CN102766381B - 高固体份深黄抗变色工程机械专用装饰面漆及其制备方法 - Google Patents
高固体份深黄抗变色工程机械专用装饰面漆及其制备方法 Download PDFInfo
- Publication number
- CN102766381B CN102766381B CN201210280800.4A CN201210280800A CN102766381B CN 102766381 B CN102766381 B CN 102766381B CN 201210280800 A CN201210280800 A CN 201210280800A CN 102766381 B CN102766381 B CN 102766381B
- Authority
- CN
- China
- Prior art keywords
- yellow
- finish paint
- engineering machinery
- add
- barium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
高固体份深黄抗变色工程机械专用装饰面漆由以下重量百分比原料制成:深铬黄30-32%,纳米硫酸钡0.8-1%,70%丙烯酸树脂57-61.6%,紫外线吸收剂0.1-0.2%,位阻胺抗氧剂0.5-0.8%,钡镉锌复合稳定剂1-1.5%,亚磷酸三苯酯1-1.5%,稀释剂4-5%,分散剂0.5%,成膜助剂0.5%。将上述物质通过搅拌、分散等工艺之后,当粘度达标准,再过滤包装。本发明具有如下优点:本产品采用热塑性丙烯酸树脂挥发干燥成膜技术,并采用紫外线吸收剂、位阻胺抗氧剂,配以涂料行业首次发明使用钡镉锌复合稳定剂、亚磷酸三苯酯抗氧剂;同时加入一定量的纳米硫酸钡,很好地解决了深黄等鲜艳色在室外使用时,易变色,存在老化性能等问题,同时也大幅降低了成本。
Description
技术领域
本发明涉及一种高固体份深黄抗变色工程机械专用装饰面漆及其制备方法,属于高分子材料化工领域。
背景技术
目前,工程机械塔机均使用深黄丙烯酸面漆,这种涂料优点:鲜艳、光亮。缺点是:不耐老化,半个月就出现变色,三个月就开始失光,十个月开始粉化,这样大型塔机维修十分困难。不同地区,效果也不同,特别是高温高湿地区,空气质量不好,含有SO2、CO2等,在下雨季度,变色、失光速度更快,这是酸雨造成的问题;不同季度也不同,特别是夏天,高温暴晒,变色失光也在加快。对于这些情况,亟待有一种新的涂料出现,解决上述变色、失光、粉化等问题。
发明内容
针对上述问题,本发明的目的是提供一种高固体份深黄抗变色工程机械专用装饰面漆及其制备方法,解决目前工程机械装饰涂料容易变色、失光、粉化和不耐久等问题。
本发明所述的一种高固体份深黄抗变色工程机械专用装饰面漆由以下重量百分比的原料制成:深铬黄30-32%,纳米硫酸钡0.8-1%,70%丙烯酸树脂57-61.6%,紫外线吸收剂0.1-0.2%,位阻胺抗氧剂0.5-0.8%,钡镉锌复合稳定剂1-1.5%,亚磷酸三苯酯1-1.5%,稀释剂4-5%,分散剂0.5%,成膜助剂0.5%。
本发明所述的一种高固体份深黄抗变色工程机械专用装饰面漆的制备方法包括如下步骤:
(1)、按原料重量百分比,称取稀释剂加入搅拌桶,在高速搅拌情况下,加入纳米硫酸钡,搅拌10-20分钟,使其成胶状,再逐步加入紫外线吸收剂、钡镉锌复合稳定剂、位阻胺抗氧剂、亚磷酸三苯酯,搅拌均匀后,储存备用;
(2)、按原料重量百分比,将成膜物质70%丙烯酸树脂加入配料桶,在搅拌情况下,加入深铬黄,分散剂,搅拌均匀透心后,出料,经磨砂机分散至刮板细度计达到10μm后,进入调浆桶;
(3)、对上述步骤(2)中调浆桶内的色浆进行高速搅拌的情况下,将步骤(1)中储存备用的纳米硫酸钡等浆料加入到步骤(2)中的调浆桶内,然后按原料重量百分比再向调浆桶内逐步加入成膜助剂、稀释剂,搅拌均匀后,取样用涂4#检验杯检测,当粘度达到160秒后,过滤包装。
本发明具有如下优点:本发明公开了高固体份深黄抗变色高档工程机械专用装饰面漆技术,采用热塑性丙烯酸树脂挥发干燥成膜技术,并采用紫外线吸收剂、位阻胺抗氧剂,配以涂料行业首次发明使用钡镉锌复合稳定剂、亚磷酸三苯酯抗氧剂;同时加入一定量的纳米硫酸钡利用其体积大,稳定和吸附性。采取以上措施,很好地解决了深黄等鲜艳色在室外使用时,易变色,存在老化性能等问题,同时也大幅降低了成本。还给涂膜带来了优异性能,如:附着力增强,涂层之间结合力加强等机械性能,涂料具有一定的触变性,使涂料储存时不会沉底,施工时不流挂,特别是为高固体份涂料,有机溶剂含量相对减少,节约了能源,符合国家的产业政策,深受客户欢迎。
附图说明
图1为本发明的工艺流程图。
具体实施方式
下面的实施例可更详细地说明本发明,但不以任何形式限制本发明。
实施例1:(1)、按原料重量百分比:深铬黄30-32%,纳米硫酸钡0.8-1%,70%丙烯酸树脂57-61.6%,紫外线吸收剂0.1-0.2%,位阻胺抗氧剂0.5-0.8%,钡镉锌复合稳定剂1-1.5%,亚磷酸三苯酯1-1.5%,稀释剂4-5%,分散剂0.5%,成膜助剂0.5%;称取稀释剂加入搅拌桶,在高速搅拌情况下,加入纳米硫酸钡,搅拌10-20分钟,使其成胶状,再逐步加入紫外线吸收剂,钡镉锌复合稳定剂、位阻胺抗氧剂、亚磷酸三苯酯,搅拌均匀后,储存备用;
(2)、按原料重量百分比,将成膜物质70%丙烯酸树脂加入配料桶,在搅拌情况下,加入深铬黄,分散剂,搅拌均匀透心后,出料,经磨砂机分散至刮板细度计达到10μm后,进入调浆桶;
(3)、对上述步骤(2)中调浆桶内的色浆进行高速搅拌的情况下,将步骤(1)中储存备用的纳米硫酸钡等浆料加入到步骤(2)中的调浆桶内,然后按原料重量百分比再向调浆桶内逐步加入成膜助剂、稀释剂,搅拌均匀后,取样用涂4#检验杯检测,当粘度达到160秒后,过滤包装。
下表为高固体份深黄抗变色工程机械专用装饰面漆与原有深黄丙烯酸面漆的性能对比:
Claims (2)
1.高固体份深黄抗变色工程机械专用装饰面漆,其特征在于:由以下重量百分比的原料制成:深铬黄30-32%,纳米硫酸钡0.8-1%,70%丙烯酸树脂57-61.6%,紫外线吸收剂0.1-0.2%,位阻胺抗氧剂0.5-0.8%,钡镉锌复合稳定剂1-1.5%,亚磷酸三苯酯1-1.5%,稀释剂4-5%,分散剂0.5%,成膜助剂0.5%。
2.制备权利要求1所述的高固体份深黄抗变色工程机械专用装饰面漆,包括如下步骤:
(1)、按原料重量百分比,称取稀释剂加入搅拌桶,在高速搅拌情况下,加入纳米硫酸钡,搅拌10-20分钟,使其成胶状,再逐步加入紫外线吸收剂、钡镉锌复合稳定剂、位阻胺抗氧剂、亚磷酸三苯酯,搅拌均匀后,储存备用;
(2)、按原料重量百分比,将成膜物质70%丙烯酸树脂加入配料桶,在搅拌情况下,加入深铬黄,分散剂,搅拌均匀透心后,出料,经磨砂机分散至刮板细度计达到10μm后,进入调浆桶;
(3)、对上述步骤(2)中调浆桶内的色浆进行高速搅拌的情况下,将步骤(1)中储存备用的纳米硫酸钡等浆料加入到步骤(2)中的调浆桶内,然后按原料重量百分比再向调浆桶内逐步加入成膜助剂、稀释剂,搅拌均匀后,取样用涂4#检验杯检测,当粘度达到160秒后,过滤包装。