CN102505530A - Production process of photosensitive color-changing printed fabric - Google Patents
Production process of photosensitive color-changing printed fabric Download PDFInfo
- Publication number
- CN102505530A CN102505530A CN2011103232100A CN201110323210A CN102505530A CN 102505530 A CN102505530 A CN 102505530A CN 2011103232100 A CN2011103232100 A CN 2011103232100A CN 201110323210 A CN201110323210 A CN 201110323210A CN 102505530 A CN102505530 A CN 102505530A
- Authority
- CN
- China
- Prior art keywords
- fabric
- coating
- printed fabric
- production technology
- handled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a production process of a photosensitive color-changing printed fabric. The production process comprises the following steps of: preparing a base fabric: adopting a polyester/cotton blended fabric, carrying out overflow dyeing on the blended fabric, then washing and setting the dyed fabric, and then after-finishing and printing the fabric to obtain the base fabric; sewing the base fabric, and then enabling the base fabric to enter a desizing machine to undergo scouring pre-treatment; selecting dyeing equipment to dye the fabric material treated in the step 2; setting the dyed fabric at high temperature, and adding fluorocarbon resin; coating the set fabric, and then adopting a surface treatment gravure printing machine to print the fabric; and carrying out surface curing on the printed fabric, thus finally obtaining a finished product. The production process has the following beneficial effects: the photosensitive printed fabric can be used for high-grade sun umbrellas and clothes; and the peculiar color-changing effect of the printed fabric has a good use effect.
Description
Technical field
The present invention relates to the lining production technology, refer in particular to a kind of sensitization discoloration printed fabric production technology.
Background technology
The output of China's printing textile ranks first in the world, and produces about 1,800,000,000 meters per year, but owing to lack the innovative product appearance of independent research, is in the low side of industrial chain, and price is merely about half of developed country's like product.And improving constantly of Along with people's quality of life simultaneously; Also more and more pay close attention to the color of textiles; Function and other rat-fuck style; Even the lining that but clothes or other field adopted now has some special function such as variable color, the stamp etc. of swimming, but its quality is unsatisfactory, can't satisfy the quality demand of people to printed fabric fully.Therefore for printing textile, we need badly has more high added value and function and the good lining of quality tool.
The inventor provides a kind of new printed fabric production technology to the problems referred to above, has solved above-mentioned technical problem.
Summary of the invention
The present invention is directed to the disappearance of prior art existence; Its main purpose provides the production technology of the good sensitization discoloration printed fabric of a kind of function and quality tool; Lining behind this technology stamp of process is after the solar radiation of outdoor conditions; Obvious change can take place in pattern color, waits to get back to indoor back color and can be returned to original effect again.
For realizing above-mentioned purpose, the present invention adopts following technical scheme: a kind of sensitization discoloration printed fabric production technology, it is characterized in that: this production technology comprises the steps:
Step 1: prepare base cloth, promptly adopt polyester fabric or polyester cotton blending lining, through overflow dyeing, then process washing typing is carried out back arrangement stamp again and is handled the acquisition base cloth;
Step 2: the destarch boiling-off, promptly above-mentioned base cloth is carried out margin to seam and handle, then let it get into desizing machine and carry out the boiling-off pre-treatment;
Step 3: dye according to fabric treated material selective staining equipment in step 2;
Step 4: above-mentioned dyed polyester fabric or polyester cotton blending lining are carried out the high-temperature shaping processing and add fluorocarbon resin in baking oven, oven temperature was 140～180 ℃ during this typing was handled;
Step 5: carry out the coating processing to above-mentioned through the typing fabric treated, this coating is an acrylic acid formicester resinous coat; It is last rubber coating that coating is handled the board that uses, and its floating coat cutter is controlled at 1.5mm deeply, and wet coating weight is controlled at 35～40g/m, and four joint oven temperatures are controlled at 100 ℃, 120 ℃, 140 ℃ and 140 ℃ respectively;
Step 6: adopt surface treatment intaglio plate printing machine to carry out stamp to above-mentioned through the coating fabric treated, surface treatment intaglio plate printing machine flower version adopts laser engraving round metal version, several 100 orders of mesh order/CM
2, between 100～120 microns of the carving depths; Its concentrator that adopts is added with the microcapsules sensitizing powder, and abundant with the polyurethane resin dissolving;
Step 7: the surface cure that above-mentioned fabric through stamp is carried out top layer is handled, and obtains finished product behind the formation protective layer.
Institute's fluorocarbon resin was the fluouine water extraction agent during said step 4 high-temperature shaping was handled, and consumption is 30g/l.Also can adopt polyamide fibre lining or bright and beautiful cotton blended spinning face fabric in baking oven, to carry out high-temperature shaping processing and the agent of interpolation fluouine water extraction in addition in the step 4, consumption is 25g/l, and oven temperature was 180 ℃ during this typing was handled, and the lining translational speed is 30 meters/minute.
Above-mentioned steps 5 said acrylic acid formicester resinous coats comprise the acrylic acid formicester coating adhesive of 89.3% mass ratio, the toluene of the curing agent of 1.7% mass ratio and 9% mass ratio respectively.In addition, said coating also can be polyurethane resin pearly-lustre mill base coating, and it is 58% polyurethane, 16 % butanone, 2 % curing agent, 1% catalyst, 3% slipping agent, 15% mill base and 5% pearl essence that this polyurethane resin pearly-lustre mill base coating comprises mass ratio respectively.
During stamp was handled in the above-mentioned steps 6, the dynamo-electric heating power of said surface treatment intaglio plate stamp guaranteed that at 50～55KW oven temperature is controlled between 150 ℃～155 ℃.The concentrator viscosity that adopts is 500～1000GPS/T in the step 6 stamp process in addition, and the starching amount is controlled at 20～25g/y, and concentrator supplies the stamp use after before following seal, will using the strainer filtering of 200 orders/c ㎡.And it is 40 parts polyurethane, 15 parts microcapsules sensitizing powder, 10 parts dimethylformaldehyde amine, 30 parts butanone, 4 parts curing agent, 2 parts catalyst, 6 parts slipping agent that concentrator comprises quality successively; This concentrator adds successively by the said components order and stirs, and institute's employing mixer rotating speed is 1200 rev/mins.
The surface cure of said step 7 adopts 80 order net rollers in handling, blade thickness 1.0mm wherein, the starching amount is controlled at 20g/y, and said protective layer to comprise mass ratio respectively be 45% polyurethane, 45% butanone, 4% curing agent and 6% slipping agent.
After the present invention adopts technique scheme; Its beneficial effect is: through to this sensitization discoloration printed fabric controlling of production process and raw-material selection; And the photochromic pigment that adopts special microcapsules coating technology to process; And be printed on fabric face through the coating of special technology allotment, make that the sensitization discoloration fabric quality that the present invention produced is really up to the mark.The printed fabric that this technology of while is produced is applicable to the umbrella and the clothes of novel fashion; And it is again after the solar radiation of outdoor conditions; Obvious change can take place in pattern color, waits to get back to indoor back color and can be returned to original effect again, has good sensitization discoloration effect.Therefore this production technology obtained printed fabric function and quality tool are good.
In addition, in this printed fabric technology, adopt international advanced surface treatment intaglio plate transfer apparatus to produce; Has environmental protection, low power consuming, without sewage discharge; The photographic printing lining can be used for high-grade sunshade and garment material, and its distinctive color changeable effect has boundless market value.
The specific embodiment:
Come the present invention is elaborated below in conjunction with specific embodiment:
Embodiment one: a kind of sensitization discoloration printed fabric production technology comprises the steps:
Step 1: prepare base cloth, promptly adopt the polyester cotton blending lining, through overflow dyeing, then process washing typing is carried out back arrangement stamp again and is handled the acquisition base cloth;
Step 2: the destarch boiling-off, promptly above-mentioned base cloth is carried out margin to seam and handle, then let it get into desizing machine and carry out the boiling-off pre-treatment;
Step 3: select overflow dyeing machine to dye according to fabric treated material in step 2;
Step 4: above-mentioned dyed polyester cotton blending lining is carried out the high-temperature shaping processing and adds the fluouine water extraction agent in baking oven; Consumption is 30g/l, and it is handled back drying degree and should be up to state standards: GB4745 " textile fabric-surperficial moisture resistance assay method--dip experiment method " GB is more than 4 grades; And the polyester cotton blending lining moves in baking oven and is 30 meters/minute of speed, and oven temperature is 140 ℃ simultaneously;
Step 5: carry out the coating processing to above-mentioned through the typing fabric treated, this coating is acrylic acid formicester resinous coat (being commonly called as AC glue), comprises the acrylic acid formicester coating adhesive of 89.3% mass ratio respectively, the toluene of the curing agent of 1.7% mass ratio and 9% mass ratio; It is last rubber coating that coating is handled the board that uses, and its floating coat cutter is controlled at 1.5mm deeply, and wet coating weight is controlled at 35g/m, and four joint oven temperatures are controlled at 100 ℃, 120 ℃, 140 ℃ and 140 ℃ respectively;
Step 6: adopt surface treatment intaglio plate printing machine to carry out stamp to above-mentioned through the coating fabric treated, surface treatment intaglio plate printing machine flower version adopts laser engraving round metal version, several 100 orders of mesh order/CM
2, 100 microns of carving depths; The dynamo-electric heating power of said surface treatment intaglio plate stamp guarantees that at 50KW oven temperature is controlled at 150 ℃; The used concentrator of this stamp process is added with the microcapsules sensitizing powder; And it is abundant with the polyurethane resin dissolving; It is 40 parts polyurethane, 15 parts microcapsules sensitizing powder, 10 parts dimethylformaldehyde amine, 30 parts butanone, 4 parts curing agent, 2 parts catalyst, 6 parts slipping agent that this concentrator comprises quality successively; This concentrator adds successively by the said components order and stirs, and institute's employing mixer rotating speed is 1200 rev/mins, and wherein concentrator viscosity is 500GPS/T; The starching amount is controlled at 20g/y, and concentrator supplies the stamp use after before following seal, will using the strainer filtering of 200 orders/c ㎡.
Step 7: the surface cure that above-mentioned fabric through stamp is carried out top layer is handled; Adopt 80 order net rollers; Blade thickness 1.0mm wherein; The starching amount is controlled at 20g/y, obtains finished product after forming protective layer, and this protective layer to comprise mass ratio respectively be 45% polyurethane, 45% butanone, 4% curing agent and 6% slipping agent.
Embodiment two: a kind of sensitization discoloration printed fabric production technology comprises the steps:
Step 1: prepare base cloth, promptly adopt the polyester cotton blending lining, through overflow dyeing, then process washing typing is carried out back arrangement stamp again and is handled the acquisition base cloth;
Step 2: the destarch boiling-off, promptly above-mentioned base cloth is carried out margin to seam and handle, then let it get into desizing machine and carry out the boiling-off pre-treatment;
Step 3: select overflow dyeing machine to dye according to fabric treated material in step 2;
Step 4: above-mentioned dyed polyester cotton blending lining is carried out the high-temperature shaping processing and adds the fluouine water extraction agent in baking oven; Consumption is 30g/l, and it is handled back drying degree and should be up to state standards: GB4745 " textile fabric-surperficial moisture resistance assay method--dip experiment method " GB is more than 4 grades; And the polyester cotton blending lining moves in baking oven and is 30 meters/minute of speed, and oven temperature is 180 ℃ simultaneously;
Step 5: carry out the coating processing to above-mentioned through the typing fabric treated, this coating is acrylic acid formicester resinous coat (being commonly called as AC glue), comprises the acrylic acid formicester coating adhesive of 89.3% mass ratio respectively, the toluene of the curing agent of 1.7% mass ratio and 9% mass ratio; It is last rubber coating that coating is handled the board that uses, and its floating coat cutter is controlled at 1.5mm deeply, and wet coating weight is controlled at 40g/m, and four joint oven temperatures are controlled at 100 ℃, 120 ℃, 140 ℃ and 140 ℃ respectively;
Step 6: adopt surface treatment intaglio plate printing machine to carry out stamp to above-mentioned through the coating fabric treated, surface treatment intaglio plate printing machine flower version adopts laser engraving round metal version, several 100 orders of mesh order/CM
2, 120 microns of carving depths; The dynamo-electric heating power of said surface treatment intaglio plate stamp guarantees that at 55KW oven temperature is controlled at 155 ℃; The used concentrator of this stamp process is added with the microcapsules sensitizing powder; And it is abundant with the polyurethane resin dissolving; It is 40 parts polyurethane, 15 parts microcapsules sensitizing powder, 10 parts dimethylformaldehyde amine, 30 parts butanone, 4 parts curing agent, 2 parts catalyst, 6 parts slipping agent that this concentrator comprises quality successively; This concentrator adds successively by the said components order and stirs, and institute's employing mixer rotating speed is 1200 rev/mins, and wherein concentrator viscosity is 1000GPS/T; The starching amount is controlled at 25g/y, and concentrator supplies the stamp use after before following seal, will using the strainer filtering of 200 orders/c ㎡.
Step 7: the surface cure that above-mentioned fabric through stamp is carried out top layer is handled; Adopt 80 order net rollers; Blade thickness 1.0mm wherein; The starching amount is controlled at 20g/y, obtains finished product after forming protective layer, and this protective layer to comprise mass ratio respectively be 45% polyurethane, 45% butanone, 4% curing agent and 6% slipping agent.
Embodiment three: a kind of sensitization discoloration printed fabric production technology comprises the steps:
Step 1: prepare base cloth, promptly adopt the polyester cotton blending lining, through overflow dyeing, then process washing typing is carried out back arrangement stamp again and is handled the acquisition base cloth;
Step 2: the destarch boiling-off, promptly above-mentioned base cloth is carried out margin to seam and handle, then let it get into desizing machine and carry out the boiling-off pre-treatment;
Step 3: select overflow dyeing machine to dye according to fabric treated material in step 2;
Step 4: above-mentioned dyed polyester cotton blending lining is carried out the high-temperature shaping processing and adds the fluouine water extraction agent in baking oven; Consumption is 30g/l, and it is handled back drying degree and should be up to state standards: GB4745 " textile fabric-surperficial moisture resistance assay method--dip experiment method " GB is more than 4 grades; And the polyester cotton blending lining moves in baking oven and is 30 meters/minute of speed, and oven temperature is 162 ℃ simultaneously;
Step 5: carry out the coating processing to above-mentioned through the typing fabric treated, this coating is acrylic acid formicester resinous coat (being commonly called as AC glue), comprises the acrylic acid formicester coating adhesive of 89.3% mass ratio respectively, the toluene of the curing agent of 1.7% mass ratio and 9% mass ratio; It is last rubber coating that coating is handled the board that uses, and its floating coat cutter is controlled at 1.5mm deeply, and wet coating weight is controlled at 37g/m, and four joint oven temperatures are controlled at 100 ℃, 120 ℃, 140 ℃ and 140 ℃ respectively;
Step 6: adopt surface treatment intaglio plate printing machine to carry out stamp to above-mentioned through the coating fabric treated, surface treatment intaglio plate printing machine flower version adopts laser engraving round metal version, several 100 orders of mesh order/CM
2, 110 microns of carving depths; The dynamo-electric heating power of said surface treatment intaglio plate stamp guarantees that at 53KW oven temperature is controlled at 152 ℃; The used concentrator of this stamp process is added with the microcapsules sensitizing powder; And it is abundant with the polyurethane resin dissolving; It is 40 parts polyurethane, 15 parts microcapsules sensitizing powder, 10 parts dimethylformaldehyde amine, 30 parts butanone, 4 parts curing agent, 2 parts catalyst, 6 parts slipping agent that this concentrator comprises quality successively; This concentrator adds successively by the said components order and stirs, and institute's employing mixer rotating speed is 1200 rev/mins, and wherein concentrator viscosity is 700GPS/T; The starching amount is controlled at 22g/y, and concentrator supplies the stamp use after before following seal, will using the strainer filtering of 200 orders/c ㎡.
Step 7: the surface cure that above-mentioned fabric through stamp is carried out top layer is handled; Adopt 80 order net rollers; Blade thickness 1.0mm wherein; The starching amount is controlled at 20g/y, obtains finished product after forming protective layer, and this protective layer to comprise mass ratio respectively be 45% polyurethane, 45% butanone, 4% curing agent and 6% slipping agent.
In addition, above-mentioned base cloth also can adopt polyester fabric to prepare base cloth, and other technologies are the same with the technology that the polyester-cotton blend lining adopts; Perhaps also can adopt polyamide fibre lining or bright and beautiful cotton blended spinning face fabric; Then adopt high temperature dye gigging dyeing; And the consumption that adds the fluouine water extraction agent when in baking oven, carrying out the high-temperature shaping processing then is 25g/l, and this moment, oven temperature should be 180 ℃, and other processing steps are identical with employing polyester-cotton blend lining.
In the technology that above-mentioned coating is handled; Also can adopt polyurethane resin pearly-lustre mill base coating (being commonly called as the PU coloring agent); It is 58% polyurethane, 16 % butanone, 2 % curing agent, 1% catalyst, 3% slipping agent, 15% mill base and 5% pearl essence that this polyurethane resin pearly-lustre mill base coating comprises mass ratio respectively, and other processing steps are identical with employing acrylic acid formicester resinous coat.
Of the present invention focusing on; Through to this sensitization discoloration printed fabric controlling of production process and raw-material selection; And the photochromic pigment that adopts special microcapsules coating technology to process; And be printed on fabric face through the coating of special technology allotment, make that the sensitization discoloration fabric quality that the present invention produced is really up to the mark.The printed fabric that this technology of while is produced is applicable to the umbrella and the clothes of novel fashion; And it is again after the solar radiation of outdoor conditions; Obvious change can take place in pattern color, waits to get back to indoor back color and can be returned to original effect again, has good sensitization discoloration effect.Therefore this production technology obtained printed fabric function and quality tool are good.
In addition, in this printed fabric technology, adopt international advanced surface treatment intaglio plate transfer apparatus to produce; Has environmental protection, low power consuming, without sewage discharge; The photographic printing lining can be used for high-grade sunshade and garment material, and its distinctive color changeable effect has boundless market value.
The above; It only is preferred embodiment of the present invention; Be not that technical scope of the present invention is done any restriction, so every foundation technical spirit of the present invention all still belongs in the scope of technical scheme of the present invention any trickle modification, equivalent variations and modification that above embodiment did.
Claims (10)
1. sensitization discoloration printed fabric production technology, it is characterized in that: this production technology comprises the steps:
Step 1: prepare base cloth, promptly adopt polyester fabric or polyester cotton blending lining, through overflow dyeing, then process washing typing is carried out back arrangement stamp again and is handled the acquisition base cloth;
Step 2: the destarch boiling-off, promptly above-mentioned base cloth is carried out margin to seam and handle, then let it get into desizing machine and carry out the boiling-off pre-treatment;
Step 3: dye according to fabric treated material selective staining equipment in step 2;
Step 4: above-mentioned dyed polyester fabric or polyester cotton blending lining are carried out the high-temperature shaping processing and add fluorocarbon resin in baking oven, oven temperature was 140～180 ℃ during this typing was handled;
Step 5: carry out the coating processing to above-mentioned through the typing fabric treated, this coating is an acrylic acid formicester resinous coat; It is last rubber coating that coating is handled the board that uses, and its floating coat cutter is controlled at 1.5mm deeply, and wet coating weight is controlled at 35～40g/m, and four joint oven temperatures are controlled at 100 ℃, 120 ℃, 140 ℃ and 140 ℃ respectively;
Step 6: adopt surface treatment intaglio plate printing machine to carry out stamp to above-mentioned through the coating fabric treated, surface treatment intaglio plate printing machine flower version adopts laser engraving round metal version, several 100 orders of mesh order/CM
2, between 100～120 microns of the carving depths; Its concentrator that adopts is added with the microcapsules sensitizing powder, and abundant with the polyurethane resin dissolving;
Step 7: the surface cure that above-mentioned fabric through stamp is carried out top layer is handled, and obtains finished product behind the formation protective layer.
2. sensitization discoloration printed fabric production technology according to claim 1 is characterized in that: institute's fluorocarbon resin was the fluouine water extraction agent during said step 4 high-temperature shaping was handled, and consumption is 30g/l.
3. sensitization discoloration printed fabric production technology according to claim 1; It is characterized in that: adopt polyamide fibre lining or bright and beautiful cotton blended spinning face fabric in baking oven, to carry out high-temperature shaping processing and the agent of interpolation fluouine water extraction in the said step 4; Consumption is 25g/l; Oven temperature was 180 ℃ during this typing was handled, and the lining translational speed is 30 meters/minute.
4. sensitization discoloration printed fabric production technology according to claim 1; It is characterized in that: above-mentioned steps 5 said acrylic acid formicester resinous coats comprise the acrylic acid formicester coating adhesive of 89.3% mass ratio, the toluene of the curing agent of 1.7% mass ratio and 9% mass ratio respectively.
5. sensitization discoloration printed fabric production technology according to claim 1 is characterized in that: above-mentioned steps 5 said coatings are polyurethane resin pearly-lustre mill base coating.
6. sensitization discoloration printed fabric production technology according to claim 5 is characterized in that: it is 58% polyurethane, 16 % butanone, 2 % curing agent, 1% catalyst, 3% slipping agent, 15% mill base and 5% pearl essence that said polyurethane resin pearly-lustre mill base coating comprises mass ratio respectively.
7. sensitization discoloration printed fabric production technology according to claim 1 is characterized in that: during stamp was handled in the above-mentioned steps 6, the dynamo-electric heating power of said surface treatment intaglio plate stamp guaranteed that at 50～55KW oven temperature is controlled between 150 ℃～155 ℃.
8. sensitization discoloration printed fabric production technology according to claim 1; It is characterized in that: the concentrator viscosity that adopts is 500～1000GPS/T in the above-mentioned steps 6 stamp processes; The starching amount is controlled at 20～25g/y, and concentrator supplies the stamp use after before following seal, will using the strainer filtering of 200 orders/c ㎡.
9. according to claim 1 or 8 described sensitization discoloration printed fabric production technologies; It is characterized in that: it is 40 parts polyurethane, 15 parts microcapsules sensitizing powder, 10 parts dimethylformaldehyde amine, 30 parts butanone, 4 parts curing agent, 2 parts catalyst, 6 parts slipping agent that said concentrator comprises quality successively; This concentrator adds successively by the said components order and stirs, and institute's employing mixer rotating speed is 1200 rev/mins.
10. sensitization discoloration printed fabric production technology according to claim 1; It is characterized in that: during the surface cure of said step 7 is handled; Adopt 80 order net rollers; Blade thickness 1.0mm wherein, the starching amount is controlled at 20g/y, and said protective layer to comprise mass ratio respectively be 45% polyurethane, 45% butanone, 4% curing agent and 6% slipping agent.