CN102747620A - Dyeing process of bamboo pulp fiber and cotton fiber blended fabric - Google Patents
Dyeing process of bamboo pulp fiber and cotton fiber blended fabric Download PDFInfo
- Publication number
- CN102747620A CN102747620A CN2012102474395A CN201210247439A CN102747620A CN 102747620 A CN102747620 A CN 102747620A CN 2012102474395 A CN2012102474395 A CN 2012102474395A CN 201210247439 A CN201210247439 A CN 201210247439A CN 102747620 A CN102747620 A CN 102747620A
- Authority
- CN
- China
- Prior art keywords
- bamboo pulp
- cotton fiber
- pulp fiber
- dyeing
- woven fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a dyeing process of bamboo pulp fiber and cotton fiber blended fabric and belongs to the technical field of textile dyeing process. The dyeing process of the bamboo pulp fiber and cotton fiber blended fabric includes the steps of padding vat dye suspension, adding a bowed roll above an evenness calender, infrared preheating, hot-air drying, drying, lake cloth pre-drawing, padding vat solution, washing with warm water, oxidizing with hydrogen peroxide, washing with warm water, soaping, washing with hot water, and drying. The bamboo pulp fiber and cotton fiber blended fabric is less prone to color distortion and is anti-wrinkle.
Description
Technical field
The present invention discloses the dyeing of a kind of bamboo pulp fiber and cotton fiber blended yarn woven fabric, belongs to the technical field of weaving face fabric dyeing.
Background technology
Along with the enhancing gradually with environmental consciousness that improves constantly of living standards of the people, the green fiber fabric more and more receives people's welcome.People more and more is paid close attention to the health of self, begins to thirst for back to nature.Because bamboo fibre has excellent physical and mechanical properties, broad-spectrum antiseptic health properties, anti-ultraviolet property and environment-friendly degradable property; Receive people's favor more and more deeply with its household textiles that is raw material is researched and developed; Green product through the exploitation high added value; Be to promote Company products market development ability, enhancing enterprise competitiveness, create the effective way of better economic benefit for enterprise.
Bamboo pulp fiber and cotton fiber belong to cellulose fibre together, and many denominators are arranged, and respectively have superiority again, adopt bamboo pulp and cotton fiber blending, make full use of gloss and drapability that bamboo pulp fiber good luster, characteristic that modulus is little are improved COTTON FABRIC; Utilize the characteristic of its hydroscopic fast-drying, improve the problem of the wet putting difference of COTTON FABRIC; Cotton fiber also can remedy the wet strong not enough shortcoming of bamboo pulp fiber simultaneously.And in actual production,, more groove and internal surface area being arranged because the bamboo pulp fiber structure is evacuated, the hydroxyl of exposure is more than cotton fiber, so chemical activity is bigger than cotton fiber, acid, alkali, oxidant is all compared responsive.Bamboo pulp fiber to the stability of alkali than cotton fiber difference, can violent expanded so that dissolving under the concentrated base effect.Therefore, the present bamboo pulp fiber and the blended yarn woven fabric of cotton fiber are easy to occur aberration on dyeing process.Simultaneously, the blended yarn woven fabric of bamboo pulp fiber and cotton fiber is easy to wrinkling very much.
Summary of the invention
For addressing the above problem, the present invention provides the dyeing of a kind of bamboo pulp fiber and cotton fiber blended yarn woven fabric, and this dyeing is not easy to occur aberration simultaneously can be crease-resistant.
For achieving the above object, the technical scheme that the present invention adopted is:
The dyeing of a kind of bamboo pulp fiber and cotton fiber blended yarn woven fabric comprises the steps:
Pad reducing dye suspended substance → evenness calender top and install roller → infrared preliminary drying → hot blast drying → oven dry → color lake cloth prestretching → pad reducing solution → Warm Wash → hydrogen peroxide oxidation → Warm Wash → soap boiling → hot water wash → oven dry additional.
As the further setting of such scheme, described padding between reducing solution operation and the Warm Wash operation is provided with the decatize operation, and temperature is 98-105 ℃, and the time is 1-2 minute.
The temperature of said hot blast drying operation is 100-105 ℃.
The temperature of said hot water wash operation is 85-90 ℃, and the time is 3-5 minute.
The present invention can promote osmotic effect and surface smoothness because the reducing dye suspended substance does not have substantivity to fiber, reduces white core phenomenon, improves colorfastness, easily aberration before and after the control.In order to reduce wrinkle, to take to install roller additional going out the evenness calender place, and suitably adjust entering cloth rack tension force, measures such as color lake cloth prestretching have been prone to the wrinkle problem thereby solve bamboo/cotton blended fabric.
The specific embodiment
The dyeing of a kind of bamboo pulp fiber of the present invention and cotton fiber blended yarn woven fabric comprises the steps:
Pad reducing dye suspended substance → evenness calender top and install roller → infrared preliminary drying → hot blast drying → oven dry → color lake cloth prestretching → pad reducing solution → decatize → Warm Wash → hydrogen peroxide oxidation → Warm Wash → soap boiling → hot water wash → oven dry additional.
Wherein, the temperature of decatize operation is 98-105 ℃, and the time is 1-2 minute.
The temperature of hot blast drying operation is 100-105 ℃.
The temperature of hot water wash operation is 85-90 ℃, and the time is 3-5 minute.
The foregoing description only is used to the inventive concept of the present invention of explaining, but not to the qualification of rights protection of the present invention, allly utilizes this design that the present invention is carried out the change of unsubstantiality, all should fall into protection scope of the present invention.
Claims (4)
1. the dyeing of bamboo pulp fiber and cotton fiber blended yarn woven fabric is characterized in that comprising the steps:
Pad reducing dye suspended substance → evenness calender top and install roller → infrared preliminary drying → hot blast drying → oven dry → color lake cloth prestretching → pad reducing solution → Warm Wash → hydrogen peroxide oxidation → Warm Wash → soap boiling → hot water wash → oven dry additional.
2. the dyeing of a kind of bamboo pulp fiber as claimed in claim 1 and cotton fiber blended yarn woven fabric is characterized in that: described padding between reducing solution operation and the Warm Wash operation, be provided with the decatize operation, and temperature is 98-105 ℃, and the time is 1-2 minute.
3. the dyeing of a kind of bamboo pulp fiber as claimed in claim 1 and cotton fiber blended yarn woven fabric is characterized in that: the temperature of said hot blast drying operation is 100-105 ℃.
4. the dyeing of a kind of bamboo pulp fiber as claimed in claim 1 and cotton fiber blended yarn woven fabric is characterized in that: the temperature of said hot water wash operation is 85-90 ℃, and the time is 3-5 minute.