CN102557669A - Pre-ground processed ceramic wine bottle - Google Patents
Pre-ground processed ceramic wine bottle Download PDFInfo
- Publication number
- CN102557669A CN102557669A CN2011104445922A CN201110444592A CN102557669A CN 102557669 A CN102557669 A CN 102557669A CN 2011104445922 A CN2011104445922 A CN 2011104445922A CN 201110444592 A CN201110444592 A CN 201110444592A CN 102557669 A CN102557669 A CN 102557669A
- Authority
- CN
- China
- Prior art keywords
- grinding
- raw material
- repair
- smear
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a process for pre-grinding and processing a ceramic wine bottle, belonging to the technical field of ceramic production. According to the process, a column grinding process is added in the original processing process for pre-grinding raw materials processed by a jaw crusher, and the pre-ground raw materials are fed into a wet ball mill. The technical scheme is that the raw materials are pre-ground by the column grinding process at first and are fed into the wet ball mill after meeting certain fineness. In particular, the process comprises the following steps: (1) coarsely crushing; (2) grinding by columns; (3) preparing materials; (4) milling by balls; (5) molding by slip casting; (6) smearing and glazing; (7) sintering into colorful decorations; and (8) inspecting finished products, sorting, packaging and warehousing. According to the process, the processing efficiency is greatly improved, and large amounts of power consumption are saved.
Description
Technical field
The invention belongs to the ceramic production technology field, be specially a kind of preparatory grinding processing ceramic bottle.
Background technology
One adopts the pattern of jaw crusher+wet-type ball mill ceramic wine bottle raw material complete processing, and it is low to have working (machining) efficiency, and energy consumption is than problems such as height.China is the country of a rich coal resources, and about coal more than 50% is used for thermal power generation, and will produce several hundred million tons flyash every year, and a large amount of flyash storages not only will take a large amount of places but also contaminate environment influences weather, destroy ecological.The deep-processing factory of flyash utilized again becomes the current technical problem that needs to be resolved hurrily.Utilizing the flyash sintered ceramic is to utilize one of approach.
Summary of the invention
The present invention aims to provide the preparatory grinding complete processing of a kind of ceramic wine bottle, and to solve the pattern that existing ceramic wine bottle raw material complete processing adopts jaw crusher+wet-type ball mill, working (machining) efficiency is low, and energy consumption is than problems such as height.
The technical solution adopted for the present invention to solve the technical problems is through after in former complete processing, increasing the raw material of post grinding process after to jaw crusher processing and carrying out preparatory grinding, gets into the wet bulb grinding machine again after reaching certain fineness, and concrete process step is following:
1, coarse crushing: adopt jaw crusher that the building stones below the block 750mm are crushed to particle diameter 15-20mm;
2, post mill: raw material pulverizing is to 0-5mm after adopting column mill with coarse crushing;
3, batching:, subsequent use by each component raw material of conventional formulation weighing;
4, ball milling: the good raw material of weighing proportioning is added water in conventional ratio, in wet-type ball mill, mix, be machined to the mud that grouting with plunger is used;
5, injection forming: on shaper, make the bottle blank of desired shape, subsequent use;
6 repair and smear glazing: utilize to repair and smear machinery and repair and smear bottleneck and relevant position, product by heating is to 50-70 ℃ of drying, and dry good base substrate is cooled to normal temperature can soak glaze or directly glaze spraying;
7 burn till illuminated: firing temperature 700-800 ℃, firing time 2-3 hour;
8 inspection after constructions: pick, packing warehouse-in.
Adopting positively effect of the present invention is to improve working (machining) efficiency greatly, and practices thrift a large amount of power consumption.
Embodiment
To produce White Spirit Bottle is example, and concrete process step is following:
1, coarse crushing: adopt jaw crusher that the building stones below the block 750mm are crushed to below the particle diameter 20mm;
Perhaps flyash is carried out mechanical magnetic force deironing, then at 1000 ℃ of following calcination activations, the time is 1～2 hour.
2, post mill: raw material pulverizing is to 2-3mm after adopting column mill with coarse crushing;
3, batching:, subsequent use by each component raw material of conventional formulation weighing;
4, ball milling: the good raw material of weighing proportioning is added water in conventional ratio, in wet-type ball mill, mix, be machined to the mud that grouting with plunger is used;
5, injection forming: on shaper, make the bottle blank of desired shape, subsequent use;
6, repair and smear glazing: utilize to repair and smear machinery and repair and smear bottleneck and relevant position, product by heating to 60 ℃ drying, dry good base substrate is cooled to normal temperature can soak glaze or directly glaze spraying;
7, burn till illuminated: 750 ℃ of firing temperatures, 2.5 hours firing times;
8, inspection after construction: pick, packing warehouse-in.
Claims (1)
1. preparatory grinding complete processing of ceramic wine bottle after it is characterized in that in former complete processing, increasing the raw material of post grinding process after to jaw crusher processing and carrying out preparatory grinding, gets into the wet bulb grinding machine after reaching certain fineness again, and concrete process step is following:
(1) coarse crushing: adopt jaw crusher that the building stones below the block 750ram are crushed to particle diameter 15-20ram;
(2) post mill: raw material pulverizing is to 0-5mm after adopting column mill with coarse crushing;
(3) batching:, subsequent use by each component raw material of conventional formulation weighing;
(4) ball milling: the good raw material of weighing proportioning is added water in conventional ratio, in wet-type ball mill, mix, be machined to the mud that grouting with plunger is used;
(5) injection forming: on shaper, make the bottle blank of desired shape, subsequent use;
(6) repair and smear glazing: utilize to repair and smear machinery and repair and smear bottleneck and relevant position, product by heating is to 50-70 ℃ of drying, and dry good base substrate is cooled to normal temperature can soak glaze or directly glaze spraying;
(7) burn till illuminated: firing temperature ' 700-800 ℃, firing time 2-3 hour;
(8) inspection after construction: pick, packing warehouse-in.