CN102746685A - Novel material for decoration of aluminum alloy doors and windows and manufacturing process thereof - Google Patents
Novel material for decoration of aluminum alloy doors and windows and manufacturing process thereof Download PDFInfo
- Publication number
- CN102746685A CN102746685A CN2012102607306A CN201210260730A CN102746685A CN 102746685 A CN102746685 A CN 102746685A CN 2012102607306 A CN2012102607306 A CN 2012102607306A CN 201210260730 A CN201210260730 A CN 201210260730A CN 102746685 A CN102746685 A CN 102746685A
- Authority
- CN
- China
- Prior art keywords
- auxiliary agent
- aluminum alloy
- alloy doors
- windows
- type material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a novel material for decoration of aluminum alloy doors and windows and a manufacturing process of the novel material. The novel material is characterized by being composed of the following raw materials by weight: 30-55% of wood flour, 10-30% of bamboo powder, 30-55% of PVC (polyvinyl chloride) plastic, 3-8% of light calcium carbonate, 0.5-1% of paraffin and 1-3% of an auxiliary agent, wherein the auxiliary agent is composed of the following raw materials by weight: 0.3-1.5% of soybean oil, 0.4-1.6% of ACR processing auxiliary agent, and 0.3-1.5% of flame retardant. The manufacturing process comprises the following steps of: A. mixing the wood flour and bamboo powder according to the ratio, and drying; B. adding the PVC plastic, fine particle calcium carbonate, paraffin and the auxiliary agent according to the ratio, and mixing; C. extruding with an injection-molding machine by a special mold, and cooling and forming with cold water; and D. sawing the formed piece according to the required specification, and sticking a grain film or transfer-printing grains. The novel material integrates the advantages of metal, plastic and wood, is good in heat insulation effect, flame-retardant, vermin-proof, waterproof and moistureproof and does not generate deformation. The novel material is suitable to be matched with various aluminum alloy doors and windows for use, so as to achieve various decorative effects.
Description
Technical field
The present invention relates to a kind of type material and ME thereof, particularly a kind of aluminum alloy doors and windows are decorated with type material and ME thereof.
Background technology
The existing decoration that is used with aluminum alloy doors and windows generally adopts metal, plastics or timber etc. as raw material with material.Adopt metal as raw material fire-retardant, insect protected is arranged, characteristics such as do not absorb water, but heat-proof quality is poor, weight is heavier, cost is higher.Adopt plastics as raw material heat insulation, insect protected is arranged, characteristics such as do not absorb water, but flame retardant properties is poor, is easy to generate distortion, easy ageing.Adopt timber good, the lightweight characteristics of heat-proof quality to be arranged, but flame retardant properties is poor as raw material, suction easily, generation distortion, and can not insect protected.
Summary of the invention
The object of the present invention is to provide a kind of good heat-insulation effect, can fire-retardant, insect protected, the aluminum alloy doors and windows that can not absorb water, produce deformation are decorated with type material and ME thereof.
The object of the invention can reach through following measure: a kind of aluminum alloy doors and windows are decorated and are used type material; It is characterized in that: this type material is made up of following raw materials according, and its weight proportion is: wood powder 30% ~ 55%, bamboo powder 10% ~ 30%, PVC plastics 30% ~ 55%, fine particle calcium carbonate 3% ~ 8%, paraffin 0.5% ~ 1%, auxiliary agent 1% ~ 3%.
A kind of aluminum alloy doors and windows are decorated the ME with type material, and it is characterized in that: this technology may further comprise the steps:
A, with wood powder and bamboo powder proportional mixing, and carry out drying;
B, add PVC plastics, fine particle calcium carbonate, paraffin, auxiliary agent in proportion, mix;
C, push out through particular manufacturing craft, and use the cold water cooling forming with injection moulding machine;
D, the moulding article by required specification sawing, and paste wood grain film or transfer wood grain.
The object of the invention can also reach through following measure: wherein the weight proportion of each component is: wood powder 45%, bamboo powder 13%, PVC plastics 35%, fine particle calcium carbonate 4.2%, paraffin 0.8%, auxiliary agent 2%.Described auxiliary agent is made up of following raw materials according, and its weight proportion is: VT 18 0.3% ~ 1.5%, ACR processing aid 0.4% ~ 1.6%, fire retardant 0.3% ~ 1.5%.Wherein the weight proportion of each component of auxiliary agent is: VT 18 0.7%, ACR processing aid 0.7%, fire retardant 0.6%.Described ACR processing aid is series modified dose an of esters of acrylic acid.
The present invention compares prior art and has following advantage: the advantage of having gathered metal, plastics and timber, good heat-insulation effect, and can be fire-retardant, insect protected can not absorb water and make moist, produces deformation.Be fit to and the supporting use of various aluminum alloy doors and windows, can reach various decorative effects.
Embodiment
The present invention below will combine embodiment to make further detailed description:
Embodiment one
Wood powder with 30% and 10% bamboo powder proportional mixing, and carry out drying; Add 50% PVC plastics (particulate state is pvc material), 8% fine particle calcium carbonate, 0.5% paraffin, 1.5% auxiliary agent, mix; Wherein VT 18 is 0.5% in the auxiliary agent, the ACR processing aid is 0.5%, fire retardant is 0.5%; Utilize said mixture injection moulding machine to pass through particular manufacturing craft (can be designed to the mould of plate shape, bar shaped and different shape as required) extruding and come out, and use the cold water cooling forming; By required specification sawing, and paste the wood grain film to the moulding article or transfer wood grain gets final product.Wherein fire retardant can adopt inorganic combustion inhibitor, halogenated flame retardant, phosphorus flame retardant or nitrogen flame retardant etc.
Embodiment two
Wood powder with 45% and 13% bamboo powder proportional mixing, and carry out drying; Add 35% PVC plastics (particulate state is pvc material), 4.2% fine particle calcium carbonate, 0.8% paraffin, 2% auxiliary agent, mix; Wherein VT 18 is 0.7% in the auxiliary agent, the ACR processing aid is 0.7%, fire retardant is 0.6%; Utilize said mixture injection moulding machine to pass through particular manufacturing craft (can be designed to the mould of plate shape, bar shaped and different shape as required) extruding and come out, and use the cold water cooling forming; By required specification sawing, and paste the wood grain film to the moulding article or transfer wood grain gets final product.
Embodiment three
Wood powder with 40% and 20% bamboo powder proportional mixing, and carry out drying; Add 30% PVC plastics (particulate state is pvc material), 6% fine particle calcium carbonate, 1% paraffin, 3% auxiliary agent, mix; Wherein VT 18 is 1% in the auxiliary agent, the ACR processing aid is 1%, fire retardant is 1%; Utilize said mixture injection moulding machine to pass through particular manufacturing craft (can be designed to the mould of plate shape, bar shaped and different shape as required) extruding and come out, and use the cold water cooling forming; By required specification sawing, and paste the wood grain film to the moulding article or transfer wood grain gets final product.
Claims (6)
1. aluminum alloy doors and windows are decorated and are used type material, and it is characterized in that: this type material is made up of following raw materials according, and its weight proportion is: wood powder 30% ~ 55%, bamboo powder 10% ~ 30%, PVC plastics 30% ~ 55%, fine particle calcium carbonate 3% ~ 8%, paraffin 0.5% ~ 1%, auxiliary agent 1% ~ 3%.
2. a kind of aluminum alloy doors and windows according to claim 1 are decorated and are used type material, and it is characterized in that: described auxiliary agent is made up of following raw materials according, and its weight proportion is: VT 18 0.3% ~ 1.5%, ACR processing aid 0.4% ~ 1.6%, fire retardant 0.3% ~ 1.5%.
3. a kind of aluminum alloy doors and windows according to claim 1 are decorated and are used type material, and it is characterized in that: wherein the weight proportion of each component is: wood powder 45%, bamboo powder 13%, PVC plastics 35%, fine particle calcium carbonate 4.2%, paraffin 0.8%, auxiliary agent 2%.
4. a kind of aluminum alloy doors and windows according to claim 2 are decorated and are used type material, and it is characterized in that: wherein the weight proportion of each component of auxiliary agent is: VT 18 0.7%, ACR processing aid 0.7%, fire retardant 0.6%.
5. a kind of aluminum alloy doors and windows according to claim 2 are decorated and are used type material, and it is characterized in that: described ACR processing aid is series modified dose an of esters of acrylic acid.
6. aluminum alloy doors and windows are decorated the ME with type material, and it is characterized in that: this technology may further comprise the steps:
A, with wood powder and bamboo powder proportional mixing, and carry out drying;
B, add PVC plastics, fine particle calcium carbonate, paraffin, auxiliary agent in proportion, mix;
C, push out through particular manufacturing craft, and use the cold water cooling forming with injection moulding machine;
D, the moulding article by required specification sawing, and paste wood grain film or transfer wood grain.