CN102735704A - 一种测量csp铸坯奥氏体晶粒尺寸的方法 - Google Patents

一种测量csp铸坯奥氏体晶粒尺寸的方法 Download PDF

Info

Publication number
CN102735704A
CN102735704A CN2012102258606A CN201210225860A CN102735704A CN 102735704 A CN102735704 A CN 102735704A CN 2012102258606 A CN2012102258606 A CN 2012102258606A CN 201210225860 A CN201210225860 A CN 201210225860A CN 102735704 A CN102735704 A CN 102735704A
Authority
CN
China
Prior art keywords
grain size
austenite
sample
steel
seconds
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012102258606A
Other languages
English (en)
Inventor
余泽金
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Baotou Iron and Steel Group Co Ltd
Inner Mongolia Baotou Steel Union Co Ltd
Original Assignee
Baotou Iron and Steel Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baotou Iron and Steel Group Co Ltd filed Critical Baotou Iron and Steel Group Co Ltd
Priority to CN2012102258606A priority Critical patent/CN102735704A/zh
Publication of CN102735704A publication Critical patent/CN102735704A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种测量CSP铸坯奥氏体晶粒尺寸的方法，其特征是：将制备好的试样打磨、抛光后放入Gleeble 1500D热模机中以15～20℃/s加热到1250～1300℃保温60～120秒后，以5～10℃/秒的冷速降至1200℃保温180～300秒后水淬，将试样的抛光面去除氧化铁皮后，再次打磨并抛光30～50s；配取10ml的苦味酸(ρ＝10mg/L)溶液和10ml浓度37at％的盐酸混合溶液对试样表面进行腐蚀15～35s，再利用95％(v/v)的工业酒精将试样表面冲洗干净并吹干，在扫描电镜上观察奥氏体组织晶粒，利用Image-Tool软件测出显微组织照片中的奥氏体的平均晶粒尺寸。其优点是：通过模拟现场真实工艺条件，测量出该钢种在粗轧道次前钢中奥氏体晶粒尺寸范围，为制定合理的轧制工艺、钢板的组织性能控制提供数据支撑。

Description

一种测量CSP铸坯奥氏体晶粒尺寸的方法
技术领域
本发明涉及一种测量CSP铸坯奥氏体晶粒尺寸的方法，属于冶金及热处理技术领域。
背景技术
在钢板、钢带的生产工艺中，热连轧CSP生产工艺与传统板带生产工艺相比其铸坯相对较薄，轧制中压缩比相对不足；同时与传统工艺相比，连铸坯出连铸机后直接进入辊底式加热炉进行加热和均热，铸坯组织没有发生γ→α和α→γ的相变过程，CSP连铸坯奥氏体晶粒尺寸相对粗大。由于上述原因，在CSP生产线上开发高强度等级的钢种，准确测量奥氏体实际晶粒尺寸范围对研究钢中组织演变规律、合理控制工艺参数、保证产品性能尤为重要。目前，测量CSP连铸坯奥氏体晶粒尺寸的方法还未见报道。
发明内容
本发明的目的是为制定合理的轧制工艺、钢板的组织性能控制提供数据支撑，提供一种测量CSP铸坯奥氏体晶粒尺寸的方法。
本发明的技术解决方案：将制备好的试样打磨、抛光后放入Gleeble 1500D热模机中以15～20℃/s加热到1250～1300℃保温60～120秒后，以5～10℃/秒的冷速降至1200℃保温180～300秒后水淬，将试样的抛光面去除氧化铁皮后，再次打磨并抛光30～50s；配取10ml的苦味酸(ρ＝10mg/L)溶液和10ml浓度37at％的盐酸混合溶液对试样表面进行腐蚀15～35s，再利用95％(v/v)的工业酒精将试样表面冲洗干净并吹干，在扫描电镜上观察奥氏体组织晶粒，利用Image-Tool软件测出显微组织照片中的奥氏体的平均晶粒尺寸。
本发明有益效果：通过模拟现场真实工艺条件，测量出该钢种在粗轧道次前钢中奥氏体晶粒尺寸范围，为制定合理的轧制工艺、钢板的组织性能控制提供数据支撑，预期具有良好的应用效果。
附图说明
图1X65钢的奥氏体显微组织图；
图2含稀土X65钢奥氏体显微组织图。
具体实施方式
以下结合实施例对本发明作进一步描述。
实施例
以X65管线钢、含稀土X65管线钢两种不同成分的钢种为原料，具体钢种成分见表1和表2。将两种钢试样均制成10mm×10mm×10mm规格，经过打磨、抛光后放入Gleeble 1500D热模机中以20℃/s加热到1300℃保温30秒后以5℃/秒的冷速降至1200℃保温300秒后水淬。将试样分别取出经过800号的砂纸磨光去除氧化铁皮后，再用抛光机轻抛30～50s；配取10ml的苦味酸(ρ＝10mg/L)溶液和10ml浓度37at％的盐酸混合溶液对试样表面分别进行腐蚀30s，再利用95％(v/v)的工业酒精将试样表面分别冲洗干净并吹干。在室温下利用QUANTA400扫描电子显微镜观察X65钢、含稀土X65钢原始奥氏体组织晶粒，X65钢奥氏体组织晶粒见图1，含稀土X65钢奥氏体组织晶粒见图2。
表1 X65钢化学成分            (质量百分数％)
  C   Si   Mn   P   S   Al   Nb
  0.05-0.08   0.30-0.60   1.45-1.65   ≤0.02   ≤0.005   0.010-0.030   0.02-0.04
表2 含稀土X65钢化学成分          (质量百分数％)
  C   Si   Mn   P   S   Al   Nb   Ce
  0.05-0.08   0.30-0.60   1.45-1.65   ≤0.02   ≤0.005   0.010-0.030   0.02-0.04   0.025-0.035
利用Image-Tool软件测出该工艺条件下两种钢奥氏体组织的平均晶粒尺寸，X65钢奥氏体组织晶粒平均尺寸为264μm，含稀土X65钢奥氏体组织晶粒平均尺寸为238μm。

Claims (1)

1.一种测量CSP铸坯奥氏体晶粒尺寸的方法，其特征是：将制备好的试样打磨、抛光后放入Gleeble 1500D热模机中以15～20℃/s加热到1250～1300℃保温60～120秒后，以5～10℃/秒的冷速降至1200℃保温180～300秒后水淬，将试样的抛光面去除氧化铁皮后，再次打磨并抛光30～50s；配取10ml的苦味酸(ρ＝10mg/L)溶液和10ml浓度37at％的盐酸混合溶液对试样表面进行腐蚀15～35s，再利用95％(v/v)的工业酒精将试样表面冲洗干净并吹干，在扫描电镜上观察奥氏体组织晶粒，利用Image-Tool软件测出显微组织照片中的奥氏体的平均晶粒尺寸。
CN2012102258606A 2012-06-20 2012-06-20 一种测量csp铸坯奥氏体晶粒尺寸的方法 Pending CN102735704A (zh)