CN102765882A

CN102765882A - Milk white glass wine bottle

Info

Publication number: CN102765882A
Application number: CN2012102897718A
Authority: CN
Inventors: 黄炳炼
Original assignee: Individual
Current assignee: Individual
Priority date: 2012-08-15
Filing date: 2012-08-15
Publication date: 2012-11-07

Abstract

The invention relates to glass ware, in particular to a milk white glass wine bottle which is formed by components including aluminum oxide, quartz sand, feldspar powder, calcite, sodium fluosilicate, industrial sodium carbonate, zinc oxide and the like. Compared with the prior art, the milk white glass wine bottle has the advantages of being high in bottle opening size accuracy, smooth in surface and strong in bottle body density structure and anti-collision strength. Therefore, the milk white glass wine bottle better prevents wine leakage at a bottle opening, wine seepage at a bottle body, bottle oxidizing and wine volatilization, greatly satisfies reliability and safety of long-distance transportation, and greatly reduces broken percentage in the disassembly process to some extent. The wine bottle belongs to environment-friendly products, broken glass can be processed for secondary molding, and characteristics of the glass wine bottle are not changed. The milk white glass wine bottle greatly reduces waste of social resources and has no pollution to environment and social life.

Description

A kind of opal glass bottle

Technical field

The present invention relates to glassware, particularly a kind of opal glass bottle.

Background technology

Liquor enterprise uses special-purpose bottle and one way bottle one after another for improving product specification in recent years, and general returnable bottle is eliminated day by day, and this has very positive pushing effect for the increase that promotes the White Spirit Bottle demand.Liquor especially needs standing storage after the Maotai-flavor liquor production; Because the market demand of high-grade liquor enlarges day by day, need transport for long-distance to product simultaneously, these have all had higher requirement to the stopping property of liquor bottle, photophobism, crash-worthiness etc.Existing liquor bottle exists that stopping property is poor, photophobism is bad, insufficient strength, be easy to generate shortcomings such as seepage, breakage.

Summary of the invention

The object of the present invention is to provide a kind of appearance looks elegant, opal glass bottle that intensity is high.

The objective of the invention is to realize through following approach: a kind of opal glass bottle, by weight percentage, its component is respectively: aluminum oxide 0.1%-1.0%; Silica sand 24.9%-36.9%, Feldspar Powder 32.3%-41.3%, calcite 0.4%-6.4%; Sodium Silicofluoride 98min 6.8%-15.8%, calcined soda for industry 6.8%-15.8%, zinc oxide 0.3%-3.4%; Glass fining agent 0.1%-1.0%, SODIUMNITRATE 0.3%-3.4%, selenium powder 0.001%-0.009%.

As the most preferred embodiment of this programme, by weight percentage, its component is respectively: aluminum oxide 0.602%, silica sand 33.9%; Feldspar Powder 35.3%, calcite 2.4%, Sodium Silicofluoride 98min 11.8%, calcined soda for industry 11.8%; Zinc oxide 1.8%, glass fining agent 0.59%, SODIUMNITRATE 1.8%, selenium powder 0.008%.

A kind of opal glass bottle of the present invention compared with prior art; Its bottle has mouth sizes precision height, smooth surface, bottle density structure and the anti-bigger characteristics of intensity of bumping; Thereby can prevent the volatilization that bottleneck leakage wine, body ooze wine, bottle oxidation and wine better; Also satisfy the reliability and security of long-distance transport greatly, reduced the breakage rate in the cargo handling process to a certain extent biglyyer.This bottle belongs to environmentfriendly products, its broken glass can post forming processing, and the characteristic of vial do not have a bit change, significantly reduced the waste to social resources, not to polluting in environment, the social life yet.

Embodiment

A kind of opal glass bottle of the present invention, its compositions in weight percentage: aluminum oxide 0.602%, silica sand 33.9%, Feldspar Powder 35.3%; Calcite 2.4%, Sodium Silicofluoride 98min 11.8%, calcined soda for industry 11.8%; Zinc oxide 1.8%, glass fining agent 0.59%, SODIUMNITRATE 1.8%; Selenium powder 0.008% becomes glass metal through the above high temperature melting of tank furnace 1500 degree, again through mould molding.

The raw material that is adopted has following characteristic:

Aluminum oxide: increase product strength, impact resistance;

Silica sand: bottle skeleton material increases product strength, color whiteness;

Feldspar Powder: bottle skeleton material increases product strength, color whiteness;

Calcite: bottle skeleton material increases product strength;

Sodium Silicofluoride 98min: tinting material (making the glass appearance color is oyster white);

Calcined soda for industry: fusing effect;

Zinc oxide: increase product antiseep property and intensity;

Glass fining agent: increase product surface smooth finish;

SODIUMNITRATE: fusing effect;

Selenium powder: increase product surface color uniformity and clarity.

At high temperature; The fusion under the effect of other auxiliary material of silica sand, three kinds of raw materials of Feldspar Powder calcite has constituted the skeleton of product; The silica sand fusing point is the highest in three kinds of raw materials; Other two kinds of fusing points are low relatively, so the product skeleton has had continuous perfecting process under the reinforced at the same time high temperature action, so the finished product in later stage is better aspect intensity, impact resistance.Calcined soda for industry, two kinds of melt raw materials of SODIUMNITRATE use together, can at high temperature reach best fusing effect, so more can guarantee the quality of later stage finished product to comprehensive, the evenly fusing of different skeleton raw materials.

Claims

1. opal glass bottle, it is characterized in that: by weight percentage, its component is respectively: aluminum oxide 0.1%-1.0%; Silica sand 24.9%-36.9%, Feldspar Powder 32.3%-41.3%, calcite 0.4%-6.4%; Sodium Silicofluoride 98min 6.8%-15.8%, calcined soda for industry 6.8%-15.8%, zinc oxide 0.3%-3.4%; Glass fining agent 0.1%-1.0%, SODIUMNITRATE 0.3%-3.4%, selenium powder 0.001%-0.009%.

2. a kind of opal glass bottle as claimed in claim 1 is characterized in that: by weight percentage, its component is respectively: aluminum oxide 0.602%; Silica sand 33.9%, Feldspar Powder 35.3%, calcite 2.4%; Sodium Silicofluoride 98min 11.8%, calcined soda for industry 11.8%, zinc oxide 1.8%; Glass fining agent 0.59%, SODIUMNITRATE 1.8%, selenium powder 0.008%.