CN102743299A - Concentrated liquid essence for liquid plastic and preparation method thereof - Google Patents
Concentrated liquid essence for liquid plastic and preparation method thereof Download PDFInfo
- Publication number
- CN102743299A CN102743299A CN2012102641665A CN201210264166A CN102743299A CN 102743299 A CN102743299 A CN 102743299A CN 2012102641665 A CN2012102641665 A CN 2012102641665A CN 201210264166 A CN201210264166 A CN 201210264166A CN 102743299 A CN102743299 A CN 102743299A
- Authority
- CN
- China
- Prior art keywords
- parts
- liquid
- carbonate
- organic
- sodium bicarbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides concentrated liquid essence for liquid plastic and a preparation method of the concentrated liquid essence. The concentrated liquid essence comprises the following components by weight: 1-3 parts of sodium bicarbonate, 0.5-2 parts of strontium carbonate, 1-3 parts of potassium carbonate, 10-20 parts of organic germanium, 1-3 parts of ferrous sulfate, 0.5-2 parts of calcium carbonate, 10-20 parts of organic selenium and 30-50 parts of deionized water. The concentrated liquid essence is prepared by the steps of mixing and dissolving the components. The concentrated liquid essence for liquid plastic comprises various mineral substances which are reasonably proportioned, and has multiple functions of thinning face, lifting skin, removing wrinkles and spots, whitening skin and the like, is quick-acting and achieves a reshaping effect without operation or injection; moreover, the concentrated liquid essence for liquid plastic is safe in component formula and edible. The preparation method of the concentrated liquid essence for liquid plastic is simple and meets the demand of large-scale industrial production.
Description
Technical field
The present invention relates to a kind of cosmetics and preparation method thereof, especially a kind of liquid shaping is with concentrated essence liquid and preparation method thereof.
Background technology
That according to investigations, accepted cosmetic surgery among the Korea S women accounts for 15%; Because of a part defectiveness, through having accounted for about 70% of plastic operation adjustment.Reach 600,000,000 in Chinese women number ratio, the vast market more than Korea S will be arranged.
For traditional plastic operation or injection shaping, if success, will become more beautiful; But its risk is also quite high, the problem that possibly occur mainly contain following some: first; The cicatrix problem: this is modal problem; If the doctor is when the design operation plan, the position of otch does not design, and cicatrix clearly will appear in postoperative; The second, the shaping failure: because cosmetic surgery hospital's technical equipment is outmoded, doctors experience is not enough, causes the situation of failure probably, make people more ugly after surgery, even some people gets killed in operating-table; The 3rd, injured nerve: all there is neural the distribution at each position of human body, in the process of carrying out plastic operation, can damage to some extent it unavoidably, if but damage excessively, will cause the situation of local paralysis; The 4th, rubbish in the body: injection beauty treatment nowadays is popular, if but quality of materials is bad, will remain among the human body, and cause the interior rubbish of body seriously to pile up, more the health of human body in serious harm.Compare beauty and shaping technology such as operating shaping, injection shaping, liquid shaping becomes the optimum selection of shaping and beauty gradually because of its safety, devoid of risk, cost performance height.
Liquid shaping is that high-tech quantum technology, far infrared are technological, the application of liquidization of mineral technology in beauty treatment; Be a kind of beauty treatment mode of extremely simple fashion, it is simple, convenient, light, and the effect that is reached can compare favourably with the shaping and beauty of operation formula; Its percutaneous absorbability is very high; Moment will penetrate epidermis, corium and subcutaneous tissue 30-50mm, and the mineral that contains plurality of active ingredients is absorbed by the body very soon, reaches beautifying and anti-aging, reverses the purpose in age 5-10 year; Therefore be referred to as liquid shaping, be described as beauty treatment gold.Compare operating shaping, these technology of injection shaping, liquid shaping more easily, more natural, fashion more, really make from inside to outside healthy beautiful, started a world that does not have wrinkle and do not have flaw.Liquid shaping is because safe and reliable non-operation; Thin face, the miraculous effects of drawing skin, wrinkle removal, light speckles, beautification and white etc. to get instant result; Accepted by more and more people that like to be beautiful; The key technology of liquid shaping then is the use of concentrated essence liquid, and its result of use difference of different concentrated essence liquids is very big, seek a kind ofly be widely used, the obvious results concentrated essence liquid will have very huge market prospect.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of liquid shaping to use concentrated essence liquid.
Another technical problem to be solved by this invention is to provide the method for preparing of above-mentioned liquid shaping with concentrated essence liquid.
For solving the problems of the technologies described above, technical scheme of the present invention is:
Concentrated essence liquid is used in a kind of liquid shaping; Form by sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium and deionized water, by its parts by weight sodium bicarbonate 1-3 part, strontium carbonate 0.5-2 part, potassium carbonate 1-3 part, organic germanium 10-20 part, ferrous sulfate 1-3 part, calcium carbonate 0.5-2 part, organic selenium 10-20 part, deionized water 30-50 part.
Preferably; Concentrated essence liquid is used in above-mentioned liquid shaping, by its parts by weight sodium bicarbonate 1.5-2 part, strontium carbonate 1.5-2 part, potassium carbonate 1.5-2.5 part, organic germanium 15-18 part, ferrous sulfate 1.5-2 part, calcium carbonate 1.5-2 part, organic selenium 13-17 part, deionized water 35-45 part.
Preferably, concentrated essence liquid is used in above-mentioned liquid shaping, by 1.5 parts of its parts by weight sodium bicarbonate, 1.5 parts of strontium carbonates, 2 parts of potassium carbonate, 15 parts of organic germaniums, 1.5 parts in ferrous sulfate, 1.5 parts of calcium carbonate, 15 parts of organic seleniums, 40 parts of deionized waters.
Above-mentioned liquid shaping is with the method for preparing of concentrated essence liquid, and concrete preparation process is following:
(1) taking by weighing sodium bicarbonate 1-3 part, strontium carbonate 0.5-2 part, potassium carbonate 1-3 part, organic germanium 10-20 part, ferrous sulfate 1-3 part, calcium carbonate 0.5-2 part, organic selenium 10-20 part, deionized water 30-50 part by above-mentioned parts by weight is raw material;
(2) in the rustless steel sealed shell of tank with sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium, mix and stir, add deionized water dissolving;
(3) continue heated and stirred to fully dissolving under 50-60 ℃ of condition, room temperature was placed 3-6 hour, got its supernatant and promptly got.
Preferably, above-mentioned liquid shaping is with the method for preparing of concentrated essence liquid, and reaction temperature is 55 ℃ in the said step (3), and room temperature was placed 4 hours.
Preferably, above-mentioned liquid shaping with diluting in step (3) the gained supernatant adding pure water, makes spray in the spray bottle of packing into the method for preparing of concentrated essence liquid, and wherein the volume ratio of supernatant and pure water is 1:30.
Preferably, above-mentioned liquid shaping is with the method for preparing of concentrated essence liquid, and the gained concentrated essence liquid is a colourless transparent liquid, slight abnormal smells from the patient, and PH 13, no viscosity, 150 ℃ of boiling points, node-10 ℃.
The usage that concentrated essence liquid is used in above-mentioned liquid shaping is as evenly smearing or be sprayed on face with said concentrated essence liquid each 1-2 time every day sooner or later, each 3 times, whenever after dried naturally, repeats to smear or spray again.
The invention has the beneficial effects as follows:
Concentrated essence liquid is used in above-mentioned liquid shaping, with various mineral reasonable formula, has thin face, draws skin, multiple effect such as wrinkle removal, light speckles, beautification and white; And instant effect; Realized not operating on, do not performed the operation, not having an injection just to reach the purpose of shaping effect, and prescription safety, edible; Its preparation method is simple, is fit to requirements of large-scale industrial production.
Description of drawings
Fig. 1 is experimenter's scar removal design sketch,
Before wherein Figure 1A is to use concentrated essence liquid, after Figure 1B is to use concentrated essence liquid;
Fig. 2 is that experimenter's muscle tightens up, the cheek proud flesh is eliminated design sketch,
Before wherein Fig. 2 A is to use concentrated essence liquid, after Fig. 2 B is to use concentrated essence liquid;
Fig. 3 is that experimenter's eye pouch is eliminated, upward palpebra inferior tightens up design sketch,
Before wherein Fig. 3 A is to use concentrated essence liquid, after Fig. 3 B is to use concentrated essence liquid;
Fig. 4 is that experimenter's pore shrinks, skin elasticity is improved design sketch,
Before wherein Fig. 4 A is to use concentrated essence liquid, after Fig. 4 B is to use concentrated essence liquid;
Fig. 5 is that the false wrinkle of experimenter reduces, true property wrinkle reduces design sketch,
Before wherein Fig. 5 A is to use concentrated essence liquid, after Fig. 5 B is to use concentrated essence liquid.
The specific embodiment
Below in conjunction with specific embodiment technical scheme according to the invention is further described.
Embodiment 1
Concentrated essence liquid is used in a kind of liquid shaping; Form by sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium and deionized water, wherein sodium bicarbonate 1.5kg, strontium carbonate 1.5kg, potassium carbonate 2kg, organic germanium 15kg, ferrous sulfate 1.5kg, calcium carbonate 1.5kg, organic selenium 15kg, deionized water 40kg.
Above-mentioned liquid shaping is with the method for preparing of concentrated essence liquid, and concrete preparation process is following:
(1) taking by weighing sodium bicarbonate 1.5kg, strontium carbonate 1.5kg, potassium carbonate 2kg, organic germanium 15kg, ferrous sulfate 1.5kg, calcium carbonate 1.5kg, organic selenium 15kg, deionized water 40kg is raw material;
(2) in the rustless steel sealed shell of tank with sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium, mix and stir, add deionized water dissolving;
Continue heated and stirred under (3) 55 ℃ of conditions to fully dissolving, room temperature was placed 4 hours, and it is for use to get its supernatant, and this supernatant is a colourless transparent liquid, slight abnormal smells from the patient, and PH 13, no viscosity, 150 ℃ of boiling points, node-10 ℃;
(4) with diluting in step (3) the gained supernatant adding pure water, make spray in the spray bottle of packing into, wherein the volume ratio of supernatant and pure water is 1:30 (supernatant 1ml, pure water 30ml).
Embodiment 2
Concentrated essence liquid is used in a kind of liquid shaping; Form by sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium and deionized water, wherein sodium bicarbonate 2kg, strontium carbonate 1.5kg, potassium carbonate 2.5kg, organic germanium 15kg, ferrous sulfate 1.5kg, calcium carbonate 2kg, organic selenium 17kg, deionized water 35kg.
Above-mentioned liquid shaping is with the method for preparing of concentrated essence liquid, and concrete preparation process is following:
(1) taking by weighing sodium bicarbonate 2kg, strontium carbonate 1.5kg, potassium carbonate 2.5kg, organic germanium 15kg, ferrous sulfate 1.5kg, calcium carbonate 2kg, organic selenium 17kg, deionized water 35kg is raw material;
(2) in the rustless steel sealed shell of tank with sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium, mix and stir, add deionized water dissolving;
Continue heated and stirred under (3) 58 ℃ of conditions to fully dissolving, room temperature was placed 5 hours, got its supernatant and promptly got.
Embodiment 3
Concentrated essence liquid is used in a kind of liquid shaping; Form by sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium and deionized water, wherein sodium bicarbonate 1.5kg, strontium carbonate 2kg, potassium carbonate 1.5kg, organic germanium 18kg, ferrous sulfate 2kg, calcium carbonate 1.5kg, organic selenium 13kg, deionized water 45kg.
Above-mentioned liquid shaping is with the method for preparing of concentrated essence liquid, and concrete preparation process is following:
(1) taking by weighing sodium bicarbonate 1.5kg, strontium carbonate 2kg, potassium carbonate 1.5kg, organic germanium 18kg, ferrous sulfate 2kg, calcium carbonate 1.5kg, organic selenium 13kg, deionized water 45kg is raw material;
(2) in the rustless steel sealed shell of tank with sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium, mix and stir, add deionized water dissolving;
Continue heated and stirred under (3) 53 ℃ of conditions to fully dissolving, room temperature was placed 4 hours, and it is for use to get its supernatant;
(4) with diluting in step (3) the gained supernatant adding pure water, make spray in the spray bottle of packing into, wherein the volume ratio of supernatant and pure water is 1:30 (supernatant 1ml, pure water 30ml).
Embodiment 4
Concentrated essence liquid is used in a kind of liquid shaping; Form by sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium and deionized water, wherein sodium bicarbonate 1kg, strontium carbonate 2kg, potassium carbonate 3kg, organic germanium 20kg, ferrous sulfate 1kg, calcium carbonate 0.5kg, organic selenium 20kg, deionized water 30kg.
Above-mentioned liquid shaping is with the method for preparing of concentrated essence liquid, and concrete preparation process is following:
(1) taking by weighing sodium bicarbonate 1kg, strontium carbonate 2kg, potassium carbonate 3kg, organic germanium 20kg, ferrous sulfate 1kg, calcium carbonate 0.5kg, organic selenium 20kg, deionized water 30kg is raw material;
(2) in the rustless steel sealed shell of tank with sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium, mix and stir, add deionized water dissolving;
Continue heated and stirred under (3) 60 ℃ of conditions to fully dissolving, room temperature was placed 3 hours, got its supernatant and promptly got.
Embodiment 5
Concentrated essence liquid is used in a kind of liquid shaping; Form by sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium and deionized water, wherein sodium bicarbonate 3kg, strontium carbonate 0.5kg, potassium carbonate 1kg, organic germanium 10kg, ferrous sulfate 3kg, calcium carbonate 2kg, organic selenium 10kg, deionized water 50kg.
Above-mentioned liquid shaping is with the method for preparing of concentrated essence liquid, and concrete preparation process is following:
(1) taking by weighing sodium bicarbonate 3kg, strontium carbonate 0.5kg, potassium carbonate 1kg, organic germanium 10kg, ferrous sulfate 3kg, calcium carbonate 2kg, organic selenium 10kg, deionized water 50kg is raw material;
(2) in the rustless steel sealed shell of tank with sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium, mix and stir, add deionized water dissolving;
Continue heated and stirred under (3) 50 ℃ of conditions to fully dissolving, room temperature was placed 6 hours, and it is for use to get its supernatant;
(4) with diluting in step (3) the gained supernatant adding pure water, make spray in the spray bottle of packing into, wherein the volume ratio of supernatant and pure water is 1:30 (supernatant 1ml, pure water 30ml).
Embodiment 6
Concentrated essence liquid is used in a kind of liquid shaping; Form by sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium and deionized water, wherein sodium bicarbonate 1.7kg, strontium carbonate 1.8kg, potassium carbonate 2.2kg, organic germanium 17kg, ferrous sulfate 1.6kg, calcium carbonate 1.6kg, organic selenium 16kg, deionized water 38kg.
Above-mentioned liquid shaping is with the method for preparing of concentrated essence liquid, and concrete preparation process is following:
(1) taking by weighing sodium bicarbonate 1.7kg, strontium carbonate 1.8kg, potassium carbonate 2.2kg, organic germanium 17kg, ferrous sulfate 1.6kg, calcium carbonate 1.6kg, organic selenium 16kg, deionized water 38kg is raw material;
(2) in the rustless steel sealed shell of tank with sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium, mix and stir, add deionized water dissolving;
Continue heated and stirred under (3) 56 ℃ of conditions to fully dissolving, room temperature was placed 5 hours, got its supernatant and promptly got.
Said each component of one of embodiment 1-6 is the commercially available prod, and each amounts of components is increased or reduces according to same ratio, and the parts by weight relation of each component of gained all belongs to protection scope of the present invention.
The composition principle of concentrated essence liquid according to the invention is: the function of each component is as shown in table 1 below in the side:
Table 1
Each component is pressed the special ratios Combination application, and Synergistic can effectively permeate skin corium each other; Promote elastic fiber and the proteinic generation of basement membrane, promote the collagen protein synthesis ability, repair the subcutaneous collagen protein tissue of fracture fast; Improve collagen protein density, make the elastic while of its full recovery, can also subdue various harmful bacterium; Divide toxolysin, problem skins such as comedo, dermatitis are had obvious effects.And can desalinate calm pigment, and whiten and receive the fine, soft fur hole, replenish the required nutrition of skin; Its mineral composition can ultraviolet blocking-up to the injury of skin, prevent because the skin aging that ultraviolet causes.
Concentrated essence liquid according to the invention is through the several mineral materials ionised species that extracts, colourless, tasteless, avirulence, nuisanceless, have no side effect, the outer time spent is passed through skin absorbs; Active cell quickens the generation of new cell, lets the old and feeble quick keratinization of cell come off; And the collagen fiber and the elastic fiber that make the degeneration of rupturing obtain repairing, and skin elasticity is increased, and wrinkle calms down disappearance gradually; The loose skin that compacts is desalinated various speckles simultaneously and is whitened and receive the fine, soft fur hole.
In sum, said concentrated essence liquid comprehensively plays a role through its functions of expelling toxin, supply trophic function, is specially:
Functions of expelling toxin: hoard harmful substance in thing and the cell through removing blood vessel, promote the fully absorption of cell, thereby the recovery damaged cell, promote cell metabolism to nutrient substance;
The supply trophic function: contain multiple mineral and the trace element of keeping cell health, wherein calcium can antiallergic, but selenium can prevent degree of depth skin cares such as skin aging; Smooth away wrinkles; Shape of face is moulded by U.S.A, and dispel eye band, speckle dispelling keep young, pale, the soft gloss of skin;
Thereby, at the wrinkle removal eye pouch of dispelling, promoting facial loose skin, light speckles, beautification and white is received the fine, soft fur hole, and the opposing ultraviolet radiation is removed the skin free radical, modifies face contour and plays a role with many-sides such as repairing allergic skin.
Clinical trial example 1:
As shown in Figure 1, through 20 routine triers are used follow-up observation, remarkably productive, concrete condition is following with the embodiment of the invention 1 said concentrated essence liquid:
1, study subject
20 routine triers, wherein:
Man's 10 examples, 25-35 year 4 examples wherein, 36-50 year 3 examples, 51-70 year 3 examples;
Ms's 10 examples, 25-35 year 5 examples wherein, 36-50 year 4 examples, 51-70 year 1 example.
2, method
All triers use embodiment 1 said concentrated essence liquids each 2 times every day sooner or later, spray 3 times at every turn, evenly are sprayed on the cicatrix place through spray bottle, spray whenever after dried naturally, to spray next time again, reach the purpose of liquid shaping through skin absorbs.Through 120 days on probation after, its result is following:
Cicatrix does not have improver 0%
The slight improver 3% of cicatrix
The obvious improver 97% of cicatrix
Clinical trial example 2:
Like Fig. 2-shown in Figure 5, through 50 routine triers are used follow-up observation, remarkably productive, concrete condition is following with the embodiment of the invention 1 said concentrated essence liquid:
1, study subject
50 routine triers, wherein:
Man's 25 examples, 25-35 year 4 examples wherein, 36-50 year 12 examples, 51-70 year 8 examples, 1 example more than 70 years old;
Ms's 25 examples, 25-35 year 5 examples wherein, 36-50 year 13 examples, 51-70 year 6 examples, 1 example more than 70 years old.
2, method
All triers use embodiment 1 said concentrated essence liquid each 1 time every day sooner or later; Each spray 3 times; Evenly be sprayed on face through spray bottle, spray every time dried naturally back (patting facial) and spray next time again, reach the purpose of liquid shaping through skin absorbs with hands.Through 90 days on probation after, its result is following:
Can find out that through this clinical trial example concentrated essence liquid according to the invention can give to replenish timely and effectively for mineral and multiple beneficial nutrient that human body can't absorb and lacked in the daily life diet.Essence has superpower penetration, and DNA cell activation effect is had outstanding effect.Be sprayed onto skin surface uniformly, repair the subcutaneous collagen protein tissue of fracture with surprising rapidity, raising collagen protein density, the effect that makes it reach full recovery elasticity and reduce wrinkle, compact.Simultaneously all right microcirculation improvement, the harmful bacterium of elimination are divided toxolysin, and problem skins such as comedo are had obvious effects; Desalinate calm pigment, replenish the skin desired nutritional, make the mineral composition go deep into skin; Improve moisture-retaining capacity, the dry generation with the expression stricture of vagina of prevention lets skin indentation pore under moisture state; And thoroughly ultraviolet blocking-up prevents to wear out to the injury of skin, for using lead, hydrargyrum, the impaired skin of hormones functional product to decompose organic toxicity; The subcutaneous cell of activation improves the effect that skin quality, body shaping all over the body reach comprehensive adjustment.
Above-mentioned detailed description of this a kind of liquid shaping being carried out with concentrated essence liquid and preparation method thereof with reference to embodiment; Be illustrative rather than determinate; Can enumerate out several embodiment according to institute's limited range; Therefore in the variation and the modification that do not break away under the general plotting of the present invention, should belong within protection scope of the present invention.
Claims (7)
1. concentrated essence liquid is used in a liquid shaping; It is characterized in that: form by sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium and deionized water, by its parts by weight sodium bicarbonate 1-3 part, strontium carbonate 0.5-2 part, potassium carbonate 1-3 part, organic germanium 10-20 part, ferrous sulfate 1-3 part, calcium carbonate 0.5-2 part, organic selenium 10-20 part, deionized water 30-50 part.
2. concentrated essence liquid is used in liquid shaping according to claim 1, it is characterized in that: by its parts by weight sodium bicarbonate 1.5-2 part, strontium carbonate 1.5-2 part, potassium carbonate 1.5-2.5 part, organic germanium 15-18 part, ferrous sulfate 1.5-2 part, calcium carbonate 1.5-2 part, organic selenium 13-17 part, deionized water 35-45 part.
3. concentrated essence liquid is used in liquid shaping according to claim 1 and 2, it is characterized in that: by 1.5 parts of its parts by weight sodium bicarbonate, 1.5 parts of strontium carbonates, 2 parts of potassium carbonate, 15 parts of organic germaniums, 1.5 parts in ferrous sulfate, 1.5 parts of calcium carbonate, 15 parts of organic seleniums, 40 parts of deionized waters.
4. the described liquid shaping of one of claim 1-3 is characterized in that with the method for preparing of concentrated essence liquid: concrete preparation process is following:
(1) taking by weighing sodium bicarbonate 1-3 part, strontium carbonate 0.5-2 part, potassium carbonate 1-3 part, organic germanium 10-20 part, ferrous sulfate 1-3 part, calcium carbonate 0.5-2 part, organic selenium 10-20 part, deionized water 30-50 part by above-mentioned parts by weight is raw material;
(2) in the rustless steel sealed shell of tank with sodium bicarbonate, strontium carbonate, potassium carbonate, organic germanium, ferrous sulfate, calcium carbonate, organic selenium, mix and stir, add deionized water dissolving;
(3) continue heated and stirred to fully dissolving under 50-60 ℃ of condition, room temperature was placed 3-6 hour, got its supernatant and promptly got.
5. liquid shaping according to claim 4 is characterized in that with the method for preparing of concentrated essence liquid: reaction temperature is 55 ℃ in the said step (3), and room temperature was placed 4 hours.
6. according to claim 4 or 5 described liquid shapings method for preparing with concentrated essence liquid; It is characterized in that: step (3) gained supernatant is added in the pure water dilute; Packing into makes spray in the spray bottle, and wherein the volume ratio of supernatant and pure water is 1:30.
According to claim 4 or 5 described liquid shapings with the method for preparing of concentrated essence liquid, it is characterized in that: the gained concentrated essence liquid is a colourless transparent liquid, slight abnormal smells from the patient, PH 13, no viscosity, 150 ℃ of boiling points, node-10 ℃.