CN102936837B - Water and oil-repellent flame-retardant all-cotton fabric preparation technology and application thereof - Google Patents
Water and oil-repellent flame-retardant all-cotton fabric preparation technology and application thereof Download PDFInfo
- Publication number
- CN102936837B CN102936837B CN201210419647.9A CN201210419647A CN102936837B CN 102936837 B CN102936837 B CN 102936837B CN 201210419647 A CN201210419647 A CN 201210419647A CN 102936837 B CN102936837 B CN 102936837B
- Authority
- CN
- China
- Prior art keywords
- water
- oil
- retardant
- flame
- preparation technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to the field of textile processing, and particularly relates to a water and oil-repellent flame-retardant all-cotton fabric preparation technology and application thereof. The water and oil-repellent flame-retardant all-cotton fabric preparation technology comprises the following steps of: 1) spinning technology: spinning and weaving cotton fiber to obtain gray fabric; 2) performing pretreatment and dyeing; 3) flame-retardant finishing: soaking the gray fabric in the flame-retardant finishing liquid, and sequentially performing padding, drying, baking, washing and drying; 4) water and oil-repellent finishing: soaking the gray fabric in the water and oil-repellent finishing liquid, and sequentially performing padding, drying, baking, soaping, washing and drying; and 5) performing an after-finishing technology. The processing technology provided by the invention is applicable to the production system of the existing textile enterprises, and does not need to replace or update the equipment; and the prepared water and oil-repellent flame-retardant all-cotton fabric has water and oil repellency and flame retardation, can effectively protect a human body, and maintains the soft hand feeling, high durability and wearing comfort of fabric.
Description
Technical field
The present invention relates to textile processing field, be specifically related to preparation technology and the application thereof of the fire-retardant all-cotton fabric of a kind of water and oil repellant.
Background technology
Because existing greasy dirt, operation place, naval vessel is infected with and disaster hidden-trouble; Work Clothes is as human body and extraneous shielding; should there is the oil of refusing, refuse water and fire resistance, thereby effectively protect human body to escape injury, keep soft feel, excellent durability and snugness of fit simultaneously.
Rear arrangement is that fabric obtains the major way of refusing oil, water repellency, and essence is in fabric face absorption layer of substance, makes the high energy surface of fabric become low-energy surface, obtains the fabric of refusing oil, refusing water effect with this; And fabric face can be less, refuse oil, refuse water effect better.
Du pont company has carried out the trial of fluoropolymer fabric water and oil repellent finish at first the 1950's.Afterwards, 3M company has researched and developed the fabric finishing agent taking perfluorocarboxylic acid chromium complex as main component, but this perfluorocarboxylic acid chromium complex fabric finishing agent is replaced by the better fluorine-containing propene vinegar of performance polymer soon, becomes the main flow of refusing now water, refusing oil and soil resistant finish.Refuse that water, oil-repellent finiss technique should " roll and cure " according to the corresponding employing of actual requirement, the process route of top finish and the two combination.
Make fabric obtain one of method of fire resistance for flame-retardant finishing method, fabric is carried out to surface treatment, to reach fire-retardant object.This processing mode comprises spraying, pads and three kinds of coatings.Wherein, the processing mode padding is mainly used in processing dress ornament series products.
Summary of the invention
The object of the invention is to overcome the defect of prior art, provide a kind of novel, possess simultaneously refuse water, refuse oil, the cotton fabric of resistant, the performance such as fire-retardant, and the preparation method and application of this fabric are disclosed, for textile processing industry provides new fabric panel.
First the present invention discloses the preparation technology of the fire-retardant all-cotton fabric of a kind of water and oil repellant, comprises the steps:
1) weaving: adopt cotton fiber to spin, weave, obtain grey cloth;
2) pre-treatment and dyeing;
3) flame-proof treatment: grey cloth is immersed in fire retarding treating liquid, pads successively, dry, bake, wash and dry;
4) water and oil repellent finish: grey cloth is immersed in water and oil repellent finish liquid, pads successively, dry, bake, soap, wash and dry;
5) postfinishing process;
Wherein, described in step 3), fire retarding treating liquid is the aqueous solution that comprises following component and concentration:
380~420g/L Pyrovarex CP (antiflaming finishing agent)
18~22g/L phosphoric acid (catalyst)
12~17g/L uric acid
10~20g/L softener
Described in step 4), water and oil repellent finish liquid is the aqueous solution that comprises following component and concentration:
45~55g/L Oleophobol CP-C (water-refusing oil-refusing finishing agent)
18~22g/L knittex FEL(crosslinking agent)
12~16g/L knittex CATALYST MO LIQ(crosslinking agent)
4~6g/L wetting agent.
Preferably, described in step 1), cotton fiber is long-staple cotton fiber.
Preferably, the resultant yarn mode of spinning described in step 1) is RING SPINNING, and the fineness of yarn is 12~20S.Preferably the fineness of yarn is 12S, 16S, 20S.
Preferably, in weaving process, fabric structure adopts 1/3 twill-weave described in step 1).
Why the present invention adopts 1/3 twill-weave to be because 1/3 twill-weave is best in the latitudinal strength of twill the inside, and other tissue affects weaving efficiency and fabric quality, increases cost.
Preferably, described in step 3), flame-proof treatment is specially: grey cloth is immersed in fire retarding treating liquid, and two soak two rolls, pick-up rate 85~95%; 100~110 DEG C of bake out temperatures, dry 2~5min; 160~180 DEG C of baking temperatures, bake 40~70s.
More excellent, flame-proof treatment is specially described in step 3): grey cloth is immersed in fire retarding treating liquid, and two soak two rolls, pick-up rate 90%; 100 DEG C of bake out temperatures, dry 3min; 170 DEG C of baking temperatures, bake 60s.Be that flame-proof finishing process flow process is: pad (two soak two rolls, pick-up rate 90%) → dry (100 DEG C, 3min) → bake (170 DEG C, 60s) → wash → dry (100 DEG C, 3min).
Preferably, the formula of described fire retarding treating liquid is as follows:
400g/L Pyrovarex CP (antiflaming finishing agent)
20g/L phosphoric acid (catalyst)
15g/L uric acid
15g/L softener
Pyrovarex CP based flame retardant is a kind of reactive flame retardant for cellulose base fiber fabric, in its molecule, contains N-methylol.Pyrovarex CP based flame retardant, baking in process and can being cross-linked by the hydroxyl in crosslinking agent and the large molecule of fiber, forms covalent bond; Pyrovarex CP based flame retardant self also can with cellulose macromolecule in hydroxyl crosslinked, therefore this fire retardant has high-durability, and good hand touch, fall lessly by force, whiteness is better, has obtained good effect.
But Pyrovarex CP contains free formaldehyde, after textile finishing, in storage and use procedure, can discharge free formaldehyde.The present invention adopts polynary acids as crosslinking agent, together COTTON FABRIC is carried out to flame-proof treatment with Pyrovarex CP based flame retardant, the flame-retardant textile discharging to obtain low formaldehyde.The present invention adopts phosphoric acid and uric acid to replace the conventional crosslinking agent containing formaldehyde, has reduced on the one hand the free formaldehyde release on content of formaldehyde and the flame-retardant textile of whole flame-retardant system; Reduce on the other hand the consumption of fire retardant and crosslinking agent, saved cost just and improved the application performance of Pyrovarex CP based flame retardant.
Preferably, water and oil repellent finish is specially described in step 4): grey cloth is immersed in water and oil repellent finish liquid, and adjusting dressing liquid pH value is 6.5 ± 0.1,18~22 DEG C of temperature, and one soaks one rolls, pick-up rate 45~55%; Bake out temperature is 110~130 DEG C, dries 2~5min; Baking temperature is 160~180 DEG C, bakes 50~60s.
More excellent, water and oil repellent finish is specially described in step 4): grey cloth is immersed in water and oil repellent finish liquid, and adjusting dressing liquid pH value is 6.5,20 DEG C of temperature, and one soaks one rolls, pick-up rate 50%; Bake out temperature is 120 DEG C, dries 3min; Baking temperature is 170 DEG C, bakes 50~60s.
Further, water and oil repellent finish technological process is: pad (body lotion pH value is 6.5,20 DEG C of temperature, one soaks one rolls, pick-up rate 50%) → dry (120 DEG C, 3min) → bake (170 DEG C, 50~60s) → soap → wash → dry (120 DEG C, 3min).
Preferably, the formula of described water and oil repellent finish liquid is as follows:
50g/L Oleophobol CP-C (water-refusing oil-refusing finishing agent)
20g/L knittex FEL(crosslinking agent)
15g/L knittex CATALYST MO LIQ(crosslinking agent)
5g/L wetting agent.
Preferably, described wetting agent is Invadine PBN.
Oleophobol CP-C water-refusing oil-refusing finishing agent has oil repellent, WATER REPELLENCY, prevents being stained with rain and resistance oil repellent dirt, refuses water-soluble dirt contamination, and water-fastness; After washing, pressed again and can be replied dynamical protection feature.And Oleophobol CP-C water-refusing oil-refusing finishing agent, not containing volatile organic solvent, does not have flash-point yet, does not need special storage facilities.
Step 2 of the present invention) postfinishing process all adopts existing conventional all-cotton fabric pre-treating method, colouring method and postfinishing process described in described pre-treatment and dyeing and step 5).Further, step 2) described pre-treatment process is: singes, destarch, kiering, mercerising; Step 2) described dyeing is: the even pad dyeing material → preliminary drying → oven dry of padding machine → training baking → cooling cropping → fixation → washing → oven dry; Described in step 5), postfinishing process is: stentering forming → preshrunk → perching → packaging.
Secondly the present invention also discloses the fire-retardant all-cotton fabric of the water and oil repellant that adopts aforementioned preparation technology to prepare.
Water and oil repellant flame-retardant textile of the present invention is made up of long-staple cotton fiber, and the resultant yarn mode of this fabric is RING SPINNING, and the fineness of yarn is 12S~20S, and fabric structure adopts 1/3 twill-weave.
The present invention finally also discloses aforementioned preparation technology and water and oil repellant flame-retardant textile is used the application in textiles, drop cloth, curtain, curtain preparation individual protection clothes, children's garment, child.
The advantage of preparation technology of the present invention and fabric is: 1) fabric have concurrently and refuse water, refuse oil, anti-flaming function, and soft, make clothes meet snugness of fit and the health requirements of human body; 2), applicable to the production system of existing textile enterprise, do not need equipment replace or upgrade.
Brief description of the drawings
Fig. 1: preparation technology's flow chart of the fire-retardant all-cotton fabric of water and oil repellant
Detailed description of the invention
Further set forth the present invention below in conjunction with specific embodiment, should be understood that embodiment is only not used in and limits the scope of the invention for the present invention is described.
Embodiment 1
1. experiment material
The superfine long-staple cotton in Xinjiang (commerce and trade Co., Ltd is newly clarified in Xinjiang), antiflaming finishing agent Pyrovarex CP(is purchased from Ciba-Geigy company of Switzerland), softener Ultratex FSA, water-refusing oil-refusing finishing agent Oleophobol CP-C(is purchased from du pont company), knittex FEL(is purchased from Ciba-Geigy company of Switzerland), knittex CATALYST MO LIQ, Invadine PBN(be purchased from company of du pont company).
2. preparation technology
1) textile technology: adopt the superfine long-staple cotton in Xinjiang to spin, weave, obtain grey cloth: adopt RING SPINNING, fineness of yarn is 16S, 12S, carries out 1/3 twill weave (16S × 12S), through close 108, filling density 58.
2) pre-treatment and dyeing: wherein, pre-treatment process is: singe, destarch, kiering, mercerising; Dyeing is: the even pad dyeing material → preliminary drying → oven dry of padding machine → training baking → cooling cropping → fixation → washing → oven dry.
3) flame-proof finishing process: pad (two soak two rolls, pick-up rate 90%) → dry (100 DEG C, 3min) → bake (170 DEG C, 60s) → wash → dry (100 DEG C, 3min).
4) water and oil repellent finish technique: pad (body lotion pH value is 6.5,20 DEG C of temperature, one soaks one rolls, pick-up rate 50%) → dry (120 DEG C, 3min) → bake (170 DEG C, 50~60s) → soap → wash → dry (120 DEG C, 3min);
5) postfinishing process: stentering forming → preshrunk → perching → packaging, obtains the fire-retardant all-cotton fabric of water and oil repellant.
Wherein, the formula of the fire retarding treating liquid of flame-proof finishing process is as follows: 400g/L Pyrovarex CP (antiflaming finishing agent), 20g/L phosphoric acid, 15g/L uric acid, 15g/L softener.
The formula of the dressing liquid of water and oil repellent finish technique is as follows: 50g/L Oleophobol CP-C (water-refusing oil-refusing finishing agent), 20g/L knittex FEL, 15g/L knittex CATALYST MO LIQ, 5g/L Invadine PBN.
The fabric obtaining, with reference to AATCC 118-2002 standard, can detect oil repellent; With reference to GB/T 4745-1997, water repellency is detected; With reference to GB/T 17591-2006, fire resistance is detected.
3. testing result
6 grades of oil repellent energy, 4 grades of water repellencies, fire resistance: the time 0s that glows, after flame time 0s, char length 104mm, reaches B1 level level.
Embodiment 2
1. experiment material
With embodiment 1.
2. preparation technology
1) textile technology: adopt the superfine long-staple cotton in Xinjiang to spin, weave, obtain fabric: adopt RING SPINNING, fineness of yarn is 16S, 20S, carries out 1/3 twill weave (20S × 16S), through close 128, filling density 60.
2) flame-proof finishing process: pad (two soak two rolls, pick-up rate 85%) → dry (110 DEG C, 2min) → bake (150 DEG C, 70s) → wash → dry (110 DEG C, 2min).
3) water and oil repellent finish technique: pad (body lotion pH value is 6.5,18 DEG C of temperature, one soaks one rolls, pick-up rate 55%) → dry (130 DEG C, 2min) → bake (160 DEG C, 50s) → soap → wash → dry (130 DEG C, 2min).
4) postfinishing process: stentering forming → preshrunk → perching → packaging, obtains the fire-retardant all-cotton fabric of water and oil repellant.
Wherein, the formula of the fire retarding treating liquid of flame-proof finishing process is as follows: 420g/L Pyrovarex CP (antiflaming finishing agent), 22g/L phosphoric acid, 12g/L uric acid, 10g/L softener.
The formula of the dressing liquid of water and oil repellent finish technique is as follows: 55g/L Oleophobol CP-C (water-refusing oil-refusing finishing agent), 18g/L knittex FEL, 12g/L knittex CATALYST MO LIQ, 4g/L Invadine PBN.
The fabric obtaining, with reference to AATCC 118-2002 standard, can detect oil repellent; With reference to GB/T 4745-1997, water repellency is detected; With reference to GB/T 17591-2006, fire resistance is detected.
3. testing result
6 grades of oil repellent energy, 4 grades of water repellencies, fire resistance: the time 0s that glows, after flame time 0s, char length 95mm, reaches B1 level level.
Embodiment 3
1. experiment material
With embodiment 1.
2. preparation technology
1) textile technology: adopt the superfine long-staple cotton in Xinjiang to spin, weave, obtain fabric: adopt RING SPINNING, fineness of yarn is 16S, 12S, carries out 1/3 twill weave (16S × 12S), through close 108, filling density 58.
2) flame-proof finishing process: pad (two soak two rolls, pick-up rate 95%) → dry (100 DEG C, 5min) → bake (180 DEG C, 40s) → wash → dry (100 DEG C, 5min).
3) water and oil repellent finish technique: pad (body lotion pH value is 6.5,22 DEG C of temperature, one soaks one rolls, pick-up rate 45%) → dry (110 DEG C, 5min) → bake (180 DEG C, 60s) → soap → wash → dry (110 DEG C, 5min).
4) postfinishing process: stentering forming → preshrunk → perching → packaging, obtains the fire-retardant all-cotton fabric of water and oil repellant.
Wherein, the formula of the fire retarding treating liquid of flame-proof finishing process is as follows: 380g/L Pyrovarex CP (antiflaming finishing agent), 18g/L phosphoric acid, 17g/L uric acid, 20g/L softener.
The formula of the dressing liquid of water and oil repellent finish technique is as follows: 45g/L Oleophobol CP-C (water-refusing oil-refusing finishing agent), 22g/L knittex FEL, 16g/L knittex CATALYST MO LIQ, 6g/L Invadine PBN.
The fabric obtaining, with reference to AATCC 118-2002 standard, can detect oil repellent; With reference to GB GB/T 4745-1997, water repellency is detected; With reference to GB GB/T 17591-2006, fire resistance is detected.
3. testing result
6 grades of oil repellent energy, 4 grades of water repellencies, fire resistance: the time 0s that glows, after flame time 0s, char length 102mm, reaches B1 level level.
Claims (6)
1. a preparation technology for the fire-retardant all-cotton fabric of water and oil repellant, comprises the steps:
1) weaving: adopt cotton fiber to spin, weave, obtain grey cloth;
2) pre-treatment and dyeing;
3) flame-proof treatment: grey cloth is immersed in fire retarding treating liquid, pads successively, dry, bake, wash and dry;
4) water and oil repellent finish: grey cloth is immersed in water and oil repellent finish liquid, pads successively, dry, bake, soap, wash and dry;
5) postfinishing process;
Wherein, described in step 3), fire retarding treating liquid is the aqueous solution that comprises following component and concentration:
Described in step 3), flame-proof treatment is specially: grey cloth is immersed in fire retarding treating liquid, and two soak two rolls, pick-up rate 85~95%; 100~110 DEG C of bake out temperatures, dry 2~5min; 160~180 DEG C of baking temperatures, bake 40~70s;
Described in step 4), water and oil repellent finish liquid is the aqueous solution that comprises following component and concentration:
Described in step 4), water and oil repellent finish is specially: grey cloth is immersed in water and oil repellent finish liquid, and adjusting dressing liquid pH value is 6.4~6.6,18~22 DEG C of temperature, and one soaks one rolls, pick-up rate 45~55%; 110~130 DEG C of bake out temperatures, dry 2~5min; 160~180 DEG C of baking temperatures, bake 50~60s.
2. preparation technology as claimed in claim 1, is characterized in that, cotton fiber is long-staple cotton fiber described in step 1).
3. preparation technology as claimed in claim 1, is characterized in that, the resultant yarn mode of spinning described in step 1) is RING SPINNING, and the fineness of yarn is 12~20S.
4. preparation technology as claimed in claim 1, is characterized in that, in weaving process, fabric structure adopts 1/3 twill-weave described in step 1).
5. the fire-retardant all-cotton fabric of water and oil repellant that described in the arbitrary claim of claim 1-4 prepared by preparation technology.
6. described in the arbitrary claim of claim 1-4, described in preparation technology and claim 5, the fire-retardant all-cotton fabric of water and oil repellant is used the application in textiles, drop cloth, curtain, curtain preparation individual protection clothes, children's garment, child.