CN102767032A - Method for preparing natural yarn-dyed fabric and application of natural yarn-dyed fabric - Google Patents
Method for preparing natural yarn-dyed fabric and application of natural yarn-dyed fabric Download PDFInfo
- Publication number
- CN102767032A CN102767032A CN2011104576967A CN201110457696A CN102767032A CN 102767032 A CN102767032 A CN 102767032A CN 2011104576967 A CN2011104576967 A CN 2011104576967A CN 201110457696 A CN201110457696 A CN 201110457696A CN 102767032 A CN102767032 A CN 102767032A
- Authority
- CN
- China
- Prior art keywords
- cotton
- yarn
- natural color
- woven fabric
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention aims to provide a natural yarn-dyed fabric and application thereof in home textile products. The pure natural yarn-dyed fabric is prepared according to a method comprising the following steps: (1) making color silk fiber and natural color cotton fiber into yarn respectively; and spinning sequentially according to the procedures of cotton grabbing, cotton blending, cotton opening, cotton feeding, coiling, cotton carding, cotton drawing, roving, spinning, and spooling; and (2) interweaving the color silk yarn and the natural color cotton yarn to obtain the natural yarn-dyed fabric, wherein the color silk yarn is 30 to 60 percent by weight, and the natural color cotton yarn is 40 to 70 percent by weight; and weaving sequentially according to the procedures of beaming, slashing, reeding, jacquard weaving, perching, plaiting, packing and warehousing. Compared with the prior art, the obtained product not only has the characteristics of softness, pendency, special tactility, elegant and dynamic feeling, air and moisture penetrability, simple but elegant luster, and the like, but also feels soft, and has the special health functions of adjusting blood circulation and metabolization of a human body, keeping skin clean, enhancing cell viability of the skin, and preventing the skin from aging and white blood cell from declining in quantity, so that the purpose of the invention is achieved.
Description
Technical field
The present invention relates to a kind of preparation method and application thereof of color-woven fabric, particularly a kind of preparation method of pure natural color-woven fabric and application thereof.
Background technology
New type of health property fiber develops by leaps and bounds in China at a terrific speed; Though also there is incomplete place on stream in some fiber; But believe along with production technology constantly improve and ripe, its performance will make moderate progress, its product has boundless development space.
In rhythm of life more and more faster 21 century, people more pay attention to the quality of living, and health becomes important topic in people's life.From market comsupton trend, people to the pursuit of bedding function by warming-type to the health transition.On lining, adopt combining of advanced staining technique and functional treatment, make bedding possess functions such as antibiotic, far infrared, uvioresistant, antistatic, wrinkle resistant, anti-mite and environmental protection.Given this, adopt natural color cotton and color silk fiber to do home textile product, need not dye natural environmental-protective.
The pigment of natural colorful silk comes from mulberry leaf or the silkworm body and self synthesizes, and can avoid the harm of chemical dye to human body, has also avoided the pollution of dyeing waste water to environment.Colorful silk fabric color is soft naturally, has been known as high-grade environmental protection and health care fabric, has vast potential for future development.
The colorful silk fabric has good pliability, warmth retention property, absorb-discharge humid and aeration, and does not contain harmful chemical composition, is a kind of desirable dress material that wears next to the skin, and can be made into high-grade underwear.
Colorful silk is as a kind of biological raw material; Be all protein with the cutin and the collagen of human body, structure is quite similar, has good bioaffinity; Its fabric has good antibacterial ability; Be rich in 18 seed amino acids, be used for the treatment that the defect of skin surface of a wound such as dermatotome are got in superficial burns, wound and shaping medically can be made into Wound surface protection film, help the regeneration breeding of Skin Cell; Can also regulate human body blood circulation and metabolism, to keeping skin clean, strengthen the Skin Cell vigor, preventing that degradation has special health care under skin aging and the human white blood ball.
Natural color cotton is the novel cotton that utilizes modern science and technology such as biological gene engineering to cultivate out; Cotton fiber just has various natural colours during blow-of-cottons in the field; So be called natural color cotton; It has been complied with consumers in general and has constantly pursued health care, comfortable, high-grade consumption fashion and requirement, causes the great attention of many countries in the world.
The natural color cotton product is soft except that having, warmth retention property good, moisture absorption and the good characteristic such as ventilative, also have the environmental protection characteristic, therefore, natural color cotton optimum exploitation infant, presses close to the textiles of human body skin etc.At present, China has developed towelling coverlet, cotton blanket, bath towel, underwear, nightwear, shirt and infant's series clothes etc. with natural color cotton.And the twice-laid product of conventional needs dyeing all has negative effect more or less to environment and health.
In sum, need a kind of preparation method and application thereof of pure natural color-woven fabric especially, to satisfy market demand.
Summary of the invention
The purpose of this invention is to provide a kind of preparation method and application thereof of pure natural color-woven fabric,,, be applied in the home textile product, increase that it is functional, improve the grade in conjunction with the advantage of colorful silk and natural color cotton to satisfy market demand.
The technical problem that the present invention solved can adopt following technical scheme to realize:
First aspect of the present invention provides a kind of preparation method of pure natural color-woven fabric, it is characterized in that, it comprises the steps:
(1) colorful silk fiber and natural color cotton fiber are processed yarn respectively;
Spinning process: grab cotton → mixed cotton → opener → give cotton → rolling → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → winder;
(2) colorful silk yarn and natural color cotton yarns interwoven are obtained the natural colour knitted fabric, wherein contain the colorful silk yarn 30-60% of percentage by weight, natural color cotton yarn 40-70%;
Weaving process: warping → sizing → denting → jacquard weave → perching → plaiting → packing → warehouse-in.
In one embodiment of the invention, yarn is processed in said natural color cotton fiber and said white cotton fiber blending, wherein contains the natural color cotton fiber 65-80% of percentage by weight, white cotton fiber 20-35%; And then with the colorful silk yarns interwoven, obtain the natural colour knitted fabric, wherein contain the natural color cotton fiber and the white cotton fiber blended yarn 40-70% of percentage by weight, colorful silk yarn 30-60%.
In one embodiment of the invention, the technological parameter of said opener: the uneven lap rate is for being not more than 1%, and percentage elongation is 1.5%, and cotton rolling quantity is 380g/m.
In one embodiment of the invention, the technological parameter of said comb and parallel cotton fibers prior to spinning: cylinder licker-in differential surface speed is 2.5-3.0, and the feed plate licker-in spaces and is that 0.18mm, licker-in rotating speed are 830r/min, cylinder rotating speed 360r/min.
In one embodiment of the invention, the technological parameter of said drafting: strip quantitatively is 15.28g/5m, and ratch is 40-45mm, and horn mouth is 3.0mm, and sliver exporting speed is 260m/min.
In one embodiment of the invention, the technological parameter of said rove: twist factor is 106, and nip gauge is 3.3mm, and ingot speed is 780r/min.
In one embodiment of the invention, the technological parameter of said spun yarn: the twist is 96.5 sth. made by twisting/10cm, and nip gauge is 2.5mm, and ingot speed is 8519r/min, and front roller speed is 174r/min.
In one embodiment of the invention, said woven technological parameter: the loom fabric width is 340cm, and the speed of a motor vehicle is 300r/min, and the grey cloth fabric width is 280cm, and the warp stop frame height is 95mm.
In one embodiment of the invention, the performance indications of said pearl fiber and tencel blended lining: finished size rate of change: warp-wise-3.0%, broadwise-3.0%; Ultimate strength:>=250N; Grammes per square metre: 200g/m
2Rub resistance:>=3 grades; COLOR FASTNESS: washable (variable color, staining)>=3 grades; Content of formaldehyde:＜75mg/kg.
Second aspect of the present invention provides a kind of application of preparation method aspect manufacturing pure natural color-woven fabric of pure natural color-woven fabric, it is characterized in that the preparation method of said pure natural color-woven fabric is used to prepare home textile product.
Pearl fiber of the present invention and tencel blended yarn; Compared with prior art; Characteristics such as the product that obtains had both had that softness is dangled, sense of touch uniqueness, elegant innervation, air-moisture-permeable and plain gloss have good skin-friendly again, can regulate human body blood circulation and metabolism; Keep skin clean, strengthen the Skin Cell vigor, prevent the special health care of degradation under skin aging and the human white blood ball, realize the object of the invention.
Characteristics of the present invention can be consulted the detailed description of following better embodiment and obtained to be well understood to.
The specific embodiment
In order to make technological means of the present invention, creation characteristic, to reach purpose and effect and be easy to understand and understand,, further set forth the present invention below in conjunction with specific embodiment.
The preparation method of pure natural color-woven fabric of the present invention, it comprises the steps:
(1) colorful silk fiber and natural color cotton fiber are processed yarn respectively;
Spinning process: grab cotton → mixed cotton → opener → give cotton → rolling → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → winder;
(2) colorful silk yarn and natural color cotton yarns interwoven are obtained the natural colour knitted fabric, wherein contain the colorful silk yarn 30-60% of percentage by weight, natural color cotton yarn 40-70%;
Weaving process: warping → sizing → denting → jacquard weave → perching → plaiting → packing → warehouse-in.
In the present invention, yarn is processed in said natural color cotton fiber and said white cotton fiber blending, wherein contains the natural color cotton fiber 65-80% of percentage by weight, white cotton fiber 20-35%; And then with the colorful silk yarns interwoven, obtain the natural colour knitted fabric, wherein contain the natural color cotton fiber and the white cotton fiber blended yarn 40-70% of percentage by weight, colorful silk yarn 30-60%.
The pigment of colorful silk comes from mulberry leaf or the silkworm body and self synthesizes, and can avoid the harm of chemical dye to human body, has also avoided the pollution of dyeing waste water to environment; Natural color cotton is the novel cotton that utilizes modern science and technology such as biological gene engineering to cultivate out, and cotton fiber just has various natural colours in the field during blow-of-cottons, does not need operations such as later stage dyeing, natural environmental-protective degradable.
In the present invention, the technological parameter of said opener: the uneven lap rate is for being not more than 1%, and percentage elongation is 1.5%, and cotton rolling quantity is 380g/m.
The technological parameter of said comb and parallel cotton fibers prior to spinning: cylinder licker-in differential surface speed is 2.5-3.0, and the feed plate licker-in spaces and is that 0.18mm, licker-in rotating speed are 830r/min, cylinder rotating speed 360r/min.
The technological parameter of said drafting: strip quantitatively is 15.28g/5m, and ratch is 40-45mm, and horn mouth is 3.0mm, and sliver exporting speed is 260m/min.
The technological parameter of said rove: twist factor is 106, and nip gauge is 3.3mm, and ingot speed is 780r/min.
The technological parameter of said spun yarn: the twist is 96.5 sth. made by twisting/10cm, and nip gauge is 2.5mm, and ingot speed is 8519r/min, and front roller speed is 174r/min.
Said woven technological parameter: the loom fabric width is 340cm, and the speed of a motor vehicle is 300r/min, and the grey cloth fabric width is 280cm, and the warp stop frame height is 95mm.
(1) opening picking: the characteristics of color cotton fiber are that fibre length is short partially, and intensity is on the low side, and mic value difference is big, and short fibre content is many etc.; Characteristics to color cotton fiber; Each mechanical hired roughneck should suitable grasp on the low side; Suitably reduce the extracting amount of grabbing cotton dolly and shorten the length that the hired roughneck stretches out rib, suitably cotton dolly decrease speed is grabbed in reduction automatically, helps abundant shredding and combing removal of impurities; Reduce spacing of opener stripping cutter and hired roughneck, the rubbing of strike repeatedly that reduces flock is beneficial to reduce cotton knot;
(2) comb and parallel cotton fibers prior to spinning: reduce cylinder, licker-in speed,, reduce cotton knot, suitably reduce feeding quantitatively to reduce strike to fiber; To reduce cylinder, cover plate dial load, guarantee good carding role, because colored fiber is powerful low; Cause short flannel in the production process easily, add raw material itself and contain the short flannel height, shorten the big end arc length of leaking so adopt; Leak end inlet and doffer's increasings of spacing, thereby reduce the big spirit flow that leaks, the doffer can normally be grasped and transfer in time;
(3) combing: because colorful cotton fibre is shorter, short flannel is more, should suitably adjust cotton noils and space, the control linters rate;
(4) drafting: the bar evenness of drafting and spun yarn resultant yarn bar evenness have certain correlation; Because color cotton fiber length is short partially; Roller grips the easy slippage of fiber, thereby floating fiber quantity is increased, and on producing, should adjust roller gauge; Reduce roller speed, to improve the yarn unevenness of drafting;
(5) rove: to short partially, the powerful on the low side characteristics of color cotton length, should adopt in the rove operation/after space greatly, concentrate proparea drawing-off 0; The technology of twist factor grasp bigger than normal; Thereby guarantee that the rove bar does, in addition, Speed frames are taked the method for heavily pressurizeing; Can effectively reduce lap-ups and aggregation phenomenon, the control strip evenness;
(6) spun yarn: to color cotton characteristics, spinning process: take heavily to pressurize, the pressure that pressure passes to front roller greatly is also big, can have better fiber to grip; Spun yarn will adopt the back zone little drawing-off of spacing greatly, helps improving the bar evenness of resultant yarn; Suitably improve the spun yarn twist factor, improve resultant yarn bar evenness and yarn strength, reduce Yarn filoplume simultaneously, reduce broken end.
In the present invention, the performance indications of said pearl fiber and tencel blended lining: finished size rate of change: warp-wise-3.0%, broadwise-3.0%; Ultimate strength:>=250N; Grammes per square metre: 200g/m
2Rub resistance:>=3 grades; COLOR FASTNESS: washable (variable color, staining)>=3 grades; Content of formaldehyde:＜75mg/kg.
Second aspect of the present invention provides a kind of application of preparation method aspect manufacturing pure natural color-woven fabric of pure natural color-woven fabric, it is characterized in that the preparation method of said pure natural color-woven fabric is used to prepare home textile product.
Embodiment 1
Colorful silk fiber and natural color cotton fiber are processed yarn respectively;
Spinning process: grab cotton → mixed cotton → opener → give cotton → rolling → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → winder;
Colorful silk yarn and natural color cotton yarns interwoven are obtained the natural colour knitted fabric, wherein contain the colorful silk yarn 50% of percentage by weight, natural color cotton yarn 50%;
Weaving process: warping → sizing → denting → jacquard weave → perching → plaiting → packing → warehouse-in.
The technological parameter of said opener is controlled in 1% for the uneven lap rate, and percentage elongation is 1.5%, and the light partially control of cotton rolling quantity is designed to 380g/m; The technological parameter of said comb and parallel cotton fibers prior to spinning is that cylinder licker-in differential surface speed is 2.5, feed plate～licker-in 0.18mm that spaces, licker-in rotating speed 830r/min, cylinder rotating speed 360r/min; The technological parameter of said drafting is that strip quantitatively is 15.28g/5m, and ratch is 40mm, horn mouth 3.0mm, sliver exporting speed 260m/min; The technological parameter of said rove is that twist factor is 106, nip gauge 3.3mm, ingot speed 780r/min; The technological parameter of said spun yarn is for being the twist 96.5 sth. made by twisting/10cm, nip gauge 2.5mm, ingot speed 8519r/min, front roller speed 174r/min; Said woven technological parameter is loom fabric width 340cm, speed of a motor vehicle 300r/min, grey cloth fabric width 280cm, warp stop frame height 95mm.
The performance indications of said pearl fiber and tencel blended lining: finished size rate of change: warp-wise 2.8%, broadwise 2.9%; Ultimate strength:>=250N; Grammes per square metre: 200g/m
2Rub resistance:>=3 grades; COLOR FASTNESS: washable (variable color, staining)>=3 grades; Content of formaldehyde:＜75mg/kg.
Embodiment 2
Colorful silk fiber and natural color cotton fiber are processed yarn respectively;
Spinning process: grab cotton → mixed cotton → opener → give cotton → rolling → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → winder;
Colorful silk yarn and natural color cotton yarns interwoven are obtained the natural colour knitted fabric, wherein contain the colorful silk yarn 55% of percentage by weight, natural color cotton yarn 45%;
Weaving process: warping → sizing → denting → jacquard weave → perching → plaiting → packing → warehouse-in.
The technological parameter of said opener is controlled in 1% for the uneven lap rate, and percentage elongation is 1.5%, and the light partially control of cotton rolling quantity is designed to 380g/m; The technological parameter of said comb and parallel cotton fibers prior to spinning is that cylinder licker-in differential surface speed is 3.0, feed plate～licker-in 0.18mm that spaces, licker-in rotating speed 830r/min, cylinder rotating speed 360r/min; The technological parameter of said drafting is that strip quantitatively is 15.28g/5m, and ratch is 45mm, horn mouth 3.0mm, sliver exporting speed 260m/min; The technological parameter of said rove is that twist factor is 106, nip gauge 3.3mm, ingot speed 780r/min; The technological parameter of said spun yarn is for being the twist 96.5 sth. made by twisting/10cm, nip gauge 2.5mm, ingot speed 8519r/min, front roller speed 174r/min; Said woven technological parameter is loom fabric width 340cm, speed of a motor vehicle 300r/min, grey cloth fabric width 280cm, warp stop frame height 95mm.
The performance indications of said pearl fiber and tencel blended lining: finished size rate of change: warp-wise 2.7%, broadwise 2.6%; Ultimate strength:>=250N; Grammes per square metre: 200g/m
2Rub resistance:>=3 grades; COLOR FASTNESS: washable (variable color, staining)>=3 grades; Content of formaldehyde:＜75mg/kg.
Embodiment 3
Colorful silk fiber and natural color cotton fiber are processed yarn respectively;
Spinning process: grab cotton → mixed cotton → opener → give cotton → rolling → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → winder;
Colorful silk yarn and natural color cotton yarns interwoven are obtained the natural colour knitted fabric, wherein contain the colorful silk yarn 45% of percentage by weight, natural color cotton yarn 55%;
Weaving process: warping → sizing → denting → jacquard weave → perching → plaiting → packing → warehouse-in.
The technological parameter of said opener is controlled in 1% for the uneven lap rate, and percentage elongation is 1.5%, and the light partially control of cotton rolling quantity is designed to 380g/m; The technological parameter of said comb and parallel cotton fibers prior to spinning is that cylinder licker-in differential surface speed is 2.8, feed plate～licker-in 0.18mm that spaces, licker-in rotating speed 830r/min, cylinder rotating speed 360r/min; The technological parameter of said drafting is that strip quantitatively is 15.28g/5m, and ratch is 43mm, horn mouth 3.0mm, sliver exporting speed 260m/min; The technological parameter of said rove is that twist factor is 106, nip gauge 3.3mm, ingot speed 780r/min; The technological parameter of said spun yarn is for being the twist 96.5 sth. made by twisting/10cm, nip gauge 2.5mm, ingot speed 8519r/min, front roller speed 174r/min; Said woven technological parameter is loom fabric width 340cm, speed of a motor vehicle 300r/min, grey cloth fabric width 280cm, warp stop frame height 95mm.
The performance indications of said pearl fiber and tencel blended lining: finished size rate of change: warp-wise 2.9%, broadwise 3%; Ultimate strength:>=250N; Grammes per square metre: 200g/m
2Rub resistance:>=3 grades; COLOR FASTNESS: washable (variable color, staining)>=3 grades; Content of formaldehyde:＜75mg/kg.
Embodiment 4
The colorful silk fiber is processed yarn; Yarn is processed in natural color cotton fiber and said white cotton fiber blending, wherein contains the natural color cotton fiber 65% of percentage by weight, white cotton fiber 35%;
Spinning process: grab cotton → mixed cotton → opener → give cotton → rolling → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → winder;
Colorful silk yarn and natural color cotton fiber and white cotton fiber blended yarn interweaved obtains the natural colour knitted fabric, wherein contains the natural color cotton fiber and the white cotton fiber blended yarn 40% of percentage by weight, colorful silk yarn 60%;
Weaving process: warping → sizing → denting → jacquard weave → perching → plaiting → packing → warehouse-in.
The technological parameter of said opener is controlled in 1% for the uneven lap rate, and percentage elongation is 1.5%, and the light partially control of cotton rolling quantity is designed to 380g/m; The technological parameter of said comb and parallel cotton fibers prior to spinning is that cylinder licker-in differential surface speed is 2.5, and the feed plate licker-in spaces and is 0.18mm, licker-in rotating speed 830r/min, cylinder rotating speed 360r/min; The technological parameter of said drafting is that strip quantitatively is 15.28g/5m, and ratch is 40mm, horn mouth 3.0mm, sliver exporting speed 260m/min; The technological parameter of said rove is that twist factor is 106, nip gauge 3.3mm, ingot speed 780r/min; The technological parameter of said spun yarn is for being the twist 96.5 sth. made by twisting/10cm, nip gauge 2.5mm, ingot speed 8519r/min, front roller speed 174r/min; Said woven technological parameter is loom fabric width 340cm, speed of a motor vehicle 300r/min, grey cloth fabric width 280cm, warp stop frame height 95mm.
The performance indications of said pearl fiber and tencel blended lining: finished size rate of change: warp-wise 2.8%, broadwise 2.8%; Ultimate strength:>=250N; Grammes per square metre: 200g/m
2Rub resistance:>=3 grades; COLOR FASTNESS: washable (variable color, staining)>=3 grades; Content of formaldehyde:＜75mg/kg.
Embodiment 5
The colorful silk fiber is processed yarn; Yarn is processed in natural color cotton fiber and said white cotton fiber blending, wherein contains the natural color cotton fiber 70% of percentage by weight, white cotton fiber 30%;
Spinning process: grab cotton → mixed cotton → opener → give cotton → rolling → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → winder;
Colorful silk yarn and natural color cotton fiber and white cotton fiber blended yarn interweaved obtains the natural colour knitted fabric, wherein contains the natural color cotton fiber and the white cotton fiber blended yarn 50% of percentage by weight, colorful silk yarn 50%;
Weaving process: warping → sizing → denting → jacquard weave → perching → plaiting → packing → warehouse-in.
The technological parameter of said opener is controlled in 1% for the uneven lap rate, and percentage elongation is 1.5%, and the light partially control of cotton rolling quantity is designed to 380g/m; The technological parameter of said comb and parallel cotton fibers prior to spinning is that cylinder licker-in differential surface speed is 3.0, and the feed plate licker-in spaces and is 0.18mm, licker-in rotating speed 830r/min, cylinder rotating speed 360r/min; The technological parameter of said drafting is that strip quantitatively is 15.28g/5m, and ratch is 45mm, horn mouth 3.0mm, sliver exporting speed 260m/min; The technological parameter of said rove is that twist factor is 106, nip gauge 3.3mm, ingot speed 780r/min; The technological parameter of said spun yarn is the twist 96.5 sth. made by twisting/10cm, nip gauge 2.5mm, ingot speed 8519r/min, front roller speed 174r/min; Said woven technological parameter is loom fabric width 340cm, speed of a motor vehicle 300r/min, grey cloth fabric width 280cm, warp stop frame height 95mm.
The performance indications of said pearl fiber and tencel blended lining: finished size rate of change: warp-wise 3%, broadwise 2.9%; Ultimate strength:>=250N; Grammes per square metre: 200g/m
2Rub resistance:>=3 grades; COLOR FASTNESS: washable (variable color, staining)>=3 grades; Content of formaldehyde:＜75mg/kg.
Embodiment 6
The colorful silk fiber is processed yarn; Yarn is processed in natural color cotton fiber and said white cotton fiber blending, wherein contains the natural color cotton fiber 80% of percentage by weight, white cotton fiber 20%;
Spinning process: grab cotton → mixed cotton → opener → give cotton → rolling → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → winder;
Colorful silk yarn and natural color cotton fiber and white cotton fiber blended yarn interweaved obtains the natural colour knitted fabric, wherein contains the natural color cotton fiber and the white cotton fiber blended yarn 50% of percentage by weight, colorful silk yarn 50%;
Weaving process: warping → sizing → denting → jacquard weave → perching → plaiting → packing → warehouse-in.
The technological parameter of said opener is controlled in 1% for the uneven lap rate, and percentage elongation is 1.5%, and the light partially control of cotton rolling quantity is designed to 380g/m; The technological parameter of said comb and parallel cotton fibers prior to spinning is that cylinder licker-in differential surface speed is 2.8, feed plate～licker-in 0.18mm that spaces, licker-in rotating speed 830r/min, cylinder rotating speed 360r/min; The technological parameter of said drafting is that strip quantitatively is 15.28g/5m, and ratch is 43mm, horn mouth 3.0mm, sliver exporting speed 260m/min; The technological parameter of said rove is that twist factor is 106, nip gauge 3.3mm, ingot speed 780r/min; The technological parameter of said spun yarn is for being the twist 96.5 sth. made by twisting/10cm, nip gauge 2.5mm, ingot speed 8519r/min, front roller speed 174r/min; Said woven technological parameter is loom fabric width 340cm, speed of a motor vehicle 300r/min, grey cloth fabric width 280cm, warp stop frame height 95mm.
The performance indications of said pearl fiber and tencel blended lining: finished size rate of change: warp-wise 3%, broadwise 3%; Ultimate strength:>=250N; Grammes per square metre: 200g/m
2Rub resistance:>=3 grades; COLOR FASTNESS: washable (variable color, staining)>=3 grades; Content of formaldehyde:＜75mg/kg.
More than show and described basic principle of the present invention, principal character and advantage of the present invention.The technical staff of the industry should understand; The present invention is not restricted to the described embodiments; That describes in the foregoing description and the specification just explains principle of the present invention; The present invention also has various changes and modifications under the prerequisite that does not break away from spirit and scope of the invention, and these variations and improvement all fall in the scope of the invention that requires protection.The present invention requires protection domain to be defined by appending claims and equivalent thereof.
Claims (10)
1. the preparation method of a pure natural color-woven fabric is characterized in that, it comprises the steps:
(1) colorful silk fiber and natural color cotton fiber are processed yarn respectively;
Spinning process: grab cotton → mixed cotton → opener → give cotton → rolling → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → winder;
(2) colorful silk yarn and natural color cotton yarns interwoven are obtained the natural colour knitted fabric, wherein contain the colorful silk yarn 30-60% of percentage by weight, natural color cotton yarn 40-70%;
Weaving process: warping → sizing → denting → jacquard weave → perching → plaiting → packing → warehouse-in.
2. the preparation method of pure natural color-woven fabric according to claim 1 is characterized in that, yarn is processed in said natural color cotton fiber and said white cotton fiber blending, wherein contains the natural color cotton fiber 65-80% of percentage by weight, white cotton fiber 20-35%; And then with the colorful silk yarns interwoven, obtain the natural colour knitted fabric, wherein contain the natural color cotton fiber and the white cotton fiber blended yarn 40-70% of percentage by weight, colorful silk yarn 30-60%.
3. the preparation method of pure natural color-woven fabric according to claim 1 is characterized in that, the technological parameter of said opener: the uneven lap rate is for being not more than 1%, and percentage elongation is 1.5%, and cotton rolling quantity is 380g/m.
4. the preparation method of pure natural color-woven fabric according to claim 1; It is characterized in that the technological parameter of said comb and parallel cotton fibers prior to spinning: cylinder licker-in differential surface speed is 2.5-3.0, and the feed plate licker-in spaces and is 0.18mm; The licker-in rotating speed is 830r/min, cylinder rotating speed 360r/min.
5. the preparation method of pure natural color-woven fabric according to claim 1 is characterized in that, the technological parameter of said drafting: strip quantitatively is 15.28g/5m, and ratch is 40-45mm, and horn mouth is 3.0mm, and sliver exporting speed is 260m/min.
6. the preparation method of pure natural color-woven fabric according to claim 1 is characterized in that, the technological parameter of said rove: twist factor is 106, and nip gauge is 3.3mm, and ingot speed is 780r/min.
7. the preparation method of pure natural color-woven fabric according to claim 1 is characterized in that, the technological parameter of said spun yarn: the twist is 96.5 sth. made by twisting/10cm, and nip gauge is 2.5mm, and ingot speed is 8519r/min, and front roller speed is 174r/min.
8. the preparation method of pure natural color-woven fabric according to claim 1 is characterized in that, said woven technological parameter: the loom fabric width is 340cm, and the speed of a motor vehicle is 300r/min, and the grey cloth fabric width is 280cm, and the warp stop frame height is 95mm.
9. the preparation method of pure natural color-woven fabric according to claim 1 is characterized in that, the performance indications of said pearl fiber and tencel blended lining: the finished size rate of change: warp-wise-3.0%, broadwise-3.0%; Ultimate strength:>=250N; Grammes per square metre: 200g/m
2Rub resistance:>=3 grades; COLOR FASTNESS: washable (variable color, staining)>=3 grades; Content of formaldehyde:＜75mg/kg.
10. the application of the preparation method of the described pure natural color-woven fabric of claim 1 aspect manufacturing pure natural color-woven fabric is characterized in that the preparation method of said pure natural color-woven fabric is used to prepare home textile product.