CN102817230A - Novel fabric flame retardant - Google Patents
Novel fabric flame retardant Download PDFInfo
- Publication number
- CN102817230A CN102817230A CN 201210341913 CN201210341913A CN102817230A CN 102817230 A CN102817230 A CN 102817230A CN 201210341913 CN201210341913 CN 201210341913 CN 201210341913 A CN201210341913 A CN 201210341913A CN 102817230 A CN102817230 A CN 102817230A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame retardant
- lithopone
- formaldehyde
- polyethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel fabric flame retardant which comprises the following components in parts by weight: 40-50 parts of sodium silicate, 1-3 parts of formaldehyde, 10-20 parts of talcum powders, 5-8 parts of polyethylene glycol, 1-3 parts of sodium hydroxide, 15-30 parts of trisodium phosphate, 20-30 parts of lithopone, 5-8 parts of methylol melamine and 120-180 parts of water. The novel fabric flame retardant has easily obtained raw materials, has a simple preparation process, has better fireproof flame retardant effect on textiles such as clothes, carpets, curtains and the like and also has the effects of mould prevention, insect prevention and corrosion prevention.
Description
Technical field
The invention belongs to the household chemicals technical field, more specifically relate to a kind of fabric fire retardant.
Background technology
Chemical fibre and cotton fabric run into fire and are easy to burning in air.For like special industries such as fire-fighting, oil, metallurgy, owing to its job specification determines, need its clothing of wearing to have fire protection flame retarding effect preferably, when running into unexpected incidents, can reduce the risk of self like this.
At present on the market the fabric flame-retardant agent kind seldom, all exist such as the fire protection flame retarding effect badly, use inconvenience, weak points such as complicated process of preparation.
Summary of the invention
The objective of the invention is to overcome the deficiency that prior art exists, a kind of fabric flame-retardant agent with good fire protection flame retarding effect is provided.
For achieving the above object, the present invention has taked following technical scheme:
A kind of fabric fire retardant, in weight portion, composed of the following components:
Sodium metasilicate: 40~50, formaldehyde: 1~3, talcum powder: 10~20,
Polyethylene glycol: 5~8, NaOH: 1~3, tertiary sodium phosphate: 15~30,
Lithopone: 20~30, melamine methylol: 5~8, water: 120~180.
In the technique scheme, the preparation method of described fabric flame-retardant agent is comparatively easy, is about to the various raw materials mix in the prescription, and gets final product through stirring.
Compared with prior art, the present invention has following beneficial effect:
Raw material of the present invention is easy to get, and preparation technology is simple, textiless such as clothing, carpet, curtain is all had fire protection flame retarding effect preferably, but also can play mildew-resistant, insect protected and corrosion-resistant effect.
The specific embodiment
Come the present invention is done further description below in conjunction with specific embodiment.
Embodiment 1
A kind of fabric fire retardant, in weight portion, composed of the following components:
Sodium metasilicate: 40, formaldehyde: 1, talcum powder: 10,
Polyethylene glycol: 5, NaOH: 1, tertiary sodium phosphate: 15,
Lithopone: 20, melamine methylol: 5, water: 120.
In the technique scheme, the preparation method of described fabric flame-retardant agent is comparatively easy, is about to the various raw materials mix in the prescription, and gets final product through stirring.
Embodiment 2
A kind of fabric fire retardant, in weight portion, composed of the following components:
Sodium metasilicate: 50, formaldehyde: 3, talcum powder: 20,
Polyethylene glycol: 8, NaOH: 3, tertiary sodium phosphate: 30,
Lithopone: 30, melamine methylol: 8, water: 180.
The preparation method is with embodiment 1.
Embodiment 3
A kind of fabric fire retardant, in weight portion, composed of the following components:
Sodium metasilicate: 46, formaldehyde: 2, talcum powder: 14,
Polyethylene glycol: 6, NaOH: 2, tertiary sodium phosphate: 20,
Lithopone: 25, melamine methylol: 6, water: 160.
The preparation method is with embodiment 1.
During use, fabric is immersed in this agent, taking-up is dried and is got final product after soaking into.
Claims (4)
1. a fabric fire retardant is characterized in that, and is in weight portion, composed of the following components:
Sodium metasilicate: 40~50, formaldehyde: 1~3, talcum powder: 10~20,
Polyethylene glycol: 5~8, NaOH: 1~3, tertiary sodium phosphate: 15~30,
Lithopone: 20~30, melamine methylol: 5~8, water: 120~180.
2. a kind of fabric fire retardant according to claim 1 is characterized in that, and is in weight portion, composed of the following components:
Sodium metasilicate: 40, formaldehyde: 1, talcum powder: 10,
Polyethylene glycol: 5, NaOH: 1, tertiary sodium phosphate: 15,
Lithopone: 20, melamine methylol: 5, water: 120.
3. a kind of fabric fire retardant according to claim 1 is characterized in that, and is in weight portion, composed of the following components:
Sodium metasilicate: 50, formaldehyde: 3, talcum powder: 20,
Polyethylene glycol: 8, NaOH: 3, tertiary sodium phosphate: 30,
Lithopone: 30, melamine methylol: 8, water: 180.
4. a kind of fabric fire retardant according to claim 1 is characterized in that, and is in weight portion, composed of the following components:
Sodium metasilicate: 46, formaldehyde: 2, talcum powder: 14,
Polyethylene glycol: 6, NaOH: 2, tertiary sodium phosphate: 20,
Lithopone: 25, melamine methylol: 6, water: 160.