CN102758122A - 轴承座的熔炼工艺 - Google Patents

轴承座的熔炼工艺 Download PDF

Info

Publication number
CN102758122A
CN102758122A CN2011101078512A CN201110107851A CN102758122A CN 102758122 A CN102758122 A CN 102758122A CN 2011101078512 A CN2011101078512 A CN 2011101078512A CN 201110107851 A CN201110107851 A CN 201110107851A CN 102758122 A CN102758122 A CN 102758122A
Authority
CN
China
Prior art keywords
furnace
iron
cupola furnace
pool
cupola
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011101078512A
Other languages
English (en)
Inventor
陆宝庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2011101078512A priority Critical patent/CN102758122A/zh
Publication of CN102758122A publication Critical patent/CN102758122A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种轴承座的熔炼工艺，包括以下步骤：配制塘炉料，塘炉料包括耐火泥、石英砂和水；将塘炉料填进冲天炉中，制成塘炉，并在塘炉上开风眼；将冲天炉中的温度调到高，将塘炉烘干；冲天炉中进行生火，温度升高到900℃；往塘炉中装料，装的料包括：焦炭、新铁、旧铁、废钢、硅、锰、铁；将冲天炉中的温度升高到900-1200℃，对冲天炉中的料进行熔炼；打开冲天炉，放出铁水，并在铁水中加入0.6％-0.75％的铜、0.5％-0.6％的铬、0.4％-0.5％的钼，放出铁水时的温度为1400-1450℃；用吊包将铁水浇入型腔内进行浇铸。本发明具有制造铸型的熔炼工艺简单、熔炼周期短、使用范围广的优点。

Description

轴承座的熔炼工艺
技术领域：
本发明涉及一种轴承座的熔炼工艺。
背景技术：
目前，轴承座的熔炼均是采用水冷铜钳埚真空电弧熔炼纽扣炉进行熔炼的，此炉熔炼过程复杂、需要反复抽真空、反复翻转熔炼，合金元素烧损挥发严重、化学成分变化大且难以控制、熔炼时间长，同时，还存在钨合金电极对合金的污染，合金成分及组织均匀性较低，只能熔炼体积小的金属，使用范围小。
发明内容：
本发明的目的是为了克服以上的不足，提供一种熔炼工艺简单、熔炼周期短、使用范围广的轴承座的熔炼工艺。
本发明的目的通过以下技术方案来实现：一种轴承座的熔炼工艺，包括以下步骤：
A、配制塘炉料，塘炉料包括10-22％的耐火泥、35-45％的石英砂和40-55％的水；
B、将塘炉料填进冲天炉中，制成塘炉，并在塘炉上开风眼；
C、将冲天炉中的温度调到400-600℃，将塘炉烘干；
D、冲天炉中进行生火，温度升高到900℃；
E、往塘炉中装料，装的料包括：5-7％的焦炭、35-42％新铁、15-22％旧铁、35-42％废钢、0.6-0.7％的硅、0.6-0.7％的锰、0.6-0.7％的铁；
F、将冲天炉中的温度升高到900-1200℃，对冲天炉中的料进行熔炼；
G、打开冲天炉，放出铁水，并在铁水中加入0.6％-0.75％的铜、0.5％-0.6％的铬、0.4％-0.5％的钼，放出铁水时的温度为1400-1450℃；
H、用吊包将铁水浇入型腔内进行浇铸。
本发明与现有技术相比具有以下优点：
本发明采用冲天炉进行熔炼，熔炼过程控制方便，产品合格率高，化铁时间和熔炼周期短，生产率高，生产链空间布局紧凑，工艺柔性好，运行成本低，污染物排放少，改善工作环境和生态环境。该熔炼工艺能够保证稳定获得高质量的铁液，产生的铸件组织、性能好、质量波动范围减小、合格率高。可以熔炼各种形状的金属，使用范围较广。
具体实施方式：
为了加深对本发明的理解，下面将结合实施例对本发明作进一步详述，该实施例仅用于解释本发明，并不构成对本发明保护范围的限定。
本发明轴承座的熔炼工艺的一种具体实施方式，包括以下步骤：
A、配制塘炉料，塘炉料包括10-22％的耐火泥、35-45％的石英砂和40-55％的水；
B、将塘炉料填进冲天炉中，制成塘炉，并在塘炉上开风眼；
C、将冲天炉中的温度调到500-700℃，将塘炉烘干；
D、冲天炉中进行生火，温度升高到900℃；
E、往塘炉中装料，装的料包括：5-7％的焦炭、35-42％新铁、15-22％旧铁、35-42％废钢、0.6-0.7％的硅、0.6-0.7％的锰、0.6-0.7％的铁；
F、将冲天炉中的温度升高到900-1200℃，对冲天炉中的料进行熔炼；
G、打开冲天炉，放出铁水，并在铁水中加入0.6％-0.75％的铜、0.5％-0.6％的铬、0.4％-0.5％的钼，放出铁水时的温度为1400-1450℃；
H、用吊包将铁水浇入型腔内进行浇铸。
本发明采用冲天炉进行熔炼，熔炼过程控制方便，产品合格率高，化铁时间和熔炼周期短，生产率高，生产链空间布局紧凑，工艺柔性好，运行成本低，污染物排放少，改善工作环境和生态环境。该熔炼工艺能够保证稳定获得高质量的铁液，产生的铸件组织、性能好、质量波动范围减小、合格率高。可以熔炼各种形状的金属，使用范围较广。

Claims (1)

1.一种轴承座的熔炼工艺，其特征在于：包括以下步骤：
A、配制塘炉料，塘炉料包括10-22％的耐火泥、35-45％的石英砂和40-55％的水；
B、将塘炉料填进冲天炉中，制成塘炉，并在塘炉上开风眼；
C、将冲天炉中的温度调到500-700℃，将塘炉烘干；
D、冲天炉中进行生火，温度升高到900℃；
E、往塘炉中装料，装的料包括：5-7％的焦炭、35-42％的新铁、15-22％的旧铁、35-42％的废钢、0.6-0.7％的硅、0.6-0.7％的锰、0.6-0.7％的铁；
F、将冲天炉中的温度升高到900-1200℃，对冲天炉中的料进行熔炼；
G、打开冲天炉，放出铁水，并在铁水中加入0.6％-0.75％的铜、0.5％-0.6％的铬、0.4％-0.5％的钼，放出铁水时的温度为1400-1450℃；
H、用吊包将铁水浇入型腔内进行浇铸。
CN2011101078512A 2011-04-27 2011-04-27 轴承座的熔炼工艺 Pending CN102758122A (zh)