CN102558745A - Processing modifier for acrylonitrile-butadiene-styrene/polycarbonate (ABS/PC) alloy waste injection plastic and using method for processing modifier - Google Patents
Processing modifier for acrylonitrile-butadiene-styrene/polycarbonate (ABS/PC) alloy waste injection plastic and using method for processing modifier Download PDFInfo
- Publication number
- CN102558745A CN102558745A CN2011104125163A CN201110412516A CN102558745A CN 102558745 A CN102558745 A CN 102558745A CN 2011104125163 A CN2011104125163 A CN 2011104125163A CN 201110412516 A CN201110412516 A CN 201110412516A CN 102558745 A CN102558745 A CN 102558745A
- Authority
- CN
- China
- Prior art keywords
- abs
- alloy
- injection molding
- molding material
- modifier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing modifier for acrylonitrile-butadiene-styrene/polycarbonate (ABS/PC) alloy waste injection plastic and a using method for the processing modifier. The processing modifier comprises the following components in part by weight: 1.5 to 2.5 parts of chlorinated polyethylene and 4 to 8 parts of high glue powder. The using method comprises the following steps of: 1, processing the ABS/PC alloy waste injection plastic; 2, detecting the melt flow index of the ABS/PC alloy waste injection plastic; 3, preparing the ABS/PC alloy waste injection plastic, the chlorinated polyethylene and the high glue powder in a ratio of 100:(1.5-2.5):(4-8), uniformly putting into a mixer, starting the mixer at normal temperature, and stopping the mixer after 10 to 15 minutes; and 4, discharging, and packaging. The invention has the advantages that: the process is reasonable, the processing modifier is easy to process, the physicochemical property of the ABS/PC alloy waste injection plastic can be effectively improved, product quality is improved, and the like. The processing modifier can be widely used for the modification processing of the ABS/PC alloy waste injection plastic.
Description
Technical field
The present invention relates to a kind of processing of plastic properties-correcting agent and method of use of being used for, particularly relate to the modifier and the method for use thereof of the useless injection molding material of a kind of ABS/PC of being used for alloy.
Background technology
ABS/PC is the english abbreviation of acrylonitrile-styrene-butadienecopolymer/polycarbonate.As everyone knows, the useless injection molding material processing means of existing ABS/PC alloy is outmoded, technology falls behind, and the product physical and chemical performance of producing is lower, second-rate, can not satisfy the demands of consumers, and also can not adapt to the demand of market development, thereby limits its range of application.
Summary of the invention
The objective of the invention is in order to overcome the deficiency of above-mentioned background technology concentrating on studies and, the modifier and the method for use thereof of the useless injection molding material of a kind of ABS/PC of being used for alloy is provided through the contriver through producing actual repeated validation.
To achieve these goals, technical scheme of the present invention is such:
A kind of modifier that is used for the useless injection molding material of ABS/PC alloy provided by the invention, described modifier comprises following component and weight part thereof: chlorinatedpolyethylene 1.5～2.5, high glue powder 4～8.
In technique scheme, described modifier comprises following component and weight part thereof: chlorinatedpolyethylene 2, high glue powder 6.
A kind of method of use that is used for the modifier of the useless injection molding material of ABS/PC alloy provided by the invention; May further comprise the steps: step 1, the useless injection molding material water of ABS/PC alloy is cleaned; Remove foreign material and dust; To remove the useless injection molding material of clean ABS/PC alloy again and be broken into the close material of size, subsequent use; The melt flow index of step 2, the useless injection molding material of detection ABS/PC alloy, setting melt flow index M1 is 0.5～3.0; Step 3, the useless injection molding material of above-mentioned subsequent use ABS/PC alloy is dropped in the mixing machine; Again in the preparation of following ratio: the ABS/PC alloy injection molding material that gives up: chlorinatedpolyethylene: high glue powder=100: 1.5～2.5: 4～8; Mixing drops in the mixing machine, and start is 10～15 minutes under normal temperature condition, shuts down; Step 4, the mixture discharging packing that processes above-mentioned get final product.
In technique scheme, when said melt flow index M1=0.5～0.8, the useless injection molding material of ABS/PC alloy then: chlorinatedpolyethylene: high glue powder=100: 1.5: 4; When said melt flow index M1=0.8～1.5, the useless injection molding material of ABS/PC alloy then: chlorinatedpolyethylene: high glue powder=100: 1.8: 5; When said melt flow index M1=1.5～2.0, the useless injection molding material of ABS/PC alloy then: chlorinatedpolyethylene: high glue powder=100: 2: 6; When said melt flow index M1=2.0～3.0, the useless injection molding material of ABS/PC alloy then: chlorinatedpolyethylene: high glue powder=100: 2.5: 8.
The present invention is alleged is used for the modifier and the method for use thereof of the useless injection molding material of ABS/PC alloy, has following beneficial effect: novel, technology rationally, processing is simple, easy to use, can realize requirement of industrialized batch production.The present invention can improve the physical and chemical performance of the useless injection molding material of ABS/PC alloy effectively, reduces melt flow index, makes material increase toughness and intensity, becomes to have the PP Pipe Compound of producing the injecting products purposes.The present invention can be widely used for the modification processing of the useless injection molding material of ABS/PC alloy.
Embodiment
Below in conjunction with embodiment the present invention is made further detailed description, but this embodiment should not be construed as limitation of the present invention.
Embodiment 1
Modifier of the present invention is prepared by following component and weight part: when melt flow index M1=0.5～0.8 of detecting the useless injection molding material of ABS/PC alloy, then get chlorinatedpolyethylene 1.5, high glue powder 4, and subsequent use; Its method of use is following:
The useless injection molding material water of ABS/PC alloy is cleaned, cuts into the close useless pipe material of size after removing foreign material and dust, get 100 parts subsequent use;
Earlier the useless injection molding material of above-mentioned 100 parts of ABS/PC alloys having handled is dropped in the mixing machine, more above-mentioned 1.5 parts of chlorinatedpolyethylenees, 4 parts of high glue powder mixings are dropped in the mixing machine, start is 10 minutes under normal temperature condition, shuts down, and the discharging packing gets final product.
Embodiment 2
Present embodiment and embodiment 1 are basic identical, and difference is: when described melt flow index M1=0.8～1.5, then get 1.8 parts of chlorinatedpolyethylenees, 5 parts of high glue powders.
In the method for use the useless injection molding material of above-mentioned 100 parts of ABS/PC alloys having handled is dropped in the mixing machine, more above-mentioned 1.8 parts of chlorinatedpolyethylenees, 5 parts of high glue powder mixings are dropped in the mixing machine, start is 12 minutes under normal temperature condition, shuts down, and the discharging packing gets final product.
Embodiment 3
Present embodiment and embodiment 1 are basic identical, and difference is: when described melt flow index M1=1.5～2.0, then get 2 parts of chlorinatedpolyethylenees, 6 parts of high glue powders.
In the method for use the useless injection molding material of above-mentioned 100 parts of ABS/PC alloys having handled is dropped in the mixing machine, more above-mentioned 2 parts of chlorinatedpolyethylenees, 6 parts of high glue powder mixings are dropped in the mixing machine, start is 14 minutes under normal temperature condition, shuts down, and the discharging packing gets final product.
Embodiment 4
Present embodiment and embodiment 1 are basic identical, and difference is: when described melt flow index M1=2.0～3.0, then get 2.5 parts of chlorinatedpolyethylenees, 8 parts of high glue powders.
In the method for use the useless injection molding material of above-mentioned 100 parts of ABS/PC alloys having handled is dropped in the mixing machine, more above-mentioned 2.5 parts of chlorinatedpolyethylenees, 8 parts of high glue powder mixings are dropped in the mixing machine, start is 15 minutes under normal temperature condition, shuts down, and the discharging packing gets final product.
Obviously, those skilled in the art can carry out various changes and modification to the present invention and not break away from the spirit and scope of the present invention.Like this, belong within the scope of claim of the present invention and equivalent technologies thereof if of the present invention these are revised with modification, then the present invention also is intended to comprise these changes and modification interior.
The content of not doing in this specification sheets to describe in detail belongs to this area professional and technical personnel's known prior art.
Claims (4)
1. modifier that is used for the useless injection molding material of ABS/PC alloy, it is characterized in that: described modifier comprises following component and weight part thereof: chlorinatedpolyethylene 1.5～2.5, high glue powder 4～8.
2. the modifier that is used for the useless injection molding material of ABS/PC alloy according to claim 1 is characterized in that: described chlorinatedpolyethylene is 2, high glue powder is 6.
3. method of use that is used for the modifier of the useless injection molding material of ABS/PC alloy is characterized in that: may further comprise the steps:
Step 1, the useless injection molding material water of ABS/PC alloy is cleaned, remove foreign material and dust, will remove the useless injection molding material of clean ABS/PC alloy again and be broken into big or small close material, subsequent use;
The melt flow index of step 2, the useless injection molding material of detection ABS/PC alloy, setting melt flow index M1 is 0.5～3.0;
Step 3, the useless injection molding material of above-mentioned subsequent use ABS/PC alloy is dropped in the mixing machine; Again in the preparation of following ratio: the ABS/PC alloy injection molding material that gives up: chlorinatedpolyethylene: high glue powder=100: 1.5～2.5: 4～8; Mixing drops in the mixing machine, and start is 10～15 minutes under normal temperature condition, shuts down;
Step 4, the mixture discharging packing that processes above-mentioned get final product.
4. the method for use that is used for the modifier of the useless injection molding material of ABS/PC alloy according to claim 4 is characterized in that:
When said melt flow index M1=0.5～0.8, the useless injection molding material of ABS/PC alloy then: chlorinatedpolyethylene: high glue powder=100: 1.5: 4;
When said melt flow index M1=0.8～1.5, the useless injection molding material of ABS/PC alloy then: chlorinatedpolyethylene: high glue powder=100: 1.8: 5;
When said melt flow index M1=1.5～2.0, the useless injection molding material of ABS/PC alloy then: chlorinatedpolyethylene: high glue powder=100: 2: 6;
When said melt flow index M1=2.0～3.0, the useless injection molding material of ABS/PC alloy then: chlorinatedpolyethylene: high glue powder=100: 2.5: 8.