CN102505460A - 一种载银抗菌剑麻纤维的制备方法 - Google Patents

一种载银抗菌剑麻纤维的制备方法 Download PDF

Info

Publication number
CN102505460A
CN102505460A CN2011102963842A CN201110296384A CN102505460A CN 102505460 A CN102505460 A CN 102505460A CN 2011102963842 A CN2011102963842 A CN 2011102963842A CN 201110296384 A CN201110296384 A CN 201110296384A CN 102505460 A CN102505460 A CN 102505460A
Authority
CN
China
Prior art keywords
fibers
sisal fibers
sisal
sisal fiber
drying
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011102963842A
Other languages
English (en)
Other versions
CN102505460B (zh
Inventor
刘峥
马肃
袁帅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG BOQIANG MACHINERY PARTS MANUFACTURING Co.,Ltd.
Original Assignee
Guilin University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guilin University of Technology filed Critical Guilin University of Technology
Priority to CN 201110296384 priority Critical patent/CN102505460B/zh
Publication of CN102505460A publication Critical patent/CN102505460A/zh
Application granted granted Critical
Publication of CN102505460B publication Critical patent/CN102505460B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种载银抗菌剑麻纤维的制备方法。将0.4-0.6g剑麻纤维用洗结精浸泡2-3小时，然后手搓至干净，再用蒸馏水洗涤，烘干备用；将烘干的剑麻纤维浸泡于重量分数为2％的氢氧化钠溶液中8小时，然后洗涤至中性，烘干备用；制得的剑麻纤维置于索氏提取器中提取24小时，提取液为体积比1∶1的无水乙醇和分析纯环己烷的混合液，烘干备用；制得的剑麻纤维放入35-45mL摩尔浓度为10mmol/L硝酸银溶液中，将其置于波长为253.9nm，功率为20W的紫外灯下55-65min，然后将剑麻纤维用蒸馏水洗涤干净，置于50℃恒温干燥箱内干燥即可制得抗菌剑麻纤维。本发明具有无毒、高效抗菌性；选择紫外光照射还原的方法，具有还原效率高、常温可进行反应的优点。

Description

一种载银抗菌剑麻纤维的制备方法
技术领域
本发明涉及非金属材料化学镀领域，特别是一种载银抗菌剑麻纤维的制备方法。
背景技术
剑麻，作为一种常见的龙舌兰属植物，是一类多年生、肉质、旱生的草本植物，主要从叶鞘中获取纤维。剑麻是当今世界用量最大，范围最广的一种硬质纤维，具有洁白、质地坚韧(拉力强)、富于弹性、耐海水浸、耐摩擦、不易碎断，且胶质少，不易打滑等特性，是生产硬质纤维的主要经济作物。近年来，剑麻(SF)作为一种原生态的纤维，具有来源广、经济、可再生等等优点，倍受企业、科研等各个领域的重视与关注。传统上，剑麻纤维主要是制成白棕绳，应用于工矿、电力、冶金、运输、农渔、森工、航海等方面。剑麻纤维的经济效益主要是通过发展深加工、增加产品附加值来体现，因此剑麻纤维的功能化研究具有重要的社会和经济意义。研究和开发新的抗菌纤维是功能材料领域中最为重要的课题，不断开发剑麻纤维新产品，提高其附值，是剑麻纤维研究的发展方向，而剑麻基抗菌纤维的研究，为剑麻纤维功能化开辟了一个新的途径。
发明内容
本发明的目的是提供一种载银抗菌剑麻纤维的制备方法。
具体步骤为：
(1)将0.4-0.6g剑麻纤维用洗结精浸泡2-3小时，然后稍微手搓至干净，再用蒸馏水洗涤，以除去剑麻表面的杂质烘干备用；
(2)将步骤(1)制得的剑麻纤维浸泡于重量分数为2％的氢氧化钠溶液中8小时，然后洗涤至中性，以除去剑麻纤维中的木质素，果胶烘干备用；
(3)将步骤(2)制得的剑麻纤维置于索氏提取器中提取24小时，提取液为体积比1∶1的无水乙醇和分析纯环己烷的混合液，以除去剑麻纤维中的果胶，烘干备用；
(4)将步骤(3)制得的剑麻纤维放入35-45mL摩尔浓度为10mmol/L硝酸银溶液中，将其置于波长为253.9nm，功率为20W的紫外灯下55-65min，然后将剑麻纤维用蒸馏水洗涤干净，置于50℃恒温干燥箱内干燥即可制得抗菌剑麻纤维。
利用扫描电镜对载银剑麻纤维进行形貌表征，可以明显看出存在的粒子以纳米级散布在剑麻纤维表面，银颗粒没有发生团聚。利用EDS对剑麻纤维表面存在的粒子进行元素分析，从而确定了纳米级别的粒子为银，并且是仅存在C、H、Ag三种元素。利用红外光谱测试仪对其进行测试分析，结果表明银主要依靠的是非化学键与剑麻纤维结合的。
本发明的优点为：
一、选择银作为抗菌剂，具有高效抗菌性，另外具有无毒等环境友好的优点；选择紫外光照射还原的方法，具有还原效率高、常温可进行反应等优点。
二、实施化学镀的基体-剑麻纤维含有亲水基团，即吸水性，使硝酸银溶液很好的被吸附在剑麻纤维表面以及结构空间内，从而使制得的银粒子很好的负载在剑麻纤维表面。
三、将抗菌剑麻纤维浸泡到水溶液中，抗菌剂在一定的时间内，能够持久的，稳定的释放出来，保证了抗菌的活性。
具体实施方式
实施例：
(1)将0.5g剪好的剑麻纤维用立白洗结精浸泡2小时，然后稍微手搓至干净，再用蒸馏水洗涤，以除去剑麻表面的杂质烘干备用；
(2)将步骤(1)制得的剑麻纤维浸泡于重量分数为2％的氢氧化钠溶液中8小时，然后洗涤至中性，以除去剑麻纤维中的木质素，果胶烘干备用；
(3)将步骤(2)制得的剑麻纤维置于索氏提取器中提取24小时，提取液为体积比1∶1的无水乙醇和分析纯环己烷的混合液，以除去剑麻纤维中的果胶，烘干备用；
(4)将步骤(3)制得的剑麻纤维放入40mL摩尔浓度为10mmol/L硝酸银溶液中，将其置于波长为253.9nm，功率为20W的紫外灯下60min，然后将剑麻纤维用蒸馏水洗涤干净，置于50℃恒温干燥箱内干燥即可制得抗菌剑麻纤维。

Claims (1)

1.一种载银抗菌剑麻纤维的制备方法，其特征在于具体步骤为：
(1)将0.4-0.6g剑麻纤维用洗结精浸泡2-3小时，然后手搓至干净，再用蒸馏水洗涤，烘干备用；
(2)将步骤(1)制得的剑麻纤维浸泡于重量分数为2％的氢氧化钠溶液中8小时，然后洗涤至中性，烘干备用；
(3)将步骤(2)制得的剑麻纤维置于索氏提取器中提取24小时，提取液为体积比1∶1的无水乙醇和分析纯环己烷的混合液，烘干备用；
(4)将步骤(3)制得的剑麻纤维放入35-45mL摩尔浓度为10mmol/L硝酸银溶液中，将其置于波长为253.9nm，功率为20W的紫外灯下55-65min，然后将剑麻纤维用蒸馏水洗涤干净，置于50℃恒温干燥箱内干燥即可制得抗菌剑麻纤维。
CN 201110296384 2011-09-30 2011-09-30 一种载银抗菌剑麻纤维的制备方法 Active CN102505460B (zh)