CN102559023A - Scratch resistance waterborne polyurethane coating and preparation method thereof - Google Patents
Scratch resistance waterborne polyurethane coating and preparation method thereof Download PDFInfo
- Publication number
- CN102559023A CN102559023A CN2010106104792A CN201010610479A CN102559023A CN 102559023 A CN102559023 A CN 102559023A CN 2010106104792 A CN2010106104792 A CN 2010106104792A CN 201010610479 A CN201010610479 A CN 201010610479A CN 102559023 A CN102559023 A CN 102559023A
- Authority
- CN
- China
- Prior art keywords
- coating
- aqueous polyurethane
- scratch resistance
- waterborne polyurethane
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a scratch resistance waterborne polyurethane coating. The scratch resistance waterborne polyurethane coating comprises the following raw materials in percentage by weight: 20-50 of waterborne acrylic acid resin, 10-30 of curing agent, 10-25 of nanometer calcium carbonate, 20-50 of waterborne polyurethane, 1-5 of reactive organic silicon and 1-3 of cosolvent. Correspondingly, the invention also discloses a preparation method of the scratch resistance waterborne polyurethane coating. According to the preparation method, the scratch resistance waterborne polyurethane coating is prepared by uniformly mixing the waterborne acrylic acid resin, the nanometer calcium carbonate, the waterborne polyurethane, an organic silicon solution and the curing agent. After the coating prepared by the method is cured, a coating film formed on the surface of a base material has scratch resistance and good extensibility and lubricative appearance; and simultaneously, a proportion of the hardness to toughness of the coating can be adjusted according to different applications of the coating; and the scratch resistance waterborne polyurethane coating has wide range of application and is low in cost.
Description
Technical field
The present invention relates to chemical technology field, relate in particular to a kind of scratch resistance aqueous polyurethane coating and preparation method thereof.
Background technology
The filming of article surface such as automobile, furniture in use receives sandstone, washing easily or artificially swipes and damage; Cause that gloss weakens, cut is obvious; Have a strong impact on film quality and attractive in appearance, therefore, scratch resistance becomes an important indicator weighing film performance.High scratch resistance means to film can make material surface keep gloss and attractive in appearance in a long time, makes the finishing material longer service life.
At present, improving scratch resistance generally is the hardness of selecting for use the higher resin of hardness to film with increase, perhaps adds the scratch resistance that nano inoganic particle is filmed with improvement.
Wherein, inorganic nano-particle is because particle diameter is little, and surface-area is big, can improve the many-sided performance of polymkeric substance with mixed with polymers, and the broad research that has therefore received all trades and professions is used.But, reunite easily between particle, thereby a part of due effect of improving of nanoparticle of adding of loss because the nanoparticle surface free energy is big.
In addition, the scratch resistance through the hardness of unilateral increase polymer coating film is filmed with raising can cause the poor ductility of filming owing to hardness is too high, makes the coating scope of application narrow down.
Summary of the invention
Embodiment of the invention technical problem to be solved is, good scratch resistance aqueous polyurethane coating of a kind of ductility and preparation method thereof is provided.
In order to solve the problems of the technologies described above, the embodiment of the invention provides a kind of scratch resistance aqueous polyurethane coating, and wherein, the raw material of said coating comprises following weight part: water-borne acrylic resin: 20-50; Solidifying agent: 10-30; Nano-calcium carbonate: 10-25; Aqueous polyurethane: 20-50; Reactive organosilicon: 1-5; Cosolvent: 1-3.
Said water-borne acrylic resin is the vinyl resin of hydroxyl, and solid content is 40%-70%, and particle diameter is 60-100nm.
Said solidifying agent is a POLYMETHYLENE POLYPHENYLISOCYANATE, and-NCO content is 15%-20%; Said aqueous polyurethane is end-blocked aqueous polyurethane, and solid content is 10%-15%; Said reactive organosilicon is that hydroxy-end capped linearity can be reacted siloxanes; Said cosolvent comprises any or the combination in ethylene glycol mono-ether, Ucar 35 monoether, Virahol, butanols and the butanone.
Correspondingly, the embodiment of the invention also provides a kind of preparation method of scratch resistance aqueous polyurethane coating, and wherein, the raw material of said coating comprises following weight part: water-borne acrylic resin: 20-50; Solidifying agent: 10-30; Nano-calcium carbonate: 10-25; Aqueous polyurethane: 20-50; Reactive organosilicon: 1-5; Cosolvent: 1-3; The preparation method of said coating may further comprise the steps:
(1) said cosolvent is added in the said reactive organosilicon, obtain organic silicon solution;
(2) said water-borne acrylic resin is mixed with organic silicon solution and the solidifying agent that nano-calcium carbonate, aqueous polyurethane, step (1) obtain successively, obtain coating.
Preferably, said water-borne acrylic resin is the vinyl resin of hydroxyl, and solid content is 40%-70%, and particle diameter is 60-100nm; Said solidifying agent is a POLYMETHYLENE POLYPHENYLISOCYANATE, and-NCO content is 15%-20%; Said aqueous polyurethane is end-blocked aqueous polyurethane, and solid content is 10%-15%; Said reactive organosilicon is that hydroxy-end capped linearity can be reacted siloxanes; Said cosolvent comprises any or the combination in ethylene glycol mono-ether, Ucar 35 monoether, Virahol, butanols and the butanone.
Select for use nano-calcium carbonate as mineral filler among the present invention, nano-calcium carbonate joins in the waterborne polymeric, is uniformly dispersed easily, can produce nano effect better.In addition, the Mohs' hardness of nano-calcium carbonate is 3, and is bigger than polymkeric substance, can improve polymkeric substance hardness, realizes scrath resistance.In the present invention, adopt mixing of hard component and soft component, make coating realize hard and tough performance, wherein soft component be end-block aqueous polyurethane, hard component is a water-borne acrylic resin.In the making processes, water-borne acrylic resin and nano-calcium carbonate, aqueous polyurethane, organic silicon solution and solidifying agent POLYMETHYLENE POLYPHENYLISOCYANATE are stirred.Since end-block aqueous polyurethane can not react with POLYMETHYLENE POLYPHENYLISOCYANATE, the soft chain segment of its molecule itself can be good at improving the toughness of coating; Simultaneously, the organosilicon in the component can be participated in polymer reaction, makes the reaction of part segment and polymer segment to improve the polymer surfaces performance, and performances such as sticking power, hardness, curing speed are improved.After stirring coating is applied at product surface; Be cured through 70 ℃ drying oven at last; As solidifying agent, film by the tough and tensile double-component acrylic acid polyurethane that when film forming is solidified, is converted into water resisting property with POLYMETHYLENE POLYPHENYLISOCYANATE for wherein hard component water-borne acrylic resin.It should be noted that reactive organosilicon need dissolve with cosolvent before use, make reactive organosilicon and water miscible.
Therefore embodiment of the present invention has scratch resistance and good ductility filming of substrate surface formation behind the paint solidification, and appearance is lubricated.Simultaneously according to the difference of coating purposes, the hardness of adjustable coating and tough sex ratio, use range is extensive, and cost is low.
Embodiment
For making the object of the invention, technical scheme and advantage clearer, will do to describe in detail further to the present invention below.
A kind of scratch resistance aqueous polyurethane coating is characterized in that the raw material of said coating comprises following weight part: water-borne acrylic resin: 20-50; Solidifying agent: 10-30; Nano-calcium carbonate: 10-25; Aqueous polyurethane: 20-50; Reactive organosilicon: 1-5; Cosolvent: 1-3.
Need to prove that the present invention adopts nano-calcium carbonate as mineral filler.
In addition, this coating adopts mixing of hard component and soft component, and to realize hard and tough performance, as solidifying agent, film by the tough and tensile double-component acrylic acid polyurethane that when film forming is solidified, is converted into water resisting property with POLYMETHYLENE POLYPHENYLISOCYANATE for wherein hard component water-borne acrylic resin; Soft component be end-block aqueous polyurethane, the soft chain segment in its molecule can be good at improving the toughness of coating.Purposes according to coating is different, can change to realize hardness and flexible through the ratio of said water-borne acrylic resin of allotment and said aqueous polyurethane, enlarges the use range of coating.
Further; Reactive organosilicon in said coating can be participated in polymer reaction; Make part segment and polymer segment react; Be intertwined with the polymer coating film molecular chain, when improving the polymer surfaces performance, a large amount of migrations can not take place, make performances such as sticking power, hardness, curing speed improve.
Preferably, said water-borne acrylic resin is the vinyl resin of hydroxyl, and solid content is 40%-70%, and particle diameter is 60-100nm.
Need to prove that said water-borne acrylic resin is polymerized by the acrylic ester monomer of hydroxy functional groups and the acrylic ester monomer of hydroxy functional groups not.Further, the acrylic ester monomer of said hydroxy functional groups is selected from any or the combination in Hydroxyethyl acrylate, Propylene glycol monoacrylate, Rocryl 400, methylacrylic acid hydroxyl propyl ester and the methylacrylic acid hydroxy butyl ester; The acrylic ester monomer of said not hydroxy functional groups is selected from any or the combination in methyl acrylate, ethyl propenoate, Bing Xisuandingzhi, TEB 3K, n-BMA and the Jia Jibingxisuanyizhi.
Preferably, said solidifying agent is a POLYMETHYLENE POLYPHENYLISOCYANATE, and-NCO content is 15%-20%.
Need to prove that said solidifying agent must just add before applying use.
Preferably, said aqueous polyurethane is end-blocked aqueous polyurethane, and solid content is 10%-15%.
Need to prove that said end-blocked aqueous polyurethane is the soft component of coating.Because end group do not contain-OH and-COOH isoreactivity group, therefore can not react, only as a kind of flexible blend components that provides with POLYMETHYLENE POLYPHENYLISOCYANATE.
Preferably, said reactive organosilicon is that hydroxy-end capped linearity can be reacted siloxanes.Further, said cosolvent comprises any or the combination in ethylene glycol mono-ether, Ucar 35 monoether, Virahol, butanols and the butanone.
Need to prove that said reactive organosilicon must be to follow polymer reaction, a large amount of migrations can not take place for a long time, little to the complete processing influence.In addition, said reactive organosilicon need dissolve with small amounts of co-solvents before use, makes the reactive organosilicon can be miscible with water.
Preferably, said coating can also add auxiliary agent; Said auxiliary agent is one or more in thinner, flow agent, skimmer, the catalyzer.
Need to prove that said auxiliary agent is not a necessary component of the present invention, can improve speed of response and effect better but in reaction process, correspondingly add auxiliary agent.Further, said auxiliary agent can not react with-NCO group.
Come to describe in more detail the present invention through embodiment below.
Embodiment 1
Present embodiment is used for explaining preparation method for coating of the present invention.
The step of making coating is:
(1) 3 parts of organic silicons are answered in negate, and add 2 parts of cosolvent Virahols to it, after the dissolving of question response organic silicon, obtain reactive organic silicon solution, and are subsequent use;
(2) the water intaking based acrylic resin stirs for 35 parts, adds 17 parts of nano-calcium carbonates, 35 parts of aqueous polyurethanes, said organic silicon solution and solidifying agent POLYMETHYLENE POLYPHENYLISOCYANATE successively to said water-borne acrylic resin while stirring and mixes for 20 parts, obtains coating;
(3) said coating is coated in product surface;
(4) the said product that scribbles coating being sent into 70 ℃ drying oven is cured.
This paint adhesion is strong, and paint film appearance is plentiful, and is smooth bright and clean, the paint film good toughness, and scratch resistance is high, has satisfactory stability property.
Embodiment 2
In the step (2) of embodiment 1, increase a small amount of flow agent, skimmer and catalyzer, all the other are identical with the method for embodiment 1.
This coating effect and embodiment 1 are basic identical, but owing to added corresponding adjuvants, speed of response is faster.
Embodiment 3
Part components contents among the embodiment 1 is changed into: water-borne acrylic resin: 50 parts; Solidifying agent POLYMETHYLENE POLYPHENYLISOCYANATE: 30 parts; Nano-calcium carbonate: 25 parts; Aqueous polyurethane: 20 parts; Reactive organosilicon: 5 parts; 3 parts of cosolvent Virahols; All the other are identical with the method for embodiment 1.
This paint adhesion is strong, and paint film appearance is plentiful, and is smooth bright and clean, and wherein hardness is particularly outstanding, has satisfactory stability property.Be applicable to the hardness requirement high product.
Embodiment 4
Part components contents among the embodiment 1 is changed into: water-borne acrylic resin: 50 parts; Solidifying agent POLYMETHYLENE POLYPHENYLISOCYANATE: 30 parts; Nano-calcium carbonate: 10 parts; Aqueous polyurethane: 20 parts; Reactive organosilicon: 1 part; 1 part of cosolvent Virahol; All the other are identical with the method for embodiment 1.
This paint adhesion is strong, and paint film appearance is plentiful, and is smooth bright and clean, and hardness is high, has satisfactory stability property.
Embodiment 5
Part components contents among the embodiment 1 is changed into: water-borne acrylic resin: 20 parts; Solidifying agent POLYMETHYLENE POLYPHENYLISOCYANATE: 13 parts; Nano-calcium carbonate: 20 parts; Aqueous polyurethane: 50 parts; Reactive organosilicon: 5 parts; 3 parts of cosolvent Virahols; All the other are identical with the method for embodiment 1.
This paint adhesion is strong, and paint film appearance is plentiful, and is smooth bright and clean, and ductility is good, stable in properties property.
Embodiment 6
Part components contents among the embodiment 1 is changed into: water-borne acrylic resin: 20 parts; Solidifying agent POLYMETHYLENE POLYPHENYLISOCYANATE: 10 parts; Nano-calcium carbonate: 10 parts; Aqueous polyurethane: 50 parts; Reactive organosilicon: 1 part; 1 part of cosolvent Virahol; All the other are identical with the method for embodiment 1.
This paint adhesion is strong, and paint film appearance is plentiful, and is smooth bright and clean, and wherein ductility is particularly outstanding, has satisfactory stability property.Be applicable to the toughness reguirements high product.
Performance test
The sticking power test:
The method of inspection: GB/T9286-1998;
Quality index: being divided into is six grades, and 0,1,2 grade is qualified.3,4,5 grades is defective.
The impact resistance performance test:
The method of inspection: GB/T1732-1993;
Quality index: do not cause single ㎝ of the high degree of paint film destructive with 1000g ± 1g weight vertical drop) be index, it is qualified that the multilayer thickness requires >=30 ㎏ ㎝.
Hardness test:
The method of inspection: GB/T6739-96;
Quality index: hardness order from high in the end is: 9H＞8H＞6H＞5H＞4H＞3H＞2H＞H＞F＞HB＞B＞2B＞3B＞4B＞5B＞6B.
The ductility test:
The method of inspection: range estimation;
Quality index: paint film does not ftracture to qualified.
Paint film appearance:
The method of inspection: range estimation;
Quality index: paint film smooth smooth be qualified.
The coating that embodiment 1-6 is obtained carries out corresponding performance test according to the method described above, and the result who records lists in the table 1.
By on can know that embodiment of the present invention has scratch resistance and good ductility filming of forming of substrate surface behind the paint solidification, appearance is lubricated.Simultaneously according to the difference of coating purposes, the hardness of adjustable coating and tough sex ratio, use range is extensive, and cost is low.
The above is a preferred implementation of the present invention; Should be pointed out that for those skilled in the art, under the prerequisite that does not break away from the principle of the invention; Can also make some improvement and retouching, these improvement and retouching also are regarded as protection scope of the present invention.
Claims (5)
1. a scratch resistance aqueous polyurethane coating is characterized in that, the raw material of said coating comprises following weight part:
Water-borne acrylic resin: 20-50;
Solidifying agent: 10-30;
Nano-calcium carbonate: 10-25;
Aqueous polyurethane: 20-50;
Reactive organosilicon: 1-5;
Cosolvent: 1-3.
2. scratch resistance aqueous polyurethane coating as claimed in claim 1 is characterized in that, said water-borne acrylic resin is the vinyl resin of hydroxyl, and solid content is 40%-70%, and particle diameter is 60-100nm.
3. scratch resistance aqueous polyurethane coating as claimed in claim 1 is characterized in that, comprising:
Said solidifying agent is a POLYMETHYLENE POLYPHENYLISOCYANATE, and-NCO content is 15%-20%;
Said aqueous polyurethane is end-blocked aqueous polyurethane, and solid content is 10%-15%;
Said reactive organosilicon is that hydroxy-end capped linearity can be reacted siloxanes;
Said cosolvent comprises any or the combination in ethylene glycol mono-ether, Ucar 35 monoether, Virahol, butanols and the butanone.
4. the preparation method of a scratch resistance aqueous polyurethane coating is characterized in that, the raw material of said coating comprises following weight part:
Water-borne acrylic resin: 20-50;
Solidifying agent: 10-30;
Nano-calcium carbonate: 10-25;
Aqueous polyurethane: 20-50;
Reactive organosilicon: 1-5;
Cosolvent: 1-3;
The preparation method of said coating may further comprise the steps:
(1) said cosolvent is added in the said reactive organosilicon, obtain organic silicon solution;
(2) said water-borne acrylic resin is mixed with organic silicon solution and the solidifying agent that nano-calcium carbonate, aqueous polyurethane, step (1) obtain successively, obtain coating.
5. the preparation method of scratch resistance aqueous polyurethane coating as claimed in claim 4 is characterized in that, comprising:
Said water-borne acrylic resin is the vinyl resin of hydroxyl, and solid content is 40%-70%, and particle diameter is 60-100nm;
Said solidifying agent is a POLYMETHYLENE POLYPHENYLISOCYANATE, and-NCO content is 15%-20%;
Said aqueous polyurethane is end-blocked aqueous polyurethane, and solid content is 10%-15%;
Said reactive organosilicon is that hydroxy-end capped linearity can be reacted siloxanes;
Said cosolvent comprises any or the combination in ethylene glycol mono-ether, Ucar 35 monoether, Virahol, butanols and the butanone.