CN102926223A - Preparation method of far-infrared textiles - Google Patents
Preparation method of far-infrared textiles Download PDFInfo
- Publication number
- CN102926223A CN102926223A CN2012104763614A CN201210476361A CN102926223A CN 102926223 A CN102926223 A CN 102926223A CN 2012104763614 A CN2012104763614 A CN 2012104763614A CN 201210476361 A CN201210476361 A CN 201210476361A CN 102926223 A CN102926223 A CN 102926223A
- Authority
- CN
- China
- Prior art keywords
- far
- infrared
- textiles
- preparation
- flocculus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of far-infrared textiles. The method comprises the following steps: adding far-infrared ceramic micro-powders into a spinning process to prepare far-infrared fibers; then preparing the far-infrared fibers into far-infrared flocculus; and adding the far-infrared flocculus into the textiles at the last. The addition amount of the far-infrared flocculus can be adjusted. The addition amount of the far-infrared flocculus is 10%-70%. The preparation method has the advantages of simple preparation process, simple operation and higher rate of finished products; the far-infrared textiles prepared by the preparation method have the advantage of good heat retention property.
Description
Technical field
The present invention relates to a kind of preparation method of textiles, relate in particular to a kind of preparation method of far-infrared textiles.
Background technology
Common textiles is because heat insulation effect is limited, when wintry weather is colder, general textiles can not satisfy the warming demand of people, generally all be by increasing textiles thickness, reach warming effect, such production process is with regard to complicated, and the production cost of product will increase, and the person's that can affect the clothing overall image after the textiles thickening.
Summary of the invention
Main purpose of the present invention is, overcomes the defective that existing textiles exists, and a kind of preparation method of far-infrared textiles is provided, technical problem to be solved is to improve the warmth retention property of existing textiles, improve yield rate, thereby more be suitable for practicality, and have the value on the industry.
The object of the invention to solve the technical problems realizes by the following technical solutions: a kind of preparation method of far-infrared textiles, the method comprises the steps: at first, far-infrared ceramic powder is joined in the spinning process, be prepared into far IR fibre, again described far IR fibre is made the far infrared flocculus, at last described far infrared flocculus is added in the textiles.
Further, the addition of described far infrared flocculus is adjustable.
Again further, the addition of described far infrared flocculus is 10%~70%.
Compared with prior art, usefulness of the present invention is: the preparation method of this far-infrared textiles, and preparation technology is simple, and is simple to operate, and yield rate is higher, and the infrared textiles warmth retention property that makes is good.
The specific embodiment
Reach technological means and the effect that predetermined goal of the invention is taked for further setting forth the present invention, its specific embodiment of preparation method, feature and the effect thereof of the far-infrared textiles that foundation the present invention is proposed are described in detail as follows.
A kind of preparation method of far-infrared textiles at first, joins the far-infrared ceramic powder of 12% content in the spinning process, is prepared into far IR fibre, far IR fibre is made the far infrared flocculus again, at last 70% far infrared flocculus is added in the textiles.
The preparation method of this far-infrared textiles, preparation technology is simple, and is simple to operate, and yield rate is higher, and the infrared textiles warmth retention property that makes is good.
The above, it only is preferred embodiment of the present invention, be not that the present invention is done any pro forma restriction, although the present invention discloses as above with preferred embodiment, yet be not to limit the present invention, any those skilled in the art, within not breaking away from the technical solution of the present invention scope, when the technology contents that can utilize above-mentioned announcement is made a little change or is modified to the equivalent embodiment of equivalent variations, in every case be the content that does not break away from technical solution of the present invention, any simple modification that foundation technical spirit of the present invention is done above embodiment, equivalent variations and modification all still belong in the scope of technical solution of the present invention.
Claims (3)
1. the preparation method of a far-infrared textiles, it is characterized in that, the method comprises the steps: at first, far-infrared ceramic powder is joined in the spinning process, be prepared into far IR fibre, again described far IR fibre is made the far infrared flocculus, at last described far infrared flocculus is added in the textiles.
2. the preparation method of far-infrared textiles according to claim 1 is characterized in that, the addition of described far infrared flocculus is adjustable.
3. the preparation method of far-infrared textiles according to claim 2 is characterized in that, the addition of described far infrared flocculus is 10%~70%.