CN102615875B - 一种不连续金属质感银白色薄膜及其镀膜方法 - Google Patents
一种不连续金属质感银白色薄膜及其镀膜方法 Download PDFInfo
- Publication number
- CN102615875B CN102615875B CN201210078107.9A CN201210078107A CN102615875B CN 102615875 B CN102615875 B CN 102615875B CN 201210078107 A CN201210078107 A CN 201210078107A CN 102615875 B CN102615875 B CN 102615875B
- Authority
- CN
- China
- Prior art keywords
- film
- membrane
- layer
- titanium dioxide
- glass substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种不连续金属质感银白色薄膜及其镀膜方法，所述的薄膜涂覆在玻璃基板上，薄膜从玻璃基板向外依次包括二氧化钛膜层、二氧化硅膜层、二氧化钛膜层、二氧化硅膜层、二氧化钛膜层；该薄膜的镀膜方法包括光学真空镀膜制备银白色薄膜，对镀膜后的产品进行丝网印刷，最后进行膜层褪膜。本发明薄膜附着力好、抗机械强度好，在镀膜面上丝印油墨不会碰伤镀膜面，制备工艺稳定、金属质感强、耐候性能好、膜层暴露空气中长时间不容易氧化，适合批量化生产。
Description
技术领域
本发明涉及一种手机触摸屏玻璃面板的真空镀膜，特别是涉及一种不连续金属质感银白色薄膜及其镀膜方法。
背景技术
随着近年来手机行业的飞速发展,功能已经不是消费者唯一追求的目标.手机外表也吸引着大众的目光。因此，拥有金属光泽和色彩的手机外壳及电容式触摸屏玻璃触摸面板发展成为手机装饰不可取代的一部分。
由于金属或者金属膜层的外壳会屏蔽手机发射的信号,所以,手机生产商希望能够得到一种既拥有金属效果又不会影响手机信号的手机外壳，目前国内真空镀膜制备手机外壳不连续膜层的镀膜方法，使用铟锡合金作为镀膜原材料。如中华人民共和国专利申请第201120065977.3、201010258327.0号均有所公开。
为了整个手机外观的协调美观统一，镀膜膜料铟锡合金镀制到玻璃表面上附着力差、抗机械强度差，在镀膜面上丝印油墨很容易碰伤镀膜面，铟锡合金在制备在玻璃表面暴露在空气中非常易氧化，氧化后的铟锡膜层会变颜色，不呈现铟锡合金本来中性的特色，不适合批量生产。
发明内容
本发明的目的在于克服现有技术的不足，提供一种不连续金属质感银白色薄膜的镀膜方法，薄膜附着力好、抗机械强度好、在镀膜面上丝印油墨不会碰伤镀膜面 ，制备工艺稳定、金属质感强、耐候性能好、膜层暴露空气中长时间不容易氧化，适合批量化生产。
为了达到上述目的，本发明采用的技术方案是：一种不连续金属质感银白色薄膜，设置于玻璃基板外侧，所述的薄膜涂覆在玻璃基板上，薄膜从玻璃基板向外依次包括若干相互涂覆或粘覆的二氧化钛膜层、二氧化硅膜层并交替设置。
进一步的，所述的薄膜从靠近玻璃基板的一侧依次包括二氧化钛膜层、二氧化硅膜层、二氧化钛膜层、二氧化硅膜层、二氧化钛膜层。
进一步的，所述的薄膜的第一层二氧化钛膜层厚度为108.06～115.30纳米，第二层二氧化硅膜层厚度为89.16～94.5纳米，第三层二氧化钛膜层厚度为54.03～57.65纳米，第四层二氧化硅膜层厚度为89.16～94.5纳米，第五层二氧化钛膜层厚度为54.03～57.65纳米。
进一步的，所述薄膜的中心波长为520～550纳米。
不连续金属质感银白色薄膜的镀膜方法，步骤如下：
步骤1、光学真空镀膜制备银白色薄膜
对真空度、玻璃基板的加热温度、镀膜基板的旋转频率、电子枪的电压、二氧化钛的蒸发速率、二氧化硅的蒸发速率进行设定；
依次在玻璃基板的表面镀二氧化钛膜层、二氧化硅膜层、二氧化钛膜层、二氧化硅膜层、二氧化钛膜层；
步骤2、对不连续金属质感银白色薄膜进行丝网印刷
对镀膜后的玻璃产品进行油墨丝网印刷，往丝网印刷网板上添加黑色油墨，把镀膜后的玻璃产品放到印刷机的网板正下方的固定底座上，按下印刷机的自动印刷开始开关，进行自动印刷，把印刷好的镀膜玻璃产品放入烘烤箱烘烤；
步骤3、膜层褪膜
把褪镀液倒入保温箱，并加热褪镀液体，温度控制在80℃恒温，再把丝印好的镀膜产品放入褪镀液中并浸没并浸泡，浸泡后取出产品放入干净的清水中，再用清水冲洗干净即获得薄膜。
进一步的，步骤1所述的镀膜真空度为1～5×10ˉ3帕，玻璃基板的加热温度为115～125℃，镀膜基板的旋转频率为50Hz，电子枪的电压为-6～10KV，二氧化钛的蒸发速率为1～10埃/秒，二氧化硅的蒸发速率为5～20埃/秒。
进一步的，步骤2所述的烤箱内的温度设定为160～200度，烘烤时间为5～30分钟。
进一步的，步骤3所述的浸泡时间为1～10分钟。
与现有技术相比，本发明的有益效果是：在光学真空镀膜机上，利用二氧化钛、二氧化硅作为镀膜原料在玻璃表面制备银白色不连续膜层，利用薄膜干涉原理，膜层附着力好、抗机械强度好、有利于批量生产。
附图说明
图1为本发明的结构示意图。
具体实施方式
下面结合实施例参照附图进行详细说明，以便对本发明的技术特征及优点进行更深入的诠释。
如图1所示，一种不连续金属质感银白色薄膜，设置于玻璃基板外侧，所述的薄膜涂覆在玻璃基板上，薄膜从靠近玻璃基板的一侧依次包括二氧化钛膜层、二氧化硅膜层、二氧化钛膜层、二氧化硅膜层、二氧化钛膜层。其中，薄膜的第一层二氧化钛膜层厚度108.06～115.30纳米，第二层二氧化硅膜层厚度89.16～94.5纳米，第三层二氧化钛膜层厚度54.03～57.65纳米，第四层二氧化硅膜层厚度89.16～94.5纳米，第五层二氧化钛膜层厚度54.03～57.65纳米。薄膜的透射光波长为520～550纳米。
下面分三个实施例来详细说明制备过程，按照薄膜透射光波长来划分，分为520、535、550纳米三个透射光波长的薄膜来说明。
实施例1：
一种不连续金属质感银白色薄膜的镀膜方法，该镀膜方法是以环保镀膜材料(二氧化钛 二氧化硅)作为原材料，并且引入光学真空镀膜技术，根据手机电容式触摸屏玻璃面板材料的具体特性，设计并优化光学真空镀膜技术的各项参数，经验证可有效解决现有技术的不足，实现本发明目的，该镀膜方法具体包括如下步骤：
步骤一：光学真空镀膜制备银白色薄膜:
（1）光学真空镀膜机型号：（联合真空2050型镀膜机）
（2）膜系结构：玻璃基板/二氧化钛/二氧化硅/二氧化钛/二氧化硅/二氧化钛/空气
（3）镀膜工艺的制备：
膜系是规整膜系，参考波长（520纳米）
第1层（二氧化钛）膜厚 108.06纳米
第2层（二氧化硅）膜厚 89.16纳米
第3层（二氧化钛）膜厚 54.03纳米
第4层（二氧化硅）膜厚 89.16纳米
第5层（二氧化钛）膜厚 54.03纳米
镀膜真空度 （1.0×10ˉ3帕）
基板加热温度 （115±5℃）
镀膜基板旋转频率 （50Hz）
电子枪的电压 （ -6KV）
蒸发速率 二氧化钛 (1埃/秒)
蒸发速率 二氧化硅 (5埃/秒)
步骤二： 丝网印刷
对镀膜后的玻璃产品进行油墨丝网印刷，往丝网印刷网板上添加黑色油墨，把镀膜后的玻璃产品放到印刷机的网板正下方的固定底座上，按下印刷机的自动印刷开始开关，进行自动印刷，把印刷好了的镀膜玻璃产品放进烘烤箱烘烤，烤箱内的温度设定在160度，烘烤的时间5分钟。
步骤三：膜层褪膜
膜层褪镀的目的：把用了印刷油墨的膜层地方保护起来，暴露的膜层褪掉，工艺过程：把腿镀液倒入保温箱，并加热褪镀液体，温度控制在80℃恒温，再把丝印好了的镀膜产品放入褪镀液中并浸没，浸泡的时间1分钟后，取出产品后放入干净的清水中，再用清水冲洗干净。
实施例2：
一种不连续金属质感银白色薄膜的镀膜方法，该镀膜方法是以环保镀膜材料(二氧化钛、二氧化硅)作为原材料，并且引入光学真空镀膜技术，根据手机电容式触摸屏玻璃面板材料的具体特性，设计并优化光学真空镀膜技术的各项参数，经验证可有效解决现有技术的不足，实现本发明目的，该镀膜方法具体包括如下步骤：
步骤一：光学真空镀膜制备银白色薄膜:
（1）光学真空镀膜机型号：（联合真空2050型镀膜机）
（2）膜系结构：玻璃基板/二氧化钛/二氧化硅/二氧化钛/二氧化硅/二氧化钛/空气
（3）镀膜工艺的制备：
膜系是规整膜系，参考波长（535纳米）
第1层（二氧化钛）膜厚 111.67纳米
第2层（二氧化硅）膜厚 91.83纳米
第3层（二氧化钛）膜厚 55.83纳米
第4层（二氧化硅）膜厚 91.83纳米
第5层（二氧化钛）膜厚 55.83纳米
镀膜真空度 （3.0×10ˉ3Pa）
基板加热温度 （120℃）
镀膜基板旋转频率 （50Hz）
电子枪的电压 （ -8KV）
蒸发速率 二氧化钛 (5埃/秒)
蒸发速率 二氧化硅 (12埃/秒)
步骤二：丝网印刷
对镀膜后的玻璃产品进行油墨丝网印刷，往丝网印刷网板上添加黑色油墨，把镀膜后的玻璃产品放到印刷机的网板正下方的固定底座上，按下印刷机的自动印刷开始开关，进行自动印刷，把印刷好了的镀膜玻璃产品放进烘烤箱烘烤，烤箱内的温度设定在180度恒温，烘烤的时间15分钟。
步骤三：膜层褪膜
膜层褪镀的目的：把用了印刷油墨的膜层地方保护起来，暴露的膜层褪掉，工艺过程：把腿镀液倒入保温箱，并加热褪镀液体，温度控制在80℃恒温，再把丝印好了的镀膜产品放入褪镀液中并浸没，浸泡的时间5分钟后，取出产品后放入干净的清水中，再用干净的清水冲洗干净。
实施方式3：
一种不连续金属质感银白色薄膜的镀膜方法，该镀膜方法是以环保镀膜材料(二氧化钛 二氧化硅)作为原材料，并且引入光学真空镀膜技术，根据手机电容式触摸屏玻璃面板材料的具体特性，设计并优化光学真空镀膜技术的各项参数，经验证可有效解决现有技术的不足，实现本发明目的，该镀膜方法具体包括如下步骤：
步骤一：光学真空镀膜制备银白色薄膜:
（1）光学真空镀膜机型号：（联合真空2050型镀膜机）
（2）膜系结构：玻璃基板/二氧化钛/二氧化硅/二氧化钛/二氧化硅/二氧化钛/空气
（3）镀膜工艺的制备：
膜系是规整膜系，参考波长（550纳米）
第1层（二氧化钛）膜厚 115.30纳米
第2层（二氧化硅）膜厚 94.5纳米
第3层（二氧化钛）膜厚 57.65纳米
第4层（二氧化硅）膜厚 94.5纳米
第5层（二氧化钛）膜厚 57.65纳米
镀膜真空度 （5.0×10ˉ3Pa）
基板加热温度 （125℃）
镀膜基板旋转频率 （50Hz）
电子枪的电压 （ -10KV）
蒸发速率 二氧化钛 (10埃/秒)
蒸发速率 二氧化硅 (20埃/秒)
步骤二：丝网印刷
对镀膜后的玻璃产品进行油墨丝网印刷，往丝网印刷网板上添加黑色油墨，把镀膜后的玻璃产品放到印刷机的网板正下方的固定底座上，按下印刷机的自动印刷开始开关，进行自动印刷，把印刷好了的镀膜玻璃产品放进烘烤箱烘烤，烤箱内的温度设定在200度恒温，烘烤的时间30分钟。
步骤三：膜层褪膜
膜层褪镀的目的：把用了印刷油墨的膜层地方保护起来，暴露的膜层褪掉，工艺过程：把腿镀液倒入保温箱，并加热褪镀液体，温度控制在80℃恒温，再把丝印好了的镀膜产品放入褪镀液中并浸没，浸泡的时间10分钟后，取出产品后放入干净的清水中，再用干净的清水冲洗干净。
以上所述为本发明较佳的实施例，在不脱离本发明的发明构思的前提下，任何显而易见的替换均在本发明的保护范围之内。
Claims (2)
1.一种不连续金属质感银白色薄膜的镀膜方法，所述薄膜设置于玻璃基板外侧，所述的薄膜通过物理气相沉积法沉积在玻璃基板上，薄膜从玻璃基板向外依次包括若干相互膜层的二氧化钛膜层、二氧化硅膜层并交替设置，其特征在于，薄膜的镀膜方法步骤如下：
步骤1、光学真空镀膜制备银白色薄膜
对真空度、玻璃基板的加热温度、镀膜基板的旋转频率、电子枪的电压、二氧化钛的蒸发速率、二氧化硅的蒸发速率进行设定；
依次在玻璃基板的表面镀二氧化钛膜层、二氧化硅膜层、二氧化钛膜层、二氧化硅膜层、二氧化钛膜层；
所述的镀膜真空度为1×10ˉ3～5×10ˉ3帕，玻璃基板的加热温度为115～125℃，镀膜基板的旋转频率为50Hz，电子枪的电压为-6～-10kV，二氧化钛的蒸发速率为2～4埃/秒，二氧化硅的蒸发速率为5-10埃/秒；
步骤2、对不连续金属质感银白色薄膜进行丝网印刷
对镀膜后的玻璃产品进行油墨丝网印刷，往丝网印刷网板上添加黑色油墨，把镀膜后的玻璃产品放到印刷机的网板正下方的固定底座上，按下印刷机的自动印刷开始开关，进行自动印刷，把印刷好的镀膜玻璃产品放入烘烤箱烘烤；
所述的烘烤箱内的温度为160～200摄氏度，烘烤时间为5～30分钟；
步骤3、膜层褪膜
把褪镀液倒入保温箱，并加热褪镀液体，温度控制在80℃恒温，再把丝印好的镀膜产品放入褪镀液中浸没并浸泡，浸泡时间为1～10分钟，浸泡后取出产品放入干净的清水中，再用清水冲洗干净即获得薄膜。
2.根据权利要求1所述的不连续金属质感银白色薄膜的镀膜方法，其特征在于：所述的薄膜的中心波长为520～550纳米。