CN102943147A - 提高钢水钙处理效果的装置 - Google Patents
提高钢水钙处理效果的装置 Download PDFInfo
- Publication number
- CN102943147A CN102943147A CN2012105344590A CN201210534459A CN102943147A CN 102943147 A CN102943147 A CN 102943147A CN 2012105344590 A CN2012105344590 A CN 2012105344590A CN 201210534459 A CN201210534459 A CN 201210534459A CN 102943147 A CN102943147 A CN 102943147A
- Authority
- CN
- China
- Prior art keywords
- line
- guide pipe
- steel
- molten steel
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种提高钢水钙处理效果的装置的技术方案，该方案包括支架，该支架上设置有喂丝机和驱动电机，该驱动电机连接有升降构件，其特征在于：所述喂丝机一端连接有丝线，该丝线外包裹有钢结构导管，该钢结构导管外浇注有抗冲刷耐高温材料，所述钢结构导管的长度大于抗冲刷耐高温材料的长度，所述钢结构导管内、丝线外套装有顺线导管，该顺线导管一端连接有喂丝机，另一端伸入到抗冲刷耐高温材料高度以下，所述钢结构导管一端固定有滑块，该滑块固定连接有固定导线管，该固定导线管道另一端通过滑块与升降构件固定连接。该装置能显著提高钙线中Ca收得率，稳定钢水中[Ca]Tot含量和减少喂丝时钢水二次氧化。
Description
技术领域
本发明涉及一种炼钢钢包炉二次精炼设备，尤其涉及一种提高钢水钙处理效果的装置。
背景技术
冶金行业中，用于炼钢钢包二次精炼设备，在生产铝脱氧钢和高级别管线钢时，为了有效防止浇铸过程中塞棒水口结瘤以及由氢致裂纹引起的管线钢失效等质量事故，必须对钢水中硫化物和氧化物进行变性处理，通常在钢水中喂入Ca-Si或Ca-Fe线对MnS和Al2O3夹杂进行变性处理，LF、RH、VD（LF、RH、VD为钢水精炼方式的简称）等钢包精炼炉处理完毕钢水[Ca]Tot（[Ca]Tot 是钢水中Ca含量的表述方式）控制在20-50×10-6，将MnS和Al2O3类夹杂物变为球形钙铝酸盐或CaO-CaS-Al2O3夹杂。但在实际生产中，由于钢包渣结壳、渣层较厚、渣中氧含量高等因素的影响，往往出现丝线在钢渣层打圈或被氧化性渣氧化现象，造成钙线中Ca收得率不稳定，钢水中[Ca]Tot偏低，不能实现钢水中非金属夹杂完全变性的目的。
发明内容
本发明所要解决的技术问题，就是针对现有技术所存在的不足，而提供一种能显著提高钙线中Ca收得率，稳定钢水中[Ca]Tot含量和减少喂丝时钢水二次氧化的提高钢水钙处理效果的装置。
本方案是通过如下技术措施来实现的：提高钢水钙处理效果的装置，包括支架，该支架上设置有喂丝机和驱动电机，该驱动电机连接有升降构件，所述喂丝机一端连接有丝线，该丝线外包裹有钢结构导管，该钢结构导管外浇注有抗冲刷耐高温材料，所述钢结构导管的长度大于抗冲刷耐高温材料的长度，所述钢结构导管内、丝线外套装有顺线导管，该顺线导管一端连接有喂丝机，另一端伸入到抗冲刷耐高温材料高度以下，所述钢结构导管一端固定有滑块，该滑块固定连接有固定导线管，该固定导线管道另一端通过滑块与升降构件固定连接。
所述升降构件包括两个传动轮，上端的传动轮与驱动电机的输出轴相连，下端的传动轮与固定座固定连接，两传动轮直接设置有传动带。
本方案的有益效果可根据对上述方案的叙述得知，由于在该方案中钢结构导管外浇注有抗冲刷耐高温材料，在钢水钙处理时，将浇铸抗冲刷耐高温材料的钢结构导管***钢水，避免由于钢包渣结壳、渣层较厚、造渣脱氧不良等条件影响造成丝线在钢渣层打圈或被氧化性渣氧化，使得钢水中[Ca]Tot不稳定，不能满足钢水中非金属夹杂变性的效果。
附图说明
图1为本发明具体实施方式的结构示意图。
图中：1为抗冲刷耐高温材料；2为丝线；3为固定导线部件；4为钢结构导管；5为顺线钢管；6为喂丝机；7为支架；8为升降构件；9为固定座；10为驱动电机。
具体实施方式
为能清楚说明本方案的技术特点，下面通过一个具体实施方式，并结合其附图，对本方案进行阐述。
通过附图可以看出，本方案的提高钢水钙处理效果的装置，包括支架，该支架上设置有喂丝机和驱动电机，该驱动电机连接有升降构件，所述喂丝机一端连接有丝线，该丝线外包裹有钢结构导管，该钢结构导管外浇注有抗冲刷耐高温材料，所述钢结构导管的长度大于抗冲刷耐高温材料的长度，所述钢结构导管内、丝线外套装有顺线导管，该顺线导管一端连接有喂丝机，另一端伸入到抗冲刷耐高温材料高度以下，所述钢结构导管一端固定有滑块，该滑块固定连接有固定导线管，该固定导线管道另一端通过滑块与升降构件固定连接。
所述升降构件包括两个传动轮，上端的传动轮与驱动电机的输出轴相连，下端的传动轮与固定座固定连接，两传动轮直接设置有传动带。
本方案的有益效果可根据对上述方案的叙述得知，由于在该方案中钢结构导管外浇注有抗冲刷耐高温材料，在钢水钙处理时，将浇铸抗冲刷耐高温材料的钢结构导管***钢水，避免由于钢包渣结壳、渣层较厚、造渣脱氧不良等条件影响造成丝线在钢渣层打圈或被氧化性渣氧化，使得钢水中[Ca]Tot不稳定，不能满足钢水中非金属夹杂变性的效果。
本发明未经描述的技术特征可以通过现有技术实现，在此不再赘述。当然，上述说明并非是对本发明的限制，本发明也并不仅限于上述举例，本技术领域的普通技术人员在本发明的实质范围内所做出的变化、改型、添加或替换，也应属于本发明的保护范围。
Claims (2)
1.一种提高钢水钙处理效果的装置，包括支架，该支架上设置有喂丝机和驱动电机，该驱动电机连接有升降构件，其特征在于：所述喂丝机一端连接有丝线，该丝线外包裹有钢结构导管，该钢结构导管外浇注有抗冲刷耐高温材料，所述钢结构导管的长度大于抗冲刷耐高温材料的长度，所述钢结构导管内、丝线外套装有顺线导管，该顺线导管一端连接有喂丝机，另一端伸入到抗冲刷耐高温材料高度以下，所述钢结构导管一端固定有滑块，该滑块固定连接有固定导线管，该固定导线管道另一端通过滑块与升降构件固定连接。
2.根据权利要求1所述的提高钢水钙处理效果的装置，其特征在于：所述升降构件包括两个传动轮，上端的传动轮与驱动电机的输出轴相连，下端的传动轮与固定座固定连接，两传动轮直接设置有传动带。