CN102627476A - Blue crystalline glaze material and use method thereof - Google Patents
Blue crystalline glaze material and use method thereof Download PDFInfo
- Publication number
- CN102627476A CN102627476A CN2012101071556A CN201210107155A CN102627476A CN 102627476 A CN102627476 A CN 102627476A CN 2012101071556 A CN2012101071556 A CN 2012101071556A CN 201210107155 A CN201210107155 A CN 201210107155A CN 102627476 A CN102627476 A CN 102627476A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- blue
- weight parts
- glaze material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a blue crystalline glaze material and a use method thereof. The blue crystalline glaze material is characterized by mixing the following materials in parts by weight: 38 parts of fuhu feldspar, 8-12 parts of high-expansion frit, 10-20 parts of quartz, 4-6 parts of calcium carbonate, 25-27 parts of zinc oxide, 5-7 parts of barium carbonate and 0.5-1.5 parts of cobalt oxide. Compared with the prior art, the blue crystalline glaze material has the advantages of obtaining a blue ceramic product with a crystallization effect, along with exquisite and attractive appearance, high decorative effect, simple formula, convenience in operation, low cost and suitability for industrial production.
Description
Technical field
The present invention relates to a kind of blue crystallization glaze, be used for producing pottery.
Background technology
Along with ceramic gets into huge numbers of families, ceramic glaze is the indispensable finishing material of ceramic, and existing ceramic glaze is can rough classification following according to classification and purposes: 1, lead glaze and leadless glaze; 2, raw glaze and fritted glaze; 3, once-firing or twice firing are used glaze; 4, ceramic tile, tableware, snitaryware and electroceramics are used glaze; 5, soak glaze, glaze spraying, water glaze by what enameling method was divided; 6, high melting glaze and low temperature glaze; 7, high expansion glaze and low bulk glaze; 8, firing atmosphere oxydizing flame, neutral flame and reducing flame; 9, coloured glaze and colourless glaze; 10, transparent and opaque glaze; 11, bright glaze, matt glaze, semi-mat glaze or figure glaze or the like.The stability of ceramic glaze, variety, glaze is decorated, pattern decoration has become the target that China pottery producer is pursued.
Summary of the invention
The purpose of this invention is to provide a kind of bright-colored and the ceramic glaze and the method for use thereof of crystallization effect arranged.
In order to achieve the above object; The invention provides a kind of blue crystallization glaze; It is characterized in that, mix by still head of a household stone 38 weight parts, high expansion frit 8～12 weight parts, quartzy 10～20 weight parts, lime carbonate 4～6 weight parts, zinc oxide 25～27 weight parts, barium carbonate 5～7 weight parts and powder blue 0.5～1.5 weight part.
The present invention also provides the method for use of above-mentioned blue crystallization glaze, it is characterized in that, concrete steps are: blue crystallization glaze is mixed according to weight ratio 100: 70～80 with water; Grind, sieve, the porcelain base is immersed in the mixture of gained; Take out behind the 2-3s; Fired 15～16 hours at 1200～1300 ℃, cooling obtains the blue ceramic goods that the part presents crystallization effect.
Compared with prior art, the present invention has following advantage:
(1) can access the blue ceramic goods with crystallization effect, exquisite attractive in appearance, decorative effect is strong;
(2) prescription is simple, easy to operate, and cost is low, is fit to industrial production.
Embodiment
Specify the present invention below in conjunction with embodiment.The various raw materials of using among the embodiment are all the commercially available prod, wherein, still head of a household Shi Hegao expansion frit available from Caro than inferior glaze (Kunshan) ltd.
Embodiment
(1) still head of a household stone 38 weight parts, high expansion frit 10 weight parts, quartzy 15 weight parts, lime carbonate 5 weight parts, zinc oxide 26 weight parts, barium carbonate 6 weight parts and powder blue 1 weight part are mixed and made into blue crystallization glaze;
(2) blue crystallization glaze is mixed according to weight ratio with water at 100: 75, grind, cross 200 mesh sieves, the ordinary porcelain base is immersed in the mixture of gained, take out behind the 2s, fired 15 hours at 1250 ℃, cooling obtains the blue ceramic goods that the part presents crystallization effect.
Claims (2)
1. blue crystallization glaze; It is characterized in that, mix by still head of a household stone 38 weight parts, high expansion frit 8～12 weight parts, quartzy 10～20 weight parts, lime carbonate 4～6 weight parts, zinc oxide 25～27 weight parts, barium carbonate 5～7 weight parts and powder blue 0.5～1.5 weight part.
2. the method for use of the described blue crystallization glaze of claim 1 is characterized in that, concrete steps are: blue crystallization glaze is mixed according to weight ratio 100: 70～80 with water; Grind, sieve, the porcelain base is immersed in the mixture of gained; Take out behind the 2-3s; Fired 15～16 hours at 1200～1300 ℃, cooling obtains the ceramic that the part presents crystallization effect.