CN102977821B - 卫生间专用嵌缝胶的制备方法 - Google Patents
卫生间专用嵌缝胶的制备方法 Download PDFInfo
- Publication number
- CN102977821B CN102977821B CN201210587101.4A CN201210587101A CN102977821B CN 102977821 B CN102977821 B CN 102977821B CN 201210587101 A CN201210587101 A CN 201210587101A CN 102977821 B CN102977821 B CN 102977821B
- Authority
- CN
- China
- Prior art keywords
- water
- caulk compound
- rest room
- cement
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
房屋装修卫生间渗漏,是最令人头疼的事情,卫生间专用嵌缝胶可以有效的解决这个问题。本发明使用丙烯酸乳液为主要成膜物质,粘接强度大,柔韧性能好,抗热耐冻,耐候性能好,能与多种填料相融合,耐碱性强,能适合卫生间的特殊环境。以水泥为主要填料,强度大,经久耐用,成本低;使用甲基纤维素醚为保水剂,抑制了水分过快流失,有足够的水分养护水泥,得以完全固化,提高强度,也改善了嵌缝胶的可塑性,使施工更容易。本发明提供的卫生间专用嵌缝胶,能够填缝密封,防渗堵漏;无毒无味,无环境污染;耐候性好,使用寿命长;耐热抗冻,延伸性能好;它施工性能好,使用方便。
Description
技术领域
[0001] 本发明属于化工类,具体说是一种建筑上使用的卫生间专用的嵌缝胶。
背景技术
[0002] 卫生间地坪与墙面的接缝,目前主要采用水泥填缝。用水泥加水调和成膏状,填充缝隙,抹平。由于水泥是水凝性材料,只有在相当一段时间内存有适量的水分,才能使其得以充分固化,体现出强度和耐久性。在家庭装修期间,绝大部分填完水泥后,没有洒水养护。这时由于水不充分,水泥不能完全水化,就开始凝固收缩,接缝处就会有许多细小裂纹。当卫生间使用时,涮洗拖把、洗衣服、洗澡,水就从这些接缝处的裂纹向下渗漏。尽管卫生间都做了防水处理,当长时间处于渗漏的水中,也就会向下渗漏,这就是目前卫生间普遍渗漏的主要原因。有的装修时,使用水泥加107胶调和,填充缝隙。107胶是聚乙烯醇加入甲醛缩合而成,使用它调和水泥,由于高分子溶液的加入,具有一定保水性,水泥就可以充分水化,凝固后就很少有裂纹,使水泥的强度和防水性都得到一定的改善。由于107胶会产生少量的游离甲醛,对室内造成环境污染,国家已经禁止室内使用107胶。有一种专利CN102618203A耐候型醚化嵌缝胶及其制备方法,粘接缝隙很好,但是价格较高,不适用于建筑装修大量使用。有的嵌缝胶填缝密封效果好,气味较大,也不适合家庭装修实用。针对目前的这种情况,特提出本发明——卫生间专用嵌缝胶。
发明内容
本发明使用丙烯酸乳液为主要成膜物质,它粘接强度大,柔韧性能好,抗热耐冻,耐候性能好,能与多种填料相融合,耐碱性强,能适合卫生间的特殊环境。乙烯—聚醋酸乙烯乳液柔韧性能好,耐碱、耐紫外光照射、耐候性能好。有机硅乳液具有卓越的防水抗渗性能。这三种聚合物乳液混合作为嵌缝胶的成膜物质,能发挥各自的特性,相互弥补不足,相得益彰。以水泥为主要填料,强度高、使用寿命长、成本低。但是单纯的水泥制品易龟裂、耐水性较差。当上述三种聚合物乳液混合物与水泥相互混合后,聚合物乳液的乳胶粒就均匀的分散在水泥相中,在这种水泥胶乳糊内,由于水泥的水化作用逐渐地形成水凝胶,这种凝胶结构的继续发展和水的逐渐蒸发失水,聚合物胶乳颗粒开始聚集在水泥凝胶结构的毛细孔中,并使其封闭,阻止水分的过快蒸发,促进水泥水化过程的进行。当水泥水化和水蒸发继续进行时,毛细孔中的水更加减少,从而使聚合物颗粒在水泥凝胶和未水化水泥颗粒混合物的表面上凝结成一个连续的密集层,最后,当水泥完全水化时,密集的聚合物颗粒将在水化水泥上形成连续的薄膜。由于这种聚合物薄膜的形成而产生的封闭效应,使得水泥的耐水渗透性、耐碱性得以大大的改善。使用甲基纤维素醚为保水剂,水泥可以充分凝固。甲基纤维素醚可大幅度提高嵌缝胶的保水能力,抑制了水分由嵌缝胶往底材过快流失,有足够的水分使水泥水化、凝固,以提高强度。此外,甲基纤维素醚也改善了嵌缝胶的可塑性,使施工更容易。滑石粉和重质碳酸钙是耐水性很好的填料。聚丙烯酸钠是分散剂,可以把填料均匀的分散在聚合物胶乳中。乙二醇是成膜助剂,可以在常温下使上述三种聚合物乳液更容易成膜。磷酸三丁酯是消泡剂,使嵌缝胶在使用过程中不产生气泡,或者产生气泡后立即消失。
本发明提供的卫生间专用嵌缝胶,能够填缝密封,防渗堵漏;无毒无味,无环境污染;耐候性好,使用寿命长;耐热抗冻,延伸性能好;它施工性能好,使用方便。
卫生间专用嵌缝胶的配方是:
原料名称 质量百分数(%)
丙烯酸乳液 20—30
乙烯—聚醋酸乙烯乳液 4—15
有机硅乳液 3—10
白水泥 10—40
滑石粉 5—15
重质碳酸钙 6—20
甲基纤维素醚 1—8
聚丙烯酸钠 1—5
乙二醇 1—6
磷酸三丁酯 0.5—4
水 5—15
上述所有组分之和等于100% 。
工艺过程:
取水,加入聚丙烯酸钠、甲基纤维素醚,搅拌均匀。加入滑石粉、重质碳酸钙、水泥,搅拌均匀。加入丙烯酸乳液、乙烯—聚醋酸乙烯乳液、有机硅乳液、乙二醇,搅拌均匀,加入磷酸三丁酯,搅拌均匀,检测,即得本发明产品。
具体实施方式
实施例一
配方:
原料名称 质量百分数(%)
丙烯酸乳液 15
乙烯—聚醋酸乙烯乳液 5
有机硅乳液 3
白水泥 32
滑石粉 10
重质碳酸钙 20
甲基纤维素醚 4
聚丙烯酸钠 1
乙二醇 1
磷酸三丁酯 0.5
水 8.5
工艺过程:
取水,加入聚丙烯酸钠、甲基纤维素醚,搅拌均匀。加入滑石粉、重质碳酸钙、水泥,搅拌均匀。加入丙烯酸酯乳液、乙烯—聚醋酸乙烯乳液、有机硅乳液、乙二醇,搅拌均匀,加入磷酸三丁酯,搅拌均匀,检测,即得本发明产品。
实施例二
配方:
原料名称 质量百分数(%)
丙烯酸乳液 17
乙烯—聚醋酸乙烯乳液 4
有机硅乳液 4
白水泥 30
滑石粉 14
重质碳酸钙 18
甲基纤维素醚 3
聚丙烯酸钠 1
乙二醇 1
磷酸三丁酯 0.5
水 7.5
工艺过程:
取水,加入聚丙烯酸钠、甲基纤维素醚,搅拌均匀。加入滑石粉、重质碳酸钙、水泥,搅拌均匀。加入丙烯酸乳液、乙烯—聚醋酸乙烯乳液、有机硅乳液、乙二醇,搅拌均匀,加入磷酸三丁酯,搅拌均匀,检测,即得本发明产品。
参考文献
1.钱祖其,钱晨娜,耐候型醚化嵌缝胶及其制备方法[P],申请号:201210050056.9,申请日期:2012.02.29。
2.辛全仓,何廷树,宋学峰,改性瓷砖胶粘剂的配制与性能[J],化学建材,2005,21(3):46-48。
Claims (1)
1. 一种卫生间专用嵌缝胶,其特征在于原料组成的质量百分数为:
原料名称 质量百分数(%)
丙烯酸乳液 20—30
乙烯—醋酸乙烯乳液 4—15
有机硅乳液 3—10
白水泥 10—40
滑石粉 5—15
重质碳酸钙 6—20
甲基纤维素醚 1—8
聚丙烯酸钠 1—5
乙二醇 1—6
磷酸三丁酯 0.5—4
水 5—15
上述所有组分之和等于100% ;
各原料组分的加入顺序及操作方法为:
取水,加入聚丙烯酸钠、甲基纤维素醚,搅拌均匀;加入滑石粉、重质碳酸钙、白水泥,搅拌均匀;加入丙烯酸乳液、乙烯—聚醋酸乙烯乳液、有机硅乳液、乙二醇,搅拌均匀,加入磷酸三丁酯,搅拌均匀,检测,即得本产品。