CN102544250B - 一种GaN基发光二极管的制作方法 - Google Patents

一种GaN基发光二极管的制作方法 Download PDF

Info

Publication number
CN102544250B
CN102544250B CN201010622187.0A CN201010622187A CN102544250B CN 102544250 B CN102544250 B CN 102544250B CN 201010622187 A CN201010622187 A CN 201010622187A CN 102544250 B CN102544250 B CN 102544250B
Authority
CN
China
Prior art keywords
sapphire substrate
emitting diode
gan
etching
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201010622187.0A
Other languages
English (en)
Other versions
CN102544250A (zh
Inventor
王立彬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Tongfang Semiconductor Co.,Ltd.
Original Assignee
TONGFANG OPTO-ELECTRONIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGFANG OPTO-ELECTRONIC Co Ltd filed Critical TONGFANG OPTO-ELECTRONIC Co Ltd
Priority to CN201010622187.0A priority Critical patent/CN102544250B/zh
Publication of CN102544250A publication Critical patent/CN102544250A/zh
Application granted granted Critical
Publication of CN102544250B publication Critical patent/CN102544250B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种GaN基发光二极管的制作方法，涉及光电技术领域。本发明方法步骤为：①在蓝宝石衬底上外延发光结构；②研磨减薄蓝宝石衬底；③在氮化镓层表面蒸镀ITO薄膜；④刻蚀出N型电极区域；⑤蒸镀SiO2钝化层；⑥蒸镀金属电极；⑦刻蚀切割道；⑧在蓝宝石衬底底面进行激光划片；⑨将蓝宝石衬底的底面向上放置于ICP设备中，进行ICP刻蚀，清除熔渣碎屑；⑩最后进行裂片，形成单个发光二极管芯片。同现有技术相比，本发明采取先研磨后做电极的工艺流程，可以有效提高发光二极管的亮度。

Description

一种GaN基发光二极管的制作方法
技术领域
本发明涉及光电技术领域，特别是GaN基发光二极管的制作方法。
背景技术
GaN基材料是最常用的制备LED芯片的方法，GaN LED制备的各种光源具有节能、环保、冷光源、显色指数高、响应速度快、体积小和工作寿命长等突出优点。GaN主要在蓝宝石衬底、SiC衬底、Si衬底上外延生长，其中宝石衬底为主流，外延层包括N-GaN，MQW，P-GaN。芯片制作工艺主要包含刻蚀，透明电极制作，金属电极制作，钝化层的制作，然后研磨减薄，划片、裂片。
现有技术中，LED芯片制作技术的主要流程为：外延，然后是前制程，包括台面刻蚀，透明电极制作，金属电极制作，钝化层的制作，之后是后制程，包括研磨，划片，裂片。如中国专利公开号为CN101355118A的《光学复合膜作电极的GaN功率型LED的制作方法》。在这个流程中，可能会增加一些工艺，比如侧壁腐蚀技术，见台湾第I270223号专利、美国第6849524号专利、美国第5631190号专利等。总体上，现有技术中的LED芯片制作技术都采用先做电极，然后研磨的顺序，发光二极管的亮度还有待提高。
发明内容
为了克服上述现有技术存在的不足，本发明的目的是提供一种GaN基发光二极管的制作方法。它采取先研磨后做电极的工艺流程，可以有效提高发光二极管的亮度。
为了达到上述发明目的，本发明的技术方案以如下方式实现：
一种GaN基发光二极管的制作方法，它的方法步骤为：
①在蓝宝石衬底上外延氮化镓层，氮化镓层包含N-GaN层、有源层和P-GaN层；
②研磨减薄蓝宝石衬底；
③在氮化镓层表面采用电子束蒸发设备蒸镀ITO薄膜；
④在器件表面涂胶、曝光和显影形成掩蔽层，用ITO刻蚀液刻蚀出N型电极区域的ITO，然后采用ICP设备刻蚀出N型电极区域，去除光刻胶，在N2气氛中退火；
⑤用PECVD蒸镀SiO2钝化层；
⑥在器件表面涂胶、曝光和显影形成掩蔽层，用BOE腐蚀SiO2钝化层(5)，用电子束蒸发设备蒸镀金属电极，剥离去胶，形成P-GaN层上的金属电极一与N-GaN上的金属电极二，然后在N2气氛中退火；
⑦在器件上表面涂胶、曝光和显影形成掩蔽层，用ICP刻蚀工艺刻蚀切割道，该刻蚀深度位置可以位于GaN外延层位置，可以位于蓝宝石衬底的上表面，也可以位于蓝宝石内的位置；
⑧在蓝宝石衬底底面进行激光划片，产生熔渣碎屑；
⑨将蓝宝石衬底的底面向上放置于ICP设备中，进行ICP刻蚀，清除熔渣碎屑；
⑩最后进行裂片，形成单个发光二极管芯片。
在上述制作方法中，所述蓝宝石衬底的厚度研磨减薄至120微米至300微米。
在上述制作方法中，所述刻蚀出N型电极区域后，器件在N2气氛中退火的温度为500℃～600℃。
在上述制作方法中，所述形成金属电极一与金属电极二后，器件在300℃的N2气氛中退火10分钟。
本发明由于采用了上述方法，采用的工艺流程为外延生长、研磨减薄、电极制作、划片和裂片。本发明主要特点为先研磨减薄，然后制作电极，能使发光二极管亮度提高1％-10％。
下面结合附图和具体实施方式对本发明作进一步说明。
附图说明
图1至图10为本发明的方法步骤示意图。
具体实施方式
本发明制作GaN基发光二极管的方法步骤为：
①参看图1，在蓝宝石衬底1上外延氮化镓层2，氮化镓层2包含N-GaN层、有源层和P-GaN层；
②参看图2，研磨减薄蓝宝石衬底1的厚度至120微米至300微米；
③参看图3，在氮化镓层2表面采用电子束蒸发设备蒸镀ITO薄膜3；
④参看图4，在器件表面涂胶、曝光和显影形成掩蔽层，用ITO刻蚀液刻蚀出N型电极区域的ITO，然后采用ICP设备刻蚀出N型电极区域4，去除光刻胶，在温度为500℃～600℃的N2气氛中退火；
⑤参看图5，用PECVD蒸镀SiO2钝化层5；
⑥参看图6，在器件表面涂胶、曝光和显影形成掩蔽层，用BOE腐蚀SiO2钝化层5，用电子束蒸发设备蒸镀金属电极，剥离去胶，形成P-GaN层上的金属电极一6与N-GaN上的金属电极二7，然后在300℃的N2气氛中退火10分钟；
⑦参看图7，在器件上表面涂胶、曝光和显影形成掩蔽层，用ICP刻蚀工艺刻蚀切割道，露出蓝宝石衬底1的部分上表面；
⑧参看图8，在蓝宝石衬底1底面进行激光划片，产生熔渣碎屑8；
⑨参看图9，将蓝宝石衬底1的底面向上放置于ICP设备中，进行ICP刻蚀，清除熔渣碎屑8；
⑩参看图10，最后进行裂片，形成单个发光二极管芯片。
以上为本发明列举的一种实施方案，在具体使用中也可以增加其他工艺步骤，如ITO图案、粗化工艺，或者减少某些步骤，如最后的ICP刻蚀等。诸如此类的技术方案均属于本发明的保护范围。

Claims (5)

1.一种GaN基发光二极管的制作方法，它的方法步骤为：
1） 在蓝宝石衬底（1）上外延氮化镓层（2），氮化镓层（2）包含N-GaN层、有源层和P-GaN层；
2） 研磨减薄蓝宝石衬底（1）；
3） 在氮化镓层（2）表面采用电子束蒸发设备蒸镀ITO薄膜（3）；
4） 在器件表面涂胶、曝光和显影形成掩蔽层，用ITO刻蚀液刻蚀出N型电极区域的ITO，然后采用ICP设备刻蚀出N型电极区域（4），去除光刻胶，在N2气氛中退火；
5） 用PECVD蒸镀SiO2钝化层（5）；
6） 在器件表面涂胶、曝光和显影形成掩蔽层，用BOE腐蚀SiO2钝化层（5），用电子束蒸发设备蒸镀金属电极，剥离去胶，形成P-GaN层上的金属电极一（6）与N-GaN上的金属电极二（7），然后在N2气氛中退火；
7） 在器件上表面涂胶、曝光和显影形成掩蔽层，用ICP刻蚀工艺刻蚀切割道，露出蓝宝石衬底（1）的部分上表面；
8） 在蓝宝石衬底（1）底面进行激光划片，产生熔渣碎屑（8）；
9） 将蓝宝石衬底（1）的底面向上放置于ICP设备中，进行ICP刻蚀，清除熔渣碎屑（8）；
10）最后进行裂片，形成单个发光二极管芯片。
2.根据权利要求1所述的GaN基发光二极管的制作方法，其特征在于，在完成外延工艺后，先做研磨工艺，然后做刻蚀、电极工艺。
3.根据权利要求1或2所述的GaN基发光二极管的制作方法，其特征在于，所述蓝宝石衬底（1）的厚度研磨减薄至120微米至300微米。
4.根据权利要求1所述的GaN基发光二极管的制作方法，其特征在于，所述的激光划片产生的熔渣碎屑（8），采用ICP刻蚀方法清除。
5.根据权利要求1所述的GaN基发光二极管的制作方法，其特征在于，所述的刻蚀切割道，刻蚀深度位置位于GaN外延层位置，或位于蓝宝石衬底的上表面，或位于蓝宝石内的位置。
CN201010622187.0A 2010-12-27 2010-12-27 一种GaN基发光二极管的制作方法 Active CN102544250B (zh)