CN102964900A - Emulsion paint thickener and preparation method thereof - Google Patents
Emulsion paint thickener and preparation method thereof Download PDFInfo
- Publication number
- CN102964900A CN102964900A CN201210488276XA CN201210488276A CN102964900A CN 102964900 A CN102964900 A CN 102964900A CN 201210488276X A CN201210488276X A CN 201210488276XA CN 201210488276 A CN201210488276 A CN 201210488276A CN 102964900 A CN102964900 A CN 102964900A
- Authority
- CN
- China
- Prior art keywords
- reaction
- emulsion paint
- preparation
- thickening material
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an emulsion paint thickener. The structural formula is as follows: the monomer before an IPDI (isophorone diisocyanate) reaction is isophorone diisocyanate; the monomer before a PEG (polyethylene glycol) reaction is polyethylene glycol; and the monomer before an HDI (Hexamethylene Diisocyanate) reaction is hexamethylene diisocyanate. The preparation method comprises the following steps: under the protection of the nitrogen, mixing polyethylene glycol, hexamethylene diisocyanate, dibutyltin dilaurate with anhydrous acetone, carrying out a backflow reaction, removing the acetone, adding isophorone diisocyanate, octadecanol and toluene, and carrying out a warming reaction to prepare the emulsion paint thickener. Non-specific association can be generated between a hydrophobic group on a thickener branched chain and components such as a wetting agent and an active agent in the emulsion paint, a three-dimensional reticulated structure is formed for thickening, the emulsion paint thickener has higher dragging viscosity, the thickness of the coating can be increased, and the leveling property of a paint film is better; and besides, the hard segment structure of a polymer molecule is increased by adopting a hydrophobic segment on the main chain, the viscosity of the emulsion at high shear is enhanced, emulsion particles can be dispersed easily, and the system is more stable.
Description
Technical field
The invention belongs to the thickening material technical field, be specifically related to a kind of emulsion paint thickening material and preparation method thereof.
Background technology
Thickening material is a kind of key ingredient of emulsion paint, and being affects the most important factor of its rheological property.At present, one of emulsion paint thickening material that hydroxylated cellulose is commonly used, the water-soluble polymer that it is a kind of better performances, range of application is wider, water-soluble after, give birth to strong hydration with steeping in water for reconstitution, produce between molecular chain and twine, thereby increased solution viscosity.But a little less than the cellulosic molecule absorption, as easy as rolling off a logly replaced by wetting agent, the tensio-active agent in the emulsion in the lacquer etc., be free on aqueous phase, thereby flocculation appears, and because the Mierocrystalline cellulose relative molecular weight is usually very high, cause coating viscosity under high shear rate little, fullness ratio and levelling property that impact is filmed.
Summary of the invention
The technical problem that the present invention mainly solves is: a kind of polyether(poly)urethane association emulsion paint thickening material is provided.
The technical scheme that mainly provides of the present invention: a kind of emulsion paint thickening material, its structural formula is:
Wherein, monomer is isophorone diisocyanate before the IPDI reaction; Monomer is polyoxyethylene glycol before the PEG reaction; Monomer is hexamethylene diisocyanate before the HDI reaction.
Second technical problem to be solved by this invention is: the preparation method that a kind of emulsion paint thickening material is provided.
For solving second technical problem, technical scheme provided by the invention is: a kind of preparation method of emulsion paint thickening material the steps include:
Under nitrogen protection; polyoxyethylene glycol and hexamethylene diisocyanate are added reactor; add dibutyl tin laurate, anhydrous propanone; be heated to 55-65 ℃, back flow reaction 5-6h, when the content of isocyanate group behind certain value; acetone is removed in underpressure distillation; add isophorone diisocyanate, stearyl alcohol, toluene, be warming up to 120-135 ℃ of reaction 2-3h, namely make the polyether(poly)urethane associative thickener.
The molar ratio of described polyoxyethylene glycol, hexamethylene diisocyanate, dibutyl tin laurate, anhydrous propanone, isophorone diisocyanate, stearyl alcohol, toluene is 1.5-2.0:1:0.2-0.3:10-20:1.2-1.8:2.0-3.0:10-15.
Described isocyanate group detection method is the Di-n-Butyl Amine method, when volumetric molar concentration reaches 0.4-0.7mol/L, reacts and finishes.
The number-average molecular weight of described polyoxyethylene glycol is 10000 ~ 10500.
Beneficial effect of the present invention is: the hydrophobic grouping on this thickening material side chain can and emulsion paint in the components such as wetting agent, promoting agent between produce nonspecific association, form simultaneously tridimensional network and thickening, have higher dragging and shoot a retrievable arrow viscosity, be conducive to increase the thickness of coating, the levelling property of paint film is better; Hydrophobic section on the main chain has increased the polymer molecule hard segment structure, improves the viscosity under the emulsion high-shear, help emulsion particle dispersion, make system more stable.
Embodiment
Be described in further detail in conjunction with specific embodiments, make advantage of the present invention more obvious.Should be appreciated that content wherein is just with explaining, and absolutely not protection scope of the present invention is construed as limiting.The experimental technique of unreceipted actual conditions in the following example usually according to normal condition, or carries out according to the condition that manufacturer advises.
Embodiment 1
Under nitrogen protection; 10mol PEG-6000 0 and 6mol hexamethylene diisocyanate are dropped into reactor; add the 1.2mol dibutyl tin laurate; add the 120mol anhydrous propanone; be heated to 55-60 ℃, back flow reaction 5-6h, when the content of isocyanate group behind 0.48-0.52mol/L; revolve steaming, remove acetone.Add 8.0mol isophorone diisocyanate, 12mol stearyl alcohol, 62mol toluene, be warming up to 120-135 ℃ of reaction 2-3h, namely make the polyether(poly)urethane associative thickener.
Embodiment 2
Under nitrogen protection; 18mol PEG-6000 0 and 10mol hexamethylene diisocyanate are dropped into reactor; add the 2mol dibutyl tin laurate; add the 150mol anhydrous propanone; be heated to 55-65 ℃, back flow reaction 5-6h is after the content of isocyanate group is 0.65-0.7mol/L; revolve steaming, remove acetone.Add 15mol isophorone diisocyanate, 23mol stearyl alcohol, 110mol toluene, be warming up to 120-135 ℃ of reaction 2-3h, namely make the polyether(poly)urethane associative thickener.
Claims (5)
2. the preparation method of a kind of emulsion paint thickening material claimed in claim 1 the steps include:
Under nitrogen protection; polyoxyethylene glycol and hexamethylene diisocyanate are added reactor; add dibutyl tin laurate, anhydrous propanone; be heated to 55-65 ℃, back flow reaction 5-6h, when the content of isocyanate group behind certain value; acetone is removed in underpressure distillation; add isophorone diisocyanate, stearyl alcohol, toluene, be warming up to 120-135 ℃ of reaction 2-3h, namely make the polyether(poly)urethane associative thickener.
3. the preparation method of a kind of emulsion paint thickening material according to claim 2, it is characterized in that: the molar ratio of described polyoxyethylene glycol, hexamethylene diisocyanate, dibutyl tin laurate, anhydrous propanone, isophorone diisocyanate, stearyl alcohol, toluene is 1.5-2.0:1:0.2-0.3:10-20:1.2-1.8:2.0-3.0:10-15.
4. the preparation method of a kind of emulsion paint thickening material according to claim 3, it is characterized in that: described isocyanate group detection method is the Di-n-Butyl Amine method, when volumetric molar concentration reaches 0.4-0.7mol/L, reaction finishes.
5. the preparation method of any described a kind of emulsion paint thickening material of claim according to claim 2-4, it is characterized in that: the number-average molecular weight of described polyoxyethylene glycol is 10000 ~ 10500.