CN102533420A - H68黄铜管拉拔润滑乳化油及生产方法 - Google Patents
H68黄铜管拉拔润滑乳化油及生产方法 Download PDFInfo
- Publication number
- CN102533420A CN102533420A CN 201110450255 CN201110450255A CN102533420A CN 102533420 A CN102533420 A CN 102533420A CN 201110450255 CN201110450255 CN 201110450255 CN 201110450255 A CN201110450255 A CN 201110450255A CN 102533420 A CN102533420 A CN 102533420A
- Authority
- CN
- China
- Prior art keywords
- kerosene
- oleic acid
- oil
- zinc naphthenate
- water emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种H68黄铜管拉拔润滑乳化油,其原料组分及重量百分比如下:油酸6~16%、三乙醇胺6~16%、石油磺酸钠1~16%、环烷酸锌1~6%、磷苯二甲酸二丁酯1~6%、苯丙三氮唑0.1~0.3%、无水乙醇0.5~1.0%、机械油6~26%及煤油余量。生产方法是先将计算称量的苯丙三氮唑用无水乙醇溶解后备用;再将机械油和煤油加入到反应斧中,加热到40~50℃,开动搅拌器控制转速80转/min,依次将计算称量的油酸、三乙醇胺、石油磺酸钠、环烷酸锌、磷苯二甲酸二丁酯以及前步骤所得的苯丙三氮唑乙醇溶液加入到反应斧中,连续搅拌1~2小时,充分搅拌均匀;降至室温。
Description
技术领域
本发明涉及一种拉拔工艺用润滑乳化油及生产方法,尤其是一种可防止拉拔金属管局部过热断管、氧化变色并可保证成品表面光洁度、光亮度的H68黄铜管拉拔润滑乳化油及生产方法。
背景技术
拉拔工艺是一种典型的金属加工方法,是在拉拔作用下,通过模具孔芯减小金属加工材料的截面积,以获得高精度、高光洁度的线材或管材的一种塑性加工工艺。在拉拔加工过程中,由于金属变形量大且不断产生新的摩擦面,需要润滑乳化油对金属材料、模具进行润滑、冷却。在如此巨大的挤压拉伸过程中,润滑乳化油起着至关重要的作用。目前,H68黄铜管拉拔润滑乳化油存在清洗性能不好和冷却效果差的问题,以至于经过多次拉拔后,在拉拔管表面与孔芯边缘粘结大量的金属粉,导致两者之间的摩擦系数急剧增大,不但使拉拔工件表面光洁度、光亮度急剧降低,还加剧对模具的磨损,影响模具的使用寿命;加之冷却效果不理想,经常发生由于H68黄铜管或模具局部过热而断管的质量问题。另外,由于清洗性能不好,对拉拔金属管后道工序热处理和退火质量都将产生不良影响。
发明内容
本发明是为了解决现有技术所存在的上述技术问题,提供一种可防止拉拔金属过热断管、氧化变色并可保证成品表面光洁度、光亮度的H68黄铜管拉拔润滑乳化油及生产方法。
本发明的技术解决方案是:一种H68黄铜管拉拔润滑乳化油,其原料组分及重量百分比如下:
油酸 6~16%
三乙醇胺 6~16%
石油磺酸钠 1~16%
环烷酸锌 1~6%
磷苯二甲酸二丁酯 1~6%
苯丙三氮唑 0.1~0.3%
无水乙醇 0.5~1.0%
机械油 6~26%
煤油 余量。
一种上述H68黄铜管拉拔润滑乳化油的生产方法,其特征在于按照如下步骤进行:
a. 先将计算称量的苯丙三氮唑用无水乙醇溶解后备用;
b. 再将机械油和煤油加入到反应斧中,加热到40~50℃,开动搅拌器控制转速80转/min,依次将计算称量的油酸、三乙醇胺、石油磺酸钠、环烷酸锌、磷苯二甲酸二丁酯以及a步骤所得的苯丙三氮唑乙醇溶液加入到反应斧中,连续搅拌1~2小时;
c. 降至室温。
本发明是以运动粘度、润滑性能、极压性能、冷却性能以及稳定性等为性能指标,采用三乙醇胺作为乳化剂,润滑、极压组合则采用具有较大吸收残留酸的耐酸化合物(石油磺酸钠)等,特殊的原料组分及配比组合使本发明同现有技术相比,具有如下优点:
1.润滑膜的化学吸附及物理吸附性好,在拉拔金属管和模具之间形成均匀连续、完整的液体介质膜,表面所形成的润滑膜吸附牢固,不易在挤压拉伸过程中被挤掉,使拉拔金属管与模具之间具有很好的润滑性,保证拉拔金属管表面具有符合标准的光洁度、光亮度,同时减少了对模具的磨损,延长了模具的使用寿命;
2.具有很好的冷却效果,即可防止由于局部过热导致拉拔金属管与模具钢芯的烧结、熔粘或抓结而引起断管的质量问题,同时又可提高每次减径率及径向拉拔增长率,使生产效率得以提高;
3.乳化性能稳定,即使是用硬质水稀释,对润滑冷却乳化剂的稳定性也没有任何影响;
4.本发明是棕黄色透明均匀油状物,添加有杀菌剂,不易变质,使用6个月时间,无毒无害无恶臭气味,利于环保,不会影响操作人员的身体健康;
5.易于从拉拔后的金属管表面上除掉,对拉拔管后道工序(热处理和退火)质量无任何不良影响。
具体实施方式
实施例1:
取原料组分,每种原料占总重量的百分比如下:
油酸6~16%、三乙醇胺6~16%、石油磺酸钠1~16%、环烷酸锌1~6%、磷苯二甲酸二丁酯1~6%、苯丙三氮唑0.1~0.3%、无水乙醇0.5~1.0%、机械油6~26%及煤油余量。
各原料质量之和为100%。
生产方法按如下步骤进行:
a. 先将计算称量的苯丙三氮唑用无水乙醇溶解后备用;
b. 再将机械油和煤油加入到反应斧中,加热到40~50℃,开动搅拌器控制转速80转/min,依次将计算称量的油酸、三乙醇胺、石油磺酸钠、环烷酸锌、磷苯二甲酸二丁酯以及a步骤所得的苯丙三氮唑乙醇溶液加入到反应斧中,连续搅拌1~2小时,充分搅拌均匀;
c. 降至室温。
实施例2:
取原料组分,每种原料占总重量的百分比如下:油酸10%、三乙醇胺10%、石油磺酸钠8%、环烷酸锌4%、磷苯二甲酸二丁酯 3%、苯丙三氮唑0.2%、无水乙醇0.8%、LN30机械油18%及煤油余量。
生产方法同实施例1。
使用时,加水将实施例1、2的产品稀释,配制成浓度为5~10%的乳化液,应用于H68黄铜管拉拔,直至将毛坯材质拉拔至所需直径,无断管现象,表面光洁度、光亮度符合GB/T14956-1994要求。
Claims (2)
1.一种H68黄铜管拉拔润滑乳化油,其原料组分及重量百分比如下:
油酸 6~16%
三乙醇胺 6~16%
石油磺酸钠 1~16%
环烷酸锌 1~6%
磷苯二甲酸二丁酯 1~6%
苯丙三氮唑 0.1~0.3%
无水乙醇 0.5~1.0%
机械油 6~26%
煤油 余量。
2.一种如权利要求1所述H68黄铜管拉拔润滑乳化油的生产方法,其特征在于按如下步骤进行:
a. 先将计算称量的苯丙三氮唑用无水乙醇溶解后备用;
b. 再将机械油和煤油加入到反应斧中,加热到40~50℃,开动搅拌器控制转速80转/min,依次将计算称量的油酸、三乙醇胺、石油磺酸钠、环烷酸锌、磷苯二甲酸二丁酯以及a步骤所得的苯丙三氮唑乙醇溶液加入到反应斧中,连续搅拌1~2小时;
c. 降至室温。