CN102976786A - Porous basalt granule ceramic product and preparation method thereof - Google Patents
Porous basalt granule ceramic product and preparation method thereof Download PDFInfo
- Publication number
- CN102976786A CN102976786A CN2012105690911A CN201210569091A CN102976786A CN 102976786 A CN102976786 A CN 102976786A CN 2012105690911 A CN2012105690911 A CN 2012105690911A CN 201210569091 A CN201210569091 A CN 201210569091A CN 102976786 A CN102976786 A CN 102976786A
- Authority
- CN
- China
- Prior art keywords
- porous basalt
- basalt particle
- porous
- temperature
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a porous basalt granule ceramic product and a preparation method thereof. The porous basalt granule ceramic product is prepared by adopting clay and porous basalt granules as raw materials and roasting the raw materials in a high temperature electric furnace or a high temperature roasting furnace or a high temperature roasting kiln at 1130-1150 DEG C according to the ceramic preparation process. The ceramic product is resistant to acid and alkali, is not glazed, is free from seepage, has good air permeability and has wide range of application. The method is simple in process, low in cost and low in energy consumption.
Description
Technical field
The present invention relates to stupalith and product technique field thereof.
Background technology
At present, existing pottery making material, succession in thousand is take clay as main, has the clay burning into sand concurrently, to increase pottery intensity.The firing temperature of pottery generally about 900 ~ 1100 ℃, how not glazing or execute the low temperature lead glaze, tire matter is careless, intensity is low, the carcass water-intake rate is high.
Basalt is now through being usually used in the industries such as construction industry, industry, garden landscape.The precedent of using as the fictile raw material take porous basalt as main component had not been arranged, and basalt is just being used aspect the making of glaze to some extent.
The present invention carries out proportioning to unselected clay and porous basalt particle according to " volume ratio ", that is: the dry clay powder 50 ~ 70 that filters through 300 mesh sieves; Less than or equal to 60 purpose porous basalt particles 30 ~ 50; The raw material that proportioning is mixed tempers and makes various types of implements; It is rear according to outward appearance needs can select whether the to polish surface of implements to dry in the shade, and selects 200 purpose sand paper that the polish clay on local top layer of needs is ground off during polishing, exposes the porous basalt particle and gets final product kiln-firing.Through 1130 ~ 1150 ℃ of porous basalt particle fictiles that are fired into, cost is low, and simple process has acid and alkali-resistance, good permeability, not glazing, impermeable characteristics; Dry in the shade pottery before firing, fall surperficial clay through sand papering, the texture coarse porous basalt itself shows, and is again a kind of good artistic expression.
Summary of the invention
Technology implementation procedure of the present invention:
Pottery powder material: porous basalt particle, clay.
Porous basalt is ground into less than or equal to 60 purpose particles for subsequent use.
The clay water cleans, and with the filtration of 300 mesh sieves, precipitates and to be dried to powder for subsequent use.
Pottery powder material and pottery wet end furnish (volume ratio): dry clay powder 50 ~ 70; Porous basalt particle 30 ~ 50.
And mud: the good porous basalt particle of proportioning and clay are added water stir, make the pottery material-mud or walk gets final product according to the requirement of doing implements.
Moulding: mould molding or manual assembly can.Carry out and dry in the shade after greenwave according to the outward appearance needs, the surface of selecting whether to polish if the polishing surface can use 200 order sand paper that the clay on greenwave surface is polished off, manifests the porous basalt particle and gets final product.
Fire: greenwave is put into high-temperature electric resistance furnace or high-temperature roasting furnace or high-temperature roasting kiln, under 110 ~ 150 ℃ temperature dry 1 hour first, then slowly be warmed up to 580 ~ 600 ℃ and be incubated 10 ~ 20 minutes, again slowly be warmed up to 1130 ~ 1150 ℃ roasting temperature 30-60 minute, can obtain after cooling various types of porous basalt particle pottery moulded products.
Claims (2)
1. porous basalt particle fictile, it is characterized in that: by porous basalt particle and Clay composition, its volume ratio is: less than or equal to 60 purpose porous basalt particle 30-50, less than or equal to 300 purpose dry clay powder 50-70; Described goods are exactly the moulded products of making of porous basalt particle and clay.
2. the preparation method of porous basalt particle fictile as claimed in claim 1, it is characterized in that: the preparation of porous basalt particle fictile comprises: the raw material in will filling a prescription evenly is in harmonious proportion according to proportioning; Through overmolding, dry in the shade; Select whether to carry out surface finish according to the outward appearance needs, if polishing, select 200 purpose sand paperings to appear to the porous basalt particle till; Greenwave is put into high-temperature electric resistance furnace or high-temperature roasting furnace or high-temperature roasting kiln, under 110 ~ 150 ℃ temperature dry 1 hour first, then slowly be warmed up to 580 ~ 600 ℃ and be incubated 10 ~ 20 minutes, again slowly be warmed up to 1130 ~ 1150 ℃ roasting temperature 30-60 minute, can obtain after cooling various types of porous basalt particle pottery moulded products.