CN102978826A - Production process of polyester composite belt - Google Patents
Production process of polyester composite belt Download PDFInfo
- Publication number
- CN102978826A CN102978826A CN2012103722104A CN201210372210A CN102978826A CN 102978826 A CN102978826 A CN 102978826A CN 2012103722104 A CN2012103722104 A CN 2012103722104A CN 201210372210 A CN201210372210 A CN 201210372210A CN 102978826 A CN102978826 A CN 102978826A
- Authority
- CN
- China
- Prior art keywords
- polyester fiber
- composite
- composite belt
- production process
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a production process of a polyester composite belt. The production process of the polyester composite belt is characterized by comprising the follow steps: a. array filament: distributing polyester fibers evenly within the width of 9-100 millimeters, b. melting mixing: placing hot melt adhesive or water based adhesive in a heater, controlling the temperature to be in the range of 50-180 DEG C, and then coating the adhesive evenly on the polyester fibers, c. cooling shaping: enabling the coated polyester fibers to be cooled and shaped, d. drying: eliminating moisture left on the composite belt during a water-cooling process, e. identifying draft: spraying information which is in need of indentifying onto the composite belt through a code spraying machine, and then drafting the composite belt to a rolling device through a draft device, f. rolling packaging: packaging the composite after being rolled through the rolling device. The production process of the polyester composite belt has the advantages that the composite belt obtained through the production process has high breaking strength of a steel belt or a rope, at the same time has good flexibility and corrosion resistant capacity, and can be used as a substantial product of the steel belt or the rope.
Description
Technical field
The present invention relates to a kind of production technology of polyester fiber composite strap.
Background technology
At present, heavy type or large cargo packing all adopts steel band (casted steel belt, stainless steel band, plating belt transect, aluminium strip etc.) to tie up the employing steel rope that transportation has.Though steel band and steel rope have very high fracture strength, also have large rigidity and sharp edge, therefore packaging or fixing goods there are larger damageability, particularly when Transport Vibration, cause goods badly damaged because lacking suitable buffering; Steel band or rope are in packing or fixedly the time, and operation easier is larger, scratches easily operating personnel's health, also scratch the goods surface simultaneously, in addition, are difficult for passing goods; Steel band or rope particularly get rusty easily, are corroded in the long-term marine transportation process in long term storage or transportation, thereby cause goods impaired or not attractive in appearance.
Summary of the invention
The object of the invention is to address the above problem and a kind of production technology of polyester fiber composite strap is provided, the polyester fiber composite strap that present patent application obtains is possessing the high fracture strength of steel band or rope simultaneously, also have good pliability and corrosion resistance, can be used as the substitute products of steel band or rope.
The present invention solves the technical scheme that the prior art problem adopts: the production technology of polyester fiber composite strap is characterized in that may further comprise the steps:
A, row's silk: some polyester fibers are placed on the creel, by thread guide, tension regulator, reverse wheel, bar guide, equal silk device, polyester fiber is evenly distributed in 9 ~ 100mm width successively;
B, melting are compound: heatmeltable adhesive or water accack are placed in the heater, the control temperature is in 50 ~ 180 ℃ of scopes, then evenly be coated in adhesive on the polyester fiber, described heatmeltable adhesive is non-response type polyamide resin lipid material, and described polyester fiber and heatmeltable adhesive composite quality ratio are 60 ~ 80:40 ~ 20; Described water accack is polychloroprene latex and tackifying resin two-component materials; The mass ratio of polychloroprene latex and tackifying resin is 50:50 in the described water accack; Described polyester fiber and water accack composite quality ratio are 60 ~ 80:40 ~ 20;
C, cooling and shaping: make the rear polyester fiber cooling and shaping of coating;
D, drying: the moisture content of staying on the composite band during with water-cooled removes;
E, sign traction: by ink jet numbering machine the information that will identify is sprayed onto on the composite band, is drawn to wrap-up by draw-gear again;
F, rolling packing: by packing after the winder rolling.
The beneficial effect that the present invention has: the polyester fiber composite strap that present patent application obtains also has good pliability and corrosion resistance possessing the high fracture strength of steel band or rope simultaneously, can be used as the substitute products of steel band or rope.
The specific embodiment
The present invention is further illustrated below in conjunction with the specific embodiment.
Embodiment: the production technology of polyester fiber composite strap is characterized in that may further comprise the steps:
A, row's silk: some polyester fibers are placed on the creel, by thread guide, tension regulator, reverse wheel, bar guide, equal silk device, polyester fiber is evenly distributed in 9 ~ 100mm width successively;
B, melting are compound: heatmeltable adhesive or water accack are placed in the heater, the control temperature is in 50 ~ 180 ℃ of scopes, then evenly be coated in adhesive on the polyester fiber, described heatmeltable adhesive is non-response type polyamide resin lipid material, and described polyester fiber and heatmeltable adhesive composite quality ratio are 60 ~ 80:40 ~ 20; Described water accack is polychloroprene latex and tackifying resin two-component materials; The mass ratio of polychloroprene latex and tackifying resin is 50:50 in the described water accack; Described polyester fiber and water accack composite quality ratio are 60 ~ 80:40 ~ 20;
C, cooling and shaping: make the rear polyester fiber cooling and shaping of coating;
D, drying: the moisture content of staying on the composite band during with water-cooled removes;
E, sign traction: by ink jet numbering machine the information that will identify is sprayed onto on the composite band, is drawn to wrap-up by draw-gear again;
F, rolling packing: by packing after the winder rolling.
Compared with prior art, because the present invention has selected polyester fiber as base material, compound heatmeltable adhesive or water accack on this base material, and be equipped with rational process conditions and produce, the flexible polyester fiber composite strap that therefore obtains has following features:
Have high fracture strength, can replace steel band or rope to use;
Have pliability, can not cause injury to goods surface or people, easy to operate;
Have corrosion resistance, can not get rusty or be subject to soda acid and corrode;
Have energy absorption capacity, but the energy of generation of vibration in the Absorption And Transportation process;
Has persistence, fracture strength rate of decay little (relatively PP, PET band);
Has the feature of environmental protection, recyclable and recycling.
Therefore, the present invention has broad application prospects.
The above is the preferred embodiments of the present invention only, is not limited to the present invention.In the above-described embodiments, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any modification of doing, be equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (1)
1. the production technology of polyester fiber composite strap is characterized in that may further comprise the steps:
A, row's silk: some polyester fibers are placed on the creel, by thread guide, tension regulator, reverse wheel, bar guide, equal silk device, polyester fiber is evenly distributed in 9 ~ 100mm width successively;
B, melting are compound: heatmeltable adhesive or water accack are placed in the heater, the control temperature is in 50 ~ 180 ℃ of scopes, then evenly be coated in adhesive on the polyester fiber, described heatmeltable adhesive is non-response type polyamide resin lipid material, and described polyester fiber and heatmeltable adhesive composite quality ratio are 60 ~ 80:40 ~ 20; Described water accack is polychloroprene latex and tackifying resin two-component materials; The mass ratio of polychloroprene latex and tackifying resin is 50:50 in the described water accack; Described polyester fiber and water accack composite quality ratio are 60 ~ 80:40 ~ 20;
C, cooling and shaping: make the rear polyester fiber cooling and shaping of coating;
D, drying: the moisture content of staying on the composite band during with water-cooled removes;
E, sign traction: by ink jet numbering machine the information that will identify is sprayed onto on the composite band, is drawn to wrap-up by draw-gear again;
F, rolling packing: by packing after the winder rolling.