CN102532456B - 应用于板材保温的环保型组合料及其制备方法 - Google Patents

应用于板材保温的环保型组合料及其制备方法 Download PDF

Info

Publication number
CN102532456B
CN102532456B CN2011104419966A CN201110441996A CN102532456B CN 102532456 B CN102532456 B CN 102532456B CN 2011104419966 A CN2011104419966 A CN 2011104419966A CN 201110441996 A CN201110441996 A CN 201110441996A CN 102532456 B CN102532456 B CN 102532456B
Authority
CN
China
Prior art keywords
heat preservation
component
environment
board
friendly type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2011104419966A
Other languages
English (en)
Other versions
CN102532456A (zh
Inventor
徐业峰
李欣
李明友
孙平平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Inov New Material Co Ltd
Original Assignee
Shandong Dongda Inov New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Dongda Inov New Material Co Ltd filed Critical Shandong Dongda Inov New Material Co Ltd
Priority to CN2011104419966A priority Critical patent/CN102532456B/zh
Publication of CN102532456A publication Critical patent/CN102532456A/zh
Application granted granted Critical
Publication of CN102532456B publication Critical patent/CN102532456B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于化学合成领域，具体涉及一种应用于板材保温的环保型组合料及其制备方法，由A组份和B组份构成，其中A组份由聚醚多元醇、聚酯多元醇、泡沫稳定剂、化学发泡剂、催化剂、物理发泡剂和阻燃剂组成；B组份为聚合二苯基甲烷二异氰酸酯。本发明的优点在于：A组份料是在常温下进行，既节约能源又减少供能设备和繁琐的操作。由A、B组份料生产的板材保温环保型聚氨酯泡沫材料也是在常温、常压下进行，工艺简单，易操作，挥发低，无三废，产品质量稳定，生产成本低。

Description

应用于板材保温的环保型组合料及其制备方法
技术领域
本发明属于化学合成领域，具体涉及一种应用于板材保温的环保型组合料及其制备方法。
背景技术
HFC-365/134a(1，1，1，3，3-五氟丁烷和1，1，1，2-四氟乙烷)是新型混合物理发泡剂。HFC-365mfc属于第三代发泡剂，沸点40℃，是所有零ODP的HFC发泡剂产品中沸点唯一高于室温的液态发泡剂，但缺点是具有一定的可燃性；HFC-134a，ODP＝0，无毒、无味、无色不燃、不爆，热稳定性好，对聚氨酯泡沫塑料无增塑效应；当HFC-365/134a以93∶7混合时，混合物无闪点，为不可燃的发泡剂，热导率(25℃)为10.9，故用其所生产的组合聚醚属于无氟型组合聚醚，具用环保的作用，用异氰酸酯与此组合聚醚反应，所制得泡沫具有导热系数低、性能稳定的特点，在节能降耗方面将会起到积极的催进作用；同时生产周期短、效率高、耗能低，逐渐取代传统的物理发泡剂如F-11(一氟三氯甲烷)、141b(一氟二氯乙烷)等，可广泛地应用于各种保温领域。HFC-365mfc为比利时的苏威公司生产的产品，欧洲同类聚氨酯公司在冰箱和冰柜行业已经开始使用HFC-365mfc，并且技术已经相对成熟。
目前，在板材保温型组合聚醚中所使用的物理发泡剂还是以141b为主，因141b的ODP＝0.11，要想达到完全环保的目的是做不到的，所以决定了其只是一种过渡型的替代产品。
发明内容
本发明的目的是提供一种应用于板材保温的环保型组合料及其制备方法，以HFC-365/134a的混合物为物理发泡剂，配置板材保温型组合聚醚的制作，在达到环保目的的同时，降低泡沫的导热系数，各项指标达到国标的要求。
本发明所述的一种应用于板材保温的环保型组合料，由A组份和B组份构成，其中：
A组份为，以重量百分数计：
聚醚多元醇A：20～50％；
聚醚多元醇B：10～40％；
聚酯多元醇：5～15％；
泡沫稳定剂：1.0～3.0％；
化学发泡剂：1.2～2.5％；
催化剂：0.3～3.5％；
物理发泡剂：15～35％；
阻燃剂：10～30％；
B组份为聚合二苯基甲烷二异氰酸酯。
其中，所述的聚醚多元醇A优选为6官能度，分子量为800～900的聚醚多元醇。
所述的聚醚多元醇B优选为5官能度，分子量为600～700的聚醚多元醇。
所述的聚酯多元醇优选为官能度，分子量为500～650的聚酯多元醇。
所述的泡沫稳定剂优选为非水解硅碳类表面活性剂，可以选用L-5440(生产厂家为美国迈图公司)。
所述的化学发泡剂优选为去离子水。
所述的催化剂优选为叔胺类催化剂，可以选用N，N二甲基环己胺和N，N二甲基苄胺的混合物。
所述的物理发泡剂优选为HFC-365mfc和HFC-134a的混合物，其中HFC-365mfc占混合物质量的93％。
所述的阻燃剂优选为添加型阻燃剂，可以选用三(2-氯丙基)磷酸酯。
本发明所述的应用于板材保温的环保型组合料的制备方法，包括以下步骤：
制备A组份料：将称量好的聚醚多元醇、聚酯多元醇、稳定剂、化学发泡剂、催化剂、物理发泡剂，依次加入反应釜中，在常温下搅拌2小时，经检测充分混合，即可装桶；
将A、B组份料按A∶B＝100∶100～110的质量比混合，即可制成应用于板材保温的环保型组合料。
本发明的优点在于：A组份料是在常温下进行，既节约能源又减少供能设备和繁琐的操作。由A、B组份料生产的板材保温环保型聚氨酯泡沫材料也是在常温、常压下进行，工艺简单，易操作，挥发低，无三废，产品质量稳定，生产成本低。A组份料利用HFC-365/134a的混合物为物理发泡剂配置板材保温型组合聚醚的制作，在达到环保目的的同时，降低泡沫的导热系数，保持性能稳定及其各项指标达到国标的要求；同时生产周期短、效率高、耗能低。经检测应用于板材保温的环保型聚氨酯泡沫产品质量指标，可以达到：
密度：40±2kg/m3
抗压强度：≥160kPa
导热系数：≤0.024W/m.k
吸水率：≤3V/V％
尺寸稳定性：≤3.0％
(+70℃～-30℃，48h)
燃烧性能(水平燃烧法)：
平均燃烧时间：≤90s
平均燃烧范围：≤50mm
性能完全达到了JB/T 6527-2006板材保温硬质聚氨酯泡沫塑料的要求。
具体实施方式
以下结合实施例对本发明做进一步说明。
实施例1：
制备A组份料100公斤，分别称量：聚醚多元醇A(6官能度，分子量为850)34.2公斤，聚醚多元醇B(5官能度，分子量为620)22公斤，聚酯多元醇(3官能度，分子量为525)6公斤，L-54401.5公斤，催化剂N，N二甲基环己胺0.6公斤，N，N二甲基苄胺1.3公斤，去离子水1.4公斤，HFC-365/134a 20公斤，三(2-氯丙基)磷酸酯13公斤。将称量好的聚醚多元醇、聚酯多元醇、稳定剂、化学发泡剂、催化剂、物理发泡剂和阻燃剂，依次加入反应釜中，在常温下搅拌2小时，取出进行检验，满足工艺参数，发出满意泡沫，即得A组份合格产品，从反应釜中取出装桶入库。
B组份为多亚甲基多苯基多异氰酸酯。
将A、B组份料按A∶B＝100∶100质量比混合制成应用于板材保温的环保型聚氨酯泡沫，经检测产品质量指标：
密度：40kg/m3
抗压强度：186kPa
导热系数：0.023W/m.k
吸水率：2.8V/V％
尺寸稳定性：2.0％
(+70℃～-30℃，48h)
燃烧性能(水平燃烧法)：
平均燃烧时间：82s
平均燃烧范围：45mm
实施例2：
制备A组份料100公斤，分别称量：聚醚多元醇A(6官能度，分子量为850)35公斤，聚醚多元醇B(5官能度，分子量为620)18.8公斤，聚酯多元醇(3.0官能度，分子量为525)6.4公斤，L-54401.5公斤，催化剂N，N二甲基环己胺0.7公斤，N，N二甲基苄胺1.2公斤，去离子水1.6公斤，HFC-365/134a 19.8公斤，三(2-氯丙基)磷酸酯15公斤。将称量好的聚醚多元醇、聚酯多元醇、稳定剂、化学发泡剂、催化剂、物理发泡剂和阻燃剂，依次加入反应釜中，在常温下搅拌2小时，取出进行检验，满足工艺参数，发出满意泡沫，即得A组份合格产品，从反应釜中取出装桶入库。
B组份为多亚甲基多苯基多异氰酸酯。
将A、B组份料按A∶B＝100∶100质量比混合制成应用于板材保温的环保型聚氨酯泡沫，经检测产品质量指标：
密度：42kg/m3
抗压强度：197kPa
导热系数：0.022W/m.k
吸水率：2.2V/V％
尺寸稳定性：1.8％
(+70℃～-30℃，48h)
燃烧性能(水平燃烧法)：
平均燃烧时间：71s
平均燃烧范围：39mm
实施例3：
制备A组份料100公斤，分别称量：聚醚多元醇A(6官能度，分子量为850)36.5公斤，聚醚多元醇B(5官能度，分子量为620)16.9公斤，聚酯多元醇(3.0官能度，分子量为525)9.5公斤，L-54401.6公斤，催化剂N，N二甲基环己胺0.9公斤，N，N二甲基苄胺1.0公斤，去离子水1.5公斤，HFC-365/134a 19.5公斤，三(2-氯丙基)磷酸酯12.6公斤。将称量好的聚醚多元醇、聚酯多元醇、稳定剂、化学发泡剂、催化剂、物理发泡剂和阻燃剂，依次加入反应釜中，在常温下搅拌2小时，取出进行检验，满足工艺参数，发出满意泡沫，即得A组份合格产品，从反应釜中取出装桶入库。
B组份为多亚甲基多苯基多异氰酸酯。
将A、B组份料按A∶B＝100∶100质量比混合制成应用于板材保温的环保型聚氨酯泡沫，经检测产品质量指标：
密度：38kg/m3
抗压强度：168kPa
导热系数：0.024W/m.k
吸水率：2.6V/V％
尺寸稳定性：2.2％
(+70℃～-30℃，48h)
燃烧性能(水平燃烧法)：
平均燃烧时间：78s
平均燃烧范围：43mm

Claims (8)

1.一种应用于板材保温的环保型组合料，其特征在于由A组份和B组份构成，其中：
A组份为，以重量百分数计：
聚醚多元醇A：20～50％；
聚醚多元醇B：10～40％；
聚酯多元醇：5～15％；
泡沫稳定剂：1.0～3.0％；
化学发泡剂：1.2～2.5％；
催化剂：0.3～3.5％；
物理发泡剂：15～35％；
阻燃剂：10～30％；
B组份为多亚甲基多苯基多异氰酸酯；
所述聚醚多元醇A为6官能度，分子量为800～900的聚醚多元醇；
所述聚醚多元醇B为5官能度，分子量为600～700的聚醚多元醇。
2.根据权利要求1所述的应用于板材保温的环保型组合料，其特征在于聚酯多元醇为3官能度，分子量为500～650的聚酯多元醇。
3.根据权利要求1所述的应用于板材保温的环保型组合料，其特征在于泡沫稳定剂为非水解硅碳类表面活性剂。
4.根据权利要求1所应的应用于板材保温的环保型组合料，其特征在于化学发泡剂为去离子水。
5.根据权利要求1所述的应用于板材保温的环保型组合料，其特征在于催化剂为叔胺类催化剂。
6.根据权利要求1所述的应用于板材保温的环保型组合料，其特征在于物理发泡剂为HFC-365mfc和HFC-134a的混合物，其中HFC-365mfc占混合物质量的93％。
7.根据权利要求1所述的应用于板材保温的环保型组合料，其特征在于阻燃剂为添加型阻燃剂，其选用三(2-氯丙基)磷酸酯。
8.一种权利要求1所述的应用于板材保温的环保型组合料的制备方法，其特征在于包括以下步骤：
制备A组份料：将称量好的聚醚多元醇、聚酯多元醇、稳定剂、化学发泡剂、催化剂、物理发泡剂和阻燃剂，依次加入反应釜中，在常温下搅拌2小时，经检测充分混合，即可装桶；
将A、B组份料按A∶B＝100∶100～110的质量比混合，即可制成应用于板材保温的环保型组合料。
CN2011104419966A 2011-12-27 2011-12-27 应用于板材保温的环保型组合料及其制备方法 Active CN102532456B (zh)