CN102995336A - Process for manufacturing seaweed fabric - Google Patents
Process for manufacturing seaweed fabric Download PDFInfo
- Publication number
- CN102995336A CN102995336A CN201210498503.7A CN201210498503A CN102995336A CN 102995336 A CN102995336 A CN 102995336A CN 201210498503 A CN201210498503 A CN 201210498503A CN 102995336 A CN102995336 A CN 102995336A
- Authority
- CN
- China
- Prior art keywords
- cloth
- marine alga
- fire
- retardant
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a process for manufacturing a seaweed fabric. The process comprises the following process steps of: (1) drying seaweeds, melting the dried seaweeds, and adding a fire retarding agent for copolymerization together to prepare seaweed fiber; (2) weaving the seaweed fiber, chinlon, terylene and cotton yarns into a flame-resistant fabric; (3) performing rolling suction treatment on the flame-resistant fabric in a flame retardant, wherein the liquid rate is more than 75 percent; and (4) drying the fabric subjected to the rolling suction treatment by baking. Therefore, by using the process for manufacturing the seaweed fabric, the operational process is easy to operate and control, and the manufactured seaweed fabric is soft in texture and portable, and has extremely strong flame-resisting and fireproofing functions.
Description
Technical field
The present invention relates to the functional fabric field, particularly relate to a kind of manufacture craft of marine alga cloth.
Background technology
Marine alga is to live in marine algae, it is botanic cryptogam, algae is with the energy-producing biology of photosynthesis, they are generally considered to be simple plant, contain protein, fat, carbohydrate, multivitamin and the mineral matter of needed by human in the marine alga, nutritive value is higher than the Lu Sheng vegetables far away, under photosynthesis, marine alga is converted into organic matter to all inorganic matters in the ocean, thereby more contains some compounds that do not have in the Lu Sheng vegetables in the marine alga body.In view of its specific function, China's marine algae resource is abundant in addition, and seaweed products just are being widely used in the aspects such as surgical dressing, pharmaceuticals industry, food preservation, textile industry, paper industry, photograph.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of good permeability, light comfortable, manufacture craft that the marine alga cloth of extremely strong fire-retardant and fire-proof function is arranged.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of manufacture craft of marine alga cloth is provided, comprises following processing step:
(1) with melting after the marine alga oven dry, add together copolymerization of fire retardant, make alginate fibre,
(2) alginate fibre, polyamide fibre, terylene, cotton yarn are woven into fire-retardant cloth,
(3) fire-retardant cloth is rolled in fire retardant inhale to process, liquid carrying rate is more than 75%,
(4) will roll the cloth of inhaling after processing and carry out drying and processing.
In a preferred embodiment of the present invention, impurity content is lower than 5% in the described alginate fibre.
In a preferred embodiment of the present invention, in the described fire-retardant cloth, alginate fibre content is 30-40%, and polyamide fibre 15-20%, terylene 15-20%, all the other are cotton yarn, and described content is weight percentage.
In a preferred embodiment of the present invention, described rolling inhaled treatment temperature and remained on the 30-50 degree, describedly rolls that to inhale the processing time be 40-80 minute.
In a preferred embodiment of the present invention, described drying and processing time-temperature is the 25-60 degree, and the described drying and processing time is 5-25 minute.
The invention has the beneficial effects as follows: the manufacture craft of marine alga cloth of the present invention is simple to operate, operating process is easy to control, and the marine alga cloth quality that is made is soft, light, extremely strong fire-retardant and fire-proof function is arranged.
The specific embodiment
The below is described in detail preferred embodiment of the present invention, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
A kind of manufacture craft of marine alga cloth comprises following processing step:
(1) with melting after the marine alga oven dry, add together copolymerization of fire retardant, make alginate fibre,
(2) alginate fibre, polyamide fibre, terylene, cotton yarn are woven into fire-retardant cloth,
(3) fire-retardant cloth is rolled suction in fire retardant and process, liquid carrying rate 85%,
(4) will roll the cloth of inhaling after processing and carry out drying and processing.
In addition, impurity content 3.5% in the described alginate fibre.
In addition, in the described fire-retardant cloth, alginate fibre content is 35%, and polyamide fibre 15%, terylene 20%, all the other are cotton yarn, and described content is weight percentage.
In addition, described rolling inhaled treatment temperature and remained on 40 degree, describedly rolls that to inhale the processing time be 50 minutes.
In addition, described drying and processing time-temperature is 30 degree, and the described drying and processing time is 10 minutes.
The manufacture craft of marine alga cloth of the present invention is simple to operate, operating process is easy to control, and the marine alga cloth quality that is made is soft, light, extremely strong fire-retardant and fire-proof function is arranged.
Be different from prior art, the marine alga cloth good permeability that the manufacture craft of marine alga cloth of the present invention is made, light comfortable, extremely strong fire-retardant and fire-proof function is arranged, can be widely used on firefighter uniform and the fire-fighting equipment.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (5)
1. the manufacture craft of a marine alga cloth is characterized in that, comprises following processing step:
(1) with melting after the marine alga oven dry, add together copolymerization of fire retardant, make alginate fibre,
(2) alginate fibre, polyamide fibre, terylene, cotton yarn are woven into fire-retardant cloth,
(3) fire-retardant cloth is rolled in fire retardant inhale to process, liquid carrying rate is more than 75%,
(4) will roll the cloth of inhaling after processing and carry out drying and processing.
2. the manufacture craft of marine alga cloth according to claim 1 is characterized in that, impurity content is lower than 5% in the described alginate fibre.
3. the manufacture craft of marine alga cloth according to claim 1 is characterized in that, in the described fire-retardant cloth, alginate fibre content is 30-40%, and polyamide fibre 15-20%, terylene 15-20%, all the other are cotton yarn, and described content is weight percentage.
4. the manufacture craft of marine alga cloth according to claim 1 is characterized in that, described rolling inhaled treatment temperature and remained on the 30-50 degree, describedly rolls that to inhale the processing time be 40-80 minute.
5. the manufacture craft of marine alga cloth according to claim 1 is characterized in that, described drying and processing time-temperature is the 25-60 degree, and the described drying and processing time is 5-25 minute.