CN102756600A - Method for producing transferring aluminum plating film for cigarette packaging - Google Patents
Method for producing transferring aluminum plating film for cigarette packaging Download PDFInfo
- Publication number
- CN102756600A CN102756600A CN2012102794181A CN201210279418A CN102756600A CN 102756600 A CN102756600 A CN 102756600A CN 2012102794181 A CN2012102794181 A CN 2012102794181A CN 201210279418 A CN201210279418 A CN 201210279418A CN 102756600 A CN102756600 A CN 102756600A
- Authority
- CN
- China
- Prior art keywords
- transfer
- pet
- transferring
- film
- oven dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for producing a transferring aluminum plating film for cigarette packaging, relates to packaging paper, and particularly belongs to the technical field of cigarette packaging material production. The method includes coating a dilute transferring coating on a polyethylene terephthalate (PET) transferring film, drying the PET transferring film until humidity is not more than 60, forming a PET transferring film with a transferring coating layer, performing a vacuum aluminum plating on the surface of the transferring coating layer of the PET transferring film, sizing, and peeling and removing the PET transferring film. According to the method, the utilized PET transferring film is a film thermostability polyester film and has excellent physical property, chemical property, dimensional stability and recoverability, and manufactured products have good smoothness, high quality and metallic luster of an aluminum foil. The thickness of an aluminum layer of the product is 1/200 of that of the aluminum foil, the product is extremely easy to decompose in natural environment, the environmental protection is facilitated, besides, the product can greatly solve the problem of waste of the aluminum foil during a direct recombination process, and raw materials are saved.
Description
Technical field
The present invention relates to package paper, particularly the production technical field of cigarette packaging material.
Background technology
Existing aluminium-foil paper is to adopt directly compound technology of aluminium foil and body paper, realizes that its used aluminium foil consumption of aluminium-foil paper of this structure is very big, wastes raw material.Especially in the cigarette pack aluminium-foil paper is produced, after abandoning, both can't reclaim, also can't reclaim as stationery as aluminum products, more can't burn fully, environment is caused very big pollution.
Summary of the invention
The present invention seeks to propose a kind of environmental protection that is beneficial to, save the transfer aluminum plated film production method of packing cigarette of materials.
Technical scheme of the present invention is: the transfer coatings that coating is diluted on the PET transfer membrane earlier through drying to humidity≤60, forms the PET transfer membrane with transfer coatings layer; Transfer coatings coating surface at the PET transfer membrane is vacuum aluminum-coated, through typing, peels off then and removes the PET transfer membrane.
The PET transfer membrane that the present invention adopts has another name called film high temperature resistance polyester film, and it has excellent physical property, chemical property and dimensional stability and recuperability, and the product planarization of processing is good, and quality is high, has the metallic luster of aluminium foil.Product aluminum layer thickness of the present invention has only 1/200 of aluminium foil, in natural environment, very easily decomposes, and helps environmental protection.Product can solve in direct recombination process the waste to aluminium foil, conservation preferably.
In addition, the transfer coatings of dilution according to the invention is the ethyl acetate solution that contains transfer coatings.
Transfer coatings according to the invention is mixed by cellulose acetate, ethyl acetate, butanone, propylene glycol monomethyl ether and n-propyl acetate by said transfer coatings and forms; Said cellulose acetate, ethyl acetate, butanone, propylene glycol monomethyl ether and n-propyl acetate account for 15~20%, 20%~30%, 20%~30%, 5%~10% and 10~20% of transfer coatings gross mass respectively.
Said oven dry is 80~135 ℃.
The segmentation oven dry is adopted in said oven dry, oven dry 1.8 seconds in 80 ℃ baking oven respectively successively, oven dry 1.8 seconds in 110 ℃ baking oven, oven dry 1.8 seconds in 135 ℃ baking oven, oven dry 1.8 seconds in 120 ℃ baking oven, oven dry 1.8 seconds in 90 ℃ baking oven.
The present invention adopts different bake out temperatures to carry out the segmented oven dry, can make coating thoroughly dry, is unlikely to occur the false phenomenon of doing, and influences product quality.
Said vacuum aluminum-coated vacuum is 20 * 10-1 handkerchief, and temperature is 1400 ℃ ± 10 ℃.
The specific embodiment
Implement explanation the present invention with concrete production below:
One, coating:
Material: 1., the PET transfer membrane.2., transfer coatings.3., diluent (ethyl acetate)
1, preparation transfer coatings: percentage by weight is following: cellulose acetate 15~20%, ethyl acetate 20%~30%, butanone 20%~30%, propylene glycol monomethyl ether 5%~10% and n-propyl acetate 10~20%.
2, the transfer coatings of preparation dilution: take by weighing ethyl acetate 6kg, transfer coatings 50 kg respectively, both are fully mixed, for use.
3, preparation has the PET transfer membrane of transfer coatings layer: the PET transfer membrane is positioned on the unwinding device; Speed with 100m/min unreels; The transfer coatings of the dilution of coating preparation on the PET transfer membrane; To scribble the oven dry 1.8 seconds in 80 ℃ baking oven successively of PET transfer membrane, oven dry 1.8 seconds in 110 ℃ baking oven, oven dry 1.8 seconds in 135 ℃ baking oven, oven dry 1.8 seconds in 120 ℃ baking oven of coating then, oven dry 1.8 seconds in 90 ℃ baking oven; Form the PET transfer membrane with transfer coatings layer of humidity≤60, for use.
Two, vacuum aluminum-coated:
1, the vacuum with the vacuum storehouse is set at 20 * 10
-1Handkerchief, temperature are set at 1400 ℃ ± 10 ℃.
The PET transfer membrane that 2, will have the transfer coatings layer is sent into the vacuum storehouse with the speed of 400m/min and is aluminized through the retractable winding apparatus.
Three, peel off:
The semi-products of aluminizing are positioned on the unwinding device, carry out peeling off of PET transfer membrane, through two wrap-ups respectively rolling obtain transfer aluminum plated film of packing cigarette and PET transfer membrane.
Four, packing:
After the transfer aluminum plated film of the packing cigarette of rolling cut, check packed.
Claims (6)
1. the transfer aluminum plated film production method of packing cigarette is characterized in that: on the PET transfer membrane, be coated with the transfer coatings of dilution earlier, through drying to humidity≤60, form the PET transfer membrane with transfer coatings layer; Transfer coatings coating surface at the PET transfer membrane is vacuum aluminum-coated, through typing, peels off then and removes the PET transfer membrane.
2. according to the transfer aluminum plated film production method of the said packing cigarette of claim 1, it is characterized in that: the transfer coatings of said dilution is the ethyl acetate solution that contains transfer coatings.
3. according to the transfer aluminum plated film production method of the said packing cigarette of claim 2, it is characterized in that: said transfer coatings is mixed by cellulose acetate, ethyl acetate, butanone, propylene glycol monomethyl ether and n-propyl acetate and forms; Said cellulose acetate, ethyl acetate, butanone, propylene glycol monomethyl ether and n-propyl acetate account for 15~20%, 20%~30%, 20%~30%, 5%~10% and 10~20% of transfer coatings gross mass respectively.
4. according to the transfer aluminum plated film production method of the said packing cigarette of claim 1, it is characterized in that: said oven dry is 80~135 ℃.
5. according to the transfer aluminum plated film production method of the said packing cigarette of claim 4; It is characterized in that: the segmentation oven dry is adopted in said oven dry, oven dry 1.8 seconds in 80 ℃ baking oven respectively successively, oven dry 1.8 seconds in 110 ℃ baking oven, oven dry 1.8 seconds in 135 ℃ baking oven, oven dry 1.8 seconds in 120 ℃ baking oven, oven dry 1.8 seconds in 90 ℃ baking oven.
6. according to the transfer aluminum plated film production method of the said packing cigarette of claim 1, it is characterized in that: said vacuum aluminum-coated vacuum is 20 * 10
-1Handkerchief, temperature are 1400 ℃ ± 10 ℃.