CN102912639A - 双面异能服装面料的制备方法 - Google Patents

双面异能服装面料的制备方法 Download PDF

Info

Publication number
CN102912639A
CN102912639A CN2012103932206A CN201210393220A CN102912639A CN 102912639 A CN102912639 A CN 102912639A CN 2012103932206 A CN2012103932206 A CN 2012103932206A CN 201210393220 A CN201210393220 A CN 201210393220A CN 102912639 A CN102912639 A CN 102912639A
Authority
CN
China
Prior art keywords
fabric
face
preparation
garment material
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103932206A
Other languages
English (en)
Inventor
严为忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KUNSHAN CITY ZHOUSHI FEIHUANG GARMENT FACTORY
Original Assignee
KUNSHAN CITY ZHOUSHI FEIHUANG GARMENT FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KUNSHAN CITY ZHOUSHI FEIHUANG GARMENT FACTORY filed Critical KUNSHAN CITY ZHOUSHI FEIHUANG GARMENT FACTORY
Priority to CN2012103932206A priority Critical patent/CN102912639A/zh
Publication of CN102912639A publication Critical patent/CN102912639A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种双面异能服装面料的制备方法，包括如下步骤：对织物的一面进行圆网印花防水整理步骤，将疏水剂施加到织物的一面，所述疏水剂为聚醚酯弹性体90-110g/kg、脂肪族异氰酸酯聚氨酯20-30k/kg、铝锆酸酯偶联剂2-5g/kg；然后再对织物的另一面进行浸轧法亲水整理步骤。本发明采用圆网印花工艺，将疏水剂施加到织物的一面，再通过浸轧工艺，将亲水剂施加到织物的另一面，因此使得织物的一面具有防水性能，另一面具有亲水性能，能将防水面和亲水面很好地结合在一起，达到双面异能的效果。不仅对织物重量影响小，而且还能改善织物的柔韧性能。

Description

双面异能服装面料的制备方法
技术领域
本发明涉及一种双面异能服装面料的制备方法。
背景技术
随着生活水平的不断提高，人们对衣物的功能性要求越来越高，尤其对内衣的选择不仅注重柔软舒适，更注重健康、保健功能。
双面异能面料，是指一面具有防水性，另一面具有亲水性的面料，如此基于虹吸效应，能将织物内层的汗液迅速吸到外层排出，使内层保持干净清爽，有效提高排湿性能，降低汗液与皮肤接触的机会；而该织物的防水面又具有良好的防水和易去污性能，即在防水、防油和防污方面具有较佳的特性。
目前，上述单亲单防织物的制造工艺一般是通过两层或者多层的复合技术，由于这种组合需要使用到两层以上的纺织品，故会使其重量增加，透气性受到限制而导致穿着舒适性的降低。
发明内容
本发明要解决的技术问题是提供一种双面异能服装面料的制备方法，以克服现有技术存在的上述缺陷。
为解决上述技术问题，本发明双面异能服装面料的制备方法，包括如下步骤：对织物的一面进行圆网印花防水整理步骤，将疏水剂施加到织物的一面，所述疏水剂为聚醚酯弹性体90-110g/kg、脂肪族异氰酸酯聚氨酯20-30k/kg、铝锆酸酯偶联剂2-5g/kg；然后再对织物的另一面进行浸轧法亲水整理步骤。
所述聚醚酯弹性体包含聚乙二醇残基、亚烷基二醇残基、和二羧酸残基，其中聚乙二醇残基占5-25wt％。
所述聚醚酯弹性体中亚烷基二醇残基中包含乙二醇残基、丁二醇残基。
所述圆网印花防水整理步骤的烘干温度110-120℃，焙烘温度130-170℃。
所述织物没有严格限定，优选涤q织物或涤棉混纺织物。
所述浸轧法亲水整理步骤中亲水剂加入量为20-40g/L，轧液率70％-80％，烘干温度80-90℃，焙烘温度120-130℃。
本发明采用圆网印花整理工艺，将疏水剂施加到织物的一面，再通过浸轧工艺，将亲水剂施加到织物的另一面，因此使得织物的一面具有防水性能，另一面具有亲水性能，能将防水面和亲水面很好地结合在一起，达到双面异能的效果。与现有技术相比，本发明避免采用双层或多层结构，而采用圆网印花技术和浸轧工艺对织物进行双面异能整理，不仅对织物重量影响小，而且还能改善织物的柔韧性能。
具体实施方式
以下给出本发明的较佳实施例，以详细说明本发明的技术方案。
实施例1
双面异能涤纶面料的制备：
对织物的一面进行圆网印花防水整理步骤，将疏水剂施加到织物的一面，所述疏水剂为聚醚酯弹性体90g/kg、脂肪族异氰酸酯聚氨酯30k/kg、铝锆酸酯偶联剂2g/kg；然后再对织物的另一面进行浸轧法亲水整理步骤。
所述圆网印花防水整理步骤的烘干温度120℃，30分钟，焙烘温度170℃30分钟。
所述浸轧法亲水整理步骤中亲水剂加入量为20g/L，轧液率70％％，烘干温度90℃，30分钟，焙烘温度130℃，30分钟。
实施例2
双面异能涤棉混纺面料的制备：
对织物的一面进行圆网印花防水整理步骤，将疏水剂施加到织物的一面，所述疏水剂为聚醚酯弹性体110g/kg、脂肪族异氰酸酯聚氨酯20k/kg、铝锆酸酯偶联剂5g/kg；然后再对织物的另一面进行浸轧法亲水整理步骤。
所述圆网印花防水整理步骤的烘干温度110℃，30分钟，焙烘温度130℃，30分钟。
所述浸轧法亲水整理步骤中亲水剂加入量为40g/L，轧液率80％，烘干温度80℃，30分钟，焙烘温度120℃，30分钟。
本发明采用圆网印花工艺，将疏水剂施加到织物的一面，再通过浸轧工艺，将亲水剂施加到织物的另一面，因此使得织物的一面具有防水性能，另一面具有亲水性能，能将防水面和亲水面很好地结合在一起，达到双面异能的效果。与现有技术相比，本发明避免采用双层或多层结构，而采用圆网印花技术和浸轧工艺对织物进行双面异能整理，不仅对织物重量影响小，而且还能改善织物的柔韧性能。

Claims (6)

1.一种双面异能服装面料的制备方法，其特征在于，包括如下步骤：对织物的一面进行圆网印花防水整理步骤，将疏水剂施加到织物的一面，所述疏水剂为聚醚酯弹性体90-110g/kg、脂肪族异氰酸酯聚氨酯20-30k/kg、铝锆酸酯偶联剂2-5g/kg；然后再对织物的另一面进行浸轧法亲水整理步骤。
2.根据权利要求1所述的双面异能服装面料的制备方法，其特征在于，所述聚醚酯弹性体包含聚乙二醇残基、亚烷基二醇残基、和二羧酸残基，其中聚乙二醇残基占5-25wt％。
3.根据权利要求2所述的双面异能服装面料的制备方法，其特征在于，所述聚醚酯弹性体中的亚烷基二醇残基中包含乙二醇残基、丁二醇残基。
4.根据权利要求1所述的双面异能服装面料的制备方法，其特征在于，所述圆网印花防水整理步骤的烘干温度110-120℃，焙烘温度130-170℃。
5.根据权利要求1所述的双面异能服装面料的制备方法，其特征在于，所述浸轧法亲水整理步骤中亲水剂加入量为20-40g/L，轧液率70％-80％，烘干温度80-90℃，焙烘温度120-130℃。
6.根据权利要求1所述的双面异能服装面料的制备方法，其特征在于，所述织物为涤纶织物或涤棉混纺织物。
CN2012103932206A 2012-09-27 2012-09-27 双面异能服装面料的制备方法 Pending CN102912639A (zh)