CN102557745A - Matt frit and preparation method thereof - Google Patents
Matt frit and preparation method thereof Download PDFInfo
- Publication number
- CN102557745A CN102557745A CN2011104160326A CN201110416032A CN102557745A CN 102557745 A CN102557745 A CN 102557745A CN 2011104160326 A CN2011104160326 A CN 2011104160326A CN 201110416032 A CN201110416032 A CN 201110416032A CN 102557745 A CN102557745 A CN 102557745A
- Authority
- CN
- China
- Prior art keywords
- parts
- frit
- zinc oxide
- preparation
- calcite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a matt frit, belonging to the technical field of ceramic production. The matt frit comprises the following components in parts by weight: 25-35 parts of quartz, 25-30 parts of calcite, 10-20 parts of potassium feldspar, 5-8 parts of zinc oxide, 3-8 parts of boric acid, 5-10 parts of zirconium silicate, 2-5 parts of raw talc and 1-3 parts of strontium carbonate. A preparation method comprises the following steps: stirring and mixing the above raw materials uniformly, putting the mixture in a frit furnace to be molten for 6-8 hours at a temperature of 1400-1500 DEG C and quenching the molten liquid with cold water. The matt frit and the preparation method have the following beneficial effects: the matt frit prepared by the method feels like jade, is exquisite and smooth and has good stability and wider firing range; when being used for decoration, the ceramic tiles prepared by the frit give people an elegant feeling and a visual treat; and the values of the ceramic tiles are elevated and the added value is greatly improved.
Description
Technical field
The present invention relates to a kind of preparing ceramic clinker and preparation method thereof, be specifically related to a kind of mute light frit and preparation method thereof, belong to the ceramic production technology field.
Background technology
Along with the development of society, high-quality pottery becomes the target that current building and ornament materials are pursued, and the many glazes with transparent light of former wall tile for building are main; The decorating interior wall brick surface luster of adopting clear frit to process is beautiful, and the effect of decoration is that light sensation is relatively good, but along with the development of ceramic technology; It is found that unglazed glaze quality is high; Beautiful lubricious sense is arranged, and the effect that decoration comes out is high-grade more, adopts the brick of matting glaze face to decorate; The effect of decorating is given a kind of dignified grand sensation of people; Can be widely used in the decoration of high-grade hotel and villa, so according to the needs in market, researching and developing high-quality architectural pottery becomes an important research tendency with the matting glaze material.
Summary of the invention
The purpose of this invention is to provide a kind of mute light frit, this frit feel exquisiteness is lubricious, and stability is high, and firing range compares broad.
In order to address the above problem, the technical scheme that the present invention adopted is:
A kind of mute light frit, each ingredients weight parts is:
Quartzy 25 ~ 35 parts, 25 ~ 30 parts in calcite, 10 ~ 20 parts of potassium felspar sands, 5 ~ 8 parts in zinc oxide, 3 ~ 8 parts of boric acid, 5 ~ 10 parts of zirconium silicates, give birth to 2 ~ 5 parts in talcum and 1 ~ 3 part of Strontium carbonate powder.
Another object of the present invention provides a kind of preparation method of mute light frit, comprises the steps:
Take by weighing quartzy 25 ~ 35 parts, 25 ~ 30 parts in calcite, 10 ~ 20 parts of potassium felspar sands, 5 ~ 8 parts in zinc oxide, 3 ~ 8 parts of boric acid, 5 ~ 10 parts of zirconium silicates, give birth to 2 ~ 5 parts in talcum and 1 ~ 3 part of Strontium carbonate powder; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1400 ~ 1500 ℃, and the thawing time is 6 ~ 8 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
The present invention with respect to the beneficial effect of prior art is:
Adopt the mute light frit feel such as the jade of present method preparation, fine and smooth lubricious, good stability; Firing range is decorated with the ceramic tile that this frit makes than broad, gives the sensation of a kind of elegance of people; Be a kind of enjoyment of vision, the value of ceramic tile gets a promotion, and added value is improved greatly.
Embodiment
Through embodiment the present invention is explained further details below, these embodiment only are used for explaining the present invention, do not limit the scope of the invention.
Embodiment 1
A kind of mute light frit, each ingredients weight parts is:
Quartzy 25 parts, 25 parts in calcite, 10 parts of potassium felspar sands, 5 parts in zinc oxide, 3 parts of boric acid, 5 parts of zirconium silicates, give birth to 1 part of 2 parts in talcum and Strontium carbonate powder.
Its preparation method comprises the steps:
Take by weighing quartzy 25 parts, 25 parts in calcite, 10 parts of potassium felspar sands, 5 parts in zinc oxide, 3 parts of boric acid, 5 parts of zirconium silicates, give birth to 1 part of 2 parts in talcum and Strontium carbonate powder; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1400 ℃, and the thawing time is 6 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
Embodiment 2
A kind of mute light frit, each ingredients weight parts is:
Quartzy 35 parts, 30 parts in calcite, 20 parts of potassium felspar sands, 8 parts in zinc oxide, 8 parts of boric acid, 10 parts of zirconium silicates, give birth to 3 parts of 5 parts in talcum and Strontium carbonate powders.
Its preparation method comprises the steps:
Take by weighing quartzy 35 parts, 30 parts in calcite, 20 parts of potassium felspar sands, 8 parts in zinc oxide, 8 parts of boric acid, 10 parts of zirconium silicates, give birth to 3 parts of 5 parts in talcum and Strontium carbonate powders; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1500 ℃, and the thawing time is 8 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
Embodiment 3
A kind of mute light frit, each ingredients weight parts is:
Quartzy 30 parts, 27 parts in calcite, 15 parts of potassium felspar sands, 6 parts in zinc oxide, 5 parts of boric acid, 8 parts of zirconium silicates, give birth to 2 parts of 4 parts in talcum and Strontium carbonate powders.
Its preparation method comprises the steps:
Take by weighing quartzy 30 parts, 27 parts in calcite, 15 parts of potassium felspar sands, 6 parts in zinc oxide, 5 parts of boric acid, 8 parts of zirconium silicates, give birth to 2 parts of 4 parts in talcum and Strontium carbonate powders; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1450 ℃, and the thawing time is 7 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
Embodiment 4
A kind of mute light frit, each ingredients weight parts is:
Quartzy 25 parts, 25 parts in calcite, 10 parts of potassium felspar sands, 8 parts in zinc oxide, 8 parts of boric acid, 10 parts of zirconium silicates, give birth to 2 parts of 5 parts in talcum and Strontium carbonate powders.
Its preparation method comprises the steps:
Take by weighing quartzy 25 parts, 25 parts in calcite, 10 parts of potassium felspar sands, 8 parts in zinc oxide, 8 parts of boric acid, 10 parts of zirconium silicates, give birth to 2 parts of 5 parts in talcum and Strontium carbonate powders; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1480 ℃, and the thawing time is 6.5 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
Embodiment 5
A kind of mute light frit, each ingredients weight parts is:
Quartzy 35 parts, 30 parts in calcite, 20 parts of potassium felspar sands, 5 parts in zinc oxide, 3 parts of boric acid, 5 parts of zirconium silicates, give birth to 1 part of 5 parts in talcum and Strontium carbonate powder.
Another object of the present invention provides a kind of preparation method of mute light frit, comprises the steps:
Take by weighing quartzy 35 parts, 30 parts in calcite, 20 parts of potassium felspar sands, 5 parts in zinc oxide, 3 parts of boric acid, 5 parts of zirconium silicates, give birth to 1 part of 5 parts in talcum and Strontium carbonate powder; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1400 ~ 1500 ℃, and the thawing time is 6 ~ 8 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
Claims (4)
1. mute light frit is characterized in that the weight part of each component is:
Quartzy 25 ~ 35 parts, 25 ~ 30 parts in calcite, 10 ~ 20 parts of potassium felspar sands, 5 ~ 8 parts in zinc oxide, 3 ~ 8 parts of boric acid, 5 ~ 10 parts of zirconium silicates, give birth to 2 ~ 5 parts in talcum and 1 ~ 3 part of Strontium carbonate powder.
2. a kind of mute light frit according to claim 1 is characterized in that described zinc oxide is that zinc oxide content is 95% zinc oxide.
3. a method that is used to prepare the described mute light frit of claim 1 comprises the steps:
Take by weighing quartzy 25 ~ 35 parts, 25 ~ 30 parts in calcite, 10 ~ 20 parts of potassium felspar sands, 5 ~ 8 parts in zinc oxide, 3 ~ 8 parts of boric acid, 5 ~ 10 parts of zirconium silicates, give birth to 2 ~ 5 parts in talcum and 1 ~ 3 part of Strontium carbonate powder; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1400 ~ 1500 ℃, and the thawing time is 6 ~ 8 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
4. the preparation method of a kind of mute light frit according to claim 2 is characterized in that described zinc oxide is that zinc oxide content is 95% zinc oxide.