CN102825431B - Machining method of high-abrasion resistance valve core - Google Patents
Machining method of high-abrasion resistance valve core Download PDFInfo
- Publication number
- CN102825431B CN102825431B CN201210334750.3A CN201210334750A CN102825431B CN 102825431 B CN102825431 B CN 102825431B CN 201210334750 A CN201210334750 A CN 201210334750A CN 102825431 B CN102825431 B CN 102825431B
- Authority
- CN
- China
- Prior art keywords
- cylindrical
- workpiece
- processing
- grinding
- centre bore
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a machining method of a high-abrasion resistance valve core. The method comprises a material preparing step, a turning step, a heat treatment step, a clinching step, a grinding step, a clinching step, a surface treatment step, a grinding step, a clinching step and the like. The valve core machined by the method is abrasion resistant, light in weight and stable in quality, and can meet the using performance of a precise control valve.
Description
Technical field
The present invention relates to a kind of processing method of high-abrasion resistance valve core, belong to field of machining.
Background technology
Spool is the important parts in control valve, in order to improve wearability and the manufacturability of spool, spool material selects steel usually, but steel spool certainly focus in fine control valve the performance affecting control valve, particularly bulky valve core, the performance affecting control valve is larger, causes control valve cisco unity malfunction.Devise a kind of high-abrasion resistance valve core, the material of its spool is aluminium alloy, lightweight for this reason, and surperficial wearability is after treatment equivalent to the steel part hardened.This kind of spool is wear-resisting, lightweight, thus meets the serviceability of control valve, stabilizes product quality.
Summary of the invention
The technical problem to be solved in the present invention is: the processing method providing a kind of lightweight, high-abrasion resistance valve core, by processing method of the present invention, the spool of processing is wear-resisting, lightweight, steady quality, thus meets the serviceability of control valve.
The present invention is achieved in that it comprises the following steps:
The first, get the raw materials ready: aluminium alloy bar;
The second, Vehicle Processing: each shelves cylindrical of Vehicle Processing and cannelure, and drill centers, cylindrical φ d1, cylindrical φ d2 are processed as d1max+ (0.15 ~ 0.35) mm, d2max+ (0.15 ~ 0.35) mm respectively, and all the other are machined to requirement;
Three, heat treatment: artificial aging;
Four, pincers processing: repair and grind two ends centre bore 60 ° of conical surfaces;
Five, mill processing: with heart carrier clamping cylindrical φ d2, the Double ejection pin of lathe holds out against two ends centre bore, heart carrier drives workpiece to rotate, cylindrical grinding φ d1, be processed as d1min-(0.01 ~ 0.02) mm, tolerance is h6, use the same method cylindrical grinding φ d2, is processed as d2min-(0.01 ~ 0.02) mm, tolerance is h6;
Six, pincers processing: repair burr clearly, sharp edge rounding is not more than 0.05mm;
7th, surface treatment: hard anodizing, require to determine hard anodizing layer thickness by design document requirement hard anodizing layer thickness and grinding, according to size and the structure of workpiece, the electrode of surface processing equipment connects with conducting electricity good wire or metal bar with between workpiece, with screw, wire or metal bar are fixed to the electrode union end place of surface processing equipment, wire with workpiece union end is made paper clip type, then connect with the non-mating surface of workpiece, or the metal bar with workpiece union end is made external screw thread, connect with the internal thread of workpiece termination again,
Eight, mill processing: with heart carrier clamping cylindrical φ d2, the Double ejection pin of lathe holds out against two ends centre bore, and heart carrier drives workpiece to rotate, cylindrical grinding φ d1 is to requiring, ensure that cylindricity e1, the cylindrical grinding φ d2 that uses the same method are to requiring, ensure cylindricity e2 and axiality φ f simultaneously simultaneously;
Nine, pincers processing: repair burr clearly, sharp edge rounding is not more than 0.05mm.
Compared with prior art, the spool of the present invention's processing is wear-resisting, lightweight, steady quality, can meet the serviceability of fine control valve completely.
Accompanying drawing explanation
Fig. 1 is the schematic diagram of the spool that need process
Detailed description of the invention
Embodiments of the invention: be described for Fig. 1.
1, get the raw materials ready: select 6A02-T6GB/T3191-1998 aluminium alloy bar.
2, Vehicle Processing:
(1) hard three-jaw folder cylindrical φ d2 end, car one end face, brill, car centre bore and screwed hole, tailstock center holds out against centre bore, rough turn cylindrical φ d1, made allowance.
(2) soft three-jaw presss from both sides car end cylindrical φ d1, car other end, drill centers, and tailstock center holds out against centre bore, rough turn cylindrical φ d2, made allowance.
(3) soft three-jaw folder cylindrical φ d1, tailstock center holds out against centre bore, half fine turning outer circle φ d2, and cylindrical stays allowance, and the cannelure of car φ d2 section is to requiring.Use the same method the cannelure of turning φ d1 and this section thereof.(4) main shaft three-jaw presss from both sides a thimble, and revises thimble 60 ° of conical surfaces.With heart carrier clamping cylindrical φ d2, lathe Double ejection pin holds out against two ends centre bore, and heart carrier drives workpiece to rotate, and fine turning outer circle φ d1, is processed as d1max+ (0.15 ~ 0.35) mm.Use the same method turning φ d2, is processed as d2max+ (0.15 ~ 0.35) mm.Surplus is 0.15mm ~ 0.35mm, chooses according to work piece cylindrical and length.
3, heat treatment: artificial aging, temperature 155 ± 5 DEG C, insulation 7h ~ 8h.
4, pincers processing: repair and grind two ends centre bore 60 ° of conical surfaces.
5, mill processing: with heart carrier clamping cylindrical φ d2, the Double ejection pin of lathe holds out against two ends centre bore, and heart carrier drives workpiece to rotate, and cylindrical grinding φ d1, is processed as d1min-(0.01 ~ 0.02) mm, tolerance is h6.Use the same method cylindrical grinding φ d2, is processed as d2min-(0.01 ~ 0.02) mm, tolerance is h6.
6, pincers processing: repair burr clearly, sharp edge rounding is not more than 0.05mm.
7, surface treatment: hard anodizing, thicknesses of layers is 0.04mm ~ 0.06mm.The electrode of surface processing equipment connects with conducting electricity good alumite alloy bar with between workpiece, with screw, aluminium alloy bars is fixed to the electrode union end place of surface processing equipment, aluminium alloy bars with workpiece union end is made external screw thread, and connects with the internal thread of workpiece termination.
8, mill processing: with heart carrier clamping cylindrical φ d2, the Double ejection pin of lathe holds out against two ends centre bore, and heart carrier drives workpiece to rotate, and cylindrical grinding φ d1, to requiring, ensures cylindricity e1 simultaneously.Using the same method cylindrical grinding φ d2 to requiring, ensureing cylindricity e2 and axiality φ f simultaneously.
9, pincers processing: repair burr clearly, sharp edge rounding is not more than 0.05mm.
Claims (1)
1. a processing method for high-abrasion resistance valve core, is characterized in that: it comprises following technological process:
The first, get the raw materials ready: aluminium alloy bar;
The second, Vehicle Processing: each shelves cylindrical of Vehicle Processing and cannelure, and drill centers, cylindrical φ d1, cylindrical φ d2 are processed as d1max+ (0.15 ~ 0.35) mm, d2max+ (0.15 ~ 0.35) mm respectively, and all the other are machined to requirement;
Three, heat treatment: artificial aging;
Four, pincers processing: repair and grind two ends centre bore 60 ° of conical surfaces;
Five, mill processing: with heart carrier clamping cylindrical φ d2, the Double ejection pin of lathe holds out against two ends centre bore, heart carrier drives workpiece to rotate, cylindrical grinding φ d1, be processed as d1min-(0.01 ~ 0.02) mm, tolerance is h6, use the same method cylindrical grinding φ d2, is processed as d2min-(0.01 ~ 0.02) mm, tolerance is h6;
Six, pincers processing: repair burr clearly, sharp edge rounding is not more than 0.05mm;
7th, surface treatment: hard anodizing, require to determine hard anodizing layer thickness by design document requirement hard anodizing layer thickness and grinding, according to size and the structure of workpiece, the electrode of surface processing equipment connects with conducting electricity good wire or metal bar with between workpiece, with screw, wire or metal bar are fixed to the electrode union end place of surface processing equipment, wire with workpiece union end is made paper clip type, then connect with the non-mating surface of workpiece, or the metal bar with workpiece union end is made external screw thread, connect with the internal thread of workpiece termination again,
Eight, mill processing: with heart carrier clamping cylindrical φ d2, the Double ejection pin of lathe holds out against two ends centre bore, and heart carrier drives workpiece to rotate, cylindrical grinding φ d1 is to requiring, ensure that cylindricity e1, the cylindrical grinding φ d2 that uses the same method are to requiring, ensure cylindricity e2 and axiality φ f simultaneously simultaneously;
Nine, pincers processing: repair burr clearly, sharp edge rounding is not more than 0.05mm.