CN102746565B - 一种耐热电缆护套料及其制备方法 - Google Patents

一种耐热电缆护套料及其制备方法 Download PDF

Info

Publication number
CN102746565B
CN102746565B CN201210185802.5A CN201210185802A CN102746565B CN 102746565 B CN102746565 B CN 102746565B CN 201210185802 A CN201210185802 A CN 201210185802A CN 102746565 B CN102746565 B CN 102746565B
Authority
CN
China
Prior art keywords
sheath material
cable sheath
compound
cross
softening agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210185802.5A
Other languages
English (en)
Other versions
CN102746565A (zh
Inventor
何忠胜
高世宏
闻广圈
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI SHENGHUA CABLE GROUP Co Ltd
Original Assignee
ANHUI SHENGHUA CABLE GROUP Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SHENGHUA CABLE GROUP Co Ltd filed Critical ANHUI SHENGHUA CABLE GROUP Co Ltd
Priority to CN201210185802.5A priority Critical patent/CN102746565B/zh
Publication of CN102746565A publication Critical patent/CN102746565A/zh
Application granted granted Critical
Publication of CN102746565B publication Critical patent/CN102746565B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种耐热电缆护套料及其制备方法，该绝缘护套料包括以下组分及含量：乙烯丙烯酸酯55-65份、聚烯烃弹性体POE？8480/美国杜邦35-45份、增塑剂3-8份、氢氧化铝50-60份、改性石蜡10-15份、抗氧剂1010？1.5-3份、辐照交联剂1-3份、ECHO.A噻二唑衍生物1-8份。本发明采用了先进的共聚改性和并用技术以及合理的配方结构，解决了目前市场该类材料不能满足在高温强磁的环境下工作使用现状，具有耐热抗磁的特性，以及具有良好的耐磨、耐油、绝缘电气、物理机械以及柔软的特性。

Description

一种耐热电缆护套料及其制备方法
技术领域
本发明涉及一种耐热电缆护套料及其制备方法，属于电缆制造领域。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，随着电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视；电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失，同时随着通讯事业、汽车工业和计算机工业的发展，特别是航空导线、汽车用线、高温仪表电缆、石油钻井平台电缆等许多场合，越来越需要使用耐高温、耐气候的耐热电缆护套料。
发明内容
本发明的目的是在于克服上述已有技术的不足，提供一种耐热电缆护套料及其制备方法。
为了实现上述目的本发明采用如下技术方案：
耐热电缆护套料，各原料组分的重量份为：
乙烯丙烯酸酯55-65份
聚烯烃弹性体POE8480/美国杜邦35-45份
增塑剂3-8份
氢氧化铝50-60份
改性石蜡10-15份
抗氧剂10101.5-3份
辐照交联剂1-3份
ECHO.A噻二唑衍生物1-3份。
所述的乙烯丙烯酸酯选用乙烯、甲基丙烯酸酯共聚物，所述的辐照交联剂采用六亚甲基二胺氨基甲酸盐和二邻甲苯胍并用，并用比例为1:2。
所述的增塑剂由柠檬酸三丁酯10-15、正丁醇3-5、聚乙二醇5-10、氯化石蜡20-25、纳米TiO20.2-0.5、纳米氧化钡0.2-0.5、环氧化甘油三酸酯10-15和磷酸三甲苯10-15混合制备而成。
耐热电缆护套料的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，将乙烯丙烯酸酯和聚烯烃弹性体POE8480/美国杜邦混合均匀，得到混合料A；
（2）在上述步骤（1）中的混合料A中按重量份加入增塑剂、氢氧化铝、改性石蜡、抗氧剂1010、辐照交联剂、ECHO.A噻二唑衍生物，常温下低速搅拌1-2分钟，使得混合均匀，得到混合料B；
（3）将上述步骤（2）得到的混合料B加入开炼机和密炼机或双螺杆挤出机混炼，接着进行高能辐射，在功率与能量分别为10KW、10Mev电子束下辐照交联，辐照剂量为170-250Gy，挤出造料，控制温度140-150℃，得到成品。
本发明的优点：
本发明由于采用乙烯丙烯酸酯和聚烯烃弹性体POE8480/美国杜邦高分子材料并用作为本发明的基础材料，该基础材料分子结构主要是碳氢化合物组成，解决了目前市场该类材料不能满足在高温强磁的环境下工作使用现状，具有耐热抗磁的特性，以及具有良好的耐磨、耐油、绝缘电气、物理机械以及柔软的特性。
具体实施方式
实施例1：
耐热电缆护套料，各原料组分的重量份为：
乙烯丙烯酸酯60份
聚烯烃弹性体POE8480/美国杜邦45份
增塑剂3-8份
氢氧化铝55份
改性石蜡13份
抗氧剂10101.9份
辐照交联剂3份
ECHO.A噻二唑衍生物1份
所述的乙烯丙烯酸酯选用乙烯、甲基丙烯酸酯共聚物，所述的辐照交联剂采用六亚甲基二胺氨基甲酸盐和二邻甲苯胍并用，并用比例为1:2。
所述的增塑剂由柠檬酸三丁酯10-15、正丁醇3-5、聚乙二醇5-10、氯化石蜡20-25、纳米TiO20.2-0.5、纳米氧化钡0.2-0.5、环氧化甘油三酸酯10-15和磷酸三甲苯10-15混合制备而成。
耐热电缆护套料的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，将乙烯丙烯酸酯和聚烯烃弹性体POE8480/美国杜邦混合均匀，得到混合料A；
（2）在上述步骤（1）中的混合料A中按重量份加入增塑剂、氢氧化铝、改性石蜡、抗氧剂1010、辐照交联剂、ECHO.A噻二唑衍生物，常温下低速搅拌1-2分钟，使得混合均匀，得到混合料B；
（3）将上述步骤（2）得到的混合料B加入开炼机和密炼机或双螺杆挤出机混炼，接着进行高能辐射，在功率与能量分别为10KW、10Mev电子束下辐照交联，辐照剂量为170-250Gy，挤出造料，控制温度140-150℃，得到成品。
本发明的电缆护套料与现有的电缆护套料一般性能比较
项 目 单 位 现有电缆料 本发明电缆料
原始断裂强度 MPa 不小于 5.00 11.50
原始断裂伸长率 % 不小于 250 430
耐158℃×168h老化后 ---- ---- -----
K1 % 不小于 碳化 125
K2 % 不小于 碳化 95
K1 % 不小于 90 110
K2 % 不小于 60 77
绝缘电阻 欧姆·厘米≥ 1015 1017

Claims (1)

1.一种耐热电缆护套料，其特征在于各原料组分的重量份为：
乙烯丙烯酸酯55-65份
聚烯烃弹性体POE8480/美国杜邦35-45份
增塑剂3-8份
氢氧化铝50-60份
改性石蜡10-15份
抗氧剂10101.5-3份
辐照交联剂1-3份
ECHO.A噻二唑衍生物1-3份；
所述的增塑剂由柠檬酸三丁酯10-15、正丁醇3-5、聚乙二醇5-10、氯化石蜡20-25、纳米TiO20.2-0.5、纳米氧化钡0.2-0.5、环氧化甘油三酸酯10-15和磷酸三甲苯10-15混合制备而成；
所述的耐热电缆护套料的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，将乙烯丙烯酸酯和聚烯烃弹性体POE8480/美国杜邦混合均匀，得到混合料A；
（2）在上述步骤（1）中的混合料A中按重量份加入增塑剂、氢氧化铝、改性石蜡、抗氧剂1010、辐照交联剂、ECHO.A噻二唑衍生物，常温下低速搅拌1-2分钟，使得混合均匀，得到混合料B；
（3）将上述步骤（2）得到的混合料B加入开炼机和密炼机或双螺杆挤出机混炼，接着进行高能辐射，在功率与能量分别为10KW、10Mev电子束下辐照交联，辐照剂量为170-250Gy，挤出造料，控制温度140-150℃，得到成品。
CN201210185802.5A 2012-06-07 2012-06-07 一种耐热电缆护套料及其制备方法 Expired - Fee Related CN102746565B (zh)