CN102822121A - 喷涂泡沫材料的方法及由此方法获得的涂层 - Google Patents
喷涂泡沫材料的方法及由此方法获得的涂层 Download PDFInfo
- Publication number
- CN102822121A CN102822121A CN2011800083831A CN201180008383A CN102822121A CN 102822121 A CN102822121 A CN 102822121A CN 2011800083831 A CN2011800083831 A CN 2011800083831A CN 201180008383 A CN201180008383 A CN 201180008383A CN 102822121 A CN102822121 A CN 102822121A
- Authority
- CN
- China
- Prior art keywords
- foam
- ammonium chloride
- salt
- carbon atom
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及喷涂泡沫材料的方法，包括下列阶段：a）在喷涂设备的混合机中，通过混合水和至少下列组分制备泡沫材料：i）选自水硬性粘合剂、硫酸钙源、石灰和填料的至少一种成分；ii）胶乳；和iii）水基泡沫；b）将所述泡沫材料转移到所述喷涂设备的泵中；c）在承载件上喷涂；和d）任选修匀厚度，用直尺校平并修匀在所述承载件上喷涂的所述泡沫材料。
Description
本发明涉及喷涂泡沫材料的方法，涉及与在建筑工程领域中的这种喷涂应用相容的泡沫材料组合物，并涉及能够通过采用此类方法获得的建筑墙壁涂层。
此类方法主要旨在覆盖（特别是通过隔绝）和翻新建筑的外墙或内墙。其还可用于填充建筑材料的表面裂纹。
当前，在新建工程中和在翻新中，建筑专业人士都在寻找与喷涂应用（例如以立面形式）相容的轻质和/或绝热的胶凝材料。通过喷涂进行此类涂施能沉积特别薄的层（至少一毫米至几厘米），能完美地匹配承载件的几何形状，并且与传统（人工）方法相比能节省时间并同时降低成本。此外，载荷减轻的胶凝材料（混凝土、砂浆、水泥等等）特别受到重视，由于较不致密，它们实际上对施加了它们的承载件，实际上甚至在整个结构上施加较小的应力。同时，重要的是，该轻质材料具有与建筑工程的规格相符的绝热性质，实际上甚至改进这些性质，并在机械强度、经时冲击强度和对各种机械应力的耐受性方面表现出良好的机械性质。
具有普通添加剂（发泡(expansé)聚苯乙烯(EPS)、软木、蛭石(vermiculite)等等）的常规绝热或轻质砂浆当涂施到基底上（特别是通过喷涂）时表现出变得稠密的缺点，这特别是由于该拌合砂浆中夹带的空气体积的减少。
这意味着，这些标准轻质砂浆在喷涂后没有表现出最佳的性质，特别是在绝热方面。特别是对于喷涂的砂浆，本领域技术人员已知的引气剂不能令人满意地控制该密度。
对于喷涂涂施而言，对预拌合浆料形式的砂浆施以一定数量的应力，所述应力限制了涂施方法：
- 混合过程中的剪切应力，
- 在喷涂设备的泵中在高压下（1至20巴）的剪切应力，
- 在通常很长（特别是10至50米）的管道中在压力下的流动（输送）应力。
同样已知的是，通过喷涂涂施的整个过程具有使砂浆浆料稠密的作用，这是由于或多或少排出了起始存在于该浆料中的空气。在喷涂具有低密度的砂浆浆料的情况下，特别是在使用混有称为胶凝泡沫的泡沫的砂浆的情况下，更加剧了这一问题（特别是对于绝热或减轻负荷(allégement)的问题）。
申请CN101439950公开了通过喷涂使用具有泡沫的混凝土；但是，获得的喷涂材料的密度保持非常高，因为它们最高达到1.1×103千克/立方米。
本发明旨在克服全部或部分缺点，并特别应结合下列优点：
- 在喷涂前获得在流变性方面响应喷涂过程中施加的应力的泡沫材料，即保持稳定和充分充气并同时在喷涂设备的管道中容易流动和经受应力的泡沫材料；
- 该泡沫材料一旦喷涂就不会流动或从墙壁上滑落，其必须能够由操作者操作，即在承载件的表面上涂铺、修匀和均匀分布，这尤其是沉积高厚度（理想地最高10厘米）的情况下，并且必须在其硬化过程中良好地粘接到喷涂其的承载件上；和
- 其在喷涂和随后的干燥后必须能够获得具有充分充气的轻质结构的涂层，该涂层具有良好的热性质，在高厚度下不会开裂或收缩，同时保持令人满意的机械强度，特别是对于经受偶发的破碎作用或冲击。
在这一点上，本发明的主题是喷涂泡沫材料的方法，包括下列阶段：
a）在喷涂设备的混合机中，通过混合水和至少下列组分制备泡沫材料：
i）选自水硬性粘合剂、硫酸钙源、石灰和填料的至少一种成分；
ii）胶乳；和
iii）水基泡沫；
b）将所述泡沫材料转移到所述喷涂设备的泵中；
c）在承载件上喷涂；和
d）任选修匀厚度，用直尺校平并修匀在所述承载件上喷涂的所述泡沫材料。
发明人已经预料不到地证明，通过这种泡沫材料体系，混合物具有足够的流动性以便被喷涂，特别是通过泵送管路。此外，该泡沫材料一旦在墙壁上喷涂就不会流动，甚至当沉积非常厚的层（通常1至最多10厘米）时也如此。干燥后获得的砂浆保持低密度，并且喷涂的浆料随后可以容易地修匀。
这种泡沫材料可以用装有软管的常规喷涂设备容易地喷涂。所得砂浆还充分充气以确保非常令人满意的热性质，并且其具有良好的机械强度。因此，获得与喷涂应用相容的非常有效的涂布。
术语“泡沫材料”在本发明中指的是例如胶凝泡沫(mousse cimentaire)，即泡沫混凝土(béton moussé)、泡沫砂浆或包含水泥浆的泡沫（泡沫水泥浆）。
对于在本发明的方法的阶段a）中制备的包含至少一种水硬性粘合剂的混合物而言，一方面可以无差别地使用如Standard EN 197中规定的任何混合水泥，如可以单独或组合包含飞灰、高炉渣和天然或煅烧火山灰的波特兰水泥混合物或火山灰混合水泥，但是另一方面也可以使用高铝水泥或硫铝酸盐水泥。
上述水泥的所有组合也可用于制备本发明的泡沫材料。
优选地，在上述喷涂方法的阶段a），i）中，将使用至少一种水硬性粘合剂（水泥）；有利地，其是波特兰水泥，更优选为Portland CEM I 52.5水泥（Standard EN 197）。
在a），i）中列举的组分中更优选仅使用水硬性粘合剂（水泥），有利地使用波特兰水泥，更优选使用Portland CEM I 52.5水泥。
可以包含在本发明的泡沫材料组合物中的硫酸钙源是例如石膏、半水石膏、磷石膏和/或无水石膏。
用于制备本发明的泡沫材料的石灰(chaux)是例如水硬石灰、生石灰或消石灰。
本发明中的术语“填料”特别是指石灰质填料、硅质填料或粘土（滑石、高岭土等等）。该填料优选为石灰质填料。
该石灰质或硅质填料通常以粒径尤其小于或等于120微米的粉末的形式提供。
术语“胶乳”在本发明的含义中特别是指通常用于建筑材料的胶乳聚合物。在属于这一类的聚合物中可以提及例如弹性体胶乳、热塑性胶乳和热固性胶乳。
在本发明中，术语“胶乳”优选理解为是指一种或多种天然或合成且通常为热塑性的聚合物的含水乳液或分散液。该聚合物可以是可自乳化的，或者在相反情况下，该乳液或分散液通过适当的表面活性剂稳定。用于本发明的胶乳有利地具有低于50℃的玻璃化转变温度Tg。理想地，该Tg为-30℃至50℃，优选为-10℃至30℃，有利地为5℃至25℃，实际上甚至为大致15℃。
可以通过混合几种胶乳来调节该泡沫材料的机械性质，所述胶乳的至少一种具有在上文规定范围内的Tg。
优选使用Tg至多略低于环境温度的聚合物以确保形成聚合物膜，该聚合物膜在硬化的胶凝材料中赋予适当的聚合物性质。同样优选Tg值不过度低的聚合物，以使得该聚合物不会太过柔软，这将会获得过分柔软的胶凝材料。
该胶乳有利地包含乙烯基型、丙烯酸型和/或衍生自羧酸的聚合物或共聚物。非常特别优选乙烯基型胶乳，特别是包含酯官能侧基或基于氯乙烯和烯烃的共聚物，其可以是或不是硅烷化的。特别可以提及基于乙酸乙烯酯、特别是基于聚乙酸乙烯酯均聚物或基于乙酸乙烯酯与特别是(甲基)丙烯酸和/或酯、马来酸酯、烯烃和/或氯乙烯的共聚物或均聚物的、或基于氯乙烯/乙烯共聚物的胶乳。其它有利的胶乳可以选自包括丙烯酸型聚合物的那些，特别是丙烯腈和丙烯酸酯的共聚物或苯乙烯/丙烯酸或酯的共聚物，其是硅烷化的（也就是说，与包含带有至少一个硅烷或硅烷醇官能团的烯属不饱和的单体共聚合）。
可以有利地使用Hexion?销售的苯乙烯/丙烯酸共聚物型的胶乳，如Axilat? 4204或Axilat? L或Axilat? DS系列的任何成员，例如Axilat? DS 805。但是，避免使用包含消泡剂的产品。
该胶乳可以选自通过自由基乳液或分散聚合法获得的其它苯乙烯/丙烯酸共聚物或完全丙烯酸共聚物（来自于不同的丙烯酸单体）。这些胶乳通过丙烯酸和/或丙烯腈稳定。此类聚合物可以由BASF以名称Acronal?标记的系列销售，特别是Acronal? S 400。还可以替代使用或联合使用Acronal?系列的任何胶乳（一种或几种）。
术语“水基泡沫”在本发明的含义中是指通过在水相，特别是在具有肥皂外观的液体中的大量混乱的气泡所获得的任何类型的泡沫。具有肥皂外观的此类液体包含水和至少一种表面活性化合物。
上述方法的阶段a）的水基泡沫包含下列化合物的混合物：
- 选自下列通式的化合物之一的至少一种阳离子表面活性剂盐：
其中R是8至24个碳原子的脂族链，R1是选自包含1至16个碳原子的烷基、包含1至16个碳原子的羟烷基、苄基或与式（I）的氮一起产生任选被至少一个氟原子取代的杂环的基团的基团，R2和R3选自包含1至6个碳原子的烷基、包含1至6个碳原子的羟烷基、氢原子、苄基或与式（I）的氮一起产生任选被至少一个氟原子取代的杂环的基团，并且X-是平衡阴离子；
- 选自下列通式（II）的化合物之一的至少一种阴离子表面活性剂盐：
其中R是10至24个碳原子的脂族链，X-是带有负电荷的基团，选自羧酸根、硫酸根和磷酸根，Y+是平衡阳离子，选自铵、钠、钾、钙和镁；
使得该阳离子表面活性剂盐的重量含量对该阴离子表面活性剂盐的重量含量的比为0.05:1至15:1、优选0.2:1至5:1、实际上甚至0.4:1至2.5:1。
在本发明中，“离子表面活性剂盐”是指与和其缔合的平衡离子一起构成的表面活性剂。
有利地，本发明的方法的阶段a）中使用的水基泡沫的阳离子表面活性剂盐选自包含10至22个碳原子的烷基基团的烷基三甲基铵盐，优选选自下列化合物的至少一种：十二烷基三甲基溴化铵（或氯化铵）、十四烷基三甲基溴化铵（或氯化铵）、十六烷基三甲基溴化铵（或氯化铵）、十八烷基三甲基溴化铵（或氯化铵）、鲸蜡基三甲基溴化铵（或氯化铵）、鲸蜡基苄基二甲基氯化铵、鲸蜡基三乙基溴化铵和牛脂基三甲基氯化铵。该阳离子表面活性剂盐更优选为牛脂基三甲基氯化铵。
有利地，上面提及的阴离子表面活性剂盐选自下列化合物的至少一种：硬脂酸铵、硬脂酸钾、硬脂酸钠、硬脂酸钙和硬脂酸镁。
或者或补充地，也可以使用由带有12至24个碳原子的脂族链的有机酸的碱金属盐组成的阴离子表面活性剂，有利地为钠、钾或铵（任选被取代）盐。
通式（II）的X-基团可以是羧酸根、硫酸根或磺酸根。可以提及包含12至24个碳原子的羧酸的盐，选自例如肉豆蔻酸盐、棕榈酸盐、硬脂酸盐、油酸盐或二十二烷酸的共轭碱的盐，特别是由盐通过甘油三酸酯水解（皂化）生成的所选阴离子。还可以提及其它羧酸盐，如处理动物脂肪酸所得到的那些，特别包括棕榈酸盐、硬脂酸盐和油酸盐。还可以使用脂肪酸的其它共轭碱，例如包含脂肪酸的肥皂/洗浴凝胶，所述脂肪酸来自于天然来源，如牛脂、椰子油或者棕榈油。
本发明主题的方法的阶段a）中所用水基泡沫的阳离子和阴离子表面活性剂优选包括在两种单独的水相中，并以上述含量混合以形成该泡沫。此类水基泡沫的制备描述在申请WO96/25475中。
本发明人已经表明，包含阳离子表面活性剂和阴离子表面活性剂的这些水基泡沫具有在喷涂过程中和甚至其后特别是在干燥和/或硬化过程中保持特别稳定的优点。
本发明主题的方法的阶段a）中所用水基泡沫的阳离子和阴离子表面活性剂优选包括在同一水相中，将其剧烈搅拌以引起发泡。
还可以规定在本发明的方法的阶段a）中添加其它组分：例如赋予具体性质的添加剂或辅助剂，例如流变剂、保水剂、加气剂、具有流变学和/或机械功能的纤维、增稠剂、杀虫和/或杀菌保护剂、防水剂、分散剂、去气剂、颜料（特别是无机颜料）、促进剂、缓凝剂或改善固化和/或硬化以及涂敷后砂浆稳定性的试剂。还可以使用改变砂浆的颜色和/或加工性能等等的试剂。
除本发明的方法的阶段a）中的混合物之外，前述组分的所有组合也是可能的。
优选在本发明的方法的阶段a）中加入砂：加入砂能够制备泡沫砂浆，特别是当粘合剂是水硬性粘合剂时。
优选在本发明的方法的阶段a）中与砂一起加入骨料（granulates）（或集料(agrégats)）：加入砂和骨料能够制备泡沫混凝土，特别是当粘合剂是水硬性粘合剂时。
本发明中所用的砂优选表现出50微米至4毫米且有利地为50微米至500微米的粒度。
优选将阶段a）中获得的泡沫材料转移到喷涂设备的泵中，并将1至20巴、优选1至5巴或有利地为2巴的压力施加到该混合物上。
本发明中使用的喷涂设备优选为Putzmeister销售的P11或S5类型的设备。其具有喷雾胶管（或管），优选具有理想的为10至50米、例如12米的长度，横截面具有优选为20至40毫米、例如25毫米的直径。
本发明的另一主题是在本发明中用于上文规定方法的泡沫材料，包含：
a）水基泡沫；
b）选自水硬性粘合剂、硫酸钙源、石灰和填料的至少一种成分；和
c）胶乳；
除了下述泡沫材料之外（à l’exclusion des matériaux mousses)：该泡沫材料包含a）、b）和c）中规定的化合物的混合物，以使得成分b）只有在与a）的水基泡沫一起时才是水硬性粘合剂，a）的水基泡沫包含下列化合物的混合物：
- 选自下列通式的化合物之一的至少一种阳离子表面活性剂盐：
其中R是8至24个碳原子的脂族链，R1是选自包含1至16个碳原子的烷基、包含1至16个碳原子的羟烷基、苄基或与式（I）的氮一起产生任选被至少一个氟原子取代的杂环的基团的基团，R2和R3选自包含1至6个碳原子的烷基、包含1至6个碳原子的羟烷基、氢原子、苄基或与式（I）的氮一起产生任选被至少一个氟原子取代的杂环的基团，且X-是平衡阴离子；
- 选自下列通式（II）的化合物之一的至少一种阴离子表面活性剂盐：
其中R是10至24个碳原子的脂族链，X-是带有负电荷的基团，选自羧酸根、硫酸根和磷酸根，Y+是平衡阳离子，选自铵、钠、钾、钙和镁；和
使得该阳离子表面活性剂盐的重量含量对该阴离子表面活性剂盐的重量含量的比为0.05:1至15:1、优选0.2:1至5:1、实际上甚至0.4:1至2.5:1。
本发明的泡沫材料中所用的水基泡沫优选包含下列化合物的混合物：
- 选自下列通式的化合物之一的至少一种阳离子表面活性剂盐：
其中R是8至24个碳原子的脂族链，R1是选自包含1至16个碳原子的烷基、包含1至16个碳原子的羟烷基、苄基或与式（I）的氮一起产生任选被至少一个氟原子取代的杂环的基团的基团，R2和R3选自包含1至6个碳原子的烷基、包含1至6个碳原子的羟烷基、氢原子、苄基或与式（I）的氮一起产生任选被至少一个氟原子取代的杂环的基团，且X-是平衡阴离子；
- 选自下列通式（II）的化合物之一的至少一种阴离子表面活性剂盐：
其中R是10至24个碳原子的脂族链，X-是带有负电荷的基团，选自羧酸根、硫酸根和磷酸根，Y+是平衡阳离子，选自铵、钠、钾、钙和镁；和
使得该阳离子表面活性剂盐的重量含量对该阴离子表面活性剂盐的重量含量的比为0.05:1至15:1、优选0.2:1至5:1、实际上甚至0.4:1至2.5:1。
有利地，本发明的泡沫材料的组合物中使用的水基泡沫的阳离子表面活性剂盐选自包含10至22个碳原子的烷基基团的烷基三甲基铵盐，优选选自下列化合物的至少一种：十二烷基三甲基溴化铵（或氯化铵）、十四烷基三甲基溴化铵（或氯化铵）、十六烷基三甲基溴化铵（或氯化铵）、十八烷基三甲基溴化铵（或氯化铵）、鲸蜡基三甲基溴化铵（或氯化铵）、鲸蜡基苄基二甲基氯化铵、鲸蜡基三乙基溴化铵和牛脂基三甲基氯化铵。该阳离子表面活性剂盐更优选为牛脂基三甲基氯化铵。
有利地，上面提及的阴离子表面活性剂盐选自下列化合物的至少一种：硬脂酸铵、硬脂酸钾、硬脂酸钠、硬脂酸钙和硬脂酸镁。
或者或补充地，也可以使用由带有12至24个碳原子的脂族链的有机酸的碱金属盐组成的阴离子表面活性剂，有利地为钠、钾或铵（任选被取代）盐。
通式（II）的X-基团可以是羧酸根、硫酸根或磺酸根。可以提及包含12至24个碳原子的羧酸的盐，选自例如肉豆蔻酸的盐、棕榈酸的盐、硬脂酸的盐、油酸的盐或二十二烷酸的共轭碱的盐，特别是由盐通过甘油三酸酯水解（皂化）生成的所选阴离子。还可以提及其它羧酸盐，如处理动物脂肪酸所得到的那些，特别包括棕榈酸盐、硬脂酸盐和油酸盐。还可以使用脂肪酸的其它共轭碱，例如包含脂肪酸的肥皂/洗浴凝胶，所述脂肪酸来自于天然来源，如牛脂、椰子油或者棕榈油。
为了制备本发明的泡沫材料，一方面可以无差别地使用如Standard EN 197中规定的任何混合水泥，如可以单独或组合包含飞灰、高炉渣和天然或煅烧火山灰的波特兰水泥混合物或火山灰混合水泥，但是另一方面也可以使用高铝水泥或硫铝酸盐水泥。
上述水泥的所有组合也可用于制备本发明的泡沫材料。
优选地，在本发明的泡沫材料的b）中列举的组分中，至少选择一种水硬性粘合剂（水泥）；有利地，其是波特兰水泥，更优选为Portland CEM I 52.5水泥。在b）中列举的组分中，优选仅使用水硬性粘合剂（水泥），有利地使用波特兰水泥，更优选使用Portland CEM I 52.5水泥。
本发明的泡沫材料组合物的胶乳优选包含乙烯基型、丙烯酸型和/或衍生自羧酸的聚合物或共聚物。非常特别优选乙烯基型胶乳，特别包含酯官能侧基或基于氯乙烯和烯烃的共聚物，其可以是或不是硅烷化的。特别可以提及基于乙酸乙烯酯、特别是基于聚乙酸乙烯酯均聚物或基于乙酸乙烯酯与特别是(甲基)丙烯酸和/或酯、马来酸酯、烯烃和/或氯乙烯的共聚物或均聚物的、或基于氯乙烯/乙烯共聚物的胶乳。其它有利的胶乳可以选自包括丙烯酸型聚合物的那些，特别是丙烯腈和丙烯酸酯的共聚物或苯乙烯和丙烯酸或酯的共聚物，其是硅烷化的（也就是说，与包含带有至少一个硅烷或硅烷醇官能团的烯属不饱和的单体共聚合）。
可以有利地使用通过Hexion?销售的苯乙烯/丙烯酸共聚物型的胶乳，如Axilat? 4204或Axilat? L或Axilat? DS系列的任何成员，例如Axilat? DS 805。但是，避免使用包含消泡剂的产品。
该胶乳还可以是通过自由基乳液或分散聚合法获得的其它苯乙烯/丙烯酸共聚物或完全丙烯酸共聚物（来自于不同的丙烯酸单体）。这些胶乳通过丙烯酸和/或丙烯腈稳定。此类聚合物可以由BASF以名称Acronal?标记的系列销售，特别是Acronal? S 400。还可以替代使用或联合使用Acronal?系列的任何胶乳（一种或几种）。
所有前述胶乳可以单独或组合取用。
本发明的泡沫材料还可以附加地包含用于在一旦喷涂后降低材料密度的轻质化(allégeant)成分。
术语“轻质化成分”在本发明的含义中是指能够降低砂浆的密度的任何内含物，并可以以固体、液体或气体形式提供。有利地，轻质化成分将为固体形式。
本发明的泡沫材料组合物中的轻质化成分优选包含至少膨胀的多孔隙火山岩（流纹岩）。此类轻质化成分可以附带包含疏水性表面处理剂，通常为Lafarge Prestia销售的Noblite? G200 EC，或不含任何疏水性表面处理剂，例如由Knauf Insulation销售的Perlite? 0/1。
本发明中的轻质化成分优选包含至少发泡聚苯乙烯（EPS）的小球，如Saint-Gobain Placoplatre销售的那些。
本发明的增强轻质化砂浆的轻质化成分优选至少以防水和绝热添加剂（其基本上为小球形式）的形式提供，并使得该绝热添加剂包含至少单胞绝热微球。所用的绝热微球有利地为来自3M的玻璃微球（硼硅玻璃的中空单胞微球，具有连续的壳(非多孔的)）和/或以Expancel? 551 DE 40 d42为名销售的具有连续壳并包含热塑性塑料（PVC和丙烯腈共混物）的中空单胞聚合物微球。
在基于本发明的胶凝泡沫的混合物中，上述轻质化成分的所有组合也是可能的。
本发明的另一主题是一种涂层，特别用于立面和/或用于内墙，能够通过本发明中上文规定的喷涂方法获得。获得的涂层相应于在其承载件（墙壁、立面或其它表面）上干燥并硬化的喷涂的泡沫材料。
在干燥和硬化后在本文中获得的涂层已经证实具有优异的热性能，因为按照本发明获得的涂层的热导率通常低于或等于250mW/m.K，有利地低于或等于200mW/m.K；特别优选地，其低于或等于170mW/m.K，实际上甚至低于或等于150mW/m.K。
在本发明中获得的涂层的热导率有利地低于或等于110mW/m.K；其优选低于或等于90mW/m.K；其更优选低于或等于75mW/m.K，并且其有利地低于或等于55mW/m.K，实际上甚至低于或等于45mW/m.K并甚至低于或等于35mW/m.K。
在干燥和硬化后按照本发明获得的胶凝涂层的密度低于或等于800千克/立方米，其有利地低于或等于400千克/立方米，其更优选低于或等于200千克/立方米。
本发明的绝热材料的密度更优选低于或等于190千克/立方米，其有利地低于或等于170千克/立方米，其实际上甚至低于或等于150千克/立方米。
上文规定的热导率值范围和密度范围的所有组合也是可能的。
阅读下列实施例将更好地理解本发明及其优点，所述实施例仅为了例示而给出，并且在任何情况下不应认为是限制性的。
实施例
用于制造泡沫水泥浆的水基泡沫的组成与制备（表1的样品1和2）
以相对于各成分总重量（泡沫1）或相对于泡沫总重量（泡沫2）的重量%为单位给出该量。
泡沫1 （Allied Foam销售的泡沫）
具有商品标号（commercial reference）425A的成分1：
- 属于长链烷基类别的阳离子表面活性剂的混合物：50-60%
- 非离子苯氧基阳离子表面活性剂的混合物：10-20%
- 乙醇：5-8%
- 水：12-35%。
具有商品标号（commercial reference）510B的成分2：
- 丙烯酸聚合物的混合物：25-35%
- 属于脂肪酸类别的阴离子表面活性剂的混合物：15-30%
- 水：35-65%。
通过Allied Foam销售的泡沫发生器生成该泡沫。
将成分1稀释至每1升水136克。
将成分2直接加入到为此提供的罐中。
泡沫2
该泡沫的组成如下：
- 100克的水
- 3.3克的Arquad? T50（丙二醇中溶液形式的49%的丙二醇和51%的牛脂基三甲基氯化铵(64%的C18烷基，31%的C16烷基，4%的C14烷基和1%的C12烷基)）
- 0.67克的Triton? X-405（70%的辛基酚乙氧基化物）
- 20克的5.3%的硬脂酸钾溶液
- 30克的Axilat? DS805胶乳（在水中的悬浮液形式的57%的苯乙烯/丙烯酸共聚物）。
Arquad?系列的产品由Akzo Nobel销售，以Triton?名称标记的那些由Dow Chemical销售，以Axilat?名称标记的那些由Hexion销售。
在8巴的空气压力下，使用常规泡沫发生器由所有这些成分的混合物一次性生成该泡沫。
用于制造泡沫水泥浆的胶凝组合物（表1的样品1和2）
用于制备样品1和2的胶凝粉末具有下列组成：85%的Portland CEM I 52.5水泥 + 14.5%的石灰 + 0.5%的由保水剂和防水剂组成的添加剂。
制造表1中描述的两个样品
使用来自Putzmeister的S5型喷涂设备进行喷涂实验。
首先，将水加入到胶凝粉末中。用于拌合的混合持续30秒。对于样品1，在拌合过程中加入胶乳（对于样品2，胶乳已经存在于泡沫2的组合物中）。
随后将如上文所述制得的泡沫以表1中所述比例加入到该混合物中；水泥浆和泡沫的混合持续时间大约为1分30秒。
随后得到均匀的泡沫水泥浆。
随后将泡沫水泥浆转移到喷涂设备的泵中以便在垂直墙壁上喷涂，同时将压力调节至2巴（后者为1至20巴）；泡沫水泥浆在长度为12米（长度最长可能为25米）、直径为25毫米（也可能使用直径小于或等于1厘米的管）的管中流动。
用于喷涂的承载件是由涂有砂浆的光滑涂层的砖块组成的墙壁，由此模拟预涂立面的涂层。
用具有喷嘴的喷枪将该泡沫水泥浆喷涂在墙壁上，所述喷嘴在出口处的内径为15毫米；在墙壁上喷涂非常厚（通常为4厘米）的泡沫水泥浆层。
该泡沫水泥浆随后在墙壁上用直尺修平以便具有均匀的厚度。
测量方案
新鲜泡沫水泥浆的密度
其通过测量一升金属容器中的泡沫水泥浆的重量来确定（砂浆常规方案）。测量结果的标准偏差为大约3%。
- 对喷涂前的胶凝泡沫的测量：在混合阶段后，刚好在将其转移到泵中用于实际喷涂之前将后者抽出。
- 对喷涂后的胶凝泡沫的测量：在喷涂后用泥刀直接从墙上取下后者。
硬化的泡沫水泥浆的密度（立面涂层）
喷涂后28天，在从墙壁上切割该胶凝涂层的20×20×3厘米样品后测量该密度。
通过样品重量对其体积的比测定该密度。
测量的精度估计为3%。
热导率的测量
喷涂后28天，按照Standard EN NF 12664使用Netzsch HFM 436/3/1热导率计由用于密度测量的样品（参见上文）测量热导率。
测量的精度估计为3%。
获得的结果总结在下表1中。
表1（*）
（*）以相对于泡沫水泥浆总重量的重量%为单位表示该量。
Claims (23)
1.喷涂泡沫材料的方法，包括下列阶段：
a）在喷涂设备的混合机中，通过混合水和至少下列组分制备泡沫材料：
i）选自水硬性粘合剂、硫酸钙源、石灰和填料的至少一种成分；
ii）胶乳；和
iii）水基泡沫；
b）将所述泡沫材料转移到所述喷涂设备的泵中；
c）在承载件上喷涂；和
d）任选修匀厚度，用直尺校平并修匀在所述承载件上喷涂的所述泡沫材料。
2.如权利要求1所述的方法，其特征在于在阶段a）中，在i）中列举的组分中使用至少一种水硬性粘合剂，优选波特兰水泥，实际上甚至为Portland CEM I 52.5水泥。
3.如权利要求1或2所述的方法，其特征在于阶段a）中使用的所述胶乳包含选自乙烯基聚合物、丙烯酸聚合物、包含衍生自羧酸的官能团的聚合物、乙烯基共聚物、丙烯酸共聚物和包含衍生自羧酸的官能团的共聚物的至少一种成分。
4.如前述权利要求任一项所述的方法，其特征在于所述胶乳包含苯乙烯/丙烯酸共聚物。
5.如前述权利要求任一项所述的方法，其特征在于所述水基泡沫包含下列化合物的混合物：
- 选自下列通式的化合物之一的至少一种阳离子表面活性剂盐：
其中R是8至24个碳原子的脂族链，R1是选自包含1至16个碳原子的烷基、包含1至16个碳原子的羟烷基、苄基或与式（I）的氮一起产生任选被至少一个氟原子取代的杂环的基团的基团，R2和R3选自包含1至6个碳原子的烷基、包含1至6个碳原子的羟烷基、氢原子、苄基或与式（I）的氮一起产生任选被至少一个氟原子取代的杂环的基团，并且X-是平衡阴离子；
- 选自下列通式（II）的化合物之一的至少一种阴离子表面活性剂盐：
其中R是10至24个碳原子的脂族链，X-是带有负电荷的基团，选自羧酸根、硫酸根和磷酸根，Y+是平衡阳离子，选自铵、钠、钾、钙和镁；
使得该阳离子型表面活性剂盐的重量含量对该阴离子型表面活性剂盐的重量含量的比为0.05:1至15:1、优选0.2:1至5:1、实际上甚至0.4:1至2.5:1。
6.如权利要求5所述的方法，其特征在于所述阳离子型表面活性剂盐选自下列成分的至少一种：十二烷基三甲基溴化铵、十二烷基三甲基氯化铵、十四烷基三甲基溴化铵、十四烷基三甲基氯化铵、十六烷基三甲基溴化铵、十六烷基三甲基氯化铵、十八烷基三甲基溴化铵、十八烷基三甲基氯化铵、鲸蜡基三甲基溴化铵、鲸蜡基三甲基氯化铵、鲸蜡基苄基二甲基氯化铵、鲸蜡基三乙基溴化铵和牛脂基三甲基氯化铵。
7.如权利要求5或6所述的方法，其特征在于所述阳离子型表面活性剂盐是牛脂基三甲基氯化铵。
8.如前述权利要求任一项所述的方法，其特征在于所述阴离子型表面活性剂盐选自下列化合物的至少一种：硬脂酸铵、硬脂酸钾、硬脂酸钠、硬脂酸钙和硬脂酸镁。
9.如前述权利要求任一项所述的方法，其特征在于在所述方法的阶段a）中另外加入砂。
10.如权利要求9所述的方法，其特征在于在所述方法的阶段a）中另外加入骨料。
11.提供用于如前述权利要求任一项所述的喷涂方法的泡沫材料，包含：
a）至少一种水基泡沫；
b）选自水硬性粘合剂、硫酸钙源、石灰和填料的至少一种成分；和
c）至少一种胶乳；
除了下述泡沫材料之外，该泡沫材料包含a）、b）和c）中定义的化合物的混合物，以使得成分b）只有在与a）的水基泡沫一起时才是水硬性粘合剂，a）的水基泡沫包含下列化合物的混合物：
- 选自下列通式的化合物之一的至少一种阳离子表面活性剂盐：
其中R是8至24个碳原子的脂族链，R1是选自包含1至16个碳原子的烷基、包含1至16个碳原子的羟烷基、苄基或与式（I）的氮一起产生任选被至少一个氟原子取代的杂环的基团的基团，R2和R3选自包含1至6个碳原子的烷基、包含1至6个碳原子的羟烷基、氢原子、苄基或与式（I）的氮一起产生任选被至少一个氟原子取代的杂环的基团，且X-是平衡阴离子；
- 选自下列通式（II）的化合物之一的至少一种阴离子表面活性剂盐：
其中R是10至24个碳原子的脂族链，X-是带有负电荷的基团，选自羧酸根、硫酸根和磷酸根，Y+是平衡阳离子，选自铵、钠、钾、钙和镁；和
使得该阳离子表面活性剂盐的重量含量对该阴离子表面活性剂盐的重量含量的比为0.05:1至15:1、优选0.2:1至5:1、实际上甚至0.4:1至2.5:1。
12.如权利要求11所述的泡沫材料，其特征在于所述水基泡沫包含下列化合物的混合物：
- 选自下列通式的化合物之一的至少一种阳离子表面活性剂盐：
其中R是8至24个碳原子的脂族链，R1是选自包含1至16个碳原子的烷基、包含1至16个碳原子的羟烷基、苄基或与式（I）的氮一起产生任选被至少一个氟原子取代的杂环的基团的基团，R2和R3选自包含1至6个碳原子的烷基、包含1至6个碳原子的羟烷基、氢原子、苄基或与式（I）的氮一起产生任选被至少一个氟原子取代的杂环的基团，且X-是平衡阴离子；
- 选自下列通式（II）的化合物之一的至少一种阴离子表面活性剂盐：
其中R是10至24个碳原子的脂族链，X-是带有负电荷的基团，选自羧酸根、硫酸根和磷酸根，Y+是平衡阳离子，选自铵、钠、钾、钙和镁；和
使得该阳离子表面活性剂盐的重量含量对该阴离子表面活性剂盐的重量含量的比为0.05:1至15:1、优选0.2:1至5:1、实际上甚至0.4:1至2.5:1。
13.如权利要求11或12所述的泡沫材料，其特征在于所述水基泡沫的所述阳离子型表面活性剂盐选自下列成分的至少一种：十二烷基三甲基溴化铵、十二烷基三甲基氯化铵、十四烷基三甲基溴化铵、十四烷基三甲基氯化铵、十六烷基三甲基溴化铵、十六烷基三甲基氯化铵、十八烷基三甲基溴化铵、十八烷基三甲基氯化铵、鲸蜡基三甲基溴化铵、鲸蜡基三甲基氯化铵、鲸蜡基苄基二甲基氯化铵、鲸蜡基三乙基溴化铵和牛脂基三甲基氯化铵。
14.如权利要求11至13任一项所述的泡沫材料，其特征在于所述水基泡沫的所述阳离子型表面活性剂盐是牛脂基三甲基氯化铵。
15.如权利要求11至14任一项所述的泡沫材料，其特征在于所述水基泡沫的所述阴离子型表面活性剂盐选自下列化合物的至少一种：硬脂酸铵、硬脂酸钾、硬脂酸钠、硬脂酸钙和硬脂酸镁。
16.如权利要求11至15任一项所述的泡沫材料，其特征在于在b）中列举的组分中选择至少一种水硬性粘合剂，优选波特兰水泥，实际上甚至为Portland CEM I 52.5水泥。
17.如权利要求11至16任一项所述的泡沫材料，其特征在于c）的所述胶乳包含选自乙烯基聚合物、丙烯酸聚合物、包含衍生自羧酸的官能团的聚合物、乙烯基共聚物、丙烯酸共聚物和包含衍生自羧酸的官能团的共聚物的至少一种成分。
18.如权利要求11至17任一项所述的泡沫材料，其特征在于所述胶乳是苯乙烯/丙烯酸共聚物。
19.能通过权利要求1至10之一所述的喷涂方法获得的用于立面或内墙的涂层。
20.如权利要求19所述的涂层，其特征在于其具有低于或等于250mW/m.K的热导率。
21.如权利要求19或20所述的涂层，其特征在于其具有低于或等于110mW/m.K的热导率。
22.如权利要求19至21任一项所述的涂层，其特征在于其具有低于或等于55mW/m.K的热导率。
23.如权利要求19至22任一项所述的涂层，其特征在于其具有低于或等于45mW/m.K的热导率。