CN102558930A - Surface coating with both hydrophobicity and oleophobic property and touch control panel - Google Patents
Surface coating with both hydrophobicity and oleophobic property and touch control panel Download PDFInfo
- Publication number
- CN102558930A CN102558930A CN2010106240903A CN201010624090A CN102558930A CN 102558930 A CN102558930 A CN 102558930A CN 2010106240903 A CN2010106240903 A CN 2010106240903A CN 201010624090 A CN201010624090 A CN 201010624090A CN 102558930 A CN102558930 A CN 102558930A
- Authority
- CN
- China
- Prior art keywords
- hydrophobicity
- topcoating
- oleophobic property
- group
- concurrently
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a surface coating with both hydrophobicity and oleophobic property and a touch control panel coated by the surface coating. The surface coating comprises nano particles of chemical structures shown as formula (I): R1 may be halogen, hydrogen, alkyl, alkoxy, hydroxyl, alkenyl, alkyne, acyl, acryl, carboxyl, alkoxycarbonyl or aromatic oxycarbonyl, R2 may be a fluorine-containing group. The touch control panel comprises a conductive layer or an outer cover plate coated by the surface coating with both hydrophobicity and oleophobic property. When the surface coating is coated on the outer cover plate or the conductive layer of the touch control panel, the touch control panel is easy to clean, can resist greasy dirt, can prevent fingerprint generation, and has excellent anti-glare properties by virtue of the excellent hydrophobicity and oleophobic property of the surface coating.
Description
Technical field
The contact panel that the present invention relates to a kind of topcoating and use this topcoating coating, particularly a kind of contact panel that possesses the topcoating of hydrophobicity and oleophobic property and use this topcoating.
Background technology
Compared to traditional input unit; Contact panel is available for users to directly use finger that electronic installation is carried out various instructions with the mode of intuitive operation; And then good human-computer interaction performance is provided, and possess simultaneously that operating speed is fast, tolerance range is high and advantage such as volume is little.Therefore, contact panel replaces like input units such as keyboard, mouses gradually, is widely used in like consumption electronic products such as PC, device for mobile communication, portable electronic device or e-book.Present stage, contact panel most on the market uses resistance-type and two big types of induction technologies of condenser type.
With electric resistance touch-control panel, its structure mainly comprises two indium tin oxides (Indium TinOxide, be called for short ITO) film and a plurality of point-like spacer, and this point-like spacer is positioned between this ito thin film, it is separated and keeps certain distance.When pressing this ito thin film, the user will produce conducting.At this moment, sensor can obtain pressing the coordinate of position by resistance change.Yet, because electric resistance touch-control panel uses ito thin film, shortcomings such as transparence is not good, not scratch resistance that it has, and press for a long time and make easily that also ito thin film deforms.
The development of capacitance type touch-control panel is for improving above-mentioned shortcoming; It can be divided into surface-type and projection type according to the structure difference; The former comprises that a glass baseplate and is located at the conduction plated film on this glass baseplate; Cover by an electrode pattern and an abrasion resisting layer in regular turn again on this conduction plated film; This kind contact panel provides voltage in four corners and forms uniform electric field in the surface, and when user's finger touches can cause electric field change during to panel, unit can be learnt touch position through the size of current ratio in detection corner.The latter is provided with one to be processed and be the electrode layer of arranged by ITO on a glass baseplate, when panel is pressed by the user, the electric capacity of this electrode layer will change, and can detect touch position thus.
No matter use which kind of contact panel of being developed of technology, the user all directly contact surface plate surface input order perhaps operate and the surface that dust that the user points or oil stain will adhere to contact panel easily, and possibly stay fingerprint or vestige.Therefore, will produce dirtyly, and and then influence the appearance of contact panel, and cause the user to be difficult for the information of distinguishing that contact panel shows, also possibly cause the decline of Operational Figure Of Merit in contact panel.In addition, under strong illumination, specular surface causes dazzle to let the user can't read contact panel institute picture displayed smoothly easily.
Summary of the invention
Main purpose of the present invention; Be to provide a kind of topcoating that has hydrophobicity and oleophobic property effect concurrently; After this topcoating is coated traditional contact panel surface, easy residual contaminants in the time of can overcoming traditional contact panel because of operation, and influence its outward appearance and cause the user to be difficult for differentiating the problem of demonstration information and sensitivity decline; In addition, also can solve traditional contact panel produces dazzle easily under high light problem.
Second purpose of the present invention is to provide a kind of aforementioned contact panel that has the topcoating of hydrophobicity and oleophobic property concurrently that is coated with, and this contact panel includes one and supplies the conductive layer of this topcoating coating.
The 3rd purpose of the present invention is to provide another kind to be coated with the aforementioned contact panel that has the topcoating of hydrophobicity and oleophobic property concurrently, and this contact panel includes one and supplies the outer cover plate of this topcoating coating.
For reaching above-mentioned purpose, the present invention provides a kind of topcoating that has hydrophobicity and oleophobic property effect concurrently, and this topcoating includes a nano particle suc as formula chemical structure shown in (I):
Wherein, R
1For being selected from the group that is formed by halogen, hydrogen, alkyl, alkoxyl group, hydroxy, thiazolinyl, alkynyl, acyl group, aromatic base, carboxyl, carbalkoxy and fragrant oxygen carbonyl, R
2It is a fluoro-containing group.
Further, said R
1For be selected from-H ,-OH ,-OCH
3,-OC
2H
5,-CH
3,-CH=CH
2,-OC
2H
4OCH
3And-C
3H
6COOC
2H
5The group that is formed.
Further, said R
2The group that fluorine polyamide-based, fluorine are polyimide-based in order to be selected from, fluoro benzoyl, fluoroalkyl, fluorine are silica-based, methyl fluoride, 3-chloro-4-fluoroanilino, perfluoroalkyl alcohol ethoxy and the hot sulfonamido of N-perfluor are formed.
Further, said R
2Be Fn, n is the integer greater than 1.
Further, the particle diameter of the nano particle of chemical structure shown in the said formula (I) is between between the 100nm to 200nm.
A kind of contact panel, said contact panel are coated with the aforementioned topcoating that has hydrophobicity and oleophobic property concurrently, and include the aforementioned conductive layer that has the topcoating coating of hydrophobicity and oleophobic property concurrently of a confession.
Further, the material of said conductive layer is to be selected from the group that is made up of tin indium oxide, antimony tin, aluminum zinc oxide and indium zinc oxide.
A kind of contact panel, said contact panel are coated with the aforementioned topcoating that has hydrophobicity and oleophobic property concurrently, and include the said outer cover plate that has the topcoating coating of hydrophobicity and oleophobic property concurrently of a confession.
Further, the material of said outer cover plate is to be selected from the group that is made up of glass, polymethylmethacrylate, SE, polycarbonate, polyethyleneterephthalate and pi.
Hence one can see that, the invention provides a kind of topcoating that has hydrophobicity and oleophobic property effect concurrently, and this topcoating includes a nano particle suc as formula (I):
Wherein, R
1For being selected from the group that is formed by halogen, hydrogen, alkyl, alkoxyl group, hydroxy, thiazolinyl, alkynyl, acyl group, aromatic base, carboxyl, carbalkoxy and fragrant oxygen carbonyl, R
2It is a fluoro-containing group.
In sum, the present invention's topcoating of having hydrophobicity and oleophobic property concurrently is compared to the beneficial effect that known technology reaches:
One, topcoating of the present invention has good hydrophobicity, so that water droplet will be difficult for will be attached to it, and can let the user clean easily;
Two, because topcoating of the present invention has good oleophobic property simultaneously, oil stain or pollutent all are difficult for attached to it, therefore, can avoid fingerprint and smeary residual, and keep its clean appearance;
Three, topcoating of the present invention can firmly be attached to the conductive layer or the outer cover plate of contact panel by the functionalized silicon group, therefore can avoid causing polluting human body or problem of environment owing to peeling off of this topcoating;
Four, the present invention have hydrophobicity and oleophobic property concurrently topcoating after coating, can present the anti-dazzle characteristic of excellence by the globosity characteristic of this nano particle itself.
Embodiment
The present invention discloses a kind of topcoating that has hydrophobicity and oleophobic property concurrently, includes a nano particle suc as formula chemical structure shown in (I):
R
1Can be halogen, hydrogen, alkyl, alkoxyl group, hydroxy, thiazolinyl, alkynyl, acyl group, aromatic base, carboxyl, carbalkoxy or fragrant oxygen carbonyl, wherein, R
1Preferably be-H ,-OH ,-OCH
3,-OC
2H
5,-CH
3,-CH=CH
2,-OC
2H
4OCH
3Or-C
3H
6COOC
2H
5R
2Then be a fluoro-containing group, wherein, R
2Preferably can be Fn, n is the integer greater than 1.Perhaps, R
2Can be that fluorine polyamide-based, fluorine are polyimide-based, fluoro benzoyl, fluoroalkyl, fluorine are silica-based, methyl fluoride, 3-chloro-4-fluoroanilino, perfluoroalkyl alcohol ethoxy or the hot sulfonamido of N-perfluor.
The topcoating that the present invention has hydrophobicity and oleophobic property concurrently can add stablizer by the compound of siliceous functional group (SiOx) and use sol-gel (sol-gel) technology to prepare.Wherein, each molecule of Sol-gel States will form excess molecule (superamolecular) because of the interaction of non covalent bonds such as therebetween hydrogen bond, Van der Waals force, co-ordination bond, thereby have high uniformity, polymolecularity and high stability.When adding stablizer in aforementioned Sol-gel States, but the restricted part particle continue to increase, and then form a plurality of nano particles transparent and spherical in shape.This stablizer can be organic amine (like trioctylamine; Octylame; Amino dodecane; Hexylamine; Pyridine; Oleyl amine; Quaternary ammonium group); Thio-alcohol is (like spicy thioalcohol; Dodecyl Mercaptan; Thiophenol); Organic phosphates is (like triphenyl phosphorus; Tributyl phosphorus; Trioctylphosphine phosphorus); Acids is (like sulfuric acid; Nitric acid; Hydrochloric acid; Acetic acid); Bases is (like sodium hydroxide; Pottasium Hydroxide; Volatile caustic); Organic alcohols is (like methyl alcohol; Ethanol; Terepthaloyl moietie; Propyl alcohol; Virahol) or alkyls (like methane; Ethane; Propane; Butane; Pentane; Hexane; Heptane; Octane; Dodecyl; Tridecane; The tetradecane; Pentadecane; N-Hexadecane; Heptadecane; Octadecane) or sodium sulfate.In addition, in the present invention, the particle diameter of this nano particle is between between the 100nm to 200nm.
On using; The topcoating that the present invention has hydrophobicity and oleophobic property concurrently can use on a contact panel; For example, this topcoating can coat on the conductive layer of this contact panel and form one comprise this nano particle antibiotic layer, the material of this conductive layer can be tin indium oxide (Indium Tin Oxide; Abbreviation ITO), antimony tin (Antimony Tin Oxide; Abbreviation ATO), aluminum zinc oxide (Aluminum Zinc Oxide is called for short AZO) or indium zinc oxide (Indium Zinc Oxide is called for short IZO); Perhaps; This topcoating can coat on the outer cover plate of a contact panel and form one comprise this nano particle antibiotic layer; The material of this outer cover plate can be glass, polymethylmethacrylate (Polymethylmethacrylate is called for short PMMA), SE (Polyvinyl chloride is called for short PVC), polycarbonate (Polycarbonate; Abbreviation PC), polyethyleneterephthalate (Polyethylene terephthalate is called for short PET) or pi (Polyimide).Coat the surface of this outer cover plate or this conductive layer when this topcoating after; Can heat this topcoating; Heating temperature is between 25 ℃ to 250 ℃; Functionalized silicon group during heating in this nano particle can form chemical covalent linkage with surface in contact, makes this antibiotic layer be able to firmly be attached to surface in contact and difficult drop-off.
The topcoating that relevant the present invention has hydrophobicity and oleophobic property concurrently is applied to the implementation method of contact panel, with and hydrophobicity, oleophobic property and anti-glare effect, illustrate as follows:
Embodiment one:
The making flow process of the present invention's one preferred embodiment: at first, this topcoating is directly coated on the outer cover plate, the material of this outer cover plate is PMMA; Or earlier this topcoating is diluted with organic solvents such as alcohols, ketone, ethers or benzene classes; Wherein, Alcohol organic solvent can be Virahol (Isopropanol) or ethanol (Ethanol); And dilute strength can be 1000 times, and the concentration of promptly controlling this topcoating is 0.1% concentration expressed in percentage by volume.Dilution is that this topcoating is mixed with this organic solvent and this mixing solutions is imposed even stirring, stirring can take as the mechanical type blade stir, stirrer rotation, mode such as concussion or drum-type rolling up and down.After this mixing solutions reaches stable high uniformity and polymolecularity; Again this mixing solutions is applied to this outer cover plate, coating method can be spray-type coating (Spray coating), immersion plating formula coating (Dipcoating), drum-type coating (Roll coating), printing-type coating (Print coating) or rotary coating (Spin coating).Then, this outer cover plate placed under 25 ℃ to 250 ℃ the temperature environment heating at least 1 minute, this topcoating is attached on this outer cover plate, again with its cooling.Wherein, the glossiness that is coated with this outer cover plate of this topcoating can be controlled in the scope between 15 to 150GU (the Gloss Unit).
Embodiment two:
Carry out surface test to being coated with the outer cover plate that the present invention has the topcoating of hydrophobicity and oleophobic property concurrently, surface test comprises that the fingerprint of surface energy test, drop particle diameter test, oil droplet size test and glossiness pushes test, and its result is as follows:
(1) surface energy test:
Carry out surface energy test with dyne pen (Dyne Test Pen) (also being called the corona test pen), be coated with the surface energy of outer cover plate of topcoating that the present invention has hydrophobicity and oleophobic property concurrently for less than 30dynes/cm; And the surface energy of general glass baseplate is 47dynes/cm, has lower surface energy so be coated with the outer cover plate of topcoating of the present invention.
(2) drop particle diameter test:
Prepare 20 chip sizes and be 5cm * 5cm and be coated with the present invention to have the outer cover plate (experimental group) of the topcoating of hydrophobicity and oleophobic property and uncoated outer cover plate (control group) concurrently; Then the water droplet of 0.1c.c. is placed the surface of the outer cover plate of experimental group and control group; And measure the size of this water droplet in this outer cover plate surface, tabular is following as a result for it:
| Group | Control group (mm 2) | Experimental group (mm 2) |
| 1 | 0.6 | 0.4 |
| 2 | 0.5 | 0.4 |
| 3 | 0.5 | 0.4 |
| 4 | 0.5 | 0.4 |
| 5 | 0.5 | 0.4 |
| 6 | 0.5 | 0.3 |
| 7 | 0.6 | 0.5 |
| 8 | 0.6 | 0.4 |
| 9 | 0.5 | 0.4 |
| 10 | 0.5 | 0.4 |
| 11 | 0.5 | 0.4 |
| 12 | 0.5 | 0.4 |
| 13 | 0.5 | 0.3 |
| 14 | 0.7 | 0.4 |
| 15 | 0.5 | 0.4 |
| 16 | 0.6 | 0.4 |
| 17 | 0.5 | 0.4 |
| 18 | 0.5 | 0.3 |
| 19 | 0.6 | 0.4 |
| 20 | 0.5 | 0.4 |
Can know that by aforementioned result the average drop particle diameter of experimental group is less than 0.4mm
2, the average drop particle diameter of control group then is about 0.5mm
2, therefore, compared to control group, the outer cover plate that is coated with topcoating of the present invention has preferable hydrophobicity.
(3) oil droplet size test:
Prepare 20 chip sizes and be 5cm * 5cm and be coated with the present invention to have the outer cover plate (experimental group) of the topcoating of hydrophobicity and oleophobic property and uncoated outer cover plate (control group) concurrently; Then the oil droplet of 0.1c.c. is placed the surface of the outer cover plate of experimental group and control group; And measure the size of this oil droplet in this outer cover plate surface, tabular is following as a result for it:
| Group | Control group (mm 2) | Control group (mm 2) |
| 1 | 50 | 9 |
| 2 | 40 | 9 |
| 3 | 50 | 9 |
| 4 | 50 | 8 |
| 5 | 50 | 9 |
| 6 | 45 | 9 |
| 7 | 50 | 9 |
| 8 | 45 | 8 |
| 9 | 40 | 8 |
| 10 | 50 | 8 |
| 11 | 50 | 9 |
| 12 | 50 | 9 |
| 13 | 50 | 9 |
| 14 | 50 | 9 |
| 15 | 50 | 9 |
| 16 | 55 | 8 |
| 17 | 50 | 9 |
| 18 | 45 | 9 |
| 19 | 40 | 8 |
| 20 | 50 | 9 |
Can know that by aforementioned result the mean oil droplet particle diameter of experimental group is less than 9mm
2, the then about 50mm of the mean oil droplet particle diameter of control group
2, therefore, compared to control group, the outer cover plate that is coated with topcoating of the present invention has preferable oleophobic property.
(4) fingerprint is pushed test:
To prepare 20 chip sizes be 5cm * 5cm and be coated with the outer cover plate that the present invention has the topcoating of hydrophobicity and oleophobic property concurrently; This outer cover plate is tested with Grossmeters (gloss meter) earlier; Then this outer cover plate being carried out fingerprint pushes; And then with the Grossmeters test, the tabular as a result of its glossiness (GU) is following:
| Group | Before pushing (GU) | Push back (GU) |
| 1 | 110 | 110 |
| 2 | 110 | 110 |
| 3 | 111 | 111 |
| 4 | 110 | 111 |
| 5 | 110 | 111 |
| 6 | 115 | 113 |
| 7 | 110 | 110 |
| 8 | 110 | 110 |
| 9 | 120 | 120 |
| 10 | 110 | 110 |
| 11 | 110 | 111 |
| 12 | 115 | 115 |
| 13 | 110 | 110 |
| 14 | 110 | 110 |
| 15 | 110 | 110 |
| 16 | 110 | 110 |
| 17 | 115 | 116 |
| 18 | 110 | 110 |
| 19 | 110 | 110 |
| 20 | 115 | 115 |
Can know that by aforementioned result apply the outer cover plate of topcoating that the present invention has hydrophobicity and oleophobic property concurrently after pushing through fingerprint, its glossiness (GU) still can maintain about 110.
Result according to above-mentioned kinds of surface test; Coating the present invention has the outer cover plate of the topcoating of hydrophobicity and oleophobic property concurrently; Demonstrate good hydrophobicity and oleophobic property, make the globule can be by wiping easily and do not stay water stainly, reach the effect of easy cleaning; And the fingerprint oil stain also is difficult for being built-up in this outer cover plate because of its oleophobic property, so have the effect of anti-fingerprint.
Embodiment three:
Carry out the weather-proof test of glossiness to being coated with the outer cover plate that the present invention has the topcoating of hydrophobicity and oleophobic property concurrently; Weather-proof test comprises high temperature test (high temperature test), low-temperature test (lowtemperature test), high humidity test (high humidity test) and thermal shock test (thermal shocktest), and its result is as follows:
(1) high temperature test:
To prepare 20 chip sizes be 5cm * 5cm and be coated with the outer cover plate that the present invention has the topcoating of hydrophobicity and oleophobic property concurrently; This outer cover plate is tested with Grossmeters (Gloss meter) earlier; Then under 80 ℃ environment, carry out 200 hours pyroprocessing; And then with the Grossmeters test, the tabular as a result of its glossiness (GU) is following:
| Group | Before the pyroprocessing (GU) | After the pyroprocessing (GU) |
| 1 | 110 | 111 |
| 2 | 115 | 115 |
| 3 | 111 | 110 |
| 4 | 110 | 110 |
| 5 | 109 | 110 |
| 6 | 115 | 113 |
| 7 | 115 | 117 |
| 8 | 115 | 115 |
| 9 | 110 | 119 |
| 10 | 110 | 110 |
| 11 | 110 | 110 |
| 12 | 115 | 115 |
| 13 | 110 | 110 |
| 14 | 115 | 115 |
| 15 | 110 | 110 |
| 16 | 115 | 115 |
| 17 | 115 | 116 |
| 18 | 110 | 111 |
| 19 | 110 | 110 |
| 20 | 110 | 110 |
(2) low-temperature test:
To prepare 20 chip sizes be 5cm * 5cm and be coated with the outer cover plate that the present invention has the topcoating of hydrophobicity and oleophobic property concurrently; This outer cover plate is tested with Grossmeters (Gloss meter) earlier; Then under-40 ℃ environment, carry out 150 hours subzero treatment; And then with the Grossmeters test, the tabular as a result of its glossiness (GU) is following:
| Group | Before the subzero treatment (GU) | After the subzero treatment (GU) |
| 1 | 115 | 115 |
| 2 | 115 | 115 |
| 3 | 115 | 116 |
| 4 | 110 | 110 |
| 5 | 109 | 110 |
| 6 | 115 | 115 |
| 7 | 110 | 115 |
| 8 | 115 | 115 |
| 9 | 110 | 110 |
| 10 | 112 | 115 |
| 11 | 110 | 110 |
| 12 | 115 | 117 |
| 13 | 110 | 110 |
| 14 | 115 | 110 |
| 15 | 110 | 110 |
| 16 | 115 | 115 |
| 17 | 116 | 117 |
| 18 | 110 | 110 |
| 19 | 110 | 110 |
| 20 | 110 | 110 |
(3) high humidity test:
To prepare 20 chip sizes be 5cm * 5cm and be coated with the outer cover plate that the present invention has the topcoating of hydrophobicity and oleophobic property concurrently; This outer cover plate is tested with Grossmeters (gloss meter) earlier; Then insert temperature and be 50 ℃ and relative humidity and be under 90% the environment and carry out 200 hours high humidity treatment; And then with the Grossmeters test, the tabular as a result of its glossiness (GU) is following:
| Group | Before the high humidity treatment (GU) | After the high humidity treatment (GU) |
| 1 | 110 | 110 |
| 2 | 105 | 105 |
| 3 | 111 | 111 |
| 4 | 110 | 110 |
| 5 | 109 | 110 |
| 6 | 110 | 110 |
| 7 | 110 | 110 |
| 8 | 115 | 115 |
| 9 | 109 | 110 |
| 10 | 110 | 110 |
| 11 | 110 | 111 |
| 12 | 115 | 115 |
| 13 | 110 | 110 |
| 14 | 115 | 115 |
| 15 | 110 | 110 |
| 16 | 115 | 115 |
| 17 | 115 | 116 |
| 18 | 110 | 110 |
| 19 | 110 | 110 |
| 20 | 105 | 105 |
(4) thermal shock test:
To prepare 20 chip sizes be 5cm * 5cm and be coated with the outer cover plate that the present invention has the topcoating of hydrophobicity and oleophobic property concurrently; This outer cover plate is tested with Grossmeters (gloss meter) earlier; Then temperature be 80 ℃ and time be 15 minutes pyroprocessing and temperature for-40 ℃ of times be 30 minutes subzero treatment between alternate cycles 40 times; And then with the Grossmeters test, the tabular as a result of its glossiness (GU) is following:
| Group | Before thermal shock is handled (GU) | Thermal shock is handled back (GU) |
| 1 | 115 | 116 |
| 2 | 115 | 115 |
| 3 | 110 | 111 |
| 4 | 110 | 110 |
| 5 | 109 | 110 |
| 6 | 115 | 115 |
| 7 | 110 | 110 |
| 8 | 115 | 115 |
| 9 | 109 | 110 |
| 10 | 110 | 110 |
| 11 | 110 | 110 |
| 12 | 107 | 110 |
| 13 | 110 | 109 |
| 14 | 115 | 116 |
| 15 | 110 | 110 |
| 16 | 115 | 115 |
| 17 | 115 | 115 |
| 18 | 110 | 110 |
| 19 | 110 | 110 |
| 20 | 115 | 115 |
According to the result of above-mentioned multiple atmospheric exposure test, be coated with the outer cover plate that the present invention has the topcoating of hydrophobicity and oleophobic property concurrently, after handling through pyroprocessing, subzero treatment, high humidity treatment or thermal shock, still can keep good anti-glare effect.
In sum, topcoating of the present invention has good hydrophobicity and oleophobic property, can reach the effect that is prone to cleaning and oil rub resistance simultaneously, and utilizes the globosity characteristic of its nano particle, can provide this topcoating performance good anti-dazzle function.In addition; By the functionalized silicon group in this nano particle; This topcoating can firmly be attached on the outer cover plate or conductive layer of contact panel with chemical covalent linkage, makes this topcoating be difficult for the increase of duration of service coming off from surface in contact and loses its antibacterial ability.
Claims (9)
1. topcoating that has hydrophobicity and oleophobic property concurrently is characterized in that including:
One nano particle suc as formula chemical structure shown in (I):
Wherein, R
1For being selected from the group that is formed by halogen, hydrogen, alkyl, alkoxyl group, hydroxy, thiazolinyl, alkynyl, acyl group, aromatic base, carboxyl, carbalkoxy and fragrant oxygen carbonyl, R
2It is a fluoro-containing group.
2. have the topcoating of hydrophobicity and oleophobic property according to claim 1 concurrently, it is characterized in that said R
1For be selected from-H ,-OH ,-OCH
3,-OC
2H
5,-CH
3,-CH=CH
2,-OC
2H
4OCH
3And-C
3H
6COOC
2H
5The group that is formed.
3. have the topcoating of hydrophobicity and oleophobic property according to claim 1 concurrently, it is characterized in that said R
2The group that fluorine polyamide-based, fluorine are polyimide-based in order to be selected from, fluoro benzoyl, fluoroalkyl, fluorine are silica-based, methyl fluoride, 3-chloro-4-fluoroanilino, perfluoroalkyl alcohol ethoxy and the hot sulfonamido of N-perfluor are formed.
4. have the topcoating of hydrophobicity and oleophobic property according to claim 1 concurrently, it is characterized in that said R
2Be Fn, n is the integer greater than 1.
5. have the topcoating of hydrophobicity and oleophobic property according to claim 1 concurrently, the particle diameter that it is characterized in that the nano particle of chemical structure shown in the said formula (I) is between between the 100nm to 200nm.
6. a contact panel is characterized in that said contact panel is coated with the said topcoating that has hydrophobicity and oleophobic property concurrently of claim 1, and includes the said conductive layer that has the topcoating coating of hydrophobicity and oleophobic property concurrently of a confession.
7. like the said contact panel of claim 6, the material that it is characterized in that said conductive layer is to be selected from the group that is made up of tin indium oxide, antimony tin, aluminum zinc oxide and indium zinc oxide.
8. a contact panel is characterized in that said contact panel is coated with the said topcoating that has hydrophobicity and oleophobic property concurrently of claim 1, and includes the said outer cover plate that has the topcoating coating of hydrophobicity and oleophobic property concurrently of a confession.
9. like the said contact panel of claim 8, the material that it is characterized in that said outer cover plate is to be selected from the group that is made up of glass, polymethylmethacrylate, SE, polycarbonate, polyethyleneterephthalate and pi.