CN103008211A - 一种用于对不良塑胶品进行返修的方法 - Google Patents
一种用于对不良塑胶品进行返修的方法 Download PDFInfo
- Publication number
- CN103008211A CN103008211A CN2012105883149A CN201210588314A CN103008211A CN 103008211 A CN103008211 A CN 103008211A CN 2012105883149 A CN2012105883149 A CN 2012105883149A CN 201210588314 A CN201210588314 A CN 201210588314A CN 103008211 A CN103008211 A CN 103008211A
- Authority
- CN
- China
- Prior art keywords
- plastic product
- paint
- spraying
- bad plastic
- described step
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种用于对不良塑胶品进行返修的方法,主要包括打磨清洁、喷涂UV返修水、喷涂UV油漆、烘烤、照射光固化的步骤,经过UV返修水处理之后的不良塑胶品对UV油漆的附着力更强,本发明非常简便地对喷涂了UV油漆之后的不良塑胶品进行处理,摈弃了碎料、注塑、喷底漆等流程,极大地降低对塑胶制品喷涂时的生产成本,使其能够重新被用于喷涂UV油漆,且良品率提高到95%以上,而且该方法对环境和人体没有不良影响,符合绿色环保的发展要求。
Description
技术领域:
本发明属于喷涂技术领域,具体是指一种对于喷涂了UV油漆之后的不良塑胶制品进行返修的方法。
背景技术:
在塑胶制品的生产流程中,往往需要对塑胶制品进行喷涂,而现有的喷涂流程中,又往往需要用到UV油漆作为面漆,以使其美观,但是在喷涂UV油漆这一道工序中,往往会产生大量的不良品。而尘点(由于灰尘落在塑胶产品上导致喷完UV油漆之后灰尘被固定在塑胶制品表面,形成小凸点)和毛丝(由于无尘布或者工人衣服上面的纤维掉落在塑胶制品表面导致喷完UV油漆之后这些纤维被固定在产品表面而形成小凸条)是导致不良品产生的最常见的原因,在现有的生产过程中,对这种不良品最经常采用的处理方案就是直接进行粉碎,然后将一定比例的这种碎料混入原装的塑胶原料中重新用于生产,但是经过粉碎之后的塑胶料力学性能较弱,相对于原装的塑胶原料其成型性能较差,容易导致注塑机生产出不良品,并且由于对油漆的附着力较差,在重新喷涂的时候也比较容易产生大量的不良品。
发明内容:
有鉴于此,本发明提供一种可用于对喷涂UV油漆之后的不良塑胶品进行返修的方法。使得在对塑胶品喷涂UV油漆的过程中由于尘点或者毛丝产生的不良品可以重新被用于喷涂UV油漆,而且该方法对环境和人体没有不良影响。
本发明所采用的技术方案包括以下步骤:
a、用砂纸对不良塑胶品表面进行打磨,直至不良塑胶品表面无凸起,然后擦试表面,保障清洁;
b、在打磨过的不良塑胶品的表面喷涂UV返修水;
c、在喷涂有UV返修水的表面喷涂UV油漆,使UV返修水和UV油漆充分匹配;
d、在完成步骤c之后将不良塑胶品静置至少2分钟,以完成干燥;
e、在完成步骤d之后将不良塑胶品置入烤箱中进行至少5分钟的烘烤;
f、将烘烤过的不良塑胶品放入UV固化炉进行至少1分钟的照射,以对喷涂的UV油漆进行光固化;
g、检验,成品。
进一步的措施是:所述步骤a的砂纸型号为600#—2000#;优选的砂纸型号为1500#。
所述步骤b的UV返修水喷涂的膜厚为2μm——6μm;优选的UV返修水喷涂的膜厚为3μm。
所述步骤c的UV油漆喷涂的膜厚为2μm——6μm;优选的UV油漆喷涂的膜厚为3μm。
所述步骤e的烤箱温度为30℃—80℃;优选的烤箱温度为55℃。
所述步骤f的UV固化炉的发热量为900MJ。
上述的UV返修水是一种聚硅氧烷类化合物,其密度为(20℃,g/ml):1.05;粘度为(岩田,2#杯): 8±1秒,具有稳定性好的特性,能够解决金属水电镀、真空电镀工艺UV涂装等后加工难附着和附着力稳定性问题,实用性广,属于新型绿色环保涂料。
上述的UV油漆全称是紫外光固化涂料(ultraviolet curing coating),是以油漆的固化方式命名的,其原料一般为环氧树脂,它是一种在紫外线(ultraviolet,简称UV)的照射下能够在几秒钟内迅速固化成膜的油漆涂料。UV油漆主要特点有:经过强紫外线光固化处理,色泽稳定,历久常新,有效解决褪色及色差问题;镜面纯平效果好,并且漆膜饱满无桔皮;耐刮划,耐酸碱,不易变形。UV油漆的固含量达到 95% 以上,使用过程中无有机溶剂的挥发,所含成分全部固化成膜。对施工操作人员的健康危害及环境的污染都是最低的,是真正的绿色环保产品。
上述的UV固化炉就是通过一种单体/低聚物的混合物的快速聚合而获得一种也可交联的涂膜的设备。UV体系的这种快速聚合是用光引发剂和高性能的灯来实现的,用于需要紫外线进行固化的涂料(油漆)、胶粘剂(胶水)或其它灌封、密封剂的物质,具有立即干燥、低运行成本、清洁高效的优点。
同现有技术相比,本发明的有益效果是:其一,该方法能够非常简便地对喷涂了UV油漆之后的不良塑胶品进行处理,使其能够重新被用于喷涂UV油漆;其二,经过UV返修水处理之后的不良塑胶品对UV油漆的附着力更强,在重新喷涂UV油漆之后仍然能够轻易地通过各种对油漆的性能测试;其三,该方法对环境和人体没有任何不良影响,符合绿色环保的发展要求;其四,利用该方法对不良塑胶品进行处理可以使得UV喷涂过程中的良品率提高到95%以上;其五,由于对不良塑胶品的处理不再需要经历碎料、注塑、喷底漆这些流程,所以该方法能极大地降低对塑胶制品喷涂时的生产成本。
具体实施方式:
选取已经喷涂有UV油漆,但其表面带有3个尘点和1个毛丝的不良塑胶品。为了使得其不良塑胶品变为良品,需要进行下列操作:
a、用1500#砂纸对不良塑胶品表面上存在尘点和毛丝的位置进行打磨,直至不良塑胶品表面上的尘点和毛丝位置不再有凸起的现象,然后擦试表面,保障清洁;
b、在打磨过的不良塑胶品的表面喷涂上膜厚为3μm的UV返修水;
c、在喷涂有UV返修水的表面喷涂膜厚为3μm的UV油漆,使UV返修水和UV油漆充分匹配,达到百分之百的附着力;
d、在完成步骤c之后将不良塑胶品在自然状态下静置2分钟,以完成干燥;
e、在完成步骤d之后将不良塑胶品置入温度为55℃的烤箱中进行5分钟的烘烤;
f、再将烘烤过的不良塑胶品放入发热量为900MJ的UV固化炉进行1分钟的照射,以对重新喷涂上去的UV油漆进行光固化;
g、最后检验,以塑胶品表面的尘点和毛丝不可见为准,成品。
以上所述,仅是本发明的较佳实施例,并非对本发明的技术范围作任何限制。本行业的技术人员,在本技术方案的启迪下,可做出一些变形与修改,凡是依据本发明的技术实质对以上的实施例所作的任何修改、等同变化与修饰,均仍属于本发明技术方案的范围内。
Claims (10)
1.一种用于对不良塑胶品进行返修的方法,其特征在于:包含以下步骤:
a、用砂纸对不良塑胶品表面进行打磨,直至不良塑胶品表面无凸起,然后擦试表面,保障清洁;
b、在打磨过的不良塑胶品的表面喷涂UV返修水;
c、在喷涂有UV返修水的表面喷涂UV油漆,使UV返修水和UV油漆充分匹配;
d、在完成步骤c之后将不良塑胶品静置至少2分钟,以完成干燥;
e、在完成步骤d之后将不良塑胶品置入烤箱中进行至少5分钟的烘烤;
f、将烘烤过的不良塑胶品放入UV固化炉进行至少1分钟的照射,以对喷涂的UV油漆进行光固化;
g、检验,成品。
2.根据权利要求1所述的一种用于对不良塑胶品进行返修的方法,其特征在于:所述步骤a的砂纸型号为600#—2000#。
3.根据权利要求1所述的一种用于对不良塑胶品进行返修的方法,其特征在于:所述步骤a的砂纸型号为1500#。
4.根据权利要求1所述的一种用于对不良塑胶品进行返修的方法,其特征在于:所述步骤b的UV返修水喷涂的膜厚为2μm——6μm。
5.根据权利要求1所述的一种用于对不良塑胶品进行返修的方法,其特征在于:所述步骤b的UV返修水喷涂的膜厚为3μm。
6.根据权利要求1所述的一种用于对不良塑胶品进行返修的方法,其特征在于:所述步骤c的UV油漆喷涂的膜厚为2μm——6μm。
7.根据权利要求1所述的一种用于对不良塑胶品进行返修的方法,其特征在于:所述步骤c的UV油漆喷涂的膜厚为3μm。
8.根据权利要求1所述的一种用于对不良塑胶品进行返修的方法,其特征在于:所述步骤e的烤箱温度为30℃—80℃。
9.根据权利要求1所述的一种用于对不良塑胶品进行返修的方法,其特征在于:所述步骤e的烤箱温度为55℃。
10.根据权利要求1所述的一种用于对不良塑胶品进行返修的方法,其特征在于:所述步骤f的UV固化炉的发热量为900MJ。