CN102675703A - 一种耐低温等速万向节护套 - Google Patents
一种耐低温等速万向节护套 Download PDFInfo
- Publication number
- CN102675703A CN102675703A CN2012101404997A CN201210140499A CN102675703A CN 102675703 A CN102675703 A CN 102675703A CN 2012101404997 A CN2012101404997 A CN 2012101404997A CN 201210140499 A CN201210140499 A CN 201210140499A CN 102675703 A CN102675703 A CN 102675703A
- Authority
- CN
- China
- Prior art keywords
- carbon black
- constant velocity
- joint sheath
- low temperature
- resistant constant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐低温等速万向节护套,包含以下重量比计的组成成分:43.0%~45.0%氯丁橡胶CR1211;1.7%~1.8%氧化镁MgO;2.1%~2.2%氧化锌ZnO;23.5%~24.5%炭黑;8.6%~8.8%碳酸钙;3.4%~3.6%白炭黑;0.4%~0.5%硬脂酸;0.8%~1.0%石蜡;4.2%~4.5%菜籽油;0.8%~0.9%FS-12;0.8%~0.9%SI-69;0.8%~0.9%防老剂;0.8%~0.9%促进剂;6.5%~6.6%聚对苯二甲酸丁二酯。本发明增加了等速万向节护套的柔顺性,改变了橡胶的结晶状态,满足北方极端低温天气下的使用要求。
Description
技术领域
本发明涉及传动机构配件,特别是一种耐低温等速万向节护套。
背景技术
护套作为等速万向节/驱动轴的关键配件,其主要作用为容纳润滑脂并密封,以保证等速万向节在使用过程中的充分润滑,降低摩擦阻力;同时阻挡外部灰尘、污物进入等速万向节内腔,并能适应相应的使用环境。目前驱动轴市场所用的护套,基本为通用型,即考虑护套的综合性能,护套中加入了能满足各种基本性能的化学元素,以保证可以在各种环境下使用。根据上述现有方案生产的护套,虽然综合平衡了护套的各种性能要求,如耐磨、耐氧化、耐撕裂等等,但是当这种护套在极端环境下使用时,如高寒、高温环境下使用时,由于其应对这种极端环境的特定性能不足够突出,因此使其使用寿命大幅度急速下降,从而影响等速万向节驱动轴总成的使用性能及安全性。
发明内容
本发明所要解决的问题就是提供一种耐低温等速万向节护套,针对现有护套的不足,在不影响其他各项性能的前提下,满足护套在高寒环境下的使用要求,弥补市场不足。
为了解决上述技术问题,本发明采用如下技术方案:一种耐低温等速万向节护套,其特征在于,包含以下重量比计的组成成分:43.0%~45.0%氯丁橡胶CR1211;1.7%~1.8%氧化镁MgO;2.1%~2.2%氧化锌ZnO;23.5%~24.5%炭黑;8.6%~8.8%碳酸钙;3.4%~3.6%白炭黑;0.4%~0.5%硬脂酸;0.8%~1.0%石蜡;4.2%~4.5%菜籽油;0.8%~0.9%FS-12;0.8%~0.9%SI-69;0.8%~0.9%防老剂;0.8%~0.9%促进剂;6.5%~6.6%聚对苯二甲酸丁二酯。
进一步的,所述防老剂包括0.4%~0.5%防老剂A和0.4%~0.5%防老剂4010。
进一步的,所述炭黑包括4.0%~4.5%炭黑N330和19.5%~20.0%炭黑N770。
进一步的,所述促进剂包括0.30%~0.33%促进剂TT、0.30%~0.33%促进剂NA-22和0.20%~0.24%促进剂DM。
进一步的,上述一种耐低温等速万向节护套,其特征在于,包含以下重量比计的组成成分:43.88%氯丁橡胶CR1211;1.76%氧化镁MgO;2.19%氧化锌ZnO;4.39%炭黑N330;19.75%炭黑N770;8.78%碳酸钙;3.51%白炭黑;0.44%硬脂酸;0.88%石蜡;4.39%菜籽油;0.88%FS-12;0.88%SI-69;0.44%防老剂A;0.44%防老剂4010;0.31%促进剂TT、0.31%促进剂NA-22和0.22%促进剂DM;6.55%聚对苯二甲酸丁二酯。
采用上述技术方案后,本发明具有如下优点:增加了产品的柔顺性,改变了橡胶的结晶状态,使其在-45℃的环境下正常使用,保证使用寿命,满足北方极端低温天气下等速万向节护套的使用要求。
具体实施方式
实施例一:
本发明的第一种实施例,一种耐低温等速万向节护套,包含以下重量比计的组成成分:43.88%氯丁橡胶CR1211;1.76%氧化镁MgO;2.19%氧化锌ZnO;4.39%炭黑N330;19.75%炭黑N770;8.78%碳酸钙;3.51%白炭黑;0.44%硬脂酸;0.88%石蜡;4.39%菜籽油;0.88%FS-12;0.88%SI-69;0.44%防老剂A;0.44%防老剂4010;0.31%促进剂TT、0.31%促进剂NA-22和0.22%促进剂DM;6.55%聚对苯二甲酸丁二酯。
实施例二:
本发明的第二种实施例,一种耐低温等速万向节护套,包含以下重量比计的组成成分:43.0%氯丁橡胶CR1211;1.8%氧化镁MgO;2.2%氧化锌ZnO;4.5%炭黑N330;20.0%炭黑N770;8.8%碳酸钙;3.6%白炭黑;0.5%硬脂酸;1.0%石蜡;4.4%菜籽油;0.9%FS-12;0.9%SI-69;0.5%防老剂A;0.5%防老剂4010;0.33%促进剂TT、0.33%促进剂NA-22和0.24%促进剂DM;6.5%聚对苯二甲酸丁二酯。
实施例三:
本发明的第三种实施例,一种耐低温等速万向节护套,包含以下重量比计的组成成分:45.0%氯丁橡胶CR1211;1.7%氧化镁MgO;2.1%氧化锌ZnO;4.2%炭黑N330;19.5%炭黑N770;8.6%碳酸钙;3.4%白炭黑;0.4%硬脂酸;0.8%石蜡;4.5%菜籽油;0.8%FS-12;0.8%SI-69;0.4%防老剂A;0.4%防老剂4010;0.3%促进剂TT、0.3%促进剂NA-22和0.2%促进剂DM;6.6%聚对苯二甲酸丁二酯。
上述实施例中,综合平衡了护套的各种性能要求,如耐磨、耐氧化、耐撕裂等等,同时在不影响其他各项性能的前提下,增加了产品的柔顺性,改变了橡胶的结晶状态,使其在-45℃的环境下正常使用,保证使用寿命,满足北方极端低温天气下等速万向节护套的使用要求。
除上述优选实施例外,本发明还有其他的实施方式,本领域技术人员可以根据本发明作出各种改变和变形,只要不脱离本发明的精神,均应属于本发明所附权利要求所定义的范围。
Claims (5)
1.一种耐低温等速万向节护套,其特征在于,包含以下重量比计的组成成分:43.0%~45.0%氯丁橡胶CR1211;1.7%~1.8%氧化镁MgO;2.1%~2.2%氧化锌ZnO;23.5%~24.5%炭黑;8.6%~8.8%碳酸钙;3.4%~3.6%白炭黑;0.4%~0.5%硬脂酸;0.8%~1.0%石蜡;4.2%~4.5%菜籽油;0.8%~0.9%FS-12;0.8%~0.9%SI-69;0.8%~0.9%防老剂;0.8%~0.9%促进剂;6.5%~6.6%聚对苯二甲酸丁二酯。
2.根据权利要求1所述的一种耐低温等速万向节护套,其特征在于,所述炭黑包括4.0%~4.5%炭黑N330和19.5%~20.0%炭黑N770。
3.根据权利要求1所述的一种耐低温等速万向节护套,其特征在于,所述防老剂包括0.4%~0.5%防老剂A和0.4%~0.5%防老剂4010。
4.根据权利要求1所述的一种耐低温等速万向节护套,其特征在于,所述促进剂包括0.30%~0.33%促进剂TT、0.30%~0.33%促进剂NA-22和0.20%~0.24%促进剂DM。
5.根据权利要求1所述的一种耐低温等速万向节护套,其特征在于,包含以下重量比计的组成成分:43.88%氯丁橡胶CR1211;1.76%氧化镁MgO;2.19%氧化锌ZnO;4.39%炭黑N330;19.75%炭黑N770;8.78%碳酸钙;3.51%白炭黑;0.44%硬脂酸;0.88%石蜡;4.39%菜籽油;0.88%FS-12;0.88%SI-69;0.44%防老剂A;0.44%防老剂4010;0.31%促进剂TT、0.31%促进剂NA-22和0.22%促进剂DM;6.55%聚对苯二甲酸丁二酯。