CN102924847A - 一种热可逆交联pvc电缆料及其制备方法 - Google Patents
一种热可逆交联pvc电缆料及其制备方法 Download PDFInfo
- Publication number
- CN102924847A CN102924847A CN201210442938XA CN201210442938A CN102924847A CN 102924847 A CN102924847 A CN 102924847A CN 201210442938X A CN201210442938X A CN 201210442938XA CN 201210442938 A CN201210442938 A CN 201210442938A CN 102924847 A CN102924847 A CN 102924847A
- Authority
- CN
- China
- Prior art keywords
- pvc
- parts
- cable materials
- pvc cable
- reversible crosslink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
性能指标 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
凝胶含量(%) | 41 | 67 | 60 | 75 |
拉伸强度(MPa) | 19.27 | 20.21 | 19.75 | 22.08 |
冲击强度(KJ/m2) | 4.06 | 8.17 | 7.65 | 10.33 |
断裂伸长率(%) | 192 | 168 | 175 | 143 |
维卡软化温度(℃) | 70.12 | 73.56 | 65.39 | 76.47 |
Claims (10)