CN102964885B - 核壳型有机硅耐久涂料及其制作方法 - Google Patents
核壳型有机硅耐久涂料及其制作方法 Download PDFInfo
- Publication number
- CN102964885B CN102964885B CN201210491373.4A CN201210491373A CN102964885B CN 102964885 B CN102964885 B CN 102964885B CN 201210491373 A CN201210491373 A CN 201210491373A CN 102964885 B CN102964885 B CN 102964885B
- Authority
- CN
- China
- Prior art keywords
- paint
- core
- organic silicon
- mentioned weight
- weight portion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了核壳型有机硅耐久涂料及其制作方法,在密闭的压力容器中,加入上述重量份的水、纤维素等50‑70℃利用水热法混合制核,反应时间不少于30min,然后以连续滴加方式加入上述重量比的分散剂DP270、杀菌剂XG‑405、涂料消泡剂NXZ等同时加入聚合,均匀搅拌、熟化、调正粘度,经过技术指标检验合格后计量包装。本发明的有益效果是:制造工艺简单、制造成本低适合产业化,是新一代水性涂料的最佳代表,集合了水性涂料的环保与油性涂料的保光、保色、超耐候、超耐污性能,涂膜具有耐酸、耐碱、耐化学品污染等性能良好,适用于各种住宅、写字楼、酒店、厂房、学校等大型建筑物的新建工程及工程。
Description
技术领域
本发明涉及核壳型有机硅耐久涂料及其制作方法,属于涂料技术领域。
背景技术
通过在纳米粉体表面包膜改变粉体性的方法是表面覆盖改性方法中的一种重要方法,壳层既可以是有机物或无机物。根据需要使其具有物物兼容性或提高其热机械及化学稳定性,改变光、磁、电性及使用寿命,控制纳米粉体的表面化学组成是提高附加值纳米粉体的关键。
核壳型聚合物是一种具有独特结构的聚合物复合粒子,它比通常的乳液共混物或无规共聚物有更好的稳定性、粘合性及力学性能,因而在黏合剂、防腐剂、装饰涂料,以及感光材料等领域有着广泛的应用。
由于已有的核壳型纳米粉体材料的制备工艺,基本上采用先制备好纳米核粒再进行包膜的工艺路线,后期经过晶化热处理,而工艺流程复杂,生产周期长,造制成本高,实现产业化有局限性。
发明内容
本发明的目的在于提供核壳型有机硅耐久涂料及其制作方法,能制作一种制造工艺简单、制造成本低适合产业化并具有良好稳定性、粘合性及力学性能的涂料。
本发明的目的是通过以下技术方案来实现的:核壳型有机硅耐久涂料,它由以下重量份的原料制成:
核壳型有机硅耐久涂料的制作方法,在密闭的压力容器中,加入上述重量份的水、纤维素、金红石、煅烧高岭土、沉淀硫酸钡、云母粉、重钙以及乙二醇在50~70℃利用水热法混合制核,反应时间不少于30min,然后以连续滴加方式加入上述重量比的分散剂DP270、杀菌剂XG-405、涂料消泡剂NXZ、功能助剂AMP-95、功能助剂2100、成膜助剂、增稠剂TT-936、流平剂HEUR-D以及防腐剂同时加入聚合,均匀搅拌、熟化、调正粘度,经过技术指标检验合格后计量包装。
本发明的有益效果在于:制造工艺简单、制造成本低适合产业化,制得的涂料具有良好稳定性、粘合性及力学性能,涂膜光泽柔和优美,使得涂膜化学稳定性极高,从而达到长期耐用的超耐久性能,采用核壳技术形成的致密而坚韧的涂膜,具有良好的憎水透气性和高自洁性,是新一代水性涂料的最佳代表,集合了水性涂料的环保与油性涂料的保光、保色、超耐候、超耐污性能,涂膜具有耐酸、耐碱、耐化学品污染等性能良好,适用于各种住宅、写字楼、酒店、厂房、学校等大型建筑物的新建工程及工程。
具体实施方式
下面结合实施例进一步描述本发明的技术方案,但要求保护的范围并不局限于所述。
实施例1
核壳型有机硅耐久涂料,它由以下重量份的原料制成:
核壳型有机硅耐久涂料的制作方法,在密闭的压力容器中,加入上述重量份的水、纤维素、金红石、煅烧高岭土、沉淀硫酸钡、云母粉、重钙以及乙二醇在70℃利用水热法混合制核,反应时间30min,然后以连续滴加方式加入上述重量比的分散剂DP270、杀菌剂XG-405、涂料消泡剂NXZ、功能助剂AMP-95、功能助剂2100、成膜助剂、增稠剂TT-936、流平剂HEUR-D以及防腐剂同时加入聚合,均匀搅拌、熟化、调正粘度,经过技术指标检验合格后计量包装。
实施例2
核壳型有机硅耐久涂料,它由以下重量份的原料制成:
核壳型有机硅耐久涂料的制作方法,在密闭的压力容器中,加入上述重量份的水、纤维素、金红石、煅烧高岭土、沉淀硫酸钡、云母粉、重钙以及乙二醇在70℃利用水热法混合制核,反应时间60min,然后以连续滴加方式加入上述重量比的分散剂DP270、杀菌剂XG-405、涂料消泡剂NXZ、功能助剂AMP-95、功能助剂2100、成膜助剂、增稠剂TT-936、流平剂HEUR-D以及防腐剂同时加入聚合,均匀搅拌、熟化、调正粘度,经过技术指标检验合格后计量包装。
实施例3
核壳型有机硅耐久涂料的制作方法,在密闭的压力容器中,加入上述重量份的水、纤维素、金红石、煅烧高岭土、沉淀硫酸钡、云母粉、重钙以及乙二醇在60℃利用水热法混合制核,反应时间50min,然后以连续滴加方式加入上述重量比的分散剂DP270、杀菌剂XG-405、涂料消泡剂NXZ、功能助剂AMP-95、功能助剂2100、成膜助剂、增稠剂TT-936、流平剂HEUR-D以及防腐剂同时加入聚合,均匀搅拌、熟化、调正粘度,经过技术指标检验合格后计量包装。
实施例4
核壳型有机硅耐久涂料的制作方法,在密闭的压力容器中,加入上述重量份的水、纤维素、金红石、煅烧高岭土、沉淀硫酸钡、云母粉、重钙以及乙二醇在55℃利用水热法混合制核,反应时间40min,然后以连续滴加方式加入上述重量比的分散剂DP270、杀菌剂XG-405、涂料消泡剂NXZ、功能助剂AMP-95、功能助剂2100、成膜助剂、增稠剂TT-936、流平剂HEUR-D以及防腐剂同时加入聚合,均匀搅拌、熟化、调正粘度,经过技术指标检验合格后计量包装。
实施例5
核壳型有机硅耐久涂料的制作方法,在密闭的压力容器中,加入上述重量份的水、纤维素、金红石、煅烧高岭土、沉淀硫酸钡、云母粉、重钙以及乙二醇在65℃利用水热法混合制核,反应时间45min,然后以连续滴加方式加入上述重量比的分散剂DP270、杀菌剂XG-405、涂料消泡剂NXZ、功能助剂AMP-95、功能助剂2100、成膜助剂、增稠剂TT-936、流平剂HEUR-D以及防腐剂同时加入聚合,均匀搅拌、熟化、调正粘度,经过技术指标检验合格后计量包装。
Claims (1)
1.核壳型有机硅耐久涂料,其特征在于:它由以下重量份的原料制成:
所述核壳型有机硅耐久涂料的制作方法:在密闭的压力容器中,加入上述重量份的水、纤维素、金红石、煅烧高岭土、沉淀硫酸钡、云母粉、重钙以及乙二醇在50~70℃利用水热法混合制核,反应时间不少于30min,然后以连续滴加方式加入上述重量份的分散剂DP270、杀菌剂XG-405、涂料消泡剂NXZ、功能助剂AMP-95、功能助剂2100、成膜助剂、增稠剂TT-936、流平剂HEUR-D以及防腐剂同时加入聚合,均匀搅拌、熟化、调整粘度,经过技术指标检验合格后计量包装。