CN102807877A - Corrosion-resistant fire retardant - Google Patents
Corrosion-resistant fire retardant Download PDFInfo
- Publication number
- CN102807877A CN102807877A CN2012102479632A CN201210247963A CN102807877A CN 102807877 A CN102807877 A CN 102807877A CN 2012102479632 A CN2012102479632 A CN 2012102479632A CN 201210247963 A CN201210247963 A CN 201210247963A CN 102807877 A CN102807877 A CN 102807877A
- Authority
- CN
- China
- Prior art keywords
- fire retardant
- corrosion
- fire
- tricresyl phosphate
- ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a corrosion-resistant fire retardant. The corrosion-resistant fire retardant is prepared by mixing the following raw materials in part by weight: 20 to 55 parts of resorcinol bis(diphenyl phosphate) (RDP), 15 to 30 parts of tris(2-chloroethyl) phosphate(TCEP) and 30 to 50 parts of phosphoric acid tris(2-chloro-1-methylethyl) ester (TCPP); stirring and cooling the raw materials to obtain the corrosion-resistant fire retardant. The corrosion-resistant fire retardant has fire retardance as well as high corrosion resistance.
Description
Technical field
The present invention relates to a kind of antiseptic fire-retardation agent, belong to chemical field.
Background technology
At present, all by utilization widely, all kinds of inflammable products all can carry out certain fire-retardant finish to it by relevant regulations to known fire retardant, can not cause fire easily to guarantee this series products in every field such as life, productions; But a lot of products reduces the work-ing life of product easily when carrying out fire-retardant finish, addle extremely easily like products such as wood furniture, door and windows.Though fire retardant be widely used in every field, in the actual proportioning use of fire retardant still new technical problem can appear.For example: a kind of fire retardant (96103412.2) is by pentabromodiphenyl oxide and aromatic hydrocarbon or contains phenyl ring phosphorated compound and be mixed and form.Its fire retardant of the above-mentioned patent documentation that provides is filled a prescription in actual proportioning, the fire retardant that is made, and its acidity is strong excessively, when article are carried out fire-retardant finish, very easily article is caused the acid attack infringement.
Summary of the invention
Can not solve to timber, when the product fire-retardant finish such as weaving cotton cloth in order to overcome existing fire retardant; The perishable deficiency of product; The invention provides a kind of antiseptic fire-retardation agent; When this fire retardant can effectively solve the product fire-retardant finish, the weak point that product is apt to rot can prolong simultaneously product work-ing life, optimize the processibility of product.
The technical solution adopted for the present invention to solve the technical problems is: in weight fraction; Resorcinol two (diphenyl phosphoester) is 20-55 part, tricresyl phosphate (β one chloroethyl) ester (TCEP) 15-30 part, tricresyl phosphate (2 one chloropropyl) ester (TCPP) 30-50 part (RDP), makes through following method:
(1) in the 300ml flask, order adds Resorcinol two (diphenyl phosphoester) (RDP) 20-55 part, tricresyl phosphate (β one chloroethyl) ester (TCEP) 15-30 part, tricresyl phosphate (2 one chloropropyl) ester (TCPP) 30-50 part.
(2) normal temperature fully stirs cooling 20 minutes down, and this antiseptic fire-retardation agent is colourless, transparent liquid shape.
The invention has the beneficial effects as follows: this fire retardant has good flame retardant resistance, when products such as wood furniture, door and window are carried out fire-retardant finish, further strengthens its preservative property, has prolonged its work-ing life.
Description of drawings
Below in conjunction with accompanying drawing and embodiment the present invention is further specified.
Fig. 1 is the system component proportioning figure of a kind of antiseptic fire-retardation agent of the present invention.
Embodiment
Embodiment 1: in the 300ml flask; Order adds (RDP) 20 parts of Resorcinols two (diphenyl phosphoester), 30 parts of esters (TCEP) of tricresyl phosphate (β one chloroethyl), 50 parts of tricresyl phosphate (2 one chloropropyl) esters (TCPP); Normal temperature fully stirred 20 minutes down, promptly got the agent of this antiseptic fire-retardation.
Embodiment 2: in the 300ml flask; Order adds (RDP) 30 parts of Resorcinols two (diphenyl phosphoester), 30 parts of esters (TCEP) of tricresyl phosphate (β one chloroethyl), 40 parts of tricresyl phosphate (2 one chloropropyl) esters (TCPP); Normal temperature fully stirred 20 minutes down, promptly got the agent of this antiseptic fire-retardation.
Embodiment 3: in the 300ml flask; Order adds (RDP) 45 parts of Resorcinols two (diphenyl phosphoester), 25 parts of esters (TCEP) of tricresyl phosphate (β one chloroethyl), 30 parts of tricresyl phosphate (2 one chloropropyl) esters (TCPP); Normal temperature fully stirred 20 minutes down, promptly got the agent of this antiseptic fire-retardation.
Claims (3)
1. antiseptic fire-retardation agent is characterized in that: in weight fraction, Resorcinol two (diphenyl phosphoester) is 20-55 part, tricresyl phosphate (β one chloroethyl) ester (TCEP) 15-30 part, tricresyl phosphate (2 one chloropropyl) ester (TCPP) 30-50 part (RDP).
2. a kind of antiseptic fire-retardation agent according to claim 1; It is characterized in that; Make through following method: in the 300ml flask; Order adds Resorcinol two (diphenyl phosphoester) (RDP) 20-55 part, tricresyl phosphate (β one chloroethyl) ester (TCEP) 15-30 part, tricresyl phosphate (2 one chloropropyl) ester (TCPP) 30-50 part, and fully stirs cooling 20 minutes at normal temperatures.
3. a kind of antiseptic fire-retardation agent according to claim 1 is characterized in that: this antiseptic fire-retardation agent is colourless, transparent liquid shape.