CN102533202A - 一种鞋用聚氨酯胶粒的配方 - Google Patents
一种鞋用聚氨酯胶粒的配方 Download PDFInfo
- Publication number
- CN102533202A CN102533202A CN2012100000286A CN201210000028A CN102533202A CN 102533202 A CN102533202 A CN 102533202A CN 2012100000286 A CN2012100000286 A CN 2012100000286A CN 201210000028 A CN201210000028 A CN 201210000028A CN 102533202 A CN102533202 A CN 102533202A
- Authority
- CN
- China
- Prior art keywords
- shoes
- polyurethane
- prescription
- butyleneglycol
- colloidal particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种鞋用聚氨酯胶粒的配方,它包括以下组分:聚酯多元醇、1,6-己二异氰酸酯三聚体、1,4-丁二醇以及水解稳定剂。本发明制成的产品具有卓越的低温性能、优良的柔性、耐冲击性、耐水性等,特别适用于粘接膨胀系数不同的异种材料,而且其涂胶量比氯丁胶减少一半。
Description
技术领域
一种鞋用聚氨酯胶粒的配方。
背景技术
我国是世界上最大的制鞋国家,年产胶粘鞋20亿双以上,若以每双鞋20g的用胶量计算,年消耗鞋胶4000吨。目前我国制鞋工业中95%使用氯丁胶。氯丁胶粘剂初粘性好、可冷粘、价格便宜,但不耐增塑剂渗透,对软PVC、热塑性橡胶、PU革等新型鞋用材料粘接性差,此外必须应用苯内有毒溶剂,所以存在致命的弱点,已不适应制鞋工业的发展。欧、美80~90%的鞋用胶已被聚氨酯胶粘剂所占领,国内也必然是这样的趋势。
发明内容
本发明提供了一种鞋用聚氨酯胶粒的配方,该配方制成的产品具有卓越的低温性能、优良的柔性、耐冲击性、耐水性等,特别适用于粘接膨胀系数不同的异种材料,且其涂胶量比氯丁胶减少一半。
本发明采用了以下技术方案:一种鞋用聚氨酯胶粒的配方,它包括以下组分:聚酯多元醇、1,6-己二异氰酸酯三聚体、1,4-丁二醇以及水解稳定剂。
所述的聚酯多元醇、1,6-己二异氰酸酯三聚体、1,4-丁二醇三者的摩尔比为1:0.8:0.5;所述的聚酯多元醇为聚己二酸-1,4丁二醇-1,6己二醇酯二醇;所述的聚己二酸-1,4丁二醇-1,6己二醇酯二醇由1,4丁二醇与1,6己二醇按摩尔比2:3投放生成;所述的水解稳定剂占原料质量的0.2%;所述的水解稳定剂为碳化二亚胺。
本发明具有以下有益效果:本发明制成的产品具有卓越的低温性能、优良的柔性、耐冲击性、耐水性等,特别适用于粘接膨胀系数不同的异种材料,而且其涂胶量比氯丁胶减少一半。
具体实施方式
本发明公开了一种鞋用聚氨酯胶粒的配方,它包括以下组分:聚酯多元醇、1,6-己二异氰酸酯三聚体、1,4-丁二醇以及水解稳定剂。所述的聚酯多元醇、1,6-己二异氰酸酯三聚体、1,4-丁二醇三者的摩尔比为1:0.8:0.5,水解稳定剂占原料质量的0.2%。所述的聚酯多元醇为聚己二酸-1,4丁二醇-1,6己二醇酯二醇,所述的聚己二酸-1,4丁二醇-1,6己二醇酯二醇由1,4丁二醇与1,6己二醇按摩尔比2:3投放生成,所述的所述的水解稳定剂为碳化二亚胺。
Claims (6)
1.一种鞋用聚氨酯胶粒的配方,其特征是它包括以下组分:聚酯多元醇、1,6-己二异氰酸酯三聚体、1,4-丁二醇以及水解稳定剂。
2.根据权利要求1所述的一种鞋用聚氨酯胶粒的配方,其特征是所述的聚酯多元醇、1,6-己二异氰酸酯三聚体、1,4-丁二醇三者的摩尔比为1:0.8:0.5。
3.根据权利要求1或2所述的一种鞋用聚氨酯胶粒的配方,其特征是所述的聚酯多元醇为聚己二酸-1,4丁二醇-1,6己二醇酯二醇。
4.根据权利要求3所述的一种鞋用聚氨酯胶粒的配方,其特征是所述的聚己二酸-1,4丁二醇-1,6己二醇酯二醇由1,4丁二醇与1,6己二醇按摩尔比2:3投放生成。
5.根据权利要求1所述的一种鞋用聚氨酯胶粒的配方,其特征是所述的水解稳定剂占原料质量的0.2%。
6.根据权利要求1或5所述的一种鞋用聚氨酯胶粒的配方,其特征是所述的水解稳定剂为碳化二亚胺。