CN102898100A - 一种干混砂浆及其制备方法 - Google Patents
一种干混砂浆及其制备方法 Download PDFInfo
- Publication number
- CN102898100A CN102898100A CN201210406782XA CN201210406782A CN102898100A CN 102898100 A CN102898100 A CN 102898100A CN 201210406782X A CN201210406782X A CN 201210406782XA CN 201210406782 A CN201210406782 A CN 201210406782A CN 102898100 A CN102898100 A CN 102898100A
- Authority
- CN
- China
- Prior art keywords
- dry
- mixed mortar
- river sand
- mixed
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种干混砂浆的配方及其制备工艺,属于建筑材料领域。本发明所述的干混砂浆由水泥:10~20%;粉煤灰:5~10%;河砂:40~60%;碎屑:20~30%;外加剂:0.02~0.04%配比组成,该干混砂浆的制备方法为将河砂、碎屑烘干除尘过筛后,与水泥、粉煤灰、外加剂等根据建筑干混砂浆所需的不同等级,不同型号进行配比,搅拌混合,袋装或散装。本发明通过优化干混砂浆中各组分配比,获得具有抗收缩性能强、抗龟裂、粘结力强、性能稳定等优点的干混砂浆,将干混砂浆加入适当的水搅拌成稠浆状,搅拌均匀后即可投入使用。性能优越、适合产业推广应用,有效的利用了石场的碎屑,节约了河砂的使用,符合建筑环保新发展的要求。
Description
技术领域
本发明涉及到一种建筑用的干混砂浆,尤其是一种利用碎屑作为原料的干混砂浆及其制备方法。
背景技术
随着人们对建筑的工程质量、环保要求及文明施工的要求不断提高,干混砂浆在成为目前最主要的建筑用材料之一。现有的在建筑材料上使用的干混砂浆,河砂掺量一般最高达80%以上,但同时由于建筑材料上河砂的大量使用,直接导致河砂资源越来越枯竭,不利于自然环境的保护。
石场在矿山开采、砂石粉碎、块料粉磨、工厂生产中会产生大量的碎屑,大量占用场地又污染环境,但是现有技术中,直接使用碎屑替代河砂,砂浆在干燥过程中容易开裂,不能直接作为建筑材料使用,无法在干混砂浆的领域中得到充分的利用。
发明内容
本发明的目的之一是为了克服现有技术的不足,提供一种干混砂浆。
本发明所述的干混砂浆,由以下重量配比的配料混合而成:
水泥:10~20%;
粉煤灰:5~10%;
河砂:40~60%;
碎屑:20~30%;
外加剂:0.02~0.04%;
其中:
所述的粉煤灰为Ⅱ级;
所述的河砂含水量低于0.5%,粒径小于5毫米;
所述的碎屑为矿山开采时所产生的石子碎屑,含水量低于0.5%,粒径小于5毫米;
所述的外加剂为纤维素醚。
为提供上述干混砂浆的制备方法,该干混砂浆包括组分水泥、粉煤灰、河砂、碎屑、外加剂,根据建筑干混砂浆所需的不同等级,不同型号进行配比,搅拌混合,袋装或散装,其特征在于:包括以下步骤:
(1)烘干河砂,并进行筛分,控制河砂含水量至低于0.5%,产品粒径控制在5毫米以
内;
(2)烘干碎屑,并进行筛分,控制碎屑含水量至低于0.5%,产品粒径控制在5毫米以
内,进行搅拌;
(3)称量原料;
(4)将称料好的原料进行搅拌混合;
(5)计量袋装或散装。
其中,原料通过高速双轴搅拌机搅拌混合时间为3分钟。
本发明通过优化干混砂浆中各组分配比,获得具有抗收缩性能强、抗龟裂、粘结力强、性能稳定等优点的干混砂浆,将干混砂浆加入13-18%的水搅拌成稠浆状,搅拌均匀后即可投入使用。性能优越、适合产业推广应用,有效的利用了石场的碎屑,节约了河砂的使用,符合建筑环保新发展的要求。
具体实施方式
实施例一:以砌筑砂浆M10这一强度等级为例,
(1)烘干河砂,除尘、并进行筛分,控制河砂含水量至0.5%,产品粒径控制在5毫米以内;
(2)烘干碎屑,除尘、并进行筛分,控制碎屑含水量至,产品粒径控制在5毫米以内,进行搅拌;
(3)称量原料,其重量配比为水泥(P.O42.5)10%、粉煤灰(Ⅱ级)9.97%、碎屑20%、河砂60%、外加剂0.03%;
(4)将称料好的原料通过高速双轴搅拌机搅拌3分钟;
(5)计量袋装或散装,获得成品。
实施例二:以砌筑砂浆M5这一强度等级为例,
(1)烘干河砂,除尘、并进行筛分,控制河砂含水量至0.5%,产品粒径控制在5毫米以内;
(2)烘干碎屑,除尘、并进行筛分,控制碎屑含水量至0.5%,产品粒径控制在5毫米以内,进行搅拌;
(3)称量原料,其重量配比为水泥(P.O42.5)11%、粉煤灰(Ⅱ级)10%、碎屑24%、河砂54.96%、外加剂0.04%;
(4)将称料好的原料通过高速双轴搅拌机搅拌3分钟;
(5)计量袋装或散装,获得成品。
实施例三:以抹灰砂浆M5这一强度等级为例,
(1)烘干河砂,除尘、并进行筛分,控制河砂含水量至0.5%,产品粒径控制在5毫米以内;
(2)烘干碎屑,除尘、并进行筛分,控制碎屑含水量至0.5%,产品粒径控制在5毫米以内,进行搅拌;
(3)称量原料,其重量配比为水泥(P.O42.5)12%、粉煤灰(Ⅱ级)10%、碎屑24%、河砂53.97%、外加剂0.03%;
(4)将称料好的原料通过高速双轴搅拌机搅拌3分钟;
(5)计量袋装或散装,获得成品。
实施例四:以抹灰砂浆M10这一强度等级为例,
(1)烘干河砂,除尘、并进行筛分,控制河砂含水量至0.5%,产品粒径控制在5毫米以内;
(2)烘干碎屑,除尘、并进行筛分,控制碎屑含水量至0.5%,产品粒径控制在5毫米以内,进行搅拌;
(3)称量原料,其重量配比为水泥(P.O42.5)20%、粉煤灰(Ⅱ级)9.98%、碎屑30%、河砂40%、外加剂0.02%;
(4)将称料好的原料通过高速双轴搅拌机搅拌3分钟;
(5)计量袋装或散装,获得成品。
Claims (4)
1.一种干混砂浆,其特征在于:干混砂浆由以下重量配比的配料混合而成:
水泥:10~20%;
粉煤灰:5~10%;
河砂:40~60%;
碎屑:20~30%;
外加剂:0.02~0.04%。
2.根据权利要求1所述的干混砂浆,其特征在于:
所述的粉煤灰为Ⅱ级;
所述的河砂含水量低于0.5%,粒径小于5毫米;
所述的碎屑含水量低于0.5%,粒径小于5毫米;
所述的外加剂为纤维素醚。
3. 根据权利要求1所述的干混砂浆的制备方法,其特征在于:包括以下步骤:
(1)烘干河砂,并进行筛分,控制河砂含水量至低于0.5%,产品粒径控制在5毫米以
内;
(2)烘干碎屑,并进行筛分,控制碎屑含水量至低于0.5%,产品粒径控制在5毫米以
内,进行搅拌;
(3)称量原料;
(4)将称料好的原料进行搅拌混合;
(5)计量袋装或散装。
4. 根据权利要求3所述的干混砂浆的制备方法,其特征在于:所述原料通过高速双轴搅拌机搅拌混合时间不低于3分钟。