CN102850902A - Corrosion-resistant fireproof coating - Google Patents
Corrosion-resistant fireproof coating Download PDFInfo
- Publication number
- CN102850902A CN102850902A CN2012103151470A CN201210315147A CN102850902A CN 102850902 A CN102850902 A CN 102850902A CN 2012103151470 A CN2012103151470 A CN 2012103151470A CN 201210315147 A CN201210315147 A CN 201210315147A CN 102850902 A CN102850902 A CN 102850902A
- Authority
- CN
- China
- Prior art keywords
- parts
- retardant coating
- corrosion resistant
- resins
- frie retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a corrosion-resistant fireproof coating, which belongs to the technical field of coatings. The corrosion-resistant fireproof coating comprises, by weight, 2 to 3 parts of ethylene-vinyl acetate copolymer emulsion, 1 to 2 parts of decabromodiphenyl ether, 5 to 10 parts of epoxy resin, 4 to 6 parts of chlorinated rubber, 5 to 10 parts of phenolic resin, 3 to 5 parts of perchlorethylene resin, 1 part of potassium titanate whisker, 1 to 2 parts of zinc-aluminum alloy powder, 1 part of melamine, 1 part of ammonium polyphosphate, 1 part of borax, 2 to 3 parts of glass powder, 5 to 8 parts of dibutyl benzoate, 2 to 7 parts of pentaerythritol, 6 to 12 parts of gypsum, 5 to 9 parts of acrylate resin and 10 to 20 parts of a solvent. The fireproof coating provided by the invention has excellent corrosion resistance and has fire resistance in accordance with national regulations.
Description
Technical field
The invention provides a kind of corrosion resistant frie retardant coating, belong to technical field of coatings.
Background technology
Frie retardant coating generally is divided into expanded polystyrene veneer and non-expansion type two classes on fire prevention mechanism.Non-expansion type is the purpose that reaches fire-retardant fireproof by self nonflammable property, wanting to reach preferably, flameproof effect must be coated with very thickly, and add a large amount of fire retardants, this class coating easily gives out the harmful material of being always or usually as specified at ordinary times, therefore is restricted in application.Another kind of is expanding fire-proof paint, meeting expanded by heating when fuel, thus stop flame to the transmission of ground.But the corrosion resistance nature of expanding fire-proof paint commonly used is bad, and easily aging, cracking after spray time has been grown, can affect its flameproof effect.
Summary of the invention
For above commentary to prior art, technical problem to be solved by this invention is: the expanding fire-proof paint erosion resistance is relatively poor.Adopt following technical scheme:
A kind of corrosion resistant frie retardant coating includes following component by weight: 2～3 parts of ethene-vinyl acetate copolymer emulsions, 1～2 part of decabromodiphenyl oxide, 5～10 parts of Resins, epoxy, 4～6 parts of chlorinated rubbers, 5～10 parts in resol, 3～5 parts of supervinyi chloride resins, 1 part of potassium titanate crystal whisker, 1～2 part in aluminium zinc powder, 1 part of trimeric cyanamide, 1 part of ammonium polyphosphate, 1 part of borax, 2～3 parts in glass powder, 5～8 parts of phenylformic acid dibutylesters, 2～7 parts of tetramethylolmethanes, 6～12 parts in gypsum, 5～9 parts of acrylate resins, 10～20 parts of solvents.
Above-mentioned solvent is selected from one or more the arbitrary proportion mixture in ethyl acetate, butylacetate, the dimethylbenzene.
Above-mentioned Resins, epoxy is preferably bisphenol A type epoxy resin.
Above-mentioned color stuffing can be selected from the mixture of one or more arbitrary proportions in barium sulfate, talcum powder, mica powder, aluminum oxide, the magnesium oxide.
Frie retardant coating provided by the invention adopts the approach well known preparation:, add resin dissolves with solvent again, stir; Sending into three-roll grinder, to be ground to fineness qualified, and the restir machine is uniformly dispersed, and filters and packages to get final product.
Decabromodiphenyl oxide can be effectively fire-retardant in the frie retardant coating provided by the invention, and supervinyi chloride resin, aluminium zinc powder, acrylate resin, Resins, epoxy can improve the sticking power of coating effectively.Tetramethylolmethane is carbon source.Trimeric cyanamide is cure-crosslinking agent.Borax and potassium titanate crystal whisker are fire-proof packing.
Frie retardant coating provided by the invention has excellent corrosion resistance nature, and fire resistance meets national regulation.
Embodiment
Take by weighing each raw material by the weight ratio in the table 1.
The weight proportion of table 1 embodiment 1～embodiment 3
Above-mentioned solvent is selected from one or more the arbitrary proportion mixture in ethyl acetate, butylacetate, the dimethylbenzene.
Above-mentioned Resins, epoxy is preferably bisphenol A type epoxy resin.
Above-mentioned color stuffing can be selected from the mixture of one or more arbitrary proportions in barium sulfate, talcum powder, mica powder, aluminum oxide, the magnesium oxide.
The preparation method is:, add resin dissolves with solvent again, stir; Sending into three-roll grinder, to be ground to fineness qualified, and the restir machine is uniformly dispersed, and filters and packages to get final product.
Performance test
When the frie retardant coating in above-described embodiment is used for wood substrate, carry out the fire resistance test according to GB12442.1-95, when above paint formulation is 1mm when dry film Baidu, behind spirit lamp baking 30min, investigate the carbonization situation of coating expansion height and wood substrate, with disclosed frie retardant coating among the patent CN92102102 in contrast.
The performance test data of table 2 embodiment 1～embodiment 3 reference examples
Claims (4)
1. a corrosion resistant frie retardant coating includes following component by weight: 2～3 parts of ethene-vinyl acetate copolymer emulsions, 1～2 part of decabromodiphenyl oxide, 5～10 parts of Resins, epoxy, 4～6 parts of chlorinated rubbers, 5～10 parts in resol, 3～5 parts of supervinyi chloride resins, 1 part of potassium titanate crystal whisker, 1～2 part in aluminium zinc powder, 1 part of trimeric cyanamide, 1 part of ammonium polyphosphate, 1 part of borax, 2～3 parts in glass powder, 5～8 parts of phenylformic acid dibutylesters, 2～7 parts of tetramethylolmethanes, 6～12 parts in gypsum, 5～9 parts of acrylate resins, 10～20 parts of solvents.
2. corrosion resistant frie retardant coating according to claim 1 is characterized in that: described solvent is one or more the arbitrary proportion mixture in ethyl acetate, butylacetate, the dimethylbenzene.
3. corrosion resistant frie retardant coating according to claim 1, it is characterized in that: described Resins, epoxy is bisphenol A type epoxy resin.
4. corrosion resistant frie retardant coating according to claim 1, it is characterized in that: described color stuffing is the mixture of one or more arbitrary proportions in barium sulfate, talcum powder, mica powder, aluminum oxide, the magnesium oxide.