CN102898722A - 一种改性聚丙烯防水卷材及其制备方法 - Google Patents
一种改性聚丙烯防水卷材及其制备方法 Download PDFInfo
- Publication number
- CN102898722A CN102898722A CN 201110207133 CN201110207133A CN102898722A CN 102898722 A CN102898722 A CN 102898722A CN 201110207133 CN201110207133 CN 201110207133 CN 201110207133 A CN201110207133 A CN 201110207133A CN 102898722 A CN102898722 A CN 102898722A
- Authority
- CN
- China
- Prior art keywords
- polypropylene
- modified polypropene
- waterproof roll
- coiled material
- waterproof coiled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种改性聚丙烯防水卷材及其制备方法，一种改性聚丙烯防水卷材，包括：聚丙烯、增强剂、增韧剂、填料、助剂等。按照配方比例称取所需的原料，通过高速混合物，在常温下混合，使原料混合均匀，加入到双螺杆挤出机中进行造粒处理。将制成的改性聚丙烯的粒料，投到挤出机压延机组的料筒中进行挤出，并经三辊压延机压延、裁切、牵引、冷却，制成改性聚丙烯防水卷材。该防水卷材可以应用于地铁、桥梁、隧道等大型混凝土工程中作为防水的屏障。
Description
技术领域
本发明属于高分子防水材料技术领域，具体涉及一种改性聚丙烯防水卷材。
背景技术
聚丙烯分子中含有甲基，按甲基排列位置分为等规聚丙烯、无规聚丙烯和间规聚丙烯。甲基排列在分子主链的同一侧称等规聚丙烯；若甲基无秩序地分布在分子主链的两侧称无规聚丙烯；当甲基交替排列在主链的两侧称间规聚丙烯。间规聚丙烯为高弹热塑性材料，它有良好的拉伸强度。低成本高性能的PP材料应用及其广阔。将聚丙烯应用于防水材料，可以提高成品的力学性能。而单一的高分子材料都不能满足建筑防水的要求。而聚丙烯作为一种低成本的防水材料，不仅能产生显著的经济效益，而且能减少树脂的用量，减轻环境污染。
发明内容
本发明的目的在于针对当前技术中存在的不能同时增强拉力和增加韧性的问题，提出一种综合力学显著的改性聚丙烯防水卷材。该聚丙烯防水卷材，在聚丙烯中加入增韧剂，达到提高其韧性的目的，同时加入增强剂，改善防水卷材的抗拉性能。由于聚丙烯价格低廉，可以有效的降低防水卷材的成本，经济效益显著。
本发明的技术方案是：
一种改性聚丙烯防水卷材，包括：聚丙烯、增强剂、增韧剂、助剂等。按质量百分比配比如下：
聚丙烯 100
增韧剂 5-30
增强剂 20-40
填料 15-30
助剂 1-5
其中，所述的聚丙烯为等规聚丙烯或间规聚丙烯；
所述的增韧剂为线性聚乙烯；
所述的增强剂为 EVA即乙烯-醋酸乙烯酯。
所述的填料包括500目活性碳酸钙、800目活性碳酸钙的一种或两种；
所述的助剂包括防老化剂、抗氧剂、光稳定剂。
所述的防老化剂为RD40；
所述的抗氧化剂为抗氧化1010；
所述的润滑剂包括硬脂酸、硬脂酸锌；
所述的改性聚丙烯防水卷材的制备方法，包括以下步骤：
1．按照配方比例称取所需的原料，通过高速混合物，在常温下混合30分钟，等原料混合均匀，加入到双螺杆挤出机中进行造粒处理。
2．将制成的改性聚丙烯的粒料，投到挤出机压延机组的料筒中进行挤出，并经三辊压延机压延、裁切、牵引、冷却，制成改性聚丙烯防水卷材。
本发明对原材料的选用、配方的设计进行了试探性的研究，进行了一系列的试验，并进行了性能测试。
由本发明所提供的改性聚丙烯防水卷材，可以大大提高聚丙烯的韧性和强度，从而使聚丙烯具有更好的力学性能，抗拉伸性能得到显著提高。
附图说明
图1为本发明的工艺流程图。
具体实施方式
为了更好的理解本发明，下面结合实例进一步阐述本发明的内容，但本发明的内容不仅仅局限于下面的试验。
实施例1：一种改性聚丙烯防水卷材的制备方法，它包括如下步骤：
产品的配方：
质量配方比例为：100份 等规聚丙烯 ,25份EVA ，线性聚乙烯 15份，800目活性碳酸钙 30份，抗氧化剂1010 0.5份，防老化剂RD40 0.3份，硬脂酸锌1份。
制作工艺：
①．按照一种的配方比例，准确称量原料，在常温下，在高速混料机中混合30分钟，使物料混合均匀。
②．在再将混合均匀的物料，投入到温度为120-170℃的双螺杆挤出机中进行造粒处理。
③．将造好的粒料在挤出机中进行挤出成型，并控制衣架模唇的温度：一区 170℃，二区 165℃，三区 155℃，四区 150℃，5区 150℃，6区 155℃，七区160℃ ，八区 165℃，九区 170℃；将熔融的片状进入三辊压延机压延成一定厚度的薄片，经过裁切，牵引、冷却、切成一定长度的卷，制成改性聚丙烯防水卷材的成品。
实施例2：一种改性聚丙烯防水卷材的制备方法，它包括如下步骤：
产品的配方：
质量配方比例为：100份 间规聚丙烯 ,35份EVA ，线性聚乙烯25份，800目活性碳酸钙 30份，抗氧化剂1010 0.5份，防老化剂RD40 0.3份，硬脂酸锌 1份。
制作工艺：
①．按照一种的配方比例，准确称量原料，在常温下，在高速混料机中混合30分钟，使物料混合均匀。
②．在再将混合均匀的物料，投入到温度为120-170℃的双螺杆挤出机中进行造粒处理。
③．将造好的粒料在挤出机中进行挤出成型，并控制衣架模唇的温度：一区 170℃，二区 165℃，三区 155℃，四区 150℃，5区 150℃，6区 155℃，七区160℃ ，八区 165℃，九区 170℃；将熔融的片状进入三辊压延机压延成一定厚度的薄片，经过裁切，牵引、冷却、切成一定长度的卷，制成改性聚丙烯防水卷材的成品。
实施例3：一种改性聚丙烯防水卷材的制备方法，它包括如下步骤：
产品的配方：
质量配方比例为：100份 间规聚丙烯 ,35份EVA ，，线性聚乙烯15份，800目活性碳酸钙 30份，抗氧化剂1010 0.5份，防老化剂RD40 0.3份，硬脂酸锌2份。
制作工艺：
制作工艺：
①．按照一种的配方比例，准确称量原料，在常温下，在高速混料机中混合30分钟，使物料混合均匀。
②．在再将混合均匀的物料，投入到温度为120-170℃的双螺杆挤出机中进行造粒处理。
③．将造好的粒料在挤出机中进行挤出成型，并控制衣架模唇的温度：一区 170℃，二区 165℃，三区 155℃，四区 150℃，5区 150℃，6区 155℃，七区160℃ ，八区 165℃，九区 170℃；将熔融的片状进入三辊压延机压延成一定厚度的薄片，经过裁切，牵引、冷却、切成一定长度的卷，制成改性聚丙烯防水卷材的成品。
性能比较表：
| 性 能 | 实施例1 | 实施例2 | 实施例3 |
| 拉伸强度MPa | 9.09 | 12.63 | 14.27 |
| 断裂伸长率% | 250 | 279 | 385 |
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。
Claims (4)
1.一种改性聚丙烯防水卷材，其特征在于，包括：聚丙烯、增强剂、增韧剂、填料、助剂等；按质量百分比配比如下：
聚丙烯 100
增韧剂 5-30
增强剂 20-40
填料 15-30
助剂 1-5
其中，所述的聚丙烯为等规聚丙烯或间规聚丙烯；所述的增韧剂为线性聚乙烯；
所述的增强剂为 EVA即乙烯-醋酸乙烯酯。
2.根据权利要求1所述的一种改性聚丙烯防水卷材，其特征在于，所述的助剂包括防老化剂、抗氧剂、光稳定剂。
3.根据权利要求1或2所述的一种改性聚丙烯防水卷材，其特征在于，所述的防老化剂为RD40；所述的抗氧化剂为抗氧化1010；所述的润滑剂包括硬脂酸、硬脂酸锌。
4. 根据权利要求1所述的一种氯化聚乙烯及其制备方法，其特征在于，按照配方比例称取所需的原料，通过高速混合物，在常温下混合30分钟，等原料混合均匀，加入入到双螺杆挤出机中进行造粒处理；将制成的改性聚丙烯的粒料，投到挤出机压延机组的料筒中进行挤出，并经三辊压延机压延、裁切、牵引、冷却，制成改性聚丙烯防水卷材。