CN102557754A - Formula of opacified glaze - Google Patents
Formula of opacified glaze Download PDFInfo
- Publication number
- CN102557754A CN102557754A CN2011104178300A CN201110417830A CN102557754A CN 102557754 A CN102557754 A CN 102557754A CN 2011104178300 A CN2011104178300 A CN 2011104178300A CN 201110417830 A CN201110417830 A CN 201110417830A CN 102557754 A CN102557754 A CN 102557754A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- opacified
- formula
- opaque
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a formula of opacified glaze. The opacified glaze comprises the following components in part by weight: 5 to 10 parts of zircon sand, 5 to 15 parts of zinc oxide, 5 to 10 parts of boric acid, 10 to 20 parts of potash feldspar, 2 to 5 parts of potassium nitrate, 4 to 10 parts of dolomite, 8 to 15 parts of calcite, 6 to 15 parts of kaolin, and 30 to 40 parts of quartz. According to the formula, the opacified glaze is low in cost, high in adaptability, and suitable for glaze surface decoration of various green bodies; and a glaze surface is good in opacification effect and high in whiteness, and the opacified glaze can be made into glossy, semimat or mat glaze, and has the characteristic of wide firing temperature range.
Description
Technical field
The present invention relates to the prescription of a kind of pottery with the prescription, particularly a kind of opaque glaze of glaze.
Background technology
Opaque glaze is a kind of method of common ceramic decoration, is widely used.Opaque glaze is the White-opalescent bright glaze; It is since exist in the glaze glass different with host glass phase specific refractory power, volume is small the 2nd mutually or the 3rd phase material, thereby when light during through the glaze layer milkiness particle make light produce scattering process to cause the lighttight phenomenon of glaze layer.
Can be divided into 3 types according to milkiness aggregation of particles state opaque glaze: the one, there is the small crystal of some amount in the host glass, be called the crystalline phase opaque glaze; The 2nd, liquid-liquid phase-splitting takes place in the glaze melt in process of cooling, in host glass, isolates the 2nd higher phase glass of the small dispersity of volume, is called the phase-splitting opaque glaze; The 3rd, below the glaze surface layer of glass, there are a large amount of micro-bubbles, be called the gas phase opaque glaze, wherein the crystalline phase opaque glaze is divided into the original grain opaque glaze again and separates out 2 kinds of crystal grain opaque glazes.The former be through add the infusibility material realize the milkiness of glaze the most frequently used the turbid glaze of zirconium arranged; The latter be in sintering process from glaze glass the spontaneous milkiness particle of separating out cause milkiness.At present, opaque glaze widespread use in ceramic industry.Opaque glaze can hide the color and some defective of base substrate, enriches the glaze of ceramic product and decorates, and simultaneously, makes a large amount of inferior raw materials or industrial residue can be used as base and uses raw material.
This has not only reduced production cost in higher-grade raw material exhausted day by day today, resource is used adequately reasonably, and can increases the assortment of product, improves product specification, has therefore received liking of people.In recent years, along with science and technology development, no matter opaque glaze was in research or in application facet; Many breakthroughs are all arranged; Be widely used at present the decoration of sanitary china, architectural pottery and domestic ceramics, make ceramic surface colorful, change all the time, represent personalization.
Summary of the invention
The object of the invention is to provide a kind of prescription of ceramic glaze.
For addressing the above problem; The technical scheme that the present invention adopted is: a kind of prescription of opaque glaze, it comprises the component of following parts by weight: 5 ~ 10 parts of zircon sands, 5 ~ 15 parts in zinc oxide, 5 ~ 10 parts of boric acid, 10 ~ 20 parts of potassium felspar sands, 2 ~ 5 parts in saltpetre, 4 ~ 10 parts of rhombspars, 8 ~ 15 parts in calcite, 6 ~ 15 parts of kaolin, 30 ~ 40 parts in quartz.
The prescription of said opaque glaze comprises the component of following parts by weight: 5 ~ 8 parts of zircon sands, 5 ~ 10 parts in zinc oxide, 5 ~ 7 parts of boric acid, 12 ~ 18 parts of potassium felspar sands, 3 ~ 4 parts in saltpetre, 4 ~ 8 parts of rhombspars, 8 ~ 12 parts in calcite, 6 ~ 12 parts of kaolin, quartzy 30 ~ 35 parts.
The present invention with respect to the beneficial effect of prior art is: the prescription of opaque glaze of the present invention; Cost is low, has wide adaptability, can be applicable to that the glaze of multiple base substrate is decorated; The glaze opaque effect is good; Whiteness is high, can be made into gloss, semi-matt or matt glaze, and this glaze has the wide characteristics of firing range.
Embodiment
Through embodiment the present invention is explained further details below, these embodiment only are used for explaining the present invention, do not limit the scope of the invention.
Embodiment 1Adopt following formulation opaque glaze according to the invention: in the raw material of parts by weight: 5 parts of zircon sands, 15 parts in zinc oxide, 10 parts of boric acid, 10 parts of potassium felspar sands, 2 parts in saltpetre, 4 parts of rhombspars, 10 parts in calcite, 6 parts of kaolin, quartzy 38 parts.
Embodiment 2Adopt following formulation opaque glaze according to the invention: in the raw material of parts by weight: 8 parts of zircon sands, 10 parts in zinc oxide, 8 parts of boric acid, 128 parts of potassium felspar sands, 3 parts in saltpetre, 10 parts of rhombspars, 15 parts in calcite, 8 parts of kaolin, quartzy 35 parts.
Embodiment 3Adopt following formulation opaque glaze according to the invention: in the raw material of parts by weight: 10 parts of zircon sands, 12 parts in zinc oxide, 5 parts of boric acid, 18 parts of potassium felspar sands, 5 parts in saltpetre, 8 parts of rhombspars, 12 parts in calcite, 15 parts of kaolin, quartzy 40 parts.
Embodiment 4Adopt following formulation opaque glaze according to the invention: in the raw material of parts by weight: 7 parts of zircon sands, 5 parts in zinc oxide, 7 parts of boric acid, 20 parts of potassium felspar sands, 4 parts in saltpetre, 6 parts of rhombspars, 8 parts in calcite, 10 parts of kaolin, quartzy 30 parts.
Claims (2)
1. the prescription of an opaque glaze is characterized in that: the component that comprises following parts by weight: 5 ~ 10 parts of zircon sands, 5 ~ 15 parts in zinc oxide, 5 ~ 10 parts of boric acid, 10 ~ 20 parts of potassium felspar sands, 2 ~ 5 parts in saltpetre, 4 ~ 10 parts of rhombspars, 8 ~ 15 parts in calcite, 6 ~ 15 parts of kaolin, 30 ~ 40 parts in quartz.
2. a kind of prescription of opaque glaze according to claim 1 is characterized in that: the component that comprises following parts by weight: 5 ~ 8 parts of zircon sands, 5 ~ 10 parts in zinc oxide, 5 ~ 7 parts of boric acid, 12 ~ 18 parts of potassium felspar sands, 3 ~ 4 parts in saltpetre, 4 ~ 8 parts of rhombspars, 8 ~ 12 parts in calcite, 6 ~ 12 parts of kaolin, quartzy 30 ~ 35 parts.