CN102976621A - Method for manufacturing glass carbon fiber composite material - Google Patents
Method for manufacturing glass carbon fiber composite material Download PDFInfo
- Publication number
- CN102976621A CN102976621A CN2012104741526A CN201210474152A CN102976621A CN 102976621 A CN102976621 A CN 102976621A CN 2012104741526 A CN2012104741526 A CN 2012104741526A CN 201210474152 A CN201210474152 A CN 201210474152A CN 102976621 A CN102976621 A CN 102976621A
- Authority
- CN
- China
- Prior art keywords
- glass
- fibre composite
- carbon fiber
- carbon fibre
- vitreous carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a method for manufacturing a glass carbon fiber composite material. The method comprises the following steps of: 1, supplying a raw material, wherein the raw material comprises glass, carbon fibers and an organic solvent; 2, smashing the glass to obtain glass powder; 3, dispersing the carbon fibers by the organic solvent; 4, mixing and stirring the glass powder and the dispersed carbon fiber to obtain a glass carbon fiber composite material blank body; 5, smelting the glass carbon fiber composite material blank body to obtain slurry; and 6, injecting the slurry into a die, cooling, and obtaining the glass carbon fiber composite material. By the method for preparing the glass carbon fiber composite material, the glass and the carbon fibers are fused to obtain the glass carbon fiber composite material; the glass carbon fiber composite material is relatively high in strength and flexibility; an ornament made of the composite material is high in strength and anti-abrasion; and the method is simple and easy to operate and is favorable for improving the production efficiency.
Description
Technical field
The present invention relates to vitreous carbon fibre composite field, relate in particular to a kind of making method of vitreous carbon fibre composite.
Background technology
The glass quality is hard, and is transparent, wherein adds metal or metal oxide and can show different colours, can be used for decorating, but simple glass intensity is very low, frangible.The vitreous carbon fibre composite is that glass mixes the matrix material that forms with carbon fiber, can effectively improve the shortcoming of Glass breadks easily, has the advantages such as high strength, high tenacity, high heat resistance, high corrosion resistance.Existing vitreous carbon fibre composite making method comprises the employing manual pasting forming process, the at room temperature moulding of this manufacture craft, and facility investment is few, but because the method belongs to labour-intensive production, production efficiency is low.
Summary of the invention
The object of the present invention is to provide a kind of making method of vitreous carbon fibre composite, can obtain the vitreous carbon fibre composite, attractive in appearance with the ornaments of its making, intensity is better, and the method is simple to operation, is conducive to enhance productivity.
For achieving the above object, the invention provides a kind of making method of vitreous carbon fibre composite, comprise the steps:
Step 1 is supplied raw materials, and this raw material comprises glass, carbon fiber and organic solvent;
Step 2 is made glass powder to glass;
Step 3 is disperseed carbon fiber with organic solvent;
Step 4, glass powder with disperse after carbon fiber mixes and stirring, obtain vitreous carbon fibre composite base substrate;
Step 5, melten glass carbon-fibre composite base substrate obtain molten slurry;
Step 6 is injected mould with above-mentioned molten slurry, and cooling obtains the vitreous carbon fibre composite.
In the step 2, glass added hot melt dusts in the fuse machine, obtain glass powder through air cooling.
In the step 3, the length of described carbon fiber is 1-6mm.
In the step 4, glass powder and carbon fiber after mixing and the stirring are air-dry under state of nature.
In the step 5, melt temperature is 800 ℃.
The fracture toughness property of described vitreous carbon fibre composite is 600-800MPam
1/2
Described mould is wrist-watch mould or ornament mould.
Beneficial effect of the present invention: the making method of vitreous carbon fibre composite of the present invention, by glass and carbon fiber fusion are obtained the vitreous carbon fibre composite, has higher intensity and toughness, the ornaments intensity of making of this matrix material is high, wear-resistant, the method is simple to operation, is conducive to enhance productivity.
Embodiment
The invention provides a kind of making method of vitreous carbon fibre composite, comprise the steps:
Step 1 is supplied raw materials, and this raw material comprises glass, carbon fiber and organic solvent.
Step 2 is made glass powder to glass, glass is added hot melt dusts in the fuse machine, obtains glass powder through air cooling.
Step 3 is disperseed carbon fiber with organic solvent, and obtaining length is the finely dispersed carbon fiber of 1-6mm.
Step 4, glass powder with disperse after carbon fiber mix, stir, air-dry under state of nature, obtain vitreous carbon fibre composite base substrate.
Step 5, melten glass carbon-fibre composite base substrate obtain molten slurry, and melt temperature is 800 ℃.
Step 6 is injected mould with above-mentioned molten slurry, and cooling obtains the vitreous carbon fibre composite, and this mould is wrist-watch mould or ornament mould.The fracture toughness property of this vitreous carbon fibre composite is 600-800MPam
1/2, can be used for producing the ornaments such as wrist-watch or jewelry, prepared ornaments have higher intensity and toughness, and are wear-resistant, even use still has preferably outward appearance through the long period.
In sum, the making method of vitreous carbon fibre composite of the present invention, by glass and carbon fiber fusion are obtained the vitreous carbon fibre composite, has higher intensity and toughness, the ornaments intensity of making of this matrix material is high, wear-resistant, the method is simple to operation, is conducive to enhance productivity.
The above; for the person of ordinary skill of the art; can make other various corresponding changes and distortion according to technical scheme of the present invention and technical conceive, and all these changes and distortion all should belong to the protection domain of the accompanying claim of the present invention.
Claims (7)
1. the making method of a vitreous carbon fibre composite is characterized in that, comprises the steps:
Step 1 is supplied raw materials, and this raw material comprises glass, carbon fiber, reaches organic solvent;
Step 2 is made glass powder to glass;
Step 3 is disperseed carbon fiber with organic solvent;
Step 4, glass powder with disperse after carbon fiber mixes and stirring, obtain vitreous carbon fibre composite base substrate;
Step 5, melten glass carbon-fibre composite base substrate obtain molten slurry;
Step 6 is injected mould with above-mentioned molten slurry, and cooling obtains the vitreous carbon fibre composite.
2. the making method of vitreous carbon fibre composite as claimed in claim 1 is characterized in that, in the step 2, glass is added hot melt dusts in the fuse machine, obtains glass powder through air cooling.
3. the making method of vitreous carbon fibre composite as claimed in claim 1 is characterized in that, in the step 3, described carbon fiber length is 1-6mm.
4. the making method of vitreous carbon fibre composite as claimed in claim 1 is characterized in that, in the step 4, glass powder and carbon fiber after mixing and the stirring are air-dry under state of nature.
5. the making method of vitreous carbon fibre composite as claimed in claim 1 is characterized in that, in the step 5, melt temperature is 800 ℃.
6. the making method of vitreous carbon fibre composite as claimed in claim 1 is characterized in that, the fracture toughness property of described vitreous carbon fibre composite is 600-800MPam
1/2
7. the making method of vitreous carbon fibre composite as claimed in claim 1 is characterized in that, in the step 6, described mould is wrist-watch mould or ornament mould.