrosion tests
2.1.1 test exemplar and numbering:
A: the 7075/T6 that meets QQ-A-250/13-T6 has aluminium coating aluminium alloy;
B: meet the 2024/T3 of QQ-A-250/4-T3 without aluminium coating aluminium alloy, and process (495 ℃ ± 5 ℃ thermal treatment 40 minutes, then use 100 ℃ of water quick coolings) through sensitization;
2.1.2 test and qualification determination:
When testing after 24 hours by ASTM F 483, the weight in average of test exemplar becomes should not surpass 8.2mg, can not occur corrosion phenomenon.
Test-results: 0.00 milligram of test specimen a, corrosion-free;
0.00 milligram of test specimen b; Corrosion-free.
Conclusion (of pressure testing): qualified.
2.2 enamelled coating softening tests
After testing by ASTM F502, test sample can not make enamelled coating hardness reduce to be greater than two pencil hardness levels, the corrosion phenomenon that also should not make enamelled coating fade, dye, chap, bubble.
Test-results: hardness of paint film is unchanged, does not have the corrosion phenomenon that fades, dyes, chaps, bubbles yet.Conclusion (of pressure testing): qualified.
2.3 residue tests
After testing by ASTM F485, test sample can not leave residue on test plate (panel), can not make its dyeing.Test-results: do not leave residue, also do not make its dyeing.Conclusion (of pressure testing): qualified.
The impact test of 2.4 leather pieces
Requirement by AMS 1452B 3.2.2.2.4 is carried out, and can not make leather surface produce indentation or dipping or very little colour-change, otherwise be defective.
2.4.1 test exemplar size
Adopt unified size: 2 * 4 * 0.040 0.060 inch of ∽.
2.4.2 test sample material
A: sheepskin; B: pigskin; C: ox-hide
Test-results: a, b, g surface all do not produce indentation or dipping or very little colour-change.Conclusion (of pressure testing): qualified.
2.5 polyacrylic ester cracking tests
When MIL-P-25690A type polyacrylic acid material being applied to the external stress of 4500Psi by ASTM F484, test sample must not make exemplar produce the corrosion phenomenon of be full of cracks, crackle or etch.
Test-results: exemplar is without the corrosion phenomenon of be full of cracks, crackle or etch.Conclusion (of pressure testing): qualified.
2.6 polycarbonate cracking tests
Test exemplar: the 9600-116 polycarbonate sheet of General Electric Corporation, 0.060 ± 0.005 inch.
Testing sequence:
1) load to test exemplar making its surface stress is 2000Psi;
2) absorbent cotton that is soaked with testing liquid is layered on the testpieces under loading, notes solution not being encountered the edge of test exemplar;
3) after ten minutes, separate de-stress, take away absorbent cotton;
4) on test exemplar, should there is not be full of cracks, crackle, the corrosion phenomenon of staining or fading.
Otherwise be defective
Test-results: the corrosion phenomenon that does not occur be full of cracks, crackle, stains or fade on test exemplar.Conclusion (of pressure testing): qualified.
2.7 stress corrosion (cracking) test
According to ASTM F945, test, test plate (panel) can not crack.With methylethylketone (MEK) liquid in contrast.Material adopts 6Al-4V titanium alloy.
Test-results: outward appearance is without considerable change.Conclusion (of pressure testing): qualified.
Claims (2)
1. aircraft leather and painted surface rumbling compound, is characterized in that: by A group and B, formed and minute formed, wherein A group comprises: beeswax 4-12%, paraffin 8-16%, glycerine 9-21%, 32# white oil 28-41%; B group comprises: tensio-active agent 0.5-4%, and emulsifying agent S-80 0.5-4%, water 22-29%, all by weight; Described tensio-active agent is polyoxyethylene nonylphenol ether.
2. aircraft leather according to claim 1 and painted surface rumbling compound, is characterized in that: in described B component, add essence 0.1-1%.