CN102704631A - 一种屋面保温层铺设方法及施工工艺 - Google Patents
一种屋面保温层铺设方法及施工工艺 Download PDFInfo
- Publication number
- CN102704631A CN102704631A CN2012101914716A CN201210191471A CN102704631A CN 102704631 A CN102704631 A CN 102704631A CN 2012101914716 A CN2012101914716 A CN 2012101914716A CN 201210191471 A CN201210191471 A CN 201210191471A CN 102704631 A CN102704631 A CN 102704631A
- Authority
- CN
- China
- Prior art keywords
- heat
- laying
- percent
- construction process
- cementitious material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种用自制胶凝材料、无机材料、阻燃剂混合铺设屋面保温层的方法及施工工艺,主要解决现有技术中存在的保温层铺设施工工艺复杂、与基层结合不牢,易空鼓、密度小、抗压强度低、吸水率高、不透气、易燃问题。本发明的主要特点,在525#水泥中加入粒径600-100目的河砂;2-3%长度5-10mm玻纤维材料,20-25%重质碳酸钙粉;20-25%乳胶粉;3-5%纤维素;5-10%石膏粉合成胶凝材料,在配成胶凝材料中加入15-25%阻燃剂、密度在80-160kg/m3珍珠岩混合成保温材料。采用先铺设结合层,再铺保温层,最后结合层的施工工艺。本发明的优点:通过胶凝材料改进,使保温层与屋面结合牢固、抗压、抗裂强度提高,阻燃性能增强,施工工艺简单,符合现在消防要求。
Description
技术领域:
本发明涉及一种用胶凝材料,玻纤网,无机材料,阻燃材料混合做屋面保温层的方法及施工工艺。
背景技术:
我国寒冷地区屋面保温的作法,从上个世纪初采用有机材料(锯末、稻草、稻壳等),到上个世纪70年代后期用的炉渣、膨胀蛭石、膨胀珍珠岩做保温均存在着:保温材料与砖、混凝土、砂浆面层结合不牢、容易起鼓,吸水率高、抗老化能力差,不耐碱、施工难度大、易变形问题,这些问题在进入二十一世纪已被采用的挤塑聚苯乙烯保温板、聚苯乙烯泡沫塑料、硬脂聚胺脂泡沫塑料及无机多孔的泡沫混凝土及加气混凝土,微孔硅酸盐复合制品的保温材料解决了一些,但仍存在着保温层材料施工工艺复杂与红砖混凝土、砂浆面层结合不牢,易空鼓、易燃,密度小,抗压强度低,吸水率高问题,这是急需解决的问题。
发明内容:
本发明主要解决现有技术中存在的“保温层施工工艺复杂,与砖、混凝土、砂浆面层结合不牢,易空鼓、易燃、密度小、强度低、吸水率高”的技术问题。
为达到解决上述问题的目的,本发明提供的技术方案是:配制有抗裂材料、粘合材料加入的粉状胶凝材料;并以其重量比加入阻燃材料,在与无机材料混合,形成具有保温、阻燃、透气、防水易于施工的复合保温材料。用自配胶凝材料与玻璃丝网做复合保温层与砖、混凝土、砂浆面层结合。达到解决现有技术中存在问题的目的。
本发明与现有技术相比具有以下优点和积极效果:
1、可直接在未干透找平层上铺特制的胶凝材料与玻纤网,从而缩短了工期,减少找平层干缩裂缝出现机会;2、使屋面保温层增加了抗裂性能、透气性能、抗压强度提高;3施工工艺简单、吸水率降低,保温层不易变形,空鼓;4、防火性能提高,符合国家消防要求。
附图说明:
以下结合附图对本发明屋面保温层铺设方法及施工工艺进行详细说明。
附图1、本发明屋面保温层构造示意图;
附图2、本发明屋面保温层施工工艺流程图;
附图1中1混凝土屋面、2找平层、3结合层、4保温层、5结合层、6找平层、7防水层
本发明所用方法是:1、配制胶凝材料。主要原料(1)525#水泥;(2)玻璃纤维;(3)细河砂;(4)可再分散性乳胶灰粉;(5)重质碳酸钙;(6)纤维素;(7)石膏。2、确定施工方案:(1)确定结合层水灰比;(2)确定保温材料配合比;(3)确定保温层压缩比。
具体实施例:
住宅屋面保温层
1、配制胶凝材料质量比:35∶45∶2∶20∶5∶3∶10;2、确定结合层水灰比(2-4)∶1;3、确定保温层配合比:胶凝材料∶无机材料∶阻燃剂∶水=2∶1∶0.5∶3;4、施工:(1)在未干透找平层抹2mm厚胶凝材料;(2)铺75g/m2玻纤网,角用护角压牢;(3)铺设保温层,压缩比确定在115-130%之间均可;(4)铺设75g/m2玻纤网;(5)抹2mm厚胶凝材料,压实。
Claims (10)
1.一种屋面保温层铺设方法及施工工艺,其特征在于,用自配胶凝材料与玻纤网铺设结合层,并用胶凝材料、无机材料、阻燃剂混合为保温材料,采用先结合层、保温层、再结合层的工艺施工。
2.根据权利要求1所述方法,其特征在于所述自配胶凝材料是由水泥、河砂、玻璃纤维、乳胶粉、重质碳酸钙、羟甲基纤维素、石膏粉组成。质量比:(30-40)∶(40-50)∶(2-3)∶(20-25)∶(5-10)∶(3-5)∶(5-10)。
3.根据权利要求1所述方法,其特征在于,所述保温材料是由自配胶凝材料:膨胀珍珠岩、阻燃剂组成。质量比:(2-2.5)∶(1-1.5)∶(0.2-0.5)。
4.根据权利要求1所述方法,其特征在于,所述层面保温层铺设方法为二网二灰一层。即一层胶凝材料、一层玻璃丝网、一层保温、一层玻璃丝网、一层胶凝材料。
5.一种用于实现权利要求1所述屋面保温层铺设方法及施工工艺包括:结合层抹灰,铺玻璃丝网=铺保温层,压实铺玻璃丝网、抹灰。
6.根据权利要求5所述方法,其特征在于,所述结合层胶凝材料水灰比(2-4)∶1,厚度2mm。
7.根据权利要求5所述方法,其特征在于,所述保温层的水灰比为1∶1。
8.根据权利要求5所述方法,其特征在于,所述的保温层设计厚度与铺设厚度压缩比为1∶(1.1-1.3)。
9.根据权利要求5所述方法,其特征在于,所述选用膨胀珍珠岩粒径1.5mm,比重80-160kg/m3以下。
10.根据权利要求5所述方法,其特征在于,所述选用玻璃纤维网要求75-100g/m2。