CN102592824A - 耐高温聚丙烯电容膜及生产方法 - Google Patents

耐高温聚丙烯电容膜及生产方法 Download PDF

Info

Publication number
CN102592824A
CN102592824A CN2012100604746A CN201210060474A CN102592824A CN 102592824 A CN102592824 A CN 102592824A CN 2012100604746 A CN2012100604746 A CN 2012100604746A CN 201210060474 A CN201210060474 A CN 201210060474A CN 102592824 A CN102592824 A CN 102592824A
Authority
CN
China
Prior art keywords
temperature
typing
film
die head
production method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100604746A
Other languages
English (en)
Inventor
徐明强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANGTONG BISON ELECTRONIC NEW MATERIAL CO Ltd
Original Assignee
NANGTONG BISON ELECTRONIC NEW MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANGTONG BISON ELECTRONIC NEW MATERIAL CO Ltd filed Critical NANGTONG BISON ELECTRONIC NEW MATERIAL CO Ltd
Priority to CN2012100604746A priority Critical patent/CN102592824A/zh
Publication of CN102592824A publication Critical patent/CN102592824A/zh
Pending legal-status Critical Current

Abstract

本发明涉及耐高温聚丙烯电容膜，在130℃-150℃温度下，加热12-15分钟，该聚丙烯电容膜的机械方向热收缩率为3%-5%，宽度方向热收缩率为0.3%-0.5%。本发明还涉及耐高温聚丙烯电容膜的生产方法，包括以下步骤：熔融挤出；模头定型；预制薄膜；机械方向预热、拉伸、定型；宽度方向预热、拉伸、定型。本发明优点：本发明的生产方法简单，节约成本，产品耐高温、拉伸强度大，使用寿命长。

Description

耐高温聚丙烯电容膜及生产方法
技术领域
本发明涉及一种耐高温聚丙烯电容膜。
本发明涉及一种耐高温聚丙烯电容膜的生产方法。
背景技术
现有的聚丙烯电容薄膜，由于横向热收缩率相对偏大，在金属化电容器制作与使用过程中，造成两端金属层与薄膜表面镀层连接不好，电容器温度升高，使电容器易击穿，质量下降。因此，需要提供一种新的技术方案来解决上述问题。
发明内容
本发明的目的是提供一种耐高温聚丙烯电容膜。
本发明的另一个目的是提供一种耐高温聚丙烯电容膜的生产方法。
为实现上述目的，本发明采用的技术方案是：
耐高温聚丙烯电容膜，在130℃-150℃温度下，加热12-15分钟，该聚丙烯电容膜的机械方向热收缩率为3%-5%，宽度方向热收缩率为0.3%-0.5% 。
耐高温聚丙烯电容膜的生产方法，包括以下步骤：
a、熔融挤出：在温度280℃-300℃下，将聚丙烯原料通过挤出机加热熔化，并挤出形成熔融均匀的粘流态熔体；
b、模头定型：上述粘流态熔体经平型模头成型和挤出，平型模头的温度为230℃-250℃；
c、预制薄膜：在离开该平型模头的熔体在激冷辊上牵引并固化成预制薄膜，固化温度为50℃-80℃，薄膜厚度为1-7μm；
d、机械方向预热、拉伸、定型：在110℃-145℃预热，纵向拉伸机将预制薄膜沿机械方向拉伸，温度降到95℃-100℃时定型；
e、宽度方向预热、拉伸、定型：在170℃-200℃预热，横向拉伸机将预制薄膜沿宽度方向拉伸，温度降到100℃-115℃时定型。
本发明的优点：本发明的生产方法简单，节约成本，产品耐高温、拉伸强度大，使用寿命长。
具体实施方式
以下实施例旨在说明本发明而不是对本方明的进一步限定。
实施例1
耐高温聚丙烯电容膜，在130℃温度下，加热12分钟，该聚丙烯电容膜的机械方向热收缩率为3%，宽度方向热收缩率为0.3%。
耐高温聚丙烯电容膜的生产方法，包括以下步骤：
a、熔融挤出：在温度280℃下，将聚丙烯原料通过挤出机加热熔化，并挤出形成熔融均匀的粘流态熔体；
b、模头定型：上述粘流态熔体经平型模头成型和挤出，平型模头的温度为230℃；
c、预制薄膜：在离开该平型模头的熔体在激冷辊上牵引并固化成预制薄膜，固化温度为50℃，薄膜厚度为1μm；
d、机械方向预热、拉伸、定型：在110℃预热，纵向拉伸机将预制薄膜沿机械方向拉伸，温度降到95℃时定型；
e、宽度方向预热、拉伸、定型：在170℃预热，横向拉伸机将预制薄膜沿宽度方向拉伸，温度降到100℃时定型。
实施例2
耐高温聚丙烯电容膜，在140℃温度下，加热13.5分钟，该聚丙烯电容膜的机械方向热收缩率为4%，宽度方向热收缩率为0.4% 。
耐高温聚丙烯电容膜的生产方法，包括以下步骤：
a、熔融挤出：在温度290℃下，将聚丙烯原料通过挤出机加热熔化，并挤出形成熔融均匀的粘流态熔体；
b、模头定型：上述粘流态熔体经平型模头成型和挤出，平型模头的温度为240℃；
c、预制薄膜：在离开该平型模头的熔体在激冷辊上牵引并固化成预制薄膜，固化温度为65℃，薄膜厚度为4μm；
d、机械方向预热、拉伸、定型：在130℃预热，纵向拉伸机将预制薄膜沿机械方向拉伸，温度降到97℃时定型；
e、宽度方向预热、拉伸、定型：在185℃预热，横向拉伸机将预制薄膜沿宽度方向拉伸，温度降到112℃时定型。
实施例3
耐高温聚丙烯电容膜，在150℃温度下，加热15分钟，该聚丙烯电容膜的机械方向热收缩率为5%，宽度方向热收缩率为0.5% 。
耐高温聚丙烯电容膜的生产方法，包括以下步骤：
a、熔融挤出：在温度300℃下，将聚丙烯原料通过挤出机加热熔化，并挤出形成熔融均匀的粘流态熔体；
b、模头定型：上述粘流态熔体经平型模头成型和挤出，平型模头的温度为250℃；
c、预制薄膜：在离开该平型模头的熔体在激冷辊上牵引并固化成预制薄膜，固化温度为80℃，薄膜厚度为7μm；
d、机械方向预热、拉伸、定型：在145℃预热，纵向拉伸机将预制薄膜沿机械方向拉伸，温度降到100℃时定型；
e、宽度方向预热、拉伸、定型：在200℃预热，横向拉伸机将预制薄膜沿宽度方向拉伸，温度降到115℃时定型。
本发明的生产方法简单，节约成本，产品耐高温、拉伸强度大，使用寿命长。

Claims (2)

1. 耐高温聚丙烯电容膜，其特征在于：在130℃-150℃温度下，加热12-15分钟，该聚丙烯电容膜的机械方向热收缩率为3%-5%，宽度方向热收缩率为0.3%-0.5% 。
2.耐高温聚丙烯电容膜的生产方法，其特征在于，包括以下步骤：
a、熔融挤出：在温度280℃-300℃下，将聚丙烯原料通过挤出机加热熔化，并挤出形成熔融均匀的粘流态熔体；
b、模头定型：上述粘流态熔体经平型模头成型和挤出，平型模头的温度为230℃-250℃；
c、预制薄膜：在离开该平型模头的熔体在激冷辊上牵引并固化成预制薄膜，固化温度为50℃-80℃，薄膜厚度为1-7μm；
d、机械方向预热、拉伸、定型：在110℃-145℃预热，纵向拉伸机将预制薄膜沿机械方向拉伸，温度降到95℃-100℃时定型；
e、宽度方向预热、拉伸、定型：在170℃-200℃预热，横向拉伸机将预制薄膜沿宽度方向拉伸，温度降到100℃-115℃时定型。
CN2012100604746A 2012-03-09 2012-03-09 耐高温聚丙烯电容膜及生产方法 Pending CN102592824A (zh)