CN102766399A - 光效凝胶、led光效凝胶及led光效指甲油 - Google Patents
光效凝胶、led光效凝胶及led光效指甲油 Download PDFInfo
- Publication number
- CN102766399A CN102766399A CN2012102704096A CN201210270409A CN102766399A CN 102766399 A CN102766399 A CN 102766399A CN 2012102704096 A CN2012102704096 A CN 2012102704096A CN 201210270409 A CN201210270409 A CN 201210270409A CN 102766399 A CN102766399 A CN 102766399A
- Authority
- CN
- China
- Prior art keywords
- light efficiency
- parts
- light
- efficiency gel
- led
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种光效凝胶，其特征在于，按照重量份数包括以下组分：光引发剂1-10；丙烯酸单体10-50；丙烯酸聚合物20-80；助剂0.1-5。本发明中的产品还具有以下有益效果：美甲操作时间缩短至现有产品所需时间的1/6，明显提高美甲工作效率。由于操作时间缩短，消费者在美甲过程中接收的UV辐射大幅降低，对皮肤的伤害性进一步降低。操作过程中无放热，令消费者在美甲过程更为舒适。适应性更广，LED光效凝胶在UV灯源、LED灯源均可以实现固化。
Description
技术领域
本发明涉及一种光效凝胶、LED光效凝胶及LED光效指甲油。
背景技术
市面上的光效凝胶多为UV光效凝胶，其配套的固化灯源为主波峰为365nm的高压汞灯，即UV（Ultraviolet)光疗灯。使用UV光效凝胶制成的指甲油，其使用时需要使用UV光疗灯照射固化。UV光效凝胶制成的指甲油，其使用过程中的不足之处有：1、操作时间长，对光效凝胶进行单次固化需时3分钟；2、UV（Ultraviolet)光疗灯发光伴随明显的红外放热，长时间工作积累的放热量持续增加，故在进行美甲时有明显热感；3、汞灯管寿命短，需要经常更换。
LED灯源是以发光二极管为发光光源，随着LED灯技术的不断发展，其应用领域也越来越宽。LED光源优点在于：1、LED光源为点光源，分布更均匀；2、LED光源为冷光源，发光不伴随发热；3、LED光源光强更集中，固化效率更高。
LED灯源相对UV灯源有许多优势，但市面的光疗胶只能使用UV灯固化，在LED灯源作用下无法进行固化反应。
发明内容
本发明的目的是为了克服现有技术中的不足，提供一种既可使用UV灯固化，又可使用LED灯固化的光效凝胶。
为实现以上目的，本发明通过以下技术方案实现：
光效凝胶，其特征在于，按照重量份数包括以下组分：
优选地是，还包括色浆2-20重量份。
色浆用于为光效凝胶调配颜色。可用的色浆包括油性色浆及水油通用色浆。其颜色可根据使用要求确定，包括但不限于：红色、蓝色、紫色、金色、银色等。
可用的油性色浆包括但不限于，氧化铁红，红色三号，红色4号，57号红，53号红等，黄色11号，黄色5号，黄色6号，黄色7号，钛白，二氧化钛，锰紫，萘酚黑，氧化铁黑，碳黑，群青蓝，蓝色2号，蓝色27号，绿色3号，绿色4号，氧化铬绿。
优选地是，还包括珠光剂0.1-3重量份。
可用的珠光剂包括但不限于：二硬脂酸乙二醇酯、覆盖云母珠光颜料。覆盖云母珠光颜料别名钛云母珠光颜料，其是以片状云母粉为基底，表面用化学方法覆盖一层云母或其他材料构成的复合颜料。钛云母珠光颜料可根据使用要求调配为金色、银色、紫色等十余种颜色。采用颜色的珠光剂还可以代替色浆。以上珠光剂既可以选择一种，也可以选择几种混合使用。
优选地是，所述助剂包括防沉剂0.05-2重量份。
可用的防沉剂包括但不限于：有机膨润土（海明斯BENTONE SD-1、BENTONE 52、BENTONE 34）；气相二氧化硅（卡博特M5、德固赛R972)；聚烯烃蜡(BYKCERAMAT250,258,131)；改性氢化蓖麻油（CRAYVALLAC SF，CRAYVALLAC MT，CrayValley CVP）；聚酰胺蜡（台湾德谦229，日本楠本化学6900-20，日本楠本化学4300）系列；改性脲N-甲基吡咯烷酮（BYK-411，BYK-420)；改性高分子聚合物（英国奥维斯Solthix250、法国哥帝士THIXOL100,BYK-428)等。以上防沉剂既可以选择一种，也可以选择几种混合使用。
优选地是，所述助剂包括流平剂0.05-2重量份。
可用的流平剂包括但不限于：聚醚硅氧烷共聚物，(Tego Glide482，Glide410，共荣社PolyflowNo7，No75，BYM354);交联型有机硅丙烯酸酯（Tego Red2500,2600,2700），有机改性硅氧烷（Efka-3239，HX-3080,HX-5600，YCK-1180,)，氟碳改性丙烯酸聚合物（Irgaflow110，Efka3777，Efka3600）,聚醚改性有机硅（BYK-UV 3510，BYK306)。以上流平剂既可以选择一种，也可以选择几种混合使用。
优选地是，所述助剂包括润湿剂0.05-2重量份。可用的润湿剂包括但不限于：聚醚改性有机硅氧烷（Silok 8030，8000，BYK348，BYK246，BYK337，Tego Wet260，Wet270，Wet500）聚醚改性聚二甲基硅氧烷共聚体（BYK333），氟碳改性聚合物（Efka3777，Efka3600,FC430，BYK-340，BYK388,CYTEC ADDITOLVXM6396）。以上润湿剂既可以选择一种，也可以选择几种混合使用。
优选地是，还包括香精0.02-0.5重量份。
可用的香精包括但不限于：日化复合型合成香精，水果香型或花香型。
优选地是，可用的光引发剂包括但不限于：自裂解型引发剂和光敏剂。
可用的裂解型引发剂包括但不限于：所述的光引发剂选自光引发剂1173、光引发剂184、光引发剂907、MBF、光引发剂651、光引发剂369、TPO-L、TPO、光引发剂819和BP中的一种或几种。
光引发剂1173，即2-羟基-2-甲基-1-苯基丙酮；光引发剂184，即1-羟基环己基苯基甲酮；光引发剂907，即2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮；MBF，即苯甲酰甲酸甲酯；光引发剂651，即安息香双甲醚，化学名2,2－二甲氧基－1,2－二苯乙酮；光引发剂369，即2-苯基苄-2-二甲基胺-1-（4-吗啉苄苯基）丁酮；TPO-L，即2,4,6-三甲基苯甲酰基苯基膦酸乙酯；TPO，即2,4,6-三甲基苯甲酰基-二苯基氧化膦；光引发剂819，即苯基双（2,4，6-三甲基苯甲酰基）氧化膦。
可用的光敏引发剂包括但不限于：BP，即BP二苯甲酮。
以上光引发剂既可以选择一种，也可以选择几种混合使用。
优选地是，可用的丙烯酸酯单体，包括但不限于：丙烯酸月桂酯、丙烯酸异辛酯、丙烯酸丁酯、丙烯酸-2-乙基己酯、甲基丙烯酸-2-羟基乙酯（HEMA）、甲基丙烯酸-2-羟基丙酯、甲基丙烯酸甲酯、甲基丙烯酸丁酯、甲基丙烯酸异丁酯、丙烯酸异冰片酯、甲基丙烯酸异冰片酯、1,3-丁二醇二丙烯酸酯、新戊二醇二丙烯酸酯、（2）丙氧化新戊二醇二丙烯酸酯、聚乙二醇二甲基丙烯酸酯、氧化二缩三乙二醇二甲基丙烯酸酯、二缩三丙二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯、季戊四醇三丙烯酸酯及（3）丙氧基化三羟甲基丙烷三丙烯酸酯。以上丙烯酸单体既可以选择一种，也可以选择几种混合使用。
优选地是，所述丙烯酸聚合物为脂肪族聚氨酯丙烯酸酯聚合物或聚氨酯丙烯酸酯聚合物或丙烯酸酯化的聚氨酯丙烯酸酯聚合物中的一种或几种。
可用的聚氨酯丙烯酸酯聚合物包括但不限于，沙多玛CN9893,CN929,CN965,CN971A80,CN963E80,CN9007;氰特EB230,EB8200,EB264,EB4858,EB9626,EB8402,EB284;长兴611B85,6113,DR-U300,6115J-80,6148T-85；科宁PHOTOMER 6008,PHOTOMER 6019,PHOTOMER 6010,PHOTOMER 6892；帝斯曼NeoRad U-6282,NeoRad U-20-12H,AgiSyn 230 S1-B85，AgiSyn230 T1,AgiSyn230 TH,AgiSyn235;日本合成，UV-3000B,UV-2750B，UV-2000B,UV-3200B。以上聚氨酯丙烯酸酯聚合物可以选用一种或几种混合使用。
以上光效凝胶，既可以使用LED灯固化，也可以使用UV灯固化。
本发明的目的之二是提供一种LED光效凝胶。
LED光效凝胶，其特征在于，包括前述的光效凝胶。
本发明的目的之三是提供一种LED光效指甲油。
LED光效指甲油，其特征在于，包括前述的光效凝胶。
本发明为LED灯源配套开发的LED光疗胶，该胶产品在LED灯源作用下10s-30s范围内即可完成固化成膜，成膜过程中无发热，成膜强韧，固化程度良好，并且可以做成各种颜色效果的产品。
本发明中的产品还具有以下有益效果：
1、美甲操作时间缩短至现有产品所需时间的1/6，明显提高美甲工作效率。
2、由于操作时间缩短，消费者在美甲过程中接收的UV辐射大幅降低，对皮肤的伤害性进一步降低。
3、操作过程中无放热，令消费者在美甲过程更为舒适。
4、适应性更广，LED光效凝胶在UV灯源、LED灯源均可以实现固化。
具体实施方式
下面结合实施例对本发明进行详细的描述。
以下实施例中的份数均为重量份。
实施例1
取1份光引发剂369加入到15份丙烯酸月桂酯和5份二缩三乙二醇二甲基丙烯酸酯中，高速分散使其完全溶解；再投入脂肪族聚氨酯丙烯酸酯聚合物CN965 78份，分散均匀；再依次投入0.3份流平剂EFKA 3239、0.2份润湿剂BYK348和0.5份防沉剂海明斯BENTONE SD-1，充分分散；即得起粘结自然甲与光效凝胶甲的LED底胶光效凝胶。
实施例2
取1份1-羟基环己基苯基甲酮和2份2,4,6-三甲基苯甲酰基-二苯基氧化膦加入到20份丙烯酸异辛酯和20份新戊二醇二丙烯酸酯中，高速分散使其完全溶解；再投入55份聚氨酯丙烯酸酯聚合物PHOTOMER 6010，分散均匀；再依次投入0.3份流平剂TEGO GLIDE 410，0.2份润湿剂Silok8000和1.5份防沉剂卡博特M5，充分分散；即得起粘结自然甲与光效凝胶甲的LED底胶光效凝胶。
实施例3
取2份BP二苯甲酮和2份光引发剂907加入到20份丙烯酸-2-乙基己酯中，高速分散使其完全溶解；再投入66份脂肪族聚氨酯丙烯酸酯聚合物EB4858，分散均匀；再依次投入0.2份流平剂POLY FLOW NO7、0.2份润湿剂BYK246和0.3份防沉剂海明斯BENGEL 828，充分分散；最后投入9.3份红色色浆，即得红色的LED光效凝胶。
实施例4
取3份MBF和4份TPO-L加入到25份丙烯酸-2-乙基己酯中，高速分散使其完全溶解；再投入聚氨酯丙烯酸酯聚合物EB9626 49份，分散均匀；再依次投入0.2份流平剂EFKA 3777，0.1份润湿剂SlLOK 8030和0.4份防沉剂THIXOL 100，充分分散；最后投入15份钛白色浆，3.3份红色3号色浆，即得粉红色效果的LED彩胶光效凝胶。
实施例5
取2份光引发剂907和0.5份光引发剂819加入到20份丙烯酸异冰片酯中，高速分散使其完全溶解；再投入70份丙烯酸酯化的聚氨酯丙烯酸酯聚合物氰特EB8200，分散均匀；再依次投入0.1份流平剂BYK354、0.1份润湿剂和2.3份防沉剂R972，充分分散；最后投入4份53号红色浆、1份蓝色27号色浆，即得枚红色的LED彩胶光效凝胶。
实施例6
取2份光引发剂184和2份光引发剂369加入到15份三羟甲基丙烷三丙烯酸酯和30份氧化二缩三乙二醇二甲基丙烯酸酯中，高速分散使其完全溶解；再投入31份脂肪族聚氨酯丙烯酸酯聚合物帝斯曼NeoRad U-6282，分散均匀；再依次投入0.3份流平剂TEGO RED 2500，0.1份润湿剂BYK340，3份防沉剂BYK CERAMAT250，充分分散；最后投入15份群青蓝色浆和1.6份金色珠光粉，即得蓝色带珠光效果的LED光效凝胶。
实施例7
取2份光引发剂651和4份TPO加入到23份聚乙二醇二甲基丙烯酸酯中，高速分散使其完全溶解；再投入60份脂肪族聚氨酯丙烯酸酯聚合物长兴6115J-80，分散均匀；再依次投入0.1份流平剂BYK354，0.1份润湿剂Irgaflow110和2.5份防沉剂卡博特M5作为，充分分散；最后投入5份白色浆、3份锰紫色浆和0.3份蓝色珠光粉，即得紫色带珠光效果的LED光效凝胶。
实施例8
取2份光引发剂1173和3份TPO-L加入到10份1,3-丁二醇二丙烯酸酯中，高速分散使其完全溶解；再投入20份脂肪族聚氨酯丙烯酸酯聚合物CN9893和56份脂肪族聚氨酯丙烯酸酯聚合物长兴6113，分散均匀；再依次投入0.3份流平剂BYK306，0.1份润湿剂BYK-340和0.3份防沉剂Solthix250，充分分散；最后投入5份钛白色浆、3份57号红色浆和0.3白色份珠光粉，即得粉色带珠光效果的LED光效凝胶。
实施例9
取4.3份2,4,6-三甲基苯甲酰基-二苯基氧化膦加入到23份甲基丙烯酸异丁酯中，高速分散使其完全溶解；再投入72份脂肪族聚氨酯丙烯酸酯聚合物AgiSyn 230 S1-B85，分散均匀；再依次投入0.3份流平剂YCK-1180，0.1份润湿剂BYK348，0.3份防沉剂BYK411，充分分散，即得起保护作用和提供高光泽效果的LED封层光效凝胶。
实施例10
取3份光引发剂184，3.3份光引发剂651和4份光引发剂TPO-L加入到30份二缩三乙二醇二甲基丙烯酸酯和20份甲基丙烯酸-2-羟基丙酯中，高速分散使其完全溶解；再投入39份脂肪族聚氨酯丙烯酸酯聚合物长兴6113，分散均匀；再依次投入0.3份流平剂HX5600，0.1份润湿剂BYK348，0.3份防沉剂楠本化学4300，充分分散；即得起保护作用和提供高光泽效果的LED封层光效凝胶。
实施例11
取4份光引发剂1173和3份光引发剂907加入到25份1,3-丁二醇二丙烯酸酯中，高速分散使其完全溶解；再投入24份聚氨酯丙烯酸树脂PHOTOMER 6892和聚氨酯丙烯酸树脂AgiSyn230 TH 32份，分散均匀；再依次投入1.5份流平剂BYK306，1份润湿剂BYK-340和0.8份防沉剂Solthix250，充分分散；最后投入5.4份钛白色浆、3份57号红色浆和0.3白色份珠光粉，即得粉色带珠光效果的LED光效凝胶。
实施例12
取1份光引发剂907，1份光引发剂TPO，0.5份光引发剂184加入到15份聚乙二醇二甲基丙烯酸酯中，高速分散使其完全溶解；再投入71份脂肪族聚氨酯丙烯酸酯聚合物EB230，分散均匀；再依次投入1.8份流平剂BYK-UV 3510，1.6份润湿剂BYK-246和1.9份防沉剂BYK-428，充分分散；最后投入1.7黄色7号色浆、4.5份钛白色浆，即得黄色效果的LED光效凝胶。
实施例13
取1份光引发剂819和2.25份光引发剂369加入到15份甲基丙烯酸-2-羟基丙酯中，高速分散使其完全溶解；再投入78.5份聚氨酯丙烯酸酯聚合物日本合成UV-2750B，分散均匀；再依次0.15份润湿剂EFKA3777和0.1份防沉剂日本楠本化学6900-20，充分分散；最后投入3份碳黑色，即得黑色效果的LED光效凝胶。
实施例14
取3.5份光引发剂369加入到38份1,3-丁二醇二丙烯酸酯中，高速分散使其完全溶解；再投入52.5份聚氨酯丙烯酸酯聚合物沙多玛CN9007，分散均匀；再依次投入0.3份流平剂共荣社Poly flow No7和0.7份防沉剂台湾德谦229，充分分散；最后投入5份绿色三号色浆，即得绿色效果的LED光效凝胶。
实施例1-14，制成品使用UV灯固化时间为2-4min，使用LED灯固化时间为20-40S；无论何种固化方式，使用本产品按照底胶、彩胶、封层胶的操作顺序，并保证固化时间，于正常甲面的保持时间均在1个月以上，并保持持久的色彩和闪亮的光泽。
本发明的LED光效凝胶，操作便捷，易刷涂、着色力强，可形成各种颜色和效果的涂层，固化后，光亮度高，保持时间久，不易剥落缺损。如需清除时，用卸甲液加清洁棉包覆10分钟，即可方便地卸除。
本发明中的实施例仅用于对本发明进行说明，并不构成对权利要求范围的限制，本领域内技术人员可以想到的其他实质上等同的替代，均在本发明保护范围内。
Claims (12)
1.光效凝胶，其特征在于，按照重量份数包括以下组分：
2.根据权利要求1所述的光效凝胶，其特征在于，还包括色浆2-20重量份。
3.根据权利要求1所述的光效凝胶，其特征在于，还包括珠光剂0.1-5重量份。
4.根据权利要求1所述的光效凝胶，其特征在于，所述助剂包括防沉剂0.05-3重量份。
5.根据权利要求1所述的光效凝胶，其特征在于，所述助剂包括流平剂0.05-2重量份。
6.根据权利要求1所述的光效凝胶，其特征在于，所述助剂包括润湿剂0.05-2重量份。
7.根据权利要求1所述的光效凝胶，其特征在于，还包括香精0.02-0.5重量份。
8.根据权利要求1所述的光效凝胶，其特征在于，所述的光引发剂选自光引发剂1173、光引发剂184、光引发剂907、MBF、光引发剂651、光引发剂369、TPO-L、TPO、光引发剂819和BP中的一种或几种。
9.根据权利要求1所述的光效凝胶，其特征在于，所述丙烯酸单体选自丙烯酸月桂酯、丙烯酸异辛酯、丙烯酸丁酯、丙烯酸-2-乙基己酯、甲基丙烯酸-2-羟基乙酯（HEMA）、甲基丙烯酸-2-羟基丙酯、甲基丙烯酸甲酯、甲基丙烯酸丁酯、甲基丙烯酸异丁酯、丙烯酸异冰片酯、甲基丙烯酸异冰片酯、1,3-丁二醇二丙烯酸酯、新戊二醇二丙烯酸酯、（2）丙氧化新戊二醇二丙烯酸酯、聚乙二醇二甲基丙烯酸酯、氧化二缩三乙二醇二甲基丙烯酸酯、二缩三丙二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯、季戊四醇三丙烯酸酯及（3）丙氧基化三羟甲基丙烷三丙烯酸酯一种或几种。
10.根据权利要求1所述的光效凝胶，其特征在于，所述丙烯酸聚合物为脂肪族聚氨酯丙烯酸酯聚合物及脂肪族聚氨酯甲基丙烯酸酯聚合物中的一种或几种。
11.LED光效凝胶，其特征在于，包括权利要求1-10任一权利要求所述的光效凝胶。
12.LED光效指甲油，其特征在于，包括权利要求1-10任一权利要求所述的光效凝胶。